CN1560513A - Method for treating waste salt dregs containing cyanogen - Google Patents
Method for treating waste salt dregs containing cyanogen Download PDFInfo
- Publication number
- CN1560513A CN1560513A CNA2004100141063A CN200410014106A CN1560513A CN 1560513 A CN1560513 A CN 1560513A CN A2004100141063 A CNA2004100141063 A CN A2004100141063A CN 200410014106 A CN200410014106 A CN 200410014106A CN 1560513 A CN1560513 A CN 1560513A
- Authority
- CN
- China
- Prior art keywords
- waste salt
- cyanogen
- salt dregs
- methyl alcohol
- ethanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a processing method for cyanogens contained waste salt dredge, the process steps are: the cyanogens contained waste salt dredge is put into the drier to be heated; the heating temperature is controlled with 60-120deg.C, the carbinol and the alcohol volatilize from the dredge, the carbinol and the alcohol are reclaimed with high purity after beings cooled in the condenser; the cyanogens contained waste salt dredge without carbinol and alcohol is baked in oxygen condition, the oxide in the dredge is fully oxidized, the organic is oxidized or volatilized off, thus eliminates the cyanogens and organic in the salt dredge; the gas generated in the baking process is transmitted to the burning furnace, the temperature is not lower than 1100deg.C, thus the tail gas may accord the discharging standard.
Description
Technical field
The present invention relates to the processing method of industrial residue, specifically, relate to a kind of processing method that contains the cyanogen waste salt dregs, be mainly used in the processing that contains the cyanogen waste salt dregs that produces in the production processes such as chemical industry methyl cyanoacetate, ethyl cyanoacetate.
Background technology
In some chemical products production process of chemical industry, have to contain the generation of cyanogen waste salt dregs in a large number.Containing the cyanogen waste residue is high violent in toxicity, as not handling, the environment and the mankind is caused great harm.Generally adopt chemical oxidization method to containing the cyanogen waste residue at present, wet oxidation process (high-temperature pressurizing oxidizing process), high temperature incineration method are removed cyanogen and organic matter, remove cyanogen and shortcomings such as organic matter is not thorough, complicated operation, generation high concentration brine waste, processing cost height but exist.
In cyanoacetic acid fatty ester such as methyl cyanoacetate, ethyl cyanoacetate production, adopt methyl chloroacetate (ethyl chloroacetate) and solid sodium cyanide reaction especially, remove and generate product methyl cyanoacetate (ethyl cyanoacetate), also separate out the waste salt dregs solid sodium chloride.Also have Cymag, methyl alcohol (ethanol), organic matters such as methyl cyanoacetate (ethyl cyanoacetate) and byproduct of reaction on the waste salt dregs sodium chloride, thisly contain the cyanogen waste salt dregs always to contain the cyanogen amount be the 3-4g/Kg waste salt dregs, methyl alcohol (ethanol) content is 10-20%, organic matters content is 0.2-0.4%, owing to contain above-mentioned organic and inorganic toxic material, this solid waste is listed " national hazardous waste register " in.Contain the cyanogen waste salt dregs and need pass through except that after the harmless treatment operations such as cyanogen, organic matter removal, could be as the general industry waste treatment.
Existing processing method mainly contains following several: 1, adopt chemical oxidization method to handle, the shortcoming of this method is to need to consume a large amount of oxidants, and cost is higher, and organic removal rate is low, produces the high concentration salt-containing organic wastewater, needs further to remove organic matter; 2, wet oxidation process (high-temperature pressurizing Hydrolyze method) is handled, though this method can be removed cyanogen and organic matter more completely, energy consumption is big, and equipment requires and invests greatly, produces the high concentration brine waste simultaneously; 3, the high temperature incineration method is handled, do not produce though this method has the high concentration brine waste,, and contain a large amount of inflammable and explosive organic solvents because the salt slag melting point is lower, primary zone's difficult control of temperature, incomplete combustion, the cyanide clearance is low, and the fuse salt slag influences the normal use of incinerator simultaneously, because it is big to handle the tail gas air quantity, the secondary combustion chamber operating cost is high, and this method can only be used for the laboratory, industrial infeasible.Many producers just adopt the method for piling up, and human and environment are caused serious hidden danger.
