CN1419052A - Method for making environment protection type stainless steel oil pump - Google Patents
Method for making environment protection type stainless steel oil pump Download PDFInfo
- Publication number
- CN1419052A CN1419052A CN 02156698 CN02156698A CN1419052A CN 1419052 A CN1419052 A CN 1419052A CN 02156698 CN02156698 CN 02156698 CN 02156698 A CN02156698 A CN 02156698A CN 1419052 A CN1419052 A CN 1419052A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- oil well
- type stainless
- inductor
- environment protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The preparation method of environment-protecting type stainless steel oil well pump is characterized by that it selects and uses stainless steel as raw material for making said pump, and before alignment procedure it adopts the following steps to make treatment, including: normalizing treatment for 3-4 hr. at 800-930 deg.c; induction heating surface hardening treatment, under the condition of that temp. is 840-1070 deg.c, gap between inducer and inner surface of pump cylinder is 2-2.5 mm, inducer moving speed is 2-8 mm/s and rotating speed of pump cylinder is 50-100 rpm utilizing hardening machine to drive pump cylinder and make it rotate, moving inducer to implement heating continuously hardening treatment; utilizing 20-30 deg.c hardening solution to make spray-cooling treatment; and using tempering furnace to make tempering treatment at 150-230 deg.c and heat-insulating for 30-60 min.
Description
Technical field:
The present invention relates to the used oil well pump preparation method in oil field development field, belong to the preparation method of environment protection type stainless steel oil well pump.
Background technique:
At present along with oil field development progressively deeply, particularly since polymer displacement of reservoir oil, the ternary composite oil-displacing, chemical composition is more complicated also, it is more and more obvious that the equipment that the oil field is used produces corrosion phenomenon.Wherein oil well pump is to recover the oil to use one of equipment, and existing pump barrel is formed through thermo-chemical treatment by structural carbon steel or alloyed steel, and corrosion phenomenon seriously causes reduce working life, is generally 1-2.And most internal surface at pump barrel of taking measures carries out the chromium plating processing, though have certain wear resistance and anti-corrosive properties, but complex manufacturing technology, cost height, difficult quality guarantee, chromium coating very easily occurring combines insecure with parent metal, defective such as bubble, pit, peeling occur or peel off has a strong impact on the quality of pump barrel, and etching problem still exists, cause the shortening of oil well pump life cycle, cause the increase of oil field operation expense; Simultaneously the electrolytic solution in the chrome-plating process is poisonous, and health is threatened or endangers, and the waste water treatment expense after the processing is big, befouling environment.
Summary of the invention:
In order to overcome existing oil well pump short deficiency in working life, the invention provides a kind of preparation method of environment protection type stainless steel oil well pump, this method can be stopped the oil well pump etching problem, prolongs the working life of oil well pump.
Adoptable technological scheme is: the preparation method of the little rust steel of this environment protection type oil well pump, in the material of selecting for use stainless steel as the oil well pump pump barrel, through operations such as cold-drawn, fracture, normalized treatment, induced surface hardening, alignment, defect detecting test, right borings, before alignment process, handle: normalizing or annealing in process by following step, be to carry out normalizing or annealing in process under 800～930 ℃ of conditions 3～4 hours in temperature promptly, slow cooling to 600～750 are ℃ fast cold; Induced surface hardening is handled, promptly temperature be 840～1070 ℃, inductor and pump barrel internal surface gaps between 2～2.5mm, the inductor travelling speed utilizes quenching machine to drive the pump barrel rotation at 2～8mm/s, pump barrel under 50～100 rev/mins condition with the lathe rotational speed, inductor moves the heating continuous quenching; Cooling promptly utilizes 20～30 ℃ of quenching liquids with spray regime, sprays by the quenching liquid spray orifice on the inductor and carries out cooling processing; Temper, promptly cooling back pump barrel is that the insulation of process tempering furnace is come out of the stove cold soon under 150～230 ℃ of conditions after 30～60 minutes in temperature.
