CN1594730A - 一种抗菌钞票纸生产工艺及其钞票纸 - Google Patents
一种抗菌钞票纸生产工艺及其钞票纸 Download PDFInfo
- Publication number
- CN1594730A CN1594730A CN 03150917 CN03150917A CN1594730A CN 1594730 A CN1594730 A CN 1594730A CN 03150917 CN03150917 CN 03150917 CN 03150917 A CN03150917 A CN 03150917A CN 1594730 A CN1594730 A CN 1594730A
- Authority
- CN
- China
- Prior art keywords
- paper
- bank
- fiber
- note paper
- antibiotic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种抗菌钞票纸生产工艺及其钞票纸,生产工艺中,在钞票纸主料纤维中加入少许瑞香狼毒纤维并加以均匀混合;将均匀混合后的纤维用精浆机进行精浆;对精浆后的混合浆液中加入化学助剂、填料、辅料进行配浆,得到纸浆;将配浆后得到的纸浆送到造纸机进行抄造;将抄造后所得到的湿纸进行干燥;对上述纸张进行表面施胶;对表面施胶后的纸张进行再次干燥,得到钞票纸。依上述工艺所得到的钞票纸因此含有瑞香狼毒纤维,由于瑞香狼毒本身含有天然抗菌药物成分,使得含有瑞香狼毒成分的钞票纸也具有天然抗菌作用,使用该种钞票纸所制得的纸张货币在流通过程中携带的一些病毒被抑杀,减少某此疾病的传播机会。
Description
技术领域
本发明涉及制作货币或类似物用的纸张,更具体地指一种抗菌钞票纸生产工艺及其钞票纸。
背景技术
纸张货币,是人人所熟知、且为常用而必不可少的一种贷币形式。纸张货币具有广泛的流通性,在流通过程中,避免不了伴随着各种病菌的传播,货币上所携带的病菌的机率以及病菌种类可能是最多的,所以大多数使用者在与货币、纸张货币直接接触后,通常均会以洗手的方式来避免病菌的传播。从2003年部分国家流行的非典型肺炎后,人们对如何避免在货币的流通中传播疾病的问题更加关注,期待能有一种本身就具有抗菌性能的纸张货币出现,以使一些病毒在流通过程中就被抑杀。
发明内容
针对上述问题,本发明的目的是提供一种抗菌钞票纸生产工艺及其钞票纸,当用该纸张制作货币后,可将一些病毒在随着货币的流通过程中就被抑杀。
为了实现上述目的,本发明采用如下技术方案:
一种抗菌钞票纸生产工艺,包括以下步骤,
a,在钞票纸主料纤维中加入少许瑞香狼毒纤维并加以均匀混合;
b,将均匀混合后的纤维用精浆机进行精浆;
c,对精浆后的混合浆液中加入化学助剂、填料、辅料进行配浆,得到纸浆;
d,将配浆后得到的纸浆送到造纸机进行抄造;
e,将抄造后所得到的湿纸进行干燥;
f,对上述纸张进行表面施胶;
g,对表面施胶后的纸张进行再次干燥,得到钞票纸。
一种抗菌钞票纸,该钞票纸的主要成份包括钞票纸主料纤维、瑞香狼毒纤维、化学助剂、填料、辅料,其中,瑞香狼毒纤维与钞票纸主料纤维按所占质量比为0.5-15比99.5-85进行混合,化学助剂、填料、辅料按适量加入其中。
在本发明的抗菌钞票纸生产工艺中,在钞票纸主料纤维中加入少许瑞香狼毒纤维并加以均匀混合,此后按传统的工艺将均匀混合后的纤维用精浆机进行精浆;对精浆后的混合浆液中加入化学助剂、填料、辅料进行配浆,得到纸浆;将配浆后得到的纸浆送到造纸机进行抄造;将抄造后所得到的湿纸进行干燥;对上述纸张进行表面施胶;对表面施胶后的纸张进行再次干燥,得到钞票纸。依上述工艺所得到的钞票纸的主要成份包括钞票纸主料纤维、瑞香狼毒纤维、化学助剂、填料、辅料,其中,瑞香狼毒纤维与钞票纸主料纤维按所占质量比为0.5-15比99.5-85进行混合,化学助剂、填料、辅料按适量加入其中。由于瑞香狼毒本身含有天然抗菌药物成分,使得含有瑞香狼毒成份的钞票纸也具有天然抗菌作用,使用该种钞票纸所制得的纸张货币在流通过程中携带的一些病毒被抑杀,减少某此疾病的传播机会。
具体实施方式
本发明的抗菌钞票纸生产工艺以下步骤:
步骤a,在钞票纸主料纤维中加入少许瑞香狼毒纤维并加以均匀混合,钞票纸主料纤维为棉纤维、木纤维、麻纤维中的任何一种,或为三者的混合。
在瑞香狼毒纤维与钞票纸主料纤维进行混合时,将瑞香狼毒纤维与钞票纸主料纤维所占质量比控制在0.5-15比99.5-85。
瑞香狼毒是一种草本类植物,瑞香狼毒以及以其为原料制作的纤维含有天然抗菌药物成分,也就是说,抗菌化学成分是瑞香狼毒本身含有的,处理加工出的纤维含有相应的化学成分。