Summary of the invention
The purpose of this invention is to provide a kind of cyanogen efficient height that removes, energy consumption is little, and the processing method that contains the cyanogen waste salt dregs that the discharging of tail gas is up to state standards.
The technical scheme that realizes above-mentioned purpose is: a kind of processing method that contains the cyanogen waste salt dregs, it is made of the following step: will contain in the cyanogen waste salt dregs adding drier and heat, heating and temperature control is at 60～120 ℃, methyl alcohol or ethanol volatilize from waste residue, methyl alcohol or alcohol gas reclaim and obtain highly purified methyl alcohol or ethanol after cooling off through condenser; With remove methyl alcohol or ethanol contain the cyanogen waste salt dregs under aerobic conditions, carry out in warm calcination, make the cyanide complete oxidation that contains in the cyanogen waste salt dregs, oxidation operation or volatilization, thereby remove cyanogen and organic matter in the salt slag; To contain gas that the cyanogen waste salt dregs produces and feed incinerator and burn in middle temperature calcination, incineration temperature is not less than 1100 ℃, makes tail gas reach discharge standard.
After adopting technique scheme, the present invention adopts low temperature to reclaim the processing method of solvent, middle temperature calcination, tail gas high temperature incineration, and low temperature reclaims solvent and obtains utilities such as highly purified methyl alcohol or ethanol, can produce certain economic benefits; Remove containing in the cyanogen waste salt dregs after the warm calcination of methyl alcohol or ethanol, cyanide complete oxidation wherein, remove cyanogen efficient height, after oxidation operation decomposition or the volatilization, also removed the organic matter that contains in the cyanogen waste salt dregs effectively, contain the calcination of cyanogen waste salt dregs after cooling obtains white solid, cyanogen and organic matter all do not detect, and show that cyanogen and organic clearance are all very high; The tail gas high temperature incineration can be eliminated and contain a certain amount of toxic and harmful that does not decompose fully that warm calcination produces in the cyanogen waste salt dregs, and tail gas is high altitude discharge after cooling off, and can reach environmental requirement.In a word, this method overcome in the high temperature incineration processing method remove that cyanogen efficient is low, temperature control is poor, energy consumption is big, dangerous, tail gas do not reach shortcomings such as national standard, waste residue after this method is handled not only meets the waste discharge standard, and investment and processing cost are low, are fit to industrialization and use.
Description of drawings
Fig. 1 contains the process chart of the processing method of cyanogen waste salt dregs for the present invention.
The specific embodiment
The present invention is further detailed explanation below in conjunction with drawings and Examples.
As shown in Figure 1, a kind of processing method that contains the cyanogen waste salt dregs, it is made of the following step:
A, recovery methyl alcohol or ethanol
For the cyanogen waste salt dregs that contains of producing the methyl cyanoacetate generation is to reclaim methyl alcohol, is to reclaim ethanol for the cyanogen waste salt dregs that contains of producing the ethyl cyanoacetate generation.
The cyanogen waste salt dregs that contains that produces in the production process is added in the continous way hollow blade drier, feed the heating agent heating in the chuck of drier, heating and temperature control is at 60～120 ℃, heating a period of time, methyl alcohol or ethanol volatilize from waste residue, methyl alcohol or alcohol gas reclaim and obtain highly purified methyl alcohol or ethanol after cooling off through condenser;
B, middle temperature calcination, aerobic removes cyanogen and organic matter
With remove methyl alcohol or ethanol contain the cyanogen waste salt dregs under aerobic conditions, add continuously reverberatory furnace or rotary kiln carry out in warm calcination, make the cyanide complete oxidation that contains in the cyanogen waste salt dregs, oxidation operation or volatilization, thereby remove cyanogen and organic matter in the salt slag; Calcination temperature is controlled between 500～800 ℃, and coefficient of excess air is controlled at 〉=and 1.2, the time of staying is 02～2 hour in the calcination process.Contain the calcination of cyanogen waste salt dregs after cooling obtains white solid, oxygen and organic matter all do not detect.
