CN1473888A - Heat insulation leak-proof antifouling outer wall mastic - Google Patents
Heat insulation leak-proof antifouling outer wall mastic Download PDFInfo
- Publication number
- CN1473888A CN1473888A CNA031401147A CN03140114A CN1473888A CN 1473888 A CN1473888 A CN 1473888A CN A031401147 A CNA031401147 A CN A031401147A CN 03140114 A CN03140114 A CN 03140114A CN 1473888 A CN1473888 A CN 1473888A
- Authority
- CN
- China
- Prior art keywords
- powder
- putty
- wall
- antifouling
- mastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to building paint, and is especially heat insulating leak-proof antifouling outer wall mastic. The mastic produced with calcite powder, expanded pearlite powder, hollow microbead, nano calcium carbonate, talc powder, calcined kaolin, superfine aluminum silicate, fluorosilicate emulsion, inorganic pigment and assistant has excellent heat isolating, leak-resisting, antifouling and weather resisting performance. It is painted to outer wall to result in outer coating with excellent decoration effect and long service life.
Description
Technical field
The present invention relates to the field of heat insulation, antiseepage, antifouling paint, in particular for the revetment decoration putty of skin.
Background technology
Exterior coating in the past generally is coated with earlier and scrapes basic putty, coating again, and its existing problems have:
1. coating and putty separate, good again coating, if putty is of poor quality, total quality is undesirable;
2. there is not heat-proof quality;
3. barrier performance is poor;
4. antifouling property is poor;
5. weather resistance is poor.
Because traditional exterior coating, coating separates with putty, and quality is inharmonious, causes coating to separate with putty or putty separates with body of wall, often occurs coming off, bulgingly splits, the seepage phenomenon; The tradition exterior coating does not all have heat-proof quality, and under summer extremely hot high temperature, solar thermal energy imports into indoor by body of wall, and people extremely feel bad, and add the influence of cold and hot weather throughout the year, and the phenomenon of expanding with heat and contract with cold causes the flexible cracking of coating, rainy day body of wall seepage phenomenon occurs; The antifouling property extreme difference of tradition exterior coating has a strong impact on the weathering resistance and the image appearance of exterior wall.Above problem also is that China's decoration of exterior wall transfers the slow important factor of coating tempo to by ceramics.
Summary of the invention
First purpose of the present invention provides a kind of heat-proof quality that has, and the good exterior wall putty of impervious stain-proof performance;
Second purpose of the present invention provides and a kind ofly coating, putty united two into one the exterior wall putty that performance is thought and acted in one and the same way.
The object of the present invention is achieved like this:
Its composition of the antifouling exterior wall putty of a kind of heat-isolating antiseepage is:
Calcite in powder 25%-35%
Swelling perlite powder 2%-6%
Cenosphere 5%-10%
Sodium rice lime carbonate (particle diameter is 15nm-30nm) 4%-8%
Talcum powder 2%-5%
Calcined kaolin 1%-3%
Superfine alumina silicate 1%-3%
Fluoro-silicone emulsion 15%-30%
Water 10%-20%
Auxiliary agent 1.5%-4%
Wherein auxiliary agent contains defoamer 0.2%-0.4%, wetting agent 0.6%-0.8%, dispersion agent 0.3%-0.6% softening agent 0.1%-0.5%, sanitas 0.3%-0.8%.
Ornamental for exterior wall putty is directly had, also can add the mineral dye of 0.1%-0.2%.
The putty that the present invention adopts calcite in powder, swelling perlite powder, cenosphere, nano-calcium carbonate, talcum powder, calcined kaolin, superfine alumina silicate, fluoro-silicone emulsion, mineral dye, the reaction of auxiliary agent batch mixing to draw divides 2～4 times batches to scrape in exterior wall surface with special-purpose scraper, its facing is smooth hard, decorates as the wall curtain especially.Swelling perlite powder wherein, cenosphere make putty have superior heat-proof quality; The coating that nano-calcium carbonate, fluoro-silicone emulsion composite reaction form, its sticking power is strong especially, makes putty have remarkable hydrophobicity performance, and facing chance water has the effect as the lotus leaf, thereby its impervious stain-proof performance is very outstanding.Experiment showed, that this product is used for external wall, decorate properties is thought and acted in one and the same way, and facing is smooth and bright like a mirror, metope waterproof, seepage control, cleaning, and almost isolated simultaneously solar thermal energy, even summer, the room is also nice and cool.
