CN1569712A - Formulation for preparing high-class polyether bottle using varicolored cullet - Google Patents
Formulation for preparing high-class polyether bottle using varicolored cullet Download PDFInfo
- Publication number
- CN1569712A CN1569712A CN 03132532 CN03132532A CN1569712A CN 1569712 A CN1569712 A CN 1569712A CN 03132532 CN03132532 CN 03132532 CN 03132532 A CN03132532 A CN 03132532A CN 1569712 A CN1569712 A CN 1569712A
- Authority
- CN
- China
- Prior art keywords
- cullet
- bottle
- glass cullet
- varicolored
- formulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a formulation for preparing high-class polyether bottle using varicolored cullet, wherein each 1000Kg of cullet is added by sodium carbonate 8.4-10Kg, sodium nitrate 9-15Kg, fluorite 3-5Kg, borax 5-7Kg, sodium sulfate 1.5-2.5Kg, zinc selenious acid 0.09-0.13Kg, cobalt oxide 0.0013-0.003Kg.
Description
(1), affiliated field
What the present invention relates to is a kind of glass.Specifically a kind of white glass goods that utilize waste and old glass cullet to produce.
(2), background technology
Utilize waste and old glass cullet to produce glasswork and not only can reduce the production cost of glasswork, and help protecting environment.But because the color more complicated of waste and old glass cullet, most of waste and old glass cullet have colors such as green, yellow.If these colors are not eliminated, will influence the quality of product.Not we can say the color in the waste and old glass cullet is eliminated, just can not produce the qualified packing bottle that is used for packings such as drinks, beverage class.
Used waste and old glass cullet decoloring method mainly is the chemical decolorization method in production practice at present.Promptly in waste and old glass cullet, add a large amount of chemicals such as yellow soda ash.Cost height not only, and cause new environmental pollution easily.
Utilize the fragility of the glasswork that waste and old glass cullet produce higher in addition merely, intensity is low.So produce in the prescription of glasswork at the waste and old glass cullet of existing usefulness, the content of waste and old glass cullet is all below 70%.This also is to cause the product cost major reason for higher.
(3), summary of the invention
The object of the present invention is to provide a kind of utilization ratio height, good product quality, production cost of waste and old glass cullet low, the variegated glass cullet of non-environmental-pollution produce the prescription of high-grade polyether bottle.
The object of the present invention is achieved like this: be added with yellow soda ash 8.4-10Kg, SODIUMNITRATE 9-15Kg, fluorite 3-5Kg, borax 5-7Kg, sodium sulfate 1.5-2.5Kg, zincium selenious acid 0.09-0.13Kg, cobalt oxide 0.0013-0.003Kg in every 1000Kg glass cullet.
The present invention be a kind of be the auxilliary prescription of producing high-grade polyether bottle with variegated glass cullet based on physical method, chemical process.Utilize the oxygenizement of chemical decolorization agent, the yellow that glass is infected with by organism is eliminated, and make the very competent ferrous ion of glass coloring is changed into the extremely weak ferric ion of tinting strength, so that the physical decolorization agent further made in the color and, increase the transparence of glass near colourless.Zincium selenious acid among the present invention can produce purple in glass, the green neutralization of this purple and waste and old glass cullet; And cobalt oxide can produce blueness in glass, the yellow neutralization of this blueness and waste and old glass cullet, thus make glass reach water white transparency.
Compositions such as fluorite, borax have been added among the present invention, can improve the fragility of glass, improve glass intensity, the content that makes waste and old glass cullet is under the situation more than 97%, can produce food product pack such as can being widely used in drinks, beverage class, various physicochemical properties such as physical strength, stress, hardness, density, chemical stability reach the white bottle of national light industry standard-required.Certain prescription of the present invention also can be produced other glasswork.
The present invention is based on physical decolorization, and the consumption of chemical feedstocks is extremely low, and the content of waste and old glass cullet wherein can reach more than 97%, so that the production cost of glass reduces greatly, the reduction amplitude can reach more than 30%.The present invention simultaneously can not produce secondary environmental pollution.
(4), specific embodiments
For example the present invention is done in more detail below and describes:
With yellow soda ash 8.4-10Kg, SODIUMNITRATE 9-15Kg, fluorite 3-5Kg, borax 5-7Kg, sodium sulfate 1.5-2.5Kg, zincium selenious acid 0.09-0.13Kg, cobalt oxide 0.0013-0.003Kg, add in the 1000Kg glass cullet complete processing to and make vial according to vial.
With yellow soda ash 8.4-9Kg, SODIUMNITRATE 12-15Kg, fluorite 3-4Kg, borax 5-6Kg, sodium sulfate 1.5-2.0Kg, zincium selenious acid 0.09-0.10Kg, cobalt oxide 0.0013-0.002Kg, add in the 1000Kg glass cullet complete processing to and make vial according to vial.
With yellow soda ash 8.4Kg, SODIUMNITRATE 12Kg, fluorite 3Kg, borax 5Kg, sodium sulfate 1.5Kg, zincium selenious acid 90g, cobalt oxide 1.3g, add in the 1000Kg glass cullet complete processing to and make vial according to vial.
Claims (2)
1, a kind of variegated glass cullet are produced the prescription of high-grade polyether bottle, it is characterized in that: be added with yellow soda ash 8.4-10Kg, SODIUMNITRATE 9-15Kg, fluorite 3-5Kg, borax 5-7Kg, sodium sulfate 1.5-2.5Kg, zincium selenious acid 0.09-0.13Kg, cobalt oxide 0.0013-0.003Kg in every 1000Kg glass cullet.
2, variegated glass cullet according to claim 1 are produced the prescription of high-grade polyether bottle, it is characterized in that: be added with yellow soda ash 8.4-9Kg, SODIUMNITRATE 12-15Kg, fluorite 3-4Kg, borax 5-6Kg, sodium sulfate 1.5-2.0Kg, zincium selenious acid 0.09-0.10Kg, cobalt oxide 0.0013-0.002Kg in every 1000Kg glass cullet.