步骤b,将均匀混合后的纤维用精浆机进行精浆。
步骤c,对精浆后的混合浆液中加入化学助剂、填料、辅料进行配浆,化学助剂为树脂或类似物,如脲醛树脂、三聚氰胺甲醛树脂。
填料为钛白粉、高岭土或类似物。
辅料为助留剂、助滤剂、消泡剂或类似物。
通过这一步骤即得到纸浆。
步骤d,将配浆后得到的纸浆送到造纸机进行抄造。
当然在生产过程中,还可以添加一些其他至少有一种有机合成抗菌材料、无机抗菌材料或其他抗菌材料,如在步骤c的精浆过程中或步骤d过程中,可添加载银二氧化钛或类似抗菌物,以使抄造后所得到的湿纸进一步增加抗菌作用。
步骤e,将抄造后所得到的湿纸进行干燥。
步骤f,对上述纸张进行表面施胶,在对干燥后的纸张进行表面施胶过程中,在胶料中添加2.4.4’-三氯-2’-羟基二苯醚、4-氯-3,5-二甲基苯酚或类似物。
步骤g,对表面施胶后的纸张进行再次干燥,得到钞票纸。
实施例1:
在精浆工序步骤前,向浆池中添加瑞香狼毒纤维,控制瑞香狼毒纤维与主料纤维的质量比例为15比85,混合均匀后开始精浆,经过配浆等工序后,浆料被输送到造纸机进行抄造,制造抗菌纸张。
实施例2:
在精浆工序步骤前,向浆池中添加瑞香狼毒纤维,控制瑞香狠毒纤维与主料纤维的质量比例为0.5比99.5,混合均匀后开始精浆,精浆后,在配浆工序中按3比97的绝干比例,向浆料中添加载银二氧化钛粉体,混合均匀的浆料最终被输送到造纸机进行抄造,制造抗菌纸张。
实施例3:
将瑞香狼毒纤维和主料纤维分别打浆后,按2比98的绝干质量比混合,再添加0.5%的载银二氧化钛粉体,混合均匀后的浆被输送到造纸机上进行纸张抄造,抄造的纸张进一步经过表面施胶处理,在施胶过程中,在胶料中添加2.4.4’-三氯-2’-羟基二苯醚或2.4.4’-三氯-2’-羟基二苯醚。2.4.4’-三氯-2’-羟基二苯醚或2.4.4’-三氯-2’-羟基二苯醚占胶料绝干质量控制在0.3%。
依上述生产工艺所得到的抗菌钞票纸的主要成份包括钞票纸主料纤维、瑞香狼毒纤维、化学助剂、填料、辅料,其中,瑞香狼毒纤维与钞票纸主料纤维按所占质量比为0.5-15比99.5-85进行混合,化学助剂、填料、辅料按适量加入其中。
所述的钞票纸主料纤维为棉纤维、木纤维、麻纤维中的任何一种,或为三者的混合。
所述的钞票纸中进一步包括载银二氧化钛或类似抗菌物。
所述的钞票纸表面涂覆有2.4.4’-三氯-2’-羟基二苯醚、4-氯-3,5-二甲基苯酚或类似物。
Claims (10)
1、一种抗菌钞票纸生产工艺,其特征在于,该生产工艺包括以下步骤:
a,在钞票纸主料纤维中加入少许瑞香狼毒纤维并加以均匀混合;
b,将均匀混合后的纤维用精浆机进行精浆;
c,对精浆后的混合浆液中加入化学助剂、填料、辅料进行配浆,得到纸浆;
d,将配浆后得到的纸浆送到造纸机进行抄造;
e,将抄造后所得到的湿纸进行干燥;
f,对上述纸张进行表面施胶;
g,对表面施胶后的纸张进行再次干燥,得到钞票纸。
2、如权利要求1所述的抗菌钞票纸生产工艺,其特征在于:
所述的步骤a中,将瑞香狼毒纤维加入钞票纸主料纤维中混合时,所述的瑞香狼毒纤维与钞票纸主料纤维所占质量比为0.5-15比99.5-85。
3、如权利要求1所述的抗菌钞票纸生产工艺,其特征在于:
所述的步骤a中,钞票纸主料纤维为棉纤维、木纤维、麻纤维中的任何一种,或为三者的混合。
4、如权利要求1所述的抗菌钞票纸生产工艺,其特征在于:
所述的步骤c中,
所加入的化学助剂为树脂或类似物;
所加入的填料为钛白粉、高岭土或类似物;
所加入的辅料为助留剂、助滤剂、消泡剂或类似物。
5、如权利要求1所述的抗菌钞票纸生产工艺,其特征在于:
在所述的步骤c的精浆过程中或所述的步骤d过程中,可添加载银二氧化钛或类似抗菌物。
6、如权利要求1-5任一项所述的抗菌钞票纸生产工艺,其特征在于:
所述的步骤f中,在对干燥后的纸张进行表面施胶过程中,在胶料中添加2.4.4’-三氯-2’-羟基二苯醚、4-氯-3,5-二甲基苯酚或类似物。
7、一种抗菌钞票纸,其特征在于,该钞票纸的主要成份包括钞票纸主料纤维、瑞香狼毒纤维、化学助剂、填料、辅料,其中,瑞香狼毒纤维与钞票纸主料纤维按所占质量比为0.5-15比99.5-85进行混合,化学助剂、填料、辅料按适量加入其中。
8、如权利要求7所述的抗菌钞票纸,其特征在于:所述的钞票纸主料纤维为棉纤维、木纤维、麻纤维中的任何一种,或为三者的混合。
9、如权利要求7所述的抗菌钞票纸,其特征在于:所述的钞票纸中进一步包括载银二氧化钛或类似抗菌物。
10、如权利要求7所述的抗菌钞票纸,其特征在于:所述的钞票纸表面进一步涂覆有2.4.4’-三氯-2’-羟基二苯醚、4-氯-3,5-二甲基苯酚或类似物。