The antifouling exterior wall putty of heat-isolating antiseepage of the present invention can be modulated multiple abundant color, strengthens the decorative effect of buildings.Wherein talcum powder can increase the press polish effect, and defoamer is eliminated the coating steam bubble, and wetting agent and sanitas never degenerate coating for a long time, and dispersion agent is even with colo(u)rant dispersion, and softening agent strengthens the coatingsurface tenacity.
It is greasy that the household skin is used the antifouling exterior wall of heat-isolating antiseepage of the present invention, the magnificent generous impervious stain-proof of metope, long-term metope cleaning as before, summer is indoor nice and cool, people live relievedly, happy, pride.The present invention has advantages such as cost is low, effective, construction is simple, long service life.
Embodiment
Embodiment one:
Antifouling each component of exterior wall putty coating of pink heat-isolating antiseepage is as follows: (units; Gross weight 1000kg)
Calcite in powder 350 swelling perlite powders 30 cenospheres 100
Nano-calcium carbonate sodium 60 talcum powder 50 calcined kaolins 20
Superfine alumina silicate 20 fluoro-silicone emulsions 200 pink mineral dyes 1
Water 150 auxiliary agents 19 are wherein:
Defoamer BYK-34 type 4
Linan, wetting agent Hangzhou P200 of coatings additive(s) factory 6
Dispersion agent anionic polycarboxylate 4
Sanitas KATHONLXE 3
Softening agent dibutylester 2
It is 1mm that putty is coated with the thickness of scraping formation.
Embodiment two:
Antifouling each component of exterior wall putty coating of beige heat-isolating antiseepage is as follows: (units; Gross weight 1000kg)
Calcite in powder 320 swelling perlite powders 40 cenospheres 90
Nano-calcium carbonate sodium 80 talcum powder 50 calcined kaolins 20
Superfine alumina silicate 30 fluoro-silicone emulsions 190 beige mineral dyes 1
Water 160 auxiliary agents 19 are wherein:
Defoamer BYK-34 type 4
Linan, wetting agent Hangzhou P200 of coatings additive(s) factory 6
Dispersion agent anionic polycarboxylate 4
Sanitas KATHONLXE 3
Softening agent dibutylester 2
It is 1.2mm that putty is coated with the thickness of scraping formation.
The production method of exterior wall putty:
(1) distilled water, fluoro-silicone emulsion being put into reactor stirred 5 minutes;
(2) mineral dye being put into reactor stirred 10 minutes;
(3) calcite in powder, swelling perlite powder, cenosphere, nano-calcium carbonate, talcum powder, calcined kaolin, superfine alumina silicate are put into reactor and stirred 30 minutes, stop carrying out in 20 minutes reactive polymeric;
(4) put into auxiliary agent and stirred 30 minutes, stopped restir 10 minutes 10 minutes.
(5) above-mentioned materials being put into shredder grinds;
(6) with product packing, packing.
Above-mentioned process sequence is (1), (2), (3), (4), (5), (6).
Certainly only enumerated two kinds of embodiments here, the protection domain that other composition that roughly the same, is equal to, technology, content etc. all should belong to this patent repeats no more here.
Claims (2)
1. antifouling exterior wall putty of heat-isolating antiseepage is characterized in that:
Calcite in powder 25%-35%
Swelling perlite powder 2%-6%
Cenosphere 5%-10%
Particle diameter is the sodium rice lime carbonate 4%-8% of 15nm-30nm
Talcum powder 2%-5%
Calcined kaolin 1%-3%
Superfine alumina silicate 1%-3%
Fluoro-silicone emulsion 15%-30%
Water 10%-20%
Auxiliary agent 1.5%-4%
Wherein auxiliary agent contains defoamer 0.2%-0.4%, wetting agent 0.6%-0.8%, dispersion agent 0.3%-0.6% softening agent 0.1%-0.5%, sanitas 0.3%-0.8%.
2. putty according to claim 1 is characterized in that also containing the mineral dye of 0.1%-0.2%.