CN1446865A - Aquosity intaglio printing ink and its preparation method - Google Patents
Aquosity intaglio printing ink and its preparation method Download PDFInfo
- Publication number
- CN1446865A CN1446865A CN 02135082 CN02135082A CN1446865A CN 1446865 A CN1446865 A CN 1446865A CN 02135082 CN02135082 CN 02135082 CN 02135082 A CN02135082 A CN 02135082A CN 1446865 A CN1446865 A CN 1446865A
- Authority
- CN
- China
- Prior art keywords
- printing ink
- intaglio printing
- water
- aquosity intaglio
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A water ink for intaglio printing is prepared from acrylic resin, alcohol, wetting agent, pigment, neutralizing agent, acrylic emulsion, defoaming agent, wax, levelling agent and water through predispersing pigment, grinding, hydrating and preparing ink. Its advantages are gay color, high transparency and printing adaptability, and low pollution.
Description
Technical field the present invention relates to the printing ink based on artificial resin, relates in particular to a kind of aquosity intaglio printing ink and preparation method thereof.
The water color ink of the existing press of background technology, form and aspect are relatively dimer, and printing adaptability is relatively poor, generally can only be applied to flexographic printing, and its printing quality is difficult to satisfy the requirement of high-grade packing materials such as cigarette-brand, wine box, gift box.
Summary of the invention is to remedy the defective that prior art exists, and the present invention proposes a kind of aquosity intaglio printing ink and preparation method thereof.The technical scheme that adopts is as follows:
This aquosity intaglio printing ink is characterized in that each component and degree are respectively:
Acrylic resin 9.00～17.50%;
Alcohols 22.50～35.00%;
Wetting agent 0.43～1.23%;
Pigment 10.07～24.60%;
Neutralizing agent 3.51～7.26%;
ACRYLIC EMULSION 18.85～33.08%;
Defoamer 0.17～0.37%;
Wax 0.43～0.99%;
Flow agent 0.43～1.23%;
Water 9.43～22.05%.
The further feature of this aquosity intaglio printing ink is:
Acrylic resin can be pure Class C resin, also can be polyfunctional group;
Pigment can be water-based paint;
Wetting agent can be surfactant-based;
Neutralizing agent can be an ammoniacal liquor, also can be organic amine;
ACRYLIC EMULSION can be multifunctional water-borne acrylic resin;
Defoamer can be a silicone antifoam agent;
Wax can be polyethylene kind wax;
Flow agent can be the organosilicon flow agent;
Water can be deionized water.
The preparation method of this aquosity intaglio printing ink is characterized in that following operation is arranged successively:
(1) pigment is pre-dispersed: alcohols is placed agitator, 50～60 ℃ of temperature, slowly add acrylic resin during stirring at low speed, all dissolve until acrylic resin, add wetting agent then, stirred 4～8 minutes, and slowly added pigment again, stirring velocity is increased to 1500 rev/mins, stirred 20～40 minutes, the test color slurry viscosity replenishes the adding alcohols, regulates viscosity to 1300～1500 centipoises (40 ℃):
(2) mill base grinds: with (1) prepared mill base, place horizontal sand mill to grind, keep 55～60 ℃ of drop temperatures, 100 kilograms/hour of flows make the mill base fineness be less than or equal to 1 micron;
(3) Water-borne modification is handled: the mill base after (2) are ground, and place the agitator high speed to stir, 1500 rev/mins of stirring velocitys slowly drip neutralizing agent, and being neutralized to the pH value is 8.5～9.5;
(4) preparation printing ink: ACRYLIC EMULSION, defoamer, wax, flow agent and water are added in the mill base after (3) Water-borne modification is handled successively, mix, water is regulated about viscosity to 50 second (Zan Shi 2# cup, 25 ℃).
The present invention's beneficial effect against existing technologies is, the component novelty, the batching science, preparation is simple, cost is lower, owing to adopted elder generation with the good solvent type resin master grind of pigment wettability, after carry out the Water-borne modification treatment process, its form and aspect are bright-coloured, the transparency is better with printing adaptability, can be used for 100 meters/minute high-speed intaglio printing machines, the form and aspect of its four looks China ink are with the international color standard aberration of PANTOAE
Be less than or equal to 1, and the color gamut broad, printing quality can satisfy the requirement of high-grade packing materials such as cigarette-brand, wine box, gift box.In addition, its alcohols content is in use less than 20%, and all the other are water, and are low to topsoil, and it is residual not have noxious solvent, helps safety in production and environment protection.
