CN1483700A - Decoration technology of low temp red glazing, low temp. pattern paper and low temp golden color decoration for ceramic wine bottle - Google Patents
Decoration technology of low temp red glazing, low temp. pattern paper and low temp golden color decoration for ceramic wine bottle Download PDFInfo
- Publication number
- CN1483700A CN1483700A CNA031178219A CN03117821A CN1483700A CN 1483700 A CN1483700 A CN 1483700A CN A031178219 A CNA031178219 A CN A031178219A CN 03117821 A CN03117821 A CN 03117821A CN 1483700 A CN1483700 A CN 1483700A
- Authority
- CN
- China
- Prior art keywords
- glaze
- red
- bottle
- low temp
- decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The decoration process of porcelain wind bottle includes the following steps: heating white porcelain bottle at 50-100 deg.C; adding adhesive whose added quantity is less than 30% of in red glaze powder and adding water according to the ratio of 1.32-1.73 kg/L to prepare red glaze slip; soaking the porcelain bottle in the glaze slip or spraying the red glazed slip on the porcelain bottle, firing at 750-950 deg.C, and making decoration of low-temp. pattern paper and low-temp. gold on the fired red glaze porcelain bottle, and pattern-firing at 550-650 deg.C so as to obtain the invented color wine bottle.
Description
Affiliated technical field
The present invention relates to the decoration technology of ceramic wine bottle, specifically is a kind of red glaze of low temperature of ceramic wine bottle and the decoration technique of low temperature gold.
Background technology
At present, ceramic utensil is after decoration technology, and glaze light and color are scarlet, and the red glaze of low temperature is only arranged.Yet the red glaze firing temperature of low temperature is 750-950 ℃.Under this firing temperature, allow the complete porcelainization of ceramic bottle base body must not, and such pottery bottle can not be used for the splendid attire alcohol product.But if becoming porcelain products to execute the red glaze of low temperature,, allow glaze slip be difficult to adhere to, easily produce major defects such as lacking glaze, excess glaze owing to become porcelain not have water-absorbent.Because the characteristic of red glaze itself, glaze layer one are thickly partially promptly burnt slightly, are unfavorable for batch process.Therefore let alone carry out the decoration of low temperature marble paper and low temperature gold on this basis owing to do not see the technology that the bright-coloured red glaze decorative winebottle of low temperature is arranged in the prior art.
Summary of the invention
Technical problem to be solved by this invention is; After bottle employing grand feu, carry out the decoration of the red glaze of low temperature again.Make the scarlet bottle of color not ooze wine, and on this basis, carry out the decoration of low temperature marble paper and/or low temperature gold.
The technical solution used in the present invention is such: be about to heat under the temperature that the ceramic whiteware bottle places 50-100 ℃, add in red glaze and be no more than 30% by weight percentage and add the red glaze slip that water is allocated as proportion 1.32-1.73kg/L after adding binding agent.So not only solve the absorption problem of glaze slip, also solved the dry problem of glaze layer.Because in the glazing process, the glaze layer can not bear friction, must soak glaze to the porcelain vase body under the help of gripping tool, in preventing to operate to the contact of glaze layer.To corner and the more bottle of platform, then adopt spray glazing, can solve the long-pending thicker easy empyreumatic problem of glaze of corner platform.The porcelain vase that will soak after glaze or the glaze spraying is fired under 750-950 ℃ of temperature; Carry out the decoration of low temperature marble paper, low temperature gold again on the red glaze porcelain vase after burning till, and promptly get red glaze bottle after decorating at decorated fire under the 550-650 ℃ of temperature.
Manufacture craft is simple, cost is low, operative technique is easily grasped, the production efficiency height owing to described technology has in the present invention, bottle bright in luster, glaze is smooth, smooth, class advantages of higher.
Description of drawings
Accompanying drawing 1 is a process flow sheet of the present invention;
Accompanying drawing 2 is the structural representation of the glaze spraying device during glazing in the technology of the present invention;
Accompanying drawing 3 is the structural representation that soaks the glaze device during glazing in the technology of the present invention;
Accompanying drawing 4 is the schematic appearance of the red glaze bottle example of the present invention's production.
1-glaze spraying cover, 2-bottle seat, 3-suction cleaner, 4-bottle grabber, 5-glaze slip bucket in the accompanying drawing
Embodiment
The red powdered frit of the low temperature of finished product is added water and caking agent, and stirring allows it fully disperse, and proportion is transferred to 1.32-1.73kg/L.Bottle grabber 4 shown in Figure 3 is installed on 50-100 ℃ of bottle of heating, immerses 2-5 second (as shown in Figure 3) in the red glaze slip that mixes up.Be put in horizontal positioned after the taking-up, allow unnecessary glaze slip flow down.Having wiped the end then fires under 750-950 ℃ of temperature and forms.But for body the unique bottle of type design more multi-platform and corner is arranged, soak glaze if adopt, then the local long-pending glaze of bottle is obvious, therefore this series products has been adopted glaze spraying.Bottle after the heating is put on the bottle seat stand 2 of glaze spraying machine (as Fig. 2), allow bottle rotate, glaze slip is sprayed on bottle wall uniformly, carries out next step red glaze again and burn till, the red glaze bottle that burns till sticks the low temperature marble paper or/and be coated with low temperature Jinsui River and burn till under 550-650 ℃ of temperature.In described technology, the supporting binding agents that provide of macromolecular organic compound or red glaze manufacturer such as CMC can be provided binding agent.
The bottle of decorating through above-mentioned processing method maintains the leading position in market competition.Also enrich simultaneously the decoration of ceramic product, promoted the renewal of ceramic technology.
Claims (2)
1, a kind of decoration technology of the red glaze of low temperature of ceramic wine bottle, it is characterized in that: the processing step that comprises is: the ceramic whiteware bottle is placed under 50-100 ℃ the temperature and heat, be no more than 30% by weight percentage and add and add water behind the caking agent and be allocated as red glaze slip by the proportion of 1.32-1.73kg/L in red powdered frit; After porcelain vase soaked glaze or glaze spraying, under 750-950 ℃ of temperature, fire and promptly get product.
2, the decoration technology of a kind of low temperature gold of the red glaze of low temperature of ceramic wine bottle and/or low temperature marble paper: it is characterized in that: processing step comprises: the ceramic whiteware bottle is placed under 50-100 ℃ the temperature and heat, add by weight percentage to be no more than in red powdered frit and add water behind 30% the caking agent and be allocated as red glaze slip by the proportion of 1.32-1.73kg/L; After porcelain vase soaked glaze or glaze spraying, under 750-950 ℃ of temperature, fire; Carry out the low temperature marble paper on the red glaze porcelain vase after burning till again or/and the decoration of low temperature gold, and decorated fire promptly gets product under 550-650 ℃ of temperature.