CN102093780A - Non-woven fabric environmental-protection water-based ink and preparation method thereof - Google Patents
Non-woven fabric environmental-protection water-based ink and preparation method thereof Download PDFInfo
- Publication number
- CN102093780A CN102093780A CN2010106189470A CN201010618947A CN102093780A CN 102093780 A CN102093780 A CN 102093780A CN 2010106189470 A CN2010106189470 A CN 2010106189470A CN 201010618947 A CN201010618947 A CN 201010618947A CN 102093780 A CN102093780 A CN 102093780A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven fabrics
- environment
- printing ink
- based printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of water-based inks, and relates to a non-woven fabric environmental-protection water-based ink and a preparation method thereof. The non-woven fabric environmental-protection water-based ink is prepared from the following raw materials in parts by weight: 12-18 parts of high-performance organic pigment, 18-25 parts of acrylic resin, 1-5 parts of dispersant, 0.1-0.5 part of defoaming agent, 8-15 parts of deionized water, 25-35 parts of self-crosslinked acrylic emulsion, 15-25 parts of acrylic emulsion, 1-5 parts of wax slurry and 0.5-0.8 part of organic anti-scratch agent. The non-woven fabric environmental-protection water-based ink has the advantages of bright color, light resistance, no discoloring and soft texture. When being printed on non-woven fabrics, the non-woven fabric environmental-protection water-based ink does not crack or crease, has high adhesive force for non-woven fabrics, and does not fade or shed when the non-woven fabrics are kneaded.
Description
Technical field
The invention belongs to the water color ink technical field, environment-friendly water-based printing ink of particularly a kind of non-woven fabrics and preparation method thereof.
Background technology
Along with country comes strictness more to environmental protection requirement, non-woven fabrics is as environment-friendly materials of new generation, be widely used in industries such as agricultural film, Pading cloth, decoration, chemical industry, printing, automobile, building materials, beauty treatment, furniture, particularly through being usually used in making gift bag, shopping bag or the like.Non-woven fabrics has powerful good, air permeable waterproof, environmental protection, pliable and tough, nonpoisonous and tasteless, and advantage such as low price.When non-woven fabrics is used, usually need the ink printing pattern to make it have the excellent decoration effect in its surface.Because non-woven fabrics is between plastics and textiles, its printing has singularity, and there is following shortcoming in existing non-woven fabrics printing-ink: the sticking power to non-woven fabrics is low, shines back variable color easily, easy cracking, wrinkling, and rubbing is faded easily, dry linting.
Summary of the invention
The objective of the invention is to provides a kind of non-woven fabrics environment-friendly water-based printing ink at the deficiencies in the prior art, and it is bright-colored, sun-proof, nondiscoloration, and the quality softness does not ftracture, and is wrinkle resistant, and the sticking power of non-woven fabrics than higher, is crumpled colour-fast, dry linting not.
Another object of the present invention is to provide the preparation method of the environment-friendly water-based printing ink of a kind of non-woven fabrics, this preparation method is simple to operate, has reduced production cost, is fit to suitability for industrialized production.
The object of the present invention is achieved like this.
The environment-friendly water-based printing ink of a kind of non-woven fabrics, it is made up of the raw material of following weight part:
12 parts ~ 18 parts of high-performance pigment dyestuffs
18 parts ~ 25 parts of acrylic resins
1 part ~ 5 parts of dispersion agents
0.1 part ~ 0.5 part of defoamer
8 parts ~ 15 parts of deionized waters
25 parts ~ 35 parts of self-crosslinking acrylic emulsions
15 parts ~ 25 parts of ACRYLIC EMULSION
1 part ~ 5 parts in wax slurry
0.5 part ~ 0.8 part of organic scratch resistance agent.
