CN1528491A - 一种环保陶瓷滤球的制造方法 - Google Patents
一种环保陶瓷滤球的制造方法 Download PDFInfo
- Publication number
- CN1528491A CN1528491A CNA2003101112097A CN200310111209A CN1528491A CN 1528491 A CN1528491 A CN 1528491A CN A2003101112097 A CNA2003101112097 A CN A2003101112097A CN 200310111209 A CN200310111209 A CN 200310111209A CN 1528491 A CN1528491 A CN 1528491A
- Authority
- CN
- China
- Prior art keywords
- ceramic filter
- kinds
- manufacture method
- ball
- balling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种陶瓷滤料的制造方法。一种环保陶瓷滤球的制造方法,其特征是包括如下步骤:1).配料:按重量百分比,氧气铝赤泥15-30,粉煤灰20-40,煤矸石10-30,黏土10-15,成孔剂20-40,高温黏结剂3-6;2);粉碎:将上述原料以球磨机粉碎、混合配料,然后过筛100~180目备用;3).成球:成球前,将低温黏结剂与水以1∶2的重量比到入水中配成混合液,再逐渐喷入成球机的坯料中,然后采用成球机成球;3).干燥:在80~120℃干燥4~5小时;4).烧制:将上述干燥后的球在1100℃~1250℃烧成。本发明生产的陶瓷滤球压碎强度达0.799KN/颗,气孔率大于50%,耐酸度大于86%,耐碱度大于99%,粒径0.5~20mm可调,耐温达800℃,是一种有广泛应用价值的高品质滤料。
Description
技术领域
本发明涉及一种滤料的制造方法,具体涉及一种陶瓷滤料的制造方法。其陶瓷滤料适用于环保水处理和煤气过滤等行业和领域。
背景技术
过滤和吸附是油田废水、化工废水、电镀废水、冶金废水等处理的一种常用方法。其中过滤和吸附的介质——滤球是提高这些废水处理效果和效率的关键。大量资料显示,人们正在制造各种人工滤料来代替目前广泛使用的天然滤料——石英砂,以进一步提高吸附能力和排污效果。正在商业化的滤料主要有陶瓷滤料、活性碳、矿物滤料和高分子滤料等。其中陶瓷滤料正在成为一种物美价廉的重要滤料。
但是,陶瓷滤料的制造一直存在一个技术难题:陶瓷滤料的压碎强度较低,无法满足反冲洗需要的强度,工业废料和普通黏土制造的滤球更是如此。比如,我们对市场出售的一种陶粒滤料(气孔率为36.54%)测试,其压碎强度仅为0.336千牛/颗。
采用铝钒土制造的陶瓷滤料(中国专利公开号1326806)可以提高强度,但原料较贵,烧成温度高达1400℃以上,气孔率也仅为30%左右。
一种用于废水处理的球型多孔轻质陶粒(中国专利公开号1380137)是以炼钢赤泥、粉煤灰、黏土为原料,配以造孔剂制造的陶瓷滤料。虽然其采用了工业废料和低温烧成技术(800℃~1100℃),成本较低,但强度较低,气孔率也较低(30%~40%)。
发明内容
本发明的目的在于提供一种高强度、高气孔率的环保陶瓷滤球的制造方法。
本发明的技术方案是:一种环保陶瓷滤球的制造方法,包括如下步骤:
1).配料:按重量百分比,氧化铝赤泥15-30,粉煤灰20-40,煤矸石10-30,黏土10-15,成孔剂20-40,高温黏结剂3-6;所述的成孔剂为锯末或白云石等中的任一种或二种以上的混合,二种以上的混合时为任意配比;所述的高温黏结剂为霞石正长石、锂辉石或钾长石等中的任一种或二种以上的混合,二种以上的混合时为任意配比。
2).粉碎:将上述原料以球磨机粉碎、混合配料,然后过筛100~180目备用。
3).成球:成球前,将低温黏结剂与水以1∶2的重量比到入水中配成混合液,再逐渐喷入成球机的坯料中,达到水份含量3-8%,然后采用成球机成球;所述的低温黏结剂为羧甲基纤维素(CMC)、水玻璃或磷酸二氢铝等中的任一种或二种以上的混合,二种以上的混合时为任意配比。
3).干燥:将成好的球放入抽屉式干燥坯车的干燥抽屉中,推入抽屉式干燥坯车,在80~120℃干燥4~5小时。
4).烧制:将上述干燥后的球再装入托盘匣钵车的托盘匣钵中,在1100℃~1250℃烧成。
本发明首次引入高温黏结剂(如霞石正长石、锂辉石或钾长石等),将成分波动较大的氧化铝赤泥、粉煤灰、煤矸石等工业废料在高温状态黏结为牢固的整体,从而在保持较高气孔率的同时,大幅度提高了其强度。一般情况下,滤球强度可提高1倍左右。