Above-mentioned stainless steel is the martensite type stainless steel, the trade mark of martensite type stainless steel is 3Cr13Mo, 9Cr18Mo, 7Cr17,8Cr17 or 11Cr17, quenching liquid is polyvinyl alcohol water solution or emulsified liquid, the diameter of quenching liquid spray orifice is that 1.2～2mm, spray angle are that 35～45 °, pitch-row are 3～5mm, and inductor is high frequency or intermediate frequency inductor.
The beneficial effect of this method is: because this method is through carrying out normalizing to martensite type stainless steel pump barrel is integrated, after induced surface hardening and the temper, the hardness of the feasible oil well pump pump barrel internal surface of handling is at 58～63HRC, case depth reaches 1.5～2mm, cancelled existing chromium plating coating, can bubble not appear at oil well pump pump barrel internal surface, pit, peeling or defective such as peel off, also can not influence the quality of pump barrel, more etching problem can not appear, thereby the oil well pump life cycle is improved greatly, can be existing 3～4 times of using the oil well pump life-span, operating cost reduces greatly; Moreover this method is fairly simple, the manufacturing efficiency height, and simultaneously treatment process is nontoxic, can not threaten or endangers health, does not have the waste water of befouling environment, belongs to the environment protection type oil field equipment, is fit to apply.
Embodiment:
Below with the present invention is further illustrated:
The preparation method of this environment protection type stainless steel oil well pump, to selecting the material of martensite type stainless steel for use as the oil well pump pump barrel, the trade mark of martensite type stainless steel can be 3Cr13Mo, 9Cr18Mo, 7Cr17, wherein a kind of of 8Cr17 or 11Cr17, through cold-drawn, fracture, normalized treatment, induced surface hardening, alignment, defect detecting test, operations such as right boring, before alignment process, handle again: normalized treatment by following step, be to carry out normalized treatment 3～4 hours under 800～930 ℃ of conditions promptly in temperature, slow cooling to 600～750 are ℃ fast cold, are the heat treatment of doing for the wear resistance that improves pump barrel in advance; Induced surface hardening is handled, promptly temperature be 840～1070 ℃, inductor and pump barrel internal surface gaps between 2～2.5mm, the inductor travelling speed utilizes the quenching machine rotation in 2～8mm/s, pump barrel rotational speed under 50～100 rev/mins condition, inductor moves the heating continuous quenching, be in order to improve intensity, hardness and corrosion resistance, wherein inductor can be high frequency or intermediate frequency inductor; Cooling, promptly utilize 20～30 ℃ of quenching liquids with spray regime, spray by the quenching liquid spray orifice on the inductor and to carry out cooling processing, quenching liquid is polyvinyl alcohol water solution or emulsified liquid, is that 35～45 °, pitch-row are 3～5mm and the diameter of quenching liquid spray orifice is 1.2～2mm, spray angle; Temper, promptly cooling back pump barrel temperature be under 150～230 ℃ of conditions through tempering furnace insulation come out of the stove coldly soon after 30～60 minutes, be for reducing the quenching stress of pump barrel, preventing cracking.