Preferably, it is made up of the raw material of following weight part:
12 parts ~ 15 parts of high-performance pigment dyestuffs
18 parts ~ 22 parts of acrylic resins
1 part ~ 5 parts of dispersion agents
0.1 part ~ 0.5 part of defoamer
8 parts ~ 10 parts of deionized waters
25 parts ~ 30 parts of self-crosslinking acrylic emulsions
15 parts ~ 20 parts of ACRYLIC EMULSION
1 part ~ 5 parts in wax slurry
0.5 part ~ 0.8 part of organic scratch resistance agent.
Preferably, it is made up of the raw material of following weight part:
15 parts ~ 18 parts of high-performance pigment dyestuffs
22 parts ~ 25 parts of acrylic resins
1 part ~ 5 parts of dispersion agents
0.1 part ~ 0.5 part of defoamer
10 parts ~ 15 parts of deionized waters
30 parts ~ 35 parts of self-crosslinking acrylic emulsions
20 parts ~ 25 parts of ACRYLIC EMULSION
1 part ~ 5 parts in wax slurry
0.5 part ~ 0.8 part of organic scratch resistance agent.
More preferably, it is made up of the raw material of following weight part:
15 parts of high-performance pigment dyestuffs
20.3 parts of acrylic resins
2 parts of dispersion agents
0.2 part of defoamer
10 parts of deionized waters
30 parts of self-crosslinking acrylic emulsions
20 parts of ACRYLIC EMULSION
2 parts in wax slurry
0.5 part of organic scratch resistance agent.
Wherein, the high-performance pigment dyestuff is that in phthalein viridescent, phthalocyanine blue, permanent bordeaux, biphenyl ammonia Huang, carbon black, the titanium dioxide one or more mix by arbitrary proportion.
Wherein, dispersion agent is any one in the high 760W of enlightening, ADDITOL VXW6394, ADDITOL VX 6528, TROYSPERSE 90W, SURFYLNOL CT-221, the SURFYLNOL CT-151 dispersion agent.
Wherein, defoamer be that enlightening is high by 805, in TEGO-815, TEGO-825, SURFYNOL DF-75, ADDITOL VXL 4951, Lu Borun 384, Lu Borun 387 defoamers any one.
Wherein, the wax slurry is any one in Mitsubishi W410, LUMAX AF-29, POLIGEN WE-6, ACUMIST A-6, the ACUMIST 3105B wax slurry.
Wherein, organic scratch resistance agent is any one in DOW CORNING DC51, the organic scratch resistance agent of TROYSOL MS-2.
The preparation method of the environment-friendly water-based printing ink of a kind of non-woven fabrics, it comprises following preparation process:
(a) by above-mentioned weight part, add acrylic resin, dispersion agent, defoamer and deionized water in container, thorough mixing adds the high-performance pigment dyestuff then, stirs, and is ground to fineness below 10 microns through shredder then, makes mill base;
(b) with mill base, self-crosslinking acrylic emulsion, ACRYLIC EMULSION, wax slurry and organic scratch resistance agent thorough mixing;
(c) be up to the standards, finished product.
Wherein, in the step (c), be up to the standards concrete method and index are: the environment-friendly water-based printing ink of the non-woven fabrics that makes is measured its viscosity with Chai Shi cup 4#, and viscosity is 20 ~ 25sec/25 ℃; Aberration △ T2 ≦ 5; The pH value is 8.0 ~ 9.0.
Beneficial effect of the present invention: the environment-friendly water-based printing ink of a kind of non-woven fabrics of the present invention, it is made up of the raw material of following weight part: 12 parts ~ 18 parts of high-performance pigment dyestuffs, 18 parts ~ 25 parts of acrylic resins, 1 part ~ 5 parts of dispersion agents, 0.1 part ~ 0.5 part of defoamer, 8 parts ~ 15 parts of deionized waters, 25 parts ~ 35 parts of self-crosslinking acrylic emulsions, 15 parts ~ 25 parts of ACRYLIC EMULSION, 1 part ~ 5 parts in wax slurry, 0.5 part ~ 0.8 part of organic scratch resistance agent.The environment-friendly water-based ink colors of this non-woven fabrics is bright-coloured, sun-proof, nondiscoloration, and the quality softness is printed on the non-woven fabrics, does not ftracture, and is wrinkle resistant, and the sticking power of non-woven fabrics than higher, is crumpled colour-fast, dry linting not.