本发明一是在成球所用的水中配以适量的低温黏结剂,如羧甲基纤维素(CMC)、水玻璃或磷酸二氢铝等,生坯强度可明显提高(30%~50%)。二是设计了抽屉式干燥坯车,使干燥时间比通常的自然堆积干燥方式缩短1/3左右(10毫米以上的大球效果更明显),干燥更加透彻和均匀。三是专门设计了适合球形滤料烧成的托盘匣钵车—“浅匣无棚板”码烧方式,既避免了球形滤料烧成中常见的生烧和黑心缺陷,又提高了装窑密度。
本发明生产的陶瓷滤球压碎强度达0.799KN/颗,气孔率大于50%,耐酸度大于86%,耐碱度大于99%,粒径0.5~20mm可调,耐温达800℃,是一种有广泛应用价值的高品质滤料。
本发明对利用氧化铝赤泥等工业废料生产高品质滤球具有重要意义,可广泛应用于石油废水、化工废水、冶金废水、电镀废水、印染废水、造纸废水、焦化厂废水等吸附过滤,还可以用于城市给排水、垃圾渗沥液等过滤。
附图说明
图1是本发明的抽屉式干燥坯车结构示意图
图2是图1中的干燥抽屉3的俯视图
图3是本发明的托盘匣钵车结构示意图
图4是图3中的托盘匣钵9结构示意图
图5是图4仰视局部剖视图
图中,1-车架,2-抽屉拉手,3-干燥抽屉,4-车拉手,5-车轮,6-金属网,7-窑车,8-立柱,9-托盘匣钵。
具体实施方式
下面是实施本发明的优选方式:
实施例1:一种环保陶瓷滤球的制造方法,
(1)按以下原料配方(重量百分比)进行配料;
氧气铝赤泥26%,粉煤灰20%,煤矸石20%,黏土10%,锯末成孔剂20%,外加高温黏结剂(霞石正长石)4%。
(2)以球磨机粉碎和混合配料,然后过筛(100~180目)备用;
(3)采用成球机成球。成球前,将低温黏结剂CMC以1∶2的比例(重量)到入水中配成混合液,再逐渐喷入成球机的坯料中。
(4)将成好的球放入干燥抽屉中,推入干燥坯车,在80~120℃干燥4~5小时,再装入托盘匣钵中在1100℃~1250℃烧成。
如图1、图2所示,本发明生产所用的抽屉式干燥坯车是一种抽屉式结构,由车架1、抽屉拉手2、干燥抽屉3、车拉手4、车轮5、金属网6组成,多个干燥抽屉3分层位于车架1上,车架1上设有车拉手4、车轮5,干燥抽屉3上设有抽屉拉手2、金属网6。干燥抽屉底部采用金属网材料,承托滤球时有利于滤球的透彻和均匀干燥,确保其入窑水分低于5%。这对于以粘性较大的氧化铝赤泥为主的配料尤为重要。
如图3、图4、图5所示,托盘匣钵车由窑车7、立柱8、托盘匣钵9组成,托盘匣钵9分层间隔位于两立柱8上,两立柱8位于窑车7上,托盘匣钵9的浅匣钵内高25~30毫米。本发明特别设计了一种码放方式——“浅匣无棚板”堆码方式,有利于充分利用窑内空间,避免陶瓷滤球因热气流不畅通而生烧或黑心。
实施例2:一种环保陶瓷滤球的制造方法,
(1)以下原料配方,按重量百分比进行配料;
氧化铝赤泥20%,粉煤灰25%,煤矸石13%,黏土12%,锯末14%和白云石10%,锂辉石2%和钾长石4%。
(2)以球磨机粉碎和混合配料,然后过筛150目备用;
(3)采用成球机成球。成球前,将低温黏结剂水玻璃和磷酸二氢铝以1∶2的比例(重量)倒入水中配成混合液,再逐渐喷入成球机的坯料中,水玻璃和磷酸二氢铝为任意配比。
(4)将成好的球放入干燥抽屉中,推入干燥坯车,在100℃干燥5小时,再装入托盘匣钵中在1100℃~1250℃烧成。
Claims (6)
1.一种环保陶瓷滤球的制造方法,其特征是包括如下步骤:
1).配料:按重量百分比,氧化铝赤泥15-30,粉煤灰20-40,煤矸石10-30,黏土10-15,成孔剂20-40,高温黏结剂3-6;
2).粉碎:将上述原料以球磨机粉碎、混合配料,然后过筛100~180目备用;
3).成球:成球前,将低温黏结剂与水以1∶2的重量比到入水中配成混合液,再逐渐喷入成球机的坯料中,达到水份含量3-8%,然后采用成球机成球;
3).干燥:在80~120℃干燥4~5小时;
4).烧制:将上述干燥后的球在1100℃~1250℃烧成。
2.根据权利要求1所述的一种环保陶瓷滤球的制造方法,其特征是:所述的成孔剂为锯末或白云石中的任一种或二种以上的混合,二种以上的混合时为任意配比。
3.根据权利要求1所述的一种环保陶瓷滤球的制造方法,其特征是:所述的高温黏结剂为霞石正长石、锂辉石或钾长石中的任一种或二种以上的混合,二种以上的混合时为任意配比。
4.根据权利要求1所述的一种环保陶瓷滤球的制造方法,其特征是:所述的低温黏结剂为羧甲基纤维素、水玻璃或磷酸二氢铝中的任一种或二种以上的混合,二种以上的混合时为任意配比。
5.根据权利要求1所述的一种环保陶瓷滤球的制造方法,其特征是:所述的干燥为:将成好的球放入抽屉式干燥坯车的干燥抽屉中,推入抽屉式干燥坯车,在80~120℃干燥4~5小时。
6.根据权利要求1所述的一种环保陶瓷滤球的制造方法,其特征是:所述的烧制为:将上述干燥后的球再装入托盘匣钵车的托盘匣钵中,在1100℃~1250℃烧成。