CN1424347A - 用于隔声降噪的软质超高比重复合材料 - Google Patents

用于隔声降噪的软质超高比重复合材料 Download PDF

Info

Publication number
CN1424347A
CN1424347A CN 02157785 CN02157785A CN1424347A CN 1424347 A CN1424347 A CN 1424347A CN 02157785 CN02157785 CN 02157785 CN 02157785 A CN02157785 A CN 02157785A CN 1424347 A CN1424347 A CN 1424347A
Authority
CN
China
Prior art keywords
soft
sound insulation
superelevation
matrix material
noise reducing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 02157785
Other languages
English (en)
Other versions
CN1176157C (zh
Inventor
蔡伟民
蔡俊
徐菲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jiaotong University
Original Assignee
Shanghai Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jiaotong University filed Critical Shanghai Jiaotong University
Priority to CNB021577854A priority Critical patent/CN1176157C/zh
Publication of CN1424347A publication Critical patent/CN1424347A/zh
Priority to PCT/CN2003/001102 priority patent/WO2004058867A1/zh
Priority to AU2003292865A priority patent/AU2003292865A1/en
Application granted granted Critical
Publication of CN1176157C publication Critical patent/CN1176157C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种用于隔声降噪的软质超高比重复合材料属于高分子材料领域。本发明各组分及其重量百分比含量为：高分子聚合物：5％～30％，粒径为100纳米～2微米的钨粉：10％～90％，增塑剂：3％～10％，稳定剂：1％～5％，偶联剂：1％～10％。本发明除具有良好的隔声和力学性能外，还具有阻燃、防化学介质、防腐蚀、无毒、可施工性等特点，而其柔软的特点克服了以往隔声材料厚重，不易加工的缺点，给本发明的应用提供了更大的空间，适合于做都市高架轨道交通、航空和港口的隔声材料，以及建筑行业轻质墙板夹层的隔振处理，使用此种隔声复合材料可以有效地降低噪声，改善工作和生活环境。

