CN1488691A - Nano internal-wall latex paint for health-care building and preparing method thereof - Google Patents
Nano internal-wall latex paint for health-care building and preparing method thereof Download PDFInfo
- Publication number
- CN1488691A CN1488691A CNA031400477A CN03140047A CN1488691A CN 1488691 A CN1488691 A CN 1488691A CN A031400477 A CNA031400477 A CN A031400477A CN 03140047 A CN03140047 A CN 03140047A CN 1488691 A CN1488691 A CN 1488691A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- latex paint
- nano
- wall latex
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a nano type health building material wall latex paint and its preparation method. It is made up by using polyvinyls emulsion, dispersing agent, moistening agent, pigment, filling material, nano predispersing liquor, thickening agent, pH regulating agent and water through the processes of combining nano predispersing liquor and emulsion, premixing, high-speed dispersing, blending paint and filtration. At the same time of ensuring that said paint has good physical properties it can make VOC be reduced to minimum value and can improve indoor air quality.
Description
Technical field
The present invention relates to paint field, particularly a kind of Nano type healthy building interiro wall latex paint that is used for the inner wall of building protection and decorates.
Background technology
Begin in the developed country occur to stimulate, " sick Building syndromess " such as weak, headaches, hypomnesis the seventies, many data presentation, and this is relevant with volatile organic matter (VOC) pollution in the buildings coating.At present, the latex coating of low VOC is all endeavoured to study and develop in countries in the world, but, in the latex coating system, unavoidably need to add multiple auxiliary agent, all contain organic solvent as coalescing aid, flow agent, frostproofer, anticorrosion and bactericidal agent etc., therefore how to become a thorny difficult problem at the situation decline low VOC content that guarantees the latex coating quality.In addition, be antimycotic antiseptic, the normal use contained metal-organic antimildew disinfectants such as mercury, copper, tin, arsenic, though have stronger sterilizing power, it renders a service short, simultaneously human body is also had bigger murder by poisoning.
Summary of the invention
For addressing the above problem, the purpose of this invention is to provide a kind of ultralow VOC content and have the excellent wet-rub resistance and the Nano type healthy building interiro wall latex paint of efficient, persistent antimycotic antiseptic ability.
Another object of the present invention provides a kind of preparation method of Nano type healthy building interiro wall latex paint.
The object of the present invention is achieved like this: a kind of Nano type healthy building interiro wall latex paint, its component is (by a % weight): 20～50% vinyl polymer emulsion, 0.2～0.9% dispersion agent, 0.1～1.2% wetting agent, 0.2～0.8% defoamer, 16～25% pigment, 0～24% filler, 0.3～3% nanometer pre-dispersed liquid, 0.2～3.0% thickening material, 0.05～1.2% PH conditioning agent, all the other are water.
Emulsion is the film forming composition of emulsion paint, is determining the performance of paint film.In order to reduce the VOC of coating, the present invention has selected zero VOC nucleocapsid structure pure-acrylic emulsion, benzene emulsion and uncle's vinegar milk liquid for use, is guaranteeing to make VOC drop to Schwellenwert effectively when coating has better physicals.The nucleocapsid structure emulsion is meant that a kind of polymkeric substance as " seed " micelle, adds another kind of monomer and initiator then, carries out the emulsion that letex polymerization obtains on the latex surface.This composite emulsion phase-splitting and not separating, the centre is a karyon, and skin is born of the same parents' shells, and shell is coating emulsion layer outward, and forming the stratiform emulsion is the nucleocapsid structure emulsion, network runs through mutually and then occurs in two-phase interface.The grain pattern emulsion of the preferred soft nuclear-duricrust of body series, the stratum nucleare polymkeric substance provides flexibility, adhesivity and cold-resistant fragility, the shell polymkeric substance provides wear resistance, thermotolerance (not viscosity) and solvent resistance, the minimum film-forming temperature of the soft phase in each particle (MFFT) is very low, can under lower envrionment temperature, form the successive film, hard phase in the particle then gives paint film outstanding antiblocking ability, need not to add any film coalescence aid.Preferably have the film forming matter of lower minimum film-forming temperature (MFFT) emulsion as Nano type healthy building interiro wall latex paint: core-shell emulsion can be used to prepare the low PVC hard-gloss paint; Non-core-shell emulsion can be used to prepare the high PVC flat paint; Core-shell emulsion and non-core-shell emulsion are mixed according to a certain percentage and can be used to PVC flat paint in the preparation.