The preparation method of the environment-friendly water-based printing ink of a kind of non-woven fabrics, it comprises following preparation process: (a) by above-mentioned weight part, in container, add acrylic resin, dispersion agent, defoamer and deionized water, thorough mixing, add the high-performance pigment dyestuff then, stir, be ground to fineness below 10 microns through shredder then, make mill base; (b) with mill base, self-crosslinking acrylic emulsion, ACRYLIC EMULSION, wax slurry and organic scratch resistance agent thorough mixing; (c) be up to the standards, finished product.This preparation method is simple to operate, has reduced production cost, is fit to suitability for industrialized production.
Embodiment
The present invention is further illustrated with specific embodiment below, but the present invention is not subjected to the qualification of following embodiment.
Embodiment 1.
The environment-friendly water-based printing ink of a kind of non-woven fabrics, it comprises following preparation process: (a) add 10 parts of 20.3 parts of acrylic resins, 2 parts of the high 760W dispersion agents of enlightening, 0.2 part of high 805 defoamer of enlightening and deionized waters in container, thorough mixing, add 15 parts of high-performance pigment dyestuff phthalein viridescents (PG.7) then, stir, be ground to fineness at 9 microns through shredder then, make mill base.
(b) mill base that step (a) is made and 30 parts of self-crosslinking acrylic emulsions, 20 parts of ACRYLIC EMULSION, 2 parts in Mitsubishi W410 wax slurry and the organic scratch resistance agent of DOW CORNING DC51 are 0.5 part, thorough mixing.
(c) measure its viscosity with Chai Shi cup 4#, viscosity is 25sec/25 ℃; Aberration △ T2=5; The pH value is 8.0, be up to the standards, finished product.
Embodiment 2.
The environment-friendly water-based printing ink of a kind of non-woven fabrics, it comprises following preparation process: (a) add 8 parts of 18 parts of acrylic resins, 1 part of ADDITOL VXW6394 dispersion agent, 0.1 part of TEGO-825 defoamer and deionized waters in container, thorough mixing, add 6 parts of high-performance pigment dyestuff phthalocyanine blues, 6 parts of titanium dioxide then, stir, be ground to fineness at 6 microns through shredder then, make mill base.
(b) mill base that step (a) is made and 25 parts of self-crosslinking acrylic emulsions, 15 parts of ACRYLIC EMULSION, 1 part in LUMAX AF-29 wax slurry and the organic scratch resistance agent of TROYSOL MS-2 are 0.5 part, thorough mixing.
(c) measure its viscosity with Chai Shi cup 4#, viscosity is 20sec/25 ℃; Aberration △ T2=3; The pH value is 8.5, be up to the standards, finished product.
Embodiment 3.
The environment-friendly water-based printing ink of a kind of non-woven fabrics, it comprises following preparation process: (a) add 15 parts of 25 parts of acrylic resins, 5 parts of SURFYLNOL CT-151 dispersion agents, 0.5 part of Lu Borun 384 defoamer and deionized waters in container, thorough mixing, add dark green 5 parts of high-performance pigment dyestuff phthalein, 5 parts of phthalocyanine blues, 4 parts of carbon blacks, 4 parts of titanium dioxide then, stir, be ground to fineness at 3 microns through shredder then, make mill base.
(b) mill base that step (a) is made and 35 parts of self-crosslinking acrylic emulsions, 25 parts of ACRYLIC EMULSION, 5 parts in ACUMIST 3105B wax slurry and the organic scratch resistance agent of DOW CORNING DC51 are 0.8 part, thorough mixing.
(c) measure its viscosity with Chai Shi cup 4#, viscosity is 23sec/25 ℃; Aberration △ T2=2; The pH value is 9, be up to the standards, finished product.