C, tail gas high-temp combustion
To contain gas that the cyanogen waste salt dregs produces and feed incinerator by air-introduced machine and burn in middle temperature calcination, incineration temperature is not less than 1100 ℃, and gas residence time is controlled at 〉=and 2 seconds, make tail gas reach discharge standard.Organic removal rate in the tail gas is greater than 99.9%, and tail gas is high altitude discharge after cooling off.
Embodiment one
The serialization process units handles that methyl cyanoacetate production produces contains the cyanogen waste salt dregs, presses the 250kg/h charging, contains and contains methyl alcohol 12% in the cyanogen waste salt dregs, and containing the cyanogen amount is the 3.6g/Kg slag, and content of organics is 0.2%.Adopt hollow paddle drier to reclaim methyl alcohol down at 70-90 ℃, the waste residue that removes behind the methyl alcohol adopts continous way reverberatory furnace aerobic calcination 1.0 hours down at 550 ℃, coefficient of excess air 1.0, contain the cyanogen amount and drop to the 0.012g/Kg slag, content of organics does not detect, but discharging salt slag contains 0.03% DIC, is light gray.
Embodiment two
Inlet amount, composition are with embodiment one, adopt hollow paddle drier to reclaim methyl alcohol down at 70-90 ℃, the waste residue that removes behind the methyl alcohol adopts continous way reverberatory furnace aerobic calcination 1.0 hours down at 600 ℃, coefficient of excess air 1.5, discharging salt slag is white in color, contain the cyanogen amount and drop to the 0.002g/Kg slag, content of organics does not detect.
Embodiment three
The serialization process units handles that ethyl cyanoacetate production produces contains the cyanogen waste salt dregs, presses the 250kg/h charging, contains and contains ethanol 12% in the cyanogen waste salt dregs, and containing the cyanogen amount is the 3.6g/Kg slag, and content of organics is 0.2%.Adopt down hollow paddle drier to reclaim ethanol at 70-90 ℃, the waste residue that removes behind the ethanol adopts continous way reverberatory furnace aerobic calcination 1.0 hours down at 650 ℃, and coefficient of excess air 1.5, discharging salt slag are white in color, and cyanogen and content of organics all do not detect.
Claims (4)
1, a kind of processing method that contains the cyanogen waste salt dregs, it is characterized in that: it is made of the following step:
A, recovery methyl alcohol or ethanol
The cyanogen waste salt dregs that contains that produces in the production process is added in the drier and heats, and heating and temperature control is at 60～120 ℃, and methyl alcohol or ethanol volatilize from waste residue, methyl alcohol or alcohol gas through the condenser cooling after, reclaim and obtain highly purified methyl alcohol or ethanol;
B, middle temperature calcination, aerobic removes cyanogen and organic matter
With remove methyl alcohol or ethanol contain the cyanogen waste salt dregs under aerobic conditions, carry out in warm calcination, make the cyanide complete oxidation that contains in the cyanogen waste salt dregs, oxidation operation or volatilization, thereby remove cyanogen and organic matter in the salt slag;
C, tail gas high-temp combustion
To contain gas that the cyanogen waste salt dregs produces and feed incinerator and burn in middle temperature calcination, incineration temperature is not less than 1100 ℃, makes tail gas reach discharge standard.
2, the processing method that contains the cyanogen waste salt dregs according to claim 1 is characterized in that: when reclaiming methyl alcohol or ethanol, will contain the cyanogen waste salt dregs and add in the continous way hollow blade drier, and feed the heating agent heating in the chuck of drier.
3, the processing method that contains the cyanogen waste salt dregs according to claim 1 and 2, it is characterized in that: middle temperature calcination is that the cyanogen waste salt dregs that contains that will remove methyl alcohol or ethanol adds continuously in reverberatory furnace or the rotary kiln and carries out, temperature is controlled at 500～800 ℃, coefficient of excess air is controlled at 〉=and 1.2, the time of staying is 0.5～2 hour in the calcination process.
4, the processing method that contains the cyanogen waste salt dregs according to claim 1 and 2 is characterized in that: contains the gas that produces in the warm calcination process in the cyanogen waste salt dregs and feeds in the efficient burning furnace by air-introduced machine and burn, and gas residence time is controlled at 〉=and 2 seconds.