White pigment and filler commonly used in the emulsion paint are more, and this coating is the environment-friendly type system, when guaranteeing coating property, have used the low color stuffing of harmful substance contents such as heavy metal.Pigment is selected titanium dioxide for use, and filler comprises water-ground limestone, kaolin, talcum powder, superfine alumina silicate etc.Except that white latex paint, the mill base that also can add other color in body series obtains the emulsion paint of various colors with modulation.
Titanium dioxide: i.e. titanium dioxide (TiO
2), nontoxic, the powder shape, particle diameter is little, the whiteness height, tinting strength and opacifying power height mainly contain two kinds of crystal formations and exist: rutile-type and anatase titanium dioxide.The rutile type as E.I.Du Pont Company that is suitable for the interior wall use of thin, the easy dispersion of body series preferable particle size, strong covering power, optimum amount is 16～25%.
Water-ground limestone: white powder is one of the most frequently used filler.Its tasteless odorless is difficult for efflorescence, can improve the hardness and the wash-resistant property of paint film.The preferred 800 purpose water-ground limestones of body series, optimum amount is 0～15%.
Kaolin: be a kind of mineral association body based on clays such as pure aluminium silicate kaolinites.Thin, the wetting dispersion stabilization of particle is good, and suspension is good, and it is anti-heavy therefore to help.Add with certain proportion, when guaranteeing opacifying power, can save the part titanium white.The preferred 1250 purpose kaolin of body series, optimum amount is 0～5%.
Talcum powder: main chemical is a hydrated magnesium silicate, uses talcum powder can improve easy application property in emulsion paint, makes coating be easy to brush and have weather resistance that good levelling property and enhancing film etc.The preferred 800 purpose talcum powder of body series, optimum amount is 0～4%.
Superfine alumina silicate: be a kind of functional filler, pure white unformed loose ultrafine powder, low alkalinity.Because of particle diameter is little, narrow particle size distribution does not have the precipitated and separated phenomenon, and the suspension of coating is improved greatly, and it is respond well to open jar, and the coating form and aspect are pure, strong coloring force, and opacifying power improves.Preferred particulates, particle diameter are the superfine alumina silicate of 0.4-0.5 micron, and it obtains the scattering power maximum to incident light, has the highest opacifying power, and the more little tinting strength of particle diameter is strong more simultaneously, can improve the dispersiveness and the fineness index of coating.Optimum amount in the body series is 0～3%.
Body series is as low VOC coatings, and when guaranteeing product performance, selected auxiliary agent all is that zero VOC or VOC value are lower.
Dispersion agent: polyacrylic acid dipersant that the preferred dispersive ability of body series is good or polymaleic acid dipersant (wherein sodium, sylvite have lower VOC than ammonium salt).
Wetting agent: in order to reach better dispersion effect, improve the wettability of base-material and pigment, promote flowability, suppress foamy simultaneously and produce, preferred many (gathering) the phosphoric acid salt wetting agent of body series is or/and press down alveolitoid nonionogenic tenside wetting agent.
Thickening material: thickening material is a kind of auxiliary rheological agents, can increase the viscosity of coating after the adding, gives the machinery and the physical and chemical stability of coating excellence simultaneously, plays the control rheological when construction.Body series preferred thickening kind comprises cellulose thickener, alkali swelling acrylic emulsion thickener and non-ionic associative type polyurethane thickening material.Cellulose thickener mainly increases the middle low-shear viscosity of emulsion paint, and its thixotropy is big, and yield value is big.Low-shear viscosity during alkali swelling acrylic emulsion thickener mainly improves, its yield value is bigger, and thixotropy is big.And non-ionic associative type polyurethane thickening material yield value is little, good fluidity.Choose this three classes thickening material and carry out composite use in body series, the dope viscosity that makes is stable, and the outward appearance exquisiteness is plentiful, and stability in storage is good, and it is effective to open jar.
Defoamer: the various auxiliary agents in the emulsion paint belong to tensio-active agent mostly, the existence of system own is bubbled easily or make the factor of bubble stabilizes.Coating stirring in process of production, spraying during construction or roller coat all can increase the degree of freedom of coating system to some extent, help foamy to produce.Air in the foam can hinder the dispersion of color stuffing, stays the bubble eye to dry film, causes surface imperfection, has both diminished outward appearance, influences the water tolerance of paint film again, therefore needs to use the low VOC defoamer that adapts with body series to solve bubble-related issues.The preferred consistency of body series is the organic silicon modified by polyether emulsion defoamer preferably, can not the solving by the synergy that presses down the alveolitoid wetting agent completely of its antifoam performance.