Description

用于隔声降噪的软质超高比重复合材料
技术领域
本发明涉及的是一种复合材料，特别是可用于隔声降噪的软质超高比重复合材料，属于高分子材料领域。
背景技术
关于隔声材料的研制和应用已有几十年的历史，但是目前市场上通常使用的隔声材料都存在一些缺点，如：产品成本高，多为硬质材料而不易二次加工和难施用于不规则物体的隔声处理等。其应用范围因此受限。众所周知，材料的隔声量遵守质量定律：TL＝20lgm+20lgf-43dB，式中：TL-声波垂直入射条件下的隔声量，dB；m-材料的面密度，kg/m2；f-入射声波频率，Hz。当材料单位面积质量增加一倍，则声音传递损失增加6dB。可见高比重特性可使材料具有高面密度，在厚度很小的情况下，即可具有较高的隔声性能。根据“质量定律”，传统的像砖墙、水泥墙或厚钢板、铅板等单位面积质量大的材料，隔声效果虽然都比较好，但是由于比较厚重，加工和可施工性差，不施用于不规则物体的隔声处理。
经文献检索，日本专利JP56059857，名称为：SOUND-INSULATINGCOMPOSITION(隔声复合材料)，公开了一种软质隔声材料的制备技术。该专利采用铅粉等无机金属为原料，制成具有一定隔声性能的软质材料。但是铅对环境有害，而且隔声效果也不够。
发明内容
本发明的目的在于克服现有技术中的不足，提供一种用于隔声降噪的软质超高比重复合材料，使其有效降低噪声，不危害环境。本发明是通过以下技术方案实现的，本发明各组分及其重量百分比含量为：高分子聚合物：5％～30％，粒径为100纳米～2微米的钨粉：10％～90％，增塑剂：3％～10％，稳定剂：1％～5％，偶联剂：1％～10％；通过混炼后经注塑、模压或压延而成型。
其中高分子聚合物可以是橡胶、热塑性塑料或两者的混合物，其中橡胶可以是丁腈胶、氯丁胶、天然橡胶，热塑性塑料是链状高分子结构，例如聚乙烯、聚苯乙烯、聚丙烯、聚氯乙烯，增塑剂包括下列增塑剂中的一种或几种：邻苯二甲酸二丁酯，邻苯二甲酸二辛酯，邻苯二甲酸二乙酯。偶联剂采用钛酸酯类偶联剂中的一种或几种。
本发明具有实质性特点和显著进步，本发明除具有良好的隔声和力学性能外，还具有阻燃、防化学介质、防腐蚀、无毒、可施工性等特点，而其柔软的特点克服了以往隔声材料厚重，不易加工的缺点，给本发明的应用提供了更大的空间，适合于做都市高架轨道交通、航空和港口的隔声材料，以及建筑行业轻质墙板夹层的隔声处理。使用此种复合材料可以有效地降低噪声，改善工作和生活环境。
具体实施方式
结合本发明的内容进一步提供以下实施例：
实施例一
将各组分以下列配比均匀混合，并在开炼机上混炼，制成1毫米的软质薄片，其平均隔声量在21.6分贝左右，硬度为86(邵氏)。
高分子聚合物：30％(聚苯乙烯：15％，丁腈橡胶：15％)，钨粉(0.1微米)：55％，单烷氧基三(二辛基磷酰氧基)钛酸酯：5％，邻苯二甲酸二丁酯：8％，硬脂酸钡：1％，三盐基硫酸铅：1％。
实施例二
将各组分以下列配比均匀混合，并在开炼机上混炼，制成1毫米的软质薄片，其隔声量在18~27分贝之间(100~1600Hz)，硬度为88(邵氏)。
PVC：15％，钨粉(60微米)：80％，异丙基三羧基钛酸酯：1％，邻苯二甲酸二丁酯：3％，硬脂酸钡：0.5％，三盐基硫酸铅：0.5％。
实施例三
将各组分以下列配比均匀混合，并在开炼机上混炼，制成1毫米的软质薄片，其平均隔声量在22分贝左右，具有良好的抗老化能力。
高分子聚合物：30％(聚乙烯：21％，丁腈橡胶：9％)，钨粉(2微米)：55％，单烷氧基三(二辛基磷酰氧基)钛酸酯：5％，邻苯二甲酸二丁酯：8％，硬脂酸钡：1％，三盐基硫酸铅：1％。
实施例四
将各组分以下列配比均匀混合，并在开炼机上混炼，制成1毫米的软质薄片，其平均隔声量在22分贝左右，具有良好的抗老化能力。
取PVC：5％，钨粉(1.8微米)：90％，异丙基三羧基钛酸酯1％，邻苯二甲酸二丁酯：3％，硬脂酸钡：0.5％，三盐基硫酸铅：0.5％混合均匀加工后，所测的密度为3.54g/cm3，硬度为92(邵氏)。

Claims (6)

1、一种用于隔声降噪的软质超高比重复合材料，其特征在于：各组分及其重量百分比含量为：高分子聚合物：5％～30％，粒径为100纳米～2微米的钨粉：10％～90％，增塑剂：3％～10％，稳定剂：1％～5％，偶联剂：1％～10％。
2、根据权利要求1所述的这种用于隔声降噪的软质超高比重复合材料，其特征是所述的高分子聚合物是橡胶、热塑性塑料或两者的混合物。
3、根据权利要求2所述的这种用于隔声降噪的软质超高比重复合材料，其特征是橡胶是丁腈胶、氯丁胶、天然橡胶。
4、根据权利要求2所述的这种用于隔声降噪的软质超高比重复合材料，其特征是热塑性塑料是链状高分子结构，如：聚乙烯、聚苯乙烯、聚丙烯、聚氯乙烯。
5、根据权利要求1所述的这种用于隔声降噪的软质超高比重复合材料，其特征是所述的增塑剂，包括下列增塑剂中的一种或几种：邻苯二甲酸二丁酯，邻苯二甲酸二辛酯，邻苯二甲酸二乙酯。
6、根据权利要求1所述的这种用于隔声降噪的软质超高比重复合材料，其特征是所述的偶联剂，其采用钛酸酯类偶联剂中的一种或几种。
CNB021577854A 2002-12-26 2002-12-26 用于隔声降噪的软质超高比重复合材料 Expired - Fee Related CN1176157C (zh)