CN1424350A - 高比重的隔声复合材料 - Google Patents

高比重的隔声复合材料 Download PDF

Info

Publication number
CN1424350A
CN1424350A CN 02157782 CN02157782A CN1424350A CN 1424350 A CN1424350 A CN 1424350A CN 02157782 CN02157782 CN 02157782 CN 02157782 A CN02157782 A CN 02157782A CN 1424350 A CN1424350 A CN 1424350A
Authority
CN
China
Prior art keywords
composite material
agent
sound insulation
specific weight
high specific
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 02157782
Other languages
English (en)
Other versions
CN1176989C (zh
Inventor
蔡伟民
蔡俊
徐菲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jiaotong University
Original Assignee
Shanghai Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jiaotong University filed Critical Shanghai Jiaotong University
Priority to CNB02157782XA priority Critical patent/CN1176989C/zh
Publication of CN1424350A publication Critical patent/CN1424350A/zh
Application granted granted Critical
Publication of CN1176989C publication Critical patent/CN1176989C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种高比重的隔声复合材料属于高分子材料领域。本发明各组分及其重量百分比含量为：PVC：5％～35％，粒径为2～60微米的钨粉：40％～90％，偶联剂：1％～10％，助剂：4％～15％。本发明的材料除具有柔软和隔声性能好外，还具有阻燃、防化学介质、防腐蚀、无毒、可施工性等特点，适合于做都市高架轨道交通、航空和港口的隔声材料，以及建筑行业轻质墙板夹层的隔声处理，使用此种隔声复合材料可以有效地降低噪声，改善工作和生活环境，当材料厚度为1mm时，对100～1600Hz声音的平均隔声量可达20～25分贝。

Description

高比重的隔声复合材料
技术领域
本发明涉及的是一种复合材料，特别是一种高比重的隔声复合材料，属于高分子材料领域。
背景技术
关于隔声材料的研制和应用已有几十年的历史，已形成了比较成熟的研制和生产体系，但是目前市场上通常使用的隔声材料都存在一些缺点如产品成本高，多为硬质材料，因此不易二次加工和难以用于不规则物体的隔声处理。其应用因此受限。经文献检索发现，中国专利号为：97197487.X，专利名称为：高密度复合材料，公布了一种高密度复合材料，该专利通过粘结剂把提高强度的纤维和直径2～40微米的钨粉结合，制成一种可用作铅替代品的材料(作为无毒、无铅、对环境安全、省钱的射弹芯替代材料)。其材料成份为钨粉和纤维和粘接剂，通过注塑、模压成型，用于很需要铅的高密度又不希望有铅污染的场合，可作为含铅高密度材料的替代品。但该材料由于其成份(纤维和粘接剂)决定了仅能用注塑或模压成型，因此难制成大面积的薄膜。
发明内容
本发明的目的在于克服背景技术中的不足，提供一种高比重的隔声复合材料，使其具有柔软，易二次加工，可施用性强，可适用于不规则物体的隔声处理等优点。本发明是通过以下技术方案实现的，本发明各组分及其重量百分比含量为：PVC：5％～35％，粒径为2～60微米的钨粉：40％～90％，偶联剂：1％～10％，助剂：4％～15％；通过混炼后经注塑、模压或压延而成型。
偶联剂采用钛酸酯类偶联剂中的一种或几种，助剂选用普通稳定剂、增塑剂和抗老化剂中的一种或几种。
本发明具有实质性特点和显著进步。本发明除具有材料的柔软好和隔声性能高外，还具有阻燃、防化学介质、防腐蚀、无毒、可施工性好等特点，特别是在材料成份中摈弃了纤维与粘接剂，因此可通过压延连续成型技术而制得大面积的软质薄膜，适合于做都市高架轨道交通、航空和港口的隔声材料，以及建筑行业轻质墙板夹层的隔声处理。使用此种隔声复合材料可以有效地降低噪声，改善工作和生活环境，当材料厚度为1mm时，对100～1600Hz声音的平均隔声量可达20～25分贝。
实施例一
将各组分以下列配比均匀混合，并在开炼机上混炼，制成1毫米的软质薄片，其平均隔声量在23分贝左右。
PVC：35％，钨粉(2微米)：40％，单烷氧基三(二辛基磷酰氧基)钛酸酯：10％，邻苯二甲酸二丁酯：10％，硬脂酸钡：2％，三盐基硫酸铅：3％。
实施例二
将下列组分混合均匀后在开炼机上混炼，制成1毫米的软质薄片，其隔声量在18~27分贝之间(100～600Hz)。
PVC：15％，钨粉(25微米)：80％，异丙基三羧基钛酸酯：1％，邻苯二甲酸二丁酯：3％，硬脂酸钡：0.5％。三盐基硫酸铅：0.5％。
实施例三
取PVC：5％，钨粉(60微米)：90％，单烷氧基三(二辛基磷酰氧基)钛酸酯：1％，邻苯二甲酸二丁酯：2％，硬脂酸钡：1％，三盐基硫酸铅：1％，加工制成1mm薄板，可以成为隔声量为21分贝的隔声材料。
实施例四
取PVC：20％，钨粉(2微米)：55％，单烷氧基三(二辛基磷酰氧基)钛酸酯：10％，邻苯二甲酸二丁酯：10％，硬脂酸钡：2％，三盐基硫酸铅：3％，在低频范围(100Hz～1600Hz)内平均隔声量为20分贝。

Claims (3)

1、一种高比重的隔声复合材料，其特征在于：各组分及其重量百分比含量为：PVC：5％～35％，粒径为2～60微米的钨粉：40％～90％，偶联剂：1％～10％，助剂：4％～15％。
2、根据权利要求1所述的这种高比重的隔声复合材料，其特征是所述的偶联剂，其采用钛酸酯类偶联剂中的一种或几种。
3、根据权利要求1所述的这种高比重的隔声复合材料，其特征是所述的助剂，是选用稳定剂、增塑剂和抗老化剂中的一种或几种。
CNB02157782XA 2002-12-26 2002-12-26 高比重的隔声复合材料 Expired - Fee Related CN1176989C (zh)