Sodium hydroxide, potassium hydroxide or the yellow soda ash etc. of the preferred non-volatility of PH conditioning agent.
Characteristics such as nano material is big because of its specific surface area, the particle micropore is many, high adsorption capacity and reactive behavior height are obvious to the viscosity and the aspect effects such as bonding strength between raising coating and the matrix that increase coating.Little because of its (nano silicon oxide) particle size, molecularity is tridimensional network, the surface exists a large amount of hydroxyls and unsaturated residual bond, has very high reactive behavior, with the emulsion compound tense, a part nanoparticle may with latex molecule generation bonding or grafting, another part also may be penetrated in the slit between macromolecular chain and the macrobead material, form unique three-dimensional net structure, thereby obviously improve the suspension stability and the film-forming properties of coating, significantly improve the performances such as compactness, ductility, hardness and abrasion resistance of filming.The antimildew disinfectant steady load in nano material, is utilized the slow-release function of nano material, can reach efficient, persistent antimycotic antiseptic function.The nanometer pre-dispersed liquid of the preferred Zhejiang of body series nano material tomorrow company limited, main component is: nano silicon oxide 〉=20%, inorganic antibacterial powder 3～5%.
Coating of the present invention can also add 0.5～3% negative ion releasable material.The negative ion releasable material constitutes permanent electrode because the positive and negative charge-site of each cell cube can't overlap, and has pyroelectricity and piezoelectricity.When outside temperature or impressed pressure generation subtle change, promptly around it, form electric field and little electric current.Simultaneously, owing to there is the existence of moment of dipole to make the negative ion paint additive have good far-infrared functional.Because of each unit of negative ion paint additive has permanent electrode, when airborne water molecules or oxygen molecule were in contact with it, permanent electrode sparked, and discharges negative ion (H
3O
2 -, O
2 -), can neutralize, wrap up obnoxious flavour particles such as the positively charged formaldehyde of free, ammonia, benzene class, make it form macroparticle group and settle down; Negative ion can also neutralize airborne oxyradical and oxidizing gas (corrupt peculiar smell), the electric field of its formation can make the organism peculiar smell decompose, thereby reach the purpose that purifies air.Bacterium is positively charged mostly, in air by negative ion coating, neutralization or redox (negative ion has higher activity), thereby reach purpose antibiotic, sterilization (intestinal bacteria, streptococcus aureus, mould etc.).The preferred negative ion releasable material of body series is that the strange ice stone flour produced of Taixing Nanometer Material Factory of solid institute of the Chinese Academy of Sciences is or/and the environment-friendly function material negative ion element that Lang Nuo Environmental Protection Technology Co., Ltd in Beijing produces.
The preparation method of Nano type healthy building interiro wall latex paint of the present invention comprises the steps:
(1) nanometer pre-dispersed liquid and emulsion are compound: stir at a slow speed under (200～400 rev/mins), order adds emulsion, water, nanometer pre-dispersed liquid, and stir about 1～2 hour is standby to evenly;
(2) pre-dispersed: stir at a slow speed under (200～400 rev/mins), order adds entry, dispersion agent, wetting agent, defoamer, cellulose thickener etc., is stirred to even back and adds negative ion releasable material, pigment and filler;
(3) high speed dispersion: high-speed stirring (1000～1500 rev/mins) 30 minutes, dispersion temperature≤60 ℃ make the color stuffing particle form the state of stably dispersing and reach required fineness;
(4) paint: stir at a slow speed down, add the nanometer pre-dispersed liquid composite emulsion of step (1), slowly add defoamer, PH conditioning agent and thickening material again after evenly;
(5) filter.
Not mercurous and compound in the product of the present invention, need not lead, the pigment coloring of cadmium, chromium and compound thereof, reduce or reduce the content of poisonous and hazardous volatile organic matter and heavy metal ion as far as possible, guaranteeing that coating has the better physical performance simultaneously, makes VOC drop to Schwellenwert.And, utilize nanotechnology that traditional product is carried out modification, wet-rub resistance can be excellent, simultaneously with the antimildew disinfectant steady load on nano material, the antimycotic antiseptic ability is efficient, lasting, to the skin nonirritant.The negative ion releasable material of adding have purify air, advantage such as deodorization and sterilization.Product conventional index of the present invention reaches GB/T9756-2001 premium grads level, and VOC, formaldehyde, heavy metal content are lower than GB18582-2001 nuisance limit standard, makes the room have good indoor-outdoor air quality, for people's life provides required a home from home.