The above only is preferred embodiment of the present invention, so all equivalences of doing according to the described structure of patent claim of the present invention, feature and principle change or modify, is included in the patent claim of the present invention.
Claims (7)
1. environment-friendly water-based printing ink of non-woven fabrics, it is characterized in that: it is made up of the raw material of following weight part:
12 parts ~ 18 parts of high-performance pigment dyestuffs
18 parts ~ 25 parts of acrylic resins
1 part ~ 5 parts of dispersion agents
0.1 part ~ 0.5 part of defoamer
8 parts ~ 15 parts of deionized waters
25 parts ~ 35 parts of self-crosslinking acrylic emulsions
15 parts ~ 25 parts of ACRYLIC EMULSION
1 part ~ 5 parts in wax slurry
0.5 part ~ 0.8 part of organic scratch resistance agent.
2. the environment-friendly water-based printing ink of a kind of non-woven fabrics according to claim 1, it is characterized in that: it is made up of the raw material of following weight part:
12 parts ~ 15 parts of high-performance pigment dyestuffs
18 parts ~ 22 parts of acrylic resins
1 part ~ 5 parts of dispersion agents
0.1 part ~ 0.5 part of defoamer
8 parts ~ 10 parts of deionized waters
25 parts ~ 30 parts of self-crosslinking acrylic emulsions
15 parts ~ 20 parts of ACRYLIC EMULSION
1 part ~ 5 parts in wax slurry
0.5 part ~ 0.8 part of organic scratch resistance agent.
3. the environment-friendly water-based printing ink of a kind of non-woven fabrics according to claim 1, it is characterized in that: it is made up of the raw material of following weight part:
15 parts ~ 18 parts of high-performance pigment dyestuffs
22 parts ~ 25 parts of acrylic resins
1 part ~ 5 parts of dispersion agents
0.1 part ~ 0.5 part of defoamer
10 parts ~ 15 parts of deionized waters
30 parts ~ 35 parts of self-crosslinking acrylic emulsions
20 parts ~ 25 parts of ACRYLIC EMULSION
1 part ~ 5 parts in wax slurry
0.5 part ~ 0.8 part of organic scratch resistance agent.
4. the environment-friendly water-based printing ink of a kind of non-woven fabrics according to claim 1, it is characterized in that: it is made up of the raw material of following weight part:
15 parts of high-performance pigment dyestuffs
20.3 parts of acrylic resins
2 parts of dispersion agents
0.2 part of defoamer
10 parts of deionized waters
30 parts of self-crosslinking acrylic emulsions
20 parts of ACRYLIC EMULSION
2 parts in wax slurry
0.5 part of organic scratch resistance agent.
5. according to any environment-friendly water-based printing ink of described a kind of non-woven fabrics of claim 1 ~ 4, it is characterized in that: the high-performance pigment dyestuff is that in phthalein viridescent, phthalocyanine blue, permanent bordeaux, biphenyl ammonia Huang, carbon black, the titanium dioxide one or more mix by arbitrary proportion.
6. the preparation method of any environment-friendly water-based printing ink of described a kind of non-woven fabrics of claim 1 ~ 4, it is characterized in that: it comprises following preparation process:
(a) by above-mentioned weight part, add acrylic resin, dispersion agent, defoamer and deionized water in container, thorough mixing adds the high-performance pigment dyestuff then, stirs, and is ground to fineness below 10 microns through shredder then, makes mill base;
(b) with mill base, self-crosslinking acrylic emulsion, ACRYLIC EMULSION, wax slurry and organic scratch resistance agent thorough mixing;
(c) be up to the standards, finished product.
7. the preparation method of the environment-friendly water-based printing ink of a kind of non-woven fabrics according to claim 6, it is characterized in that: in the step (c), concrete method and the index of being up to the standards is: the environment-friendly water-based printing ink of the non-woven fabrics that makes is measured its viscosity with Chai Shi cup 4#, and viscosity is 20 ~ 25sec/25 ℃; Aberration △ T2 ≦ 5; The pH value is 8.0 ~ 9.0.