CN1546763A - Apocynum and silky gloss blended yarn and fabric weaved thereby - Google Patents
Apocynum and silky gloss blended yarn and fabric weaved thereby Download PDFInfo
- Publication number
- CN1546763A CN1546763A CNA2003101075609A CN200310107560A CN1546763A CN 1546763 A CN1546763 A CN 1546763A CN A2003101075609 A CNA2003101075609 A CN A2003101075609A CN 200310107560 A CN200310107560 A CN 200310107560A CN 1546763 A CN1546763 A CN 1546763A
- Authority
- CN
- China
- Prior art keywords
- mercerising
- blended yarn
- fabric
- fibre
- bluish dogbane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of textile made up of dogbane and mercerizing fur blending. The invention provides a textile which has good elastane, straightness of flax, excellent hygroscopic and cold-proof performance, and it has functions of antisepsis health keeping. The weight percentage of dogbane and mercerizing fur are: dogbane fiber 20-30%, the mercerizing fur fiber 70-80%. The invention uses traditional process to produce the textile, produces them into cloth or underwear, or four-season blanket. A layer of negative ion material also can be painted on the product, the weight percentage of the layer is: calcium zeolite 30-45%, serpentine 20-45%, peridot 25-35%.
Description
Technical field
The present invention relates to a kind of textiles.
Background technology
At present, the various pure wools of selling on the market and blended cashmere lining and products thereof, though have sensation warming, comfortable and easy to wear, moisture pick-up properties and health properties are relatively poor, and can not wear next to the skin.
Summary of the invention
The present invention is in order to overcome weak point of the prior art, a kind of good springiness to be provided, and has the well-pressed of fiber crops, and hygroscopicity and warmth retention property are good, have antibacterial and health care, can adapt to bluish dogbane and the blended yarn of mercerising hair and the fabric that is made into thereof of Various Seasonal.
The present invention is achieved through the following technical solutions:
A kind of bluish dogbane and mercerising wool blended yarn comprise following component by weight percentage: apocynum fibre 20-30%, mercerising wool fibre 70-80%.
Described apocynum fibre is 20%, and the mercerising wool fibre is 80%.
The length of described apocynum fibre is 40-80mm, and fibre diameter is 17-18 μ m.
The length of described mercerising wool fibre is 50-70mm, and fibre diameter is 17-45 μ m.
The fabric that a kind of bluish dogbane and mercerising wool blended yarn are made into, the base material of fabric adopt apocynum fibre and mercerising wool fibre blended yarn to be made into; The percentage by weight of described apocynum fibre and mercerising wool fibre is respectively 20-30%, 70-80%.
Described base material is provided with the anion material layer, is made of following component by weight percentage in the described anion material layer: scolecite 30-45%, serpentine 20-45%, tourmaline 25-35%.
Described scolecite 35%, serpentine 35%, tourmaline 30%.
The area of described anion material layer is the 20-50% of fabric area.
Described fabric is dress ornament or underwear or four seasons seat.
The present invention has following beneficial effect:
1. natural apocynum fibre among the present invention can suppress the generation of bacterium, has far-infrared functional, can strengthen human body and exempt from
Epidemic disease power lessens fatigue.
2. blended yarn and fabric moisture, wet putting and the warmth retention property of bluish dogbane of the present invention and mercerising hair are good, have sky
The tonality energy has solved because the temperature difference is big, increases and decreases the problem of clothing at any time, can adapt to the needs of all temps.And
And fulling milling not.
3. used anion ceramic material in the blended yarn of bluish dogbane of the present invention and mercerising hair and the fabric thereof, at natural bar
Under the part, can discharge a large amount of anions, have the effect that bacterium generates that suppresses.
The specific embodiment
The invention will be further described below in conjunction with specific embodiment.
After apocynum degumming, shredding, selection length is that 40-80mm, diameter are the apocynum fibre of 17-18 μ m.
Select Australian Merino ultra-fine villus fiber on one's body, remove 70% scale (mercerising), to reach the purpose of anti-fulling milling.The length of mercerising wool fibre is 50-70mm, and fibre diameter is 17-18 μ m.
Adopt hair, fiber crops to divide the method for dying, dye apocynum fibre earlier, go to chase after the color of bluish dogbane again with the mercerising hair.
Embodiment 1
The mercerising hair that bluish dogbane that 30kg has been dyeed and 100kg have dyeed is put into the BC262 hair shutting machine, mixes simultaneously to add about 10% maos, fiber crops and share comprehensive auxiliary agent and antistatic additive about 3%.Weave rove through Belgian AS-304-4 (4 cylinder) combing machine for fur again.Be made into the blended yarn of bluish dogbane and mercerising hair through the Italian Bi Jiali B5SE of company fine spining machine (drafting multiple is about 30%), the charged sub-yarn clearer winder of Italian ESPERO type, ARS doubling frame plying, TDS～12 two-for-one twisters twisting again.Spinning last moisture regain on opportunity is 26%, and workshop relative humidity is 65%, about 25 ℃ of temperature.