The detected result of product of the present invention is as follows:
Contrast ratio (white and light color) 0.95
Abrasion resistance＞20000 are time not show-through
Volatile organic compounds (VOC) (g/L) 1.2
Free formaldehyde (g/kg)＜5 * 10
-3
Heavy metal dissoluble lead 7.48
(mg/kg) soluble cadmium 0.04
Soluble chromium 0.076
Soluble mercury 1.89
Antibiotic rate (%)＞99.99
0 grade of fungicidal properties
Skin irritation does not have
Embodiment
Embodiment 1
Preparation low PVC hard-gloss paint.Prescription is: 50 kilograms of pure-acrylic emulsions (nucleocapsid structure), 0.9 kilogram of sodium polyacrylate (ammonium) dipersant, 0.1 kilogram of many (gathering) phosphoric acid salt wetting agent, 0.2 kilogram of organic silicon modified by polyether emulsion defoamer, 25 kilograms of Rutile type Titanium Dioxides, 3 kilograms of negative ion releasable material, 0.3 kilogram of nanometer pre-dispersed liquid, 2.5 kilograms of thickening materials (comprising 1.8 kilograms of 0.1 kilogram of cellulose thickener, 0.6 kilogram of alkali swelling acrylic emulsion thickener and non-ionic associative type polyurethane thickening materials), 1.2 kilograms in yellow soda ash, 16.8 kilograms in water.
The configuration processing step is: (1) nanometer pre-dispersed liquid and emulsion are compound: in container, add emulsion, stir (200～400 rev/mins) down at a slow speed, add the suitable quantity of water dilution after, drip the nanometer mother liquor, drip back continuation stir about 1～2 hour until evenly, standby.(2) in disperseing cylinder (strap clamp cover), add entry; (200～400 rev/mins) stir down at a slow speed; add dispersion agent; wetting agent; defoamer; cellulose thickener etc.; continue to be stirred to the back adding negative ion releasable material that is uniformly dispersed; titanium dioxide; and rotating speed is adjusted in attention along with the increase of viscosity; the shutdown of complete back feeds intake; the material that rises dispersion impeller and note adhering on casing wall and the dispersion impeller all shovel is gone into slurry; the water flushing disperses to adjust dispersion machine behind the inside wall of cylinder and the dispersion impeller; (3) high speed dispersion (1000～1500 rev/mins) is 30 minutes, and notes using water coolant to disperse cylinder temperature (being no more than 60 ℃) with control.(4) sampling detects, and fineness should be not more than 45 μ m.Stir at a slow speed down; add the nanometer pre-dispersed liquid composite emulsion that step (1) makes in the slurry in disperseing cylinder; stir and slowly add defoamer, yellow soda ash, acrylic emulsion thickener and association type polyurethane thickener after 10 minutes, continue to be stirred to even back and shut down.(5) inspection by sampling, the qualified back of product is filtered the back with 200 order Vibrationsifters and is packed by specification.
Embodiment 2
Preparation high PVC flat paint.Prescription is: 20 kilograms of benzene emulsions, 0.5 kilogram of sodium polyacrylate (ammonium) dipersant, 0.2 kilogram of many (gathering) phosphoric acid salt wetting agent, 0.4 kilogram of organic silicon modified by polyether emulsion defoamer, 18 kilograms of Rutile type Titanium Dioxides, filler (comprises 15 kilograms of 800 purpose water-ground limestones for 22 kilograms, 3 kilograms of 1250 purpose kaolin, 2 kilograms of 800 purpose talcum powder, 2 kilograms of superfine alumina silicates), 0.5 kilogram of negative ion releasable material, 2 kilograms of nanometer pre-dispersed liquids, thickening material (comprises 0.35 kilogram of cellulose thickener for 2.15 kilograms, 1.4 kilograms of 0.4 kilogram of alkali swelling acrylic emulsion thickener and non-ionic associative type polyurethane thickening materials), 0.1 kilogram of sodium hydroxide solution, 34.15 kilograms in water.
The configuration processing step is with embodiment 1.
