CN1566008A

CN1566008A - Glaze material for color permeated polishing tile and application method thereof

Info

Publication number: CN1566008A
Application number: CN 03126848
Authority: CN
Inventors: 毛海燕
Original assignee: Individual
Current assignee: Individual
Priority date: 2003-06-16
Filing date: 2003-06-16
Publication date: 2005-01-19

Abstract

The invention discloses a glaze material for color permeated polishing tile and application method thereof, wherein the glaze is made from glaze A and B through reaction, wherein glaze A comprises (by weight percentage) nickel acetate 20-50g, sodium citrate 30-60g, water 80-120g, methyl 1.5-3.5g, ethylene glycol 6-15g, while glaze B comprises (by weight percentage) nickel acetate 10-30g, sodium citrate 10-30g, water 80-120g, methyl 1.5-3.5g, ethylene glycol 6-15g.

Description

A kind ofly ooze colored polished tile with glaze and using method

Technical field

The present invention relates to ooze glaze and the using method that colored polished tile is used.

Background technology

The glaze of prior art is produced oozes that colored polished tile color is dull, texture is more flat, and it is abundant that expressive force is owed; As application number be 99113799, the applying date is that June 21, denomination of invention in 1999 are the patent application of polished fully-vitrified ceramic tile; it forms (weight percentage) by following prescription: clay 30%～35%; feldspar 45%～50%; agalmatolite 10%～15%; magnesia mud 3%～5%; kaolin 5%～10%, color stable agent 0.2%～1%, chromogenic reagent 0.5%～5%.Above-mentioned patent has defective as mentioned above equally.

Summary of the invention

The object of the present invention is to provide a kind of make ooze that colored polished tile texture is fine and smooth more, color enrich more apparent mass good ooze the glaze that colored polished tile is used.

Another object of the present invention also is to provide the using method of above-mentioned glaze.

The present invention realizes its purpose like this: this oozes the glaze that colored polished tile is used, and is to be base-material with mantoquita, nickel salt, adds Trisodium Citrate or ammonium citrate, adopts A, the reaction of B glaze to form, wherein

A glaze (by weight proportion): nickelous acetate 20-50 gram Trisodium Citrate 30-60 gram water 80-120 gram methyl 1.5-3.5 gram ethylene glycol 6-15 gram

B glaze (by weight proportion): nickelous acetate 10-30 gram Trisodium Citrate 10-30 gram water 80-120 gram methyl 1.5-3.5 gram ethylene glycol 6-15 gram

The using method of above-mentioned glaze is:

(1) with nickelous acetate, the Trisodium Citrate water dissolution of A glaze, the dissolving of methyl spent glycol mixes stirring with above-mentioned solution;

(2) with the A glaze with lines net stamp on the brick body;

(3) with nickelous acetate, the Trisodium Citrate water dissolution of B glaze, the dissolving of methyl spent glycol mixes stirring with above-mentioned solution;

(4) get above-mentioned B glaze with big area net stamp on the brick body;

(5) water spray gets final product

The present invention compared with prior art, pattern permeating tile texture in the past resembles " freehand brushwork in traditional Chinese painting ", then become combining of " traditional Chinese painting " and " freehand brushwork in traditional Chinese painting " with the pattern permeating tile of " multicolored border glaze " of the present invention glaze manufacturing, how its meaning not only has been a kind of technique of expression, and being that the texture that embodies by this gimmick is fine and smooth more, color is more rich and varied; It is good to experiment showed, that product of the present invention has an apparent mass, rich color, advantage such as pure.

Embodiment

Of the present inventionly ooze glaze that colored polished tile uses to have adopted mantoquita, nickel salt be base-material, add Trisodium Citrate or ammonium citrate, adopt A, the reaction of B glaze to form, A glaze wherein: nickelous acetate 30 gram Trisodium Citrates 45 gram water 100 gram methyl 2.5 gram ethylene glycol 15 grams, with nickelous acetate, Trisodium Citrate water dissolution, the methyl spent glycol dissolves and two solution is mixed stirring; With mixed A glaze with lines net stamp on the brick body; Get the B glaze: nickelous acetate 20 gram Trisodium Citrates 20 gram water 100 gram methyl 2.5 gram ethylene glycol 15 grams, adopt with the same mode of A glaze and mix the B glaze, get above-mentioned mixed B glaze with big area net stamp on the brick body; Water spray 100 grams (with respect to the brick of 600mm * 600mm size) get final product.

The colored polished tile of oozing that adopts that above-mentioned glaze makes changes that the like product color is dull in the past, texture is more flat, the looks that expressive force owes to enrich, realized the big Face Changing of upgrading, its glaze can be made into that coffee is red, pink, pitch black waits until extraordinary intermingling flower colour glaze, is referred to as " multicolored border glaze ".

Claims

1, a kind ofly ooze colored polished tile glaze, it is characterized in that, it is to be base-material with mantoquita, nickel salt, adds Trisodium Citrate or ammonium citrate, adopts A, the reaction of B glaze to form, wherein

2. above-mentioned using method of oozing colored polished tile with glaze is characterized in that the using method of this glaze is:

(1) with nickelous acetate, the Trisodium Citrate water dissolution of A glaze, the dissolving of methyl spent glycol mixes stirring with two solution;

(2) with the A glaze with lines net stamp on the brick body;

(3) with nickelous acetate, the Trisodium Citrate water dissolution of B glaze, the dissolving of methyl spent glycol mixes stirring with two solution;

(4) get above-mentioned B glaze with big area net stamp on the brick body;

(5) water spray gets final product.