Embodiment 2
The mercerising hair that bluish dogbane that 37kg has been dyeed and 88kg have dyeed is put into the BC262 hair shutting machine, mixes simultaneously to add about 10% maos, fiber crops and share comprehensive auxiliary agent and antistatic additive about 3%.Weave rove through Belgian AS-304-4 (4 cylinder) combing machine for fur again.Be made into the blended yarn of bluish dogbane and mercerising hair through the Italian Bi Jiali B5SE of company fine spining machine (drafting multiple is about about 35%), the charged sub-yarn clearer winder of Italian ESPERO type, ARS doubling frame plying, TDS～12 two-for-one twisters twisting again.Spinning last moisture regain on opportunity is 28%, and workshop relative humidity is 70%, about 25 ℃ of temperature.
Embodiment 3
The mercerising hair that bluish dogbane that 31kg has been dyeed and 94kg have dyeed is put into the BC262 hair shutting machine, mixes simultaneously to add about 10% maos, fiber crops and share comprehensive auxiliary agent and antistatic additive about 3%.Weave rove through Belgian AS-304-4 (4 cylinder) combing machine for fur again.Be made into the blended yarn of bluish dogbane and mercerising hair through the Italian Bi Jiali B5SE of company fine spining machine (drafting multiple is about about 30%), the charged sub-yarn clearer winder of Italian ESPERO type, ARS doubling frame plying, TDS～12 two-for-one twisters twisting again.Spinning last moisture regain on opportunity is 26%, and workshop relative humidity is 65%, about 25 ℃ of temperature.
Embodiment 4
With the bluish dogbane of the foregoing description and the blended yarn of mercerising hair, adopt traditional handicraft to be made into fabric respectively.Make dress ornament or underwear or four seasons seat then.
Embodiment 5
On the fabric of above-mentioned bluish dogbane and mercerising wool blended yarn, coat the anion material layer, then above-mentioned fabrics is made dress ornament or underwear or four seasons seat.
The anion material coating is to grind to form powdery by scolecite 30 grams, serpentine 45 grams, tourmaline 25 grams, mixes with adhesive then, is evenly coated in fabric face, and coating accounts for 20% of fabric face and gets final product.
Embodiment 6
On the fabric of above-mentioned bluish dogbane and mercerising wool blended yarn, coat the anion material layer, then above-mentioned fabrics is made dress ornament or underwear or four seasons seat.
The anion material coating is to grind to form powdery by scolecite 35 grams, serpentine 35 grams, tourmaline 30 grams, mixes with adhesive then, is evenly coated in fabric face, and coating accounts for 30% of fabric face and gets final product.
Embodiment 7
On the fabric of above-mentioned bluish dogbane and mercerising wool blended yarn, coat the anion material layer, then above-mentioned fabrics is made dress ornament or underwear or four seasons seat.
The anion material coating is to grind to form powdery by scolecite 45 grams, serpentine 20 grams, tourmaline 35 grams, mixes with adhesive then, is evenly coated in fabric face, and coating accounts for 50% of fabric face and gets final product.
Embodiment 8
Adopt E12 pin straight-bar machines, plain stitch to become fabric, the burst braiding is sewed up ready-made clothes with sewing machine.Add softener, typing, check until packing through washing to contract again, finally become high-grade bluish dogbane and mercerising wool series products.
Although the disclosed fabric that relates to a kind of bluish dogbane and mercerising wool blended yarn and be made into has been carried out special description with reference to embodiment, those skilled in the art can understand, under the situation that does not depart from scope and spirit of the present invention, can carry out all conspicuous modification of form and details to it.Therefore, embodiment described above is illustrative and not restrictive, and under the situation that does not break away from the spirit and scope of the present invention, all variations and modification are all at this
Within the scope of invention.
Claims (9)
1. bluish dogbane and mercerising wool blended yarn is characterized in that, comprise following component by weight percentage: apocynum fibre 20-30%, mercerising wool fibre 70-80%.
2. the blended yarn of bluish dogbane according to claim 1 and mercerising hair is characterized in that, described apocynum fibre is 20%, and the mercerising wool fibre is 80%.
3. the blended yarn of bluish dogbane according to claim 1 and 2 and mercerising hair is characterized in that, the length of described apocynum fibre is 40-80mm, and fibre diameter is 17-18 μ m.
4. the blended yarn of bluish dogbane according to claim 1 and 2 and mercerising hair is characterized in that, the length of described mercerising wool fibre is 50-70mm, and fibre diameter is 17-45 μ m.
5. the fabric that is made into of bluish dogbane and mercerising wool blended yarn is characterized in that the base material of fabric adopts apocynum fibre and mercerising wool fibre blended yarn to be made into; The percentage by weight of described apocynum fibre and mercerising wool fibre is respectively 20-30%, 70-80%.
6. the fabric that bluish dogbane according to claim 5 and mercerising wool blended yarn are made into, it is characterized in that described base material is provided with the anion material layer, constitute by following component by weight percentage in the described anion material layer: scolecite 30-45%, serpentine 20-45%, tourmaline 25-35%.
7. the fabric that bluish dogbane according to claim 6 and mercerising wool blended yarn are made into is characterized in that, described scolecite 35%, serpentine 35%, tourmaline 30%.
8. the fabric that bluish dogbane according to claim 7 and mercerising wool blended yarn are made into is characterized in that, the area of described anion material layer is the 20-50% of fabric area.
9. the fabric that bluish dogbane according to claim 8 and mercerising wool blended yarn are made into is characterized in that, described fabric is dress ornament or underwear or four seasons seat.