Embodiment 3
PVC flat paint in the preparation.Prescription is: emulsion (comprises 15 kilograms of pure-acrylic emulsions for 30 kilograms, 15 kilograms of benzene emulsions) the polymaleic acid dipersant is 0.45 kilogram, 0.15 kilogram of many (gathering) phosphoric acid salt wetting agent, 0.5 kilogram of organic silicon modified by polyether emulsion defoamer, 16 kilograms of Rutile type Titanium Dioxides, filler (comprises 13 kilograms of 800 purpose water-ground limestones for 18.4 kilograms, 2.6 kilograms of 1250 purpose kaolin, 1.8 kilograms of 800 purpose talcum powder, 1 kilogram of superfine alumina silicate), 2 kilograms of negative ion releasable material, 1.0 kilograms of nanometer pre-dispersed liquids, thickening material (comprises 0.3 kilogram of cellulose thickener for 1.8 kilograms, 1.2 kilograms of 0.3 kilogram of alkali swelling acrylic emulsion thickener and non-ionic associative type polyurethane thickening materials), 0.5 kilogram in potassium hydroxide, 29.2 kilograms in water.
The configuration processing step is with embodiment 1.
Shady and cool dry and comfortable place more than 0 ℃ is deposited in the product sealing that the present invention makes, and effective service life is 18 months.Temperature is lower than 5 ℃ or humidity and should not constructs greater than 90%.
Construction guide: must stir before the construction;
Constructional method---roller coating, brushing or Airless spraying (can be without priming paint or with joining
The healthy priming paint of cover);
Surface treatment---substrate surface cleaning, dry (no greasy dirt, leakless,
No bulk materials);
Dry paint thickness---30 μ m (every layer);
Wet paint film thickness---70 μ m (every layer);
Theoretical coverage face---14m
2/ L;
Dilution ratio---construction again after can adding 10～25% clear water and stirring;
Touch the time of doing---1h/25 ℃;
Repainting hours---3h/25 ℃;
Lowest construction temperature---5 ℃.
Claims (10)
1. Nano type healthy building interiro wall latex paint, it is characterized in that: contain following component and be (by % weight): 20～50% vinyl polymer emulsion, 0.2～0.9% dispersion agent, 0.1～1.2% wetting agent, 16～25% pigment, 0～24% filler, 0.3～3% nanometer pre-dispersed liquid, 0.2～3.0% thickening material, 0.05～1.2% PH conditioning agent, surplus is a water.
2. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: also contain 0.5～3% negative ion releasable material.
3. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: described negative ion releasable material is a kind of for strange ice stone flour or negative ion element, or their mixing of two kinds.
4. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that; Described vinyl polymer emulsion is a kind of in benzene emulsion, pure-acrylic emulsion or the uncle's vinegar milk liquid, or is the mixing of two kinds of emulsions in them.
5. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: described dispersion agent is polyacrylate or polymaleic acid salt.
6. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: described wetting agent is many (gathering) phosphoric acid salt or/and press down alveolitoid nonionogenic tenside wetting agent.
7. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: described thickening material is hydroxyethyl ether cellulose, alkali swelling type polyacrylic acid and the agent of urethane association type ternary composite thickening.
8. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: described PH conditioning agent is sodium hydroxide, potassium hydroxide or yellow soda ash.
9. Nano type healthy building interiro wall latex paint according to claim 1 is characterized in that: described nanometer pre-dispersed liquid contains and is not less than 20% nano silicon oxide and 3～5% inorganic antiseptic.
10. the preparation method of a Nano type healthy building interiro wall latex paint is characterized in that comprising the steps:
(1) nanometer pre-dispersed liquid and emulsion are compound: stir at a slow speed under (200～400 rev/mins), order adds emulsion, water, nanometer pre-dispersed liquid, and stir about 1～2 hour is standby to evenly;
(2) pre-dispersed: stir at a slow speed under (200～400 rev/mins), order adds entry, dispersion agent, wetting agent, defoamer, cellulose thickener etc., is stirred to even back and adds pigment and filler;
(3) high speed dispersion: high-speed stirring (1000～1500 rev/mins) 30 minutes, dispersion temperature≤60 ℃ make the color stuffing particle form the state of stably dispersing and reach required fineness;
(4) paint: stir at a slow speed down, add the nanometer pre-dispersed liquid composite emulsion of step (1), slowly add defoamer, PH conditioning agent and thickening material again after evenly;
(5) filter.