Embodiment
A kind of aquosity intaglio printing ink
This aquosity intaglio printing ink, each component and degree are respectively acrylic resins 10.0%, alcohols 30.0%, wetting agent 1.0%, water-based paint 12.0%, ammoniacal liquor 6.0%, multifunctional water-borne acrylic resin 25.0%, defoamer 0.4%, wax 0.4%, flow agent 0.8% and deionized water 14.4%.
A kind of preparation method of aquosity intaglio printing ink
The preparation method of this aquosity intaglio printing ink has following operation successively:
(1) pigment is pre-dispersed: alcohols is placed agitator, 55 ℃ of temperature, slowly add acrylic resin during stirring at low speed, all dissolve until acrylic resin, add wetting agent then, stirred 5 minutes, and slowly added water-based paint again, stirring velocity is increased to 1500 rev/mins, stirred 30 minutes, the test color slurry viscosity replenishes the adding alcohols, regulates viscosity to 1400 centipoise (40 ℃);
(2) mill base grinds: with (1) prepared mill base, place horizontal sand mill to grind, keep 58 ℃ of drop temperatures, 100 kilograms/hour of flows make the mill base fineness be less than or equal to 1 micron;
(3) Water-borne modification is handled: the mill base after (2) are ground, and place the agitator high speed to stir, 1500 rev/mins of stirring velocitys are added dropwise to ammoniacal liquor slowly, and being neutralized to the pH value is 9;
(4) preparation printing ink: multifunctional water-borne acrylic resin, defoamer, wax, flow agent and deionized water are added in the mill base after (3) Water-borne modification is handled successively, mix, regulate about viscosity to 50 second (Zan Shi 2# cup, 25 ℃) with deionized water.
Claims (11)
1, a kind of aquosity intaglio printing ink, it is characterized in that each component and degree are respectively acrylic resins 9.00～17.50%, alcohols 22.50～35.00%, wetting agent 0.43～1.23%, pigment 10.07～24.60%, neutralizing agent 3.51～7.26%, ACRYLIC EMULSION 18.85～33.08%, defoamer 0.17～0.37%, wax 0.43～0.99%, flow agent 0.43～1.23% and water 9.43～22.05%.
2, aquosity intaglio printing ink as claimed in claim 1 is characterized in that acrylic resin can be pure Class C resin, also can be polyfunctional group.
3, aquosity intaglio printing ink as claimed in claim 1 is characterized in that pigment can be water-based paint.
4, aquosity intaglio printing ink as claimed in claim 1 is characterized in that wetting agent can be surfactant-based.
5, aquosity intaglio printing ink as claimed in claim 1 is characterized in that neutralizing agent can be an ammoniacal liquor, also can be organic amine.
6, aquosity intaglio printing ink as claimed in claim 1 is characterized in that ACRYLIC EMULSION can be multifunctional water-borne acrylic resin.
7, aquosity intaglio printing ink as claimed in claim 1 is characterized in that defoamer can be a silicone antifoam agent.
8, aquosity intaglio printing ink as claimed in claim 1 is characterized in that wax can be polyethylene kind wax.
9, aquosity intaglio printing ink as claimed in claim 1 is characterized in that flow agent can be the organosilicon flow agent.
10, aquosity intaglio printing ink as claimed in claim 1 is characterized in that water can be deionized water.
11, a kind of preparation method of aquosity intaglio printing ink has following operation successively:
111 pigment are pre-dispersed: alcohols is placed agitator, 50～60 ℃ of temperature, slowly add acrylic resin during stirring at low speed, all dissolve until acrylic resin, add wetting agent then, stirred 4～8 minutes, and slowly added pigment again, stirring velocity is increased to 1500 rev/mins, stirred 20～40 minutes, the test color slurry viscosity replenishes the adding alcohols, regulates viscosity to 1300～1500 centipoises (40 ℃);
112 mill bases grind: with 111 prepared mill bases, place horizontal sand mill to grind, keep 55～60 ℃ of drop temperatures, 100 kilograms/hour of flows make the mill base fineness be less than or equal to 1 micron;
113 Water-borne modification are handled: with the mill base after 112 grindings, place the agitator high speed to stir, 1500 rev/mins of stirring velocitys slowly drip neutralizing agent, and being neutralized to the pH value is 8.5～9.5;
114 preparation printing ink: ACRYLIC EMULSION, defoamer, wax, flow agent and water are added in the mill base after 113 Water-borne modification are handled successively, mix, water is regulated about viscosity to 50 second (Zan Shi 2# cup, 25 ℃).