Specific embodiments is as follows:
Scheme 1, utilize the material of martensite type stainless steel as the oil well pump pump barrel, in temperature is to carry out normalized treatment after 3 hours under 800～900 ℃ of conditions, in quenching temperature is 1020 ℃, intermediate frequency inductor and pump barrel internal surface gaps are at 2mm, the intermediate frequency inductor travelling speed is at 2mm/s, the pump barrel rotational speed is utilized quenching machine heating continuous quenching to carry out mid frequency induction hardening under 50 rev/mins condition and is handled, utilize 20～30 ℃ of quenching liquids with spray regime again, spray by the quenching liquid spray orifice on the inductor and to carry out cooling processing, use polyvinyl alcohol water solution, diameter as the quenching liquid spray orifice is 2mm, spray angle is 35 °, pitch-row is 3mm, to cool off back pump barrel at last is to pass through the fast cold temper of carrying out of coming out of the stove after tempering furnace is incubated 60 minutes under 150～200 ℃ of conditions in temperature, and then alignment, defect detecting test, the right boring honing, surfacing and screw thread processing can be produced the pump barrel of stainless steel, be assembled into oil well pump and be applied to the oil field, pump barrel internal surface hardness reaches 62HRC, case depth is at 1.6mm, bubble does not appear at all at the pump barrel internal surface, pit, peeling or defective such as peel off, quality guarantees to some extent, the stainless steel self character more etching problem can not occur in addition.
Scheme 2, utilize the material of martensite type stainless steel as the oil well pump pump barrel, in temperature is to carry out normalized treatment after 3.5 hours under 850～920 ℃ of conditions, in quenching temperature is 1050 ℃, high-frequency inductor and pump barrel internal surface gaps are at 2mm, the high-frequency inductor travelling speed is at 6mm/s, the pump barrel rotational speed utilizes quenching machine to drive the pump barrel rotation under 70 rev/mins condition, inductor moves the heating continuous quenching and carries out the high frequency hardening processing, utilize 25～30 ℃ of quenching liquids with spray regime again, spray by the quenching liquid spray orifice on the inductor and to carry out cooling processing, with polyvinyl alcohol water solution or emulsified liquid, and the diameter of quenching liquid spray orifice is 1.5mm, spray angle is 45 °, pitch-row is 4mm, to cool off back pump barrel at last is to pass through the fast cold temper of carrying out of coming out of the stove after tempering furnace is incubated 45 minutes under 180～230 ℃ of conditions in temperature, and then alignment, defect detecting test, the right boring honing, surfacing and screw thread processing can be produced the pump barrel of stainless steel, be assembled into oil well pump and be applied to the oil field, pump barrel internal surface hardness reaches 61HRC, case depth is at 1.5mm, metallographic structure is an acicular martensitic structure, bubble does not appear at all at the pump barrel internal surface, pit, peeling or defective such as peel off, quality guarantees to some extent, the stainless steel self character more etching problem can not occur in addition.
As seen, use the quality of the pump barrel that this method makes good, method is simple, and the efficient height etching problem can not occur, makes the raising greatly of oil well pump life cycle, and operating cost reduces greatly simultaneously; More can not threaten or endanger, not have the waste water of befouling environment, belong to the environment protection type oil field equipment, be fit to apply health.
Claims (6)
1, a kind of preparation method who relates to the used environment protection type stainless steel oil well pump in oil field development field, through operations such as cold-drawn, fracture, normalized treatment, alignment, defect detecting test, right borings, it is characterized in that: select the material of stainless steel for use as the oil well pump pump barrel, before alignment process, handle by following step
A. normalizing or annealing in process are to carry out normalizing or annealing in process under 800～930 ℃ of conditions 3～4 hours in temperature promptly, and slow cooling to 600～750 are ℃ fast cold;
B. induced surface hardening is handled, promptly temperature be 840～1070 ℃, inductor and pump barrel internal surface gaps between 2～2.5mm, the inductor travelling speed utilizes quenching machine to drive the pump barrel rotation at 2～8mm/s, pump barrel under 50～100 rev/mins condition with the lathe rotational speed, inductor moves the heating continuous quenching;
C. cooling promptly utilizes 20～30 ℃ of quenching liquids with spray regime, sprays by the quenching liquid spray orifice on the inductor and carries out cooling processing;
D. temper is promptly cooled off the back pump barrel and is come out of the stove cold soon after temperature is that the process tempering furnace is incubated 30～60 minutes under 150～230 ℃ of conditions.
2, the preparation method of environment protection type stainless steel oil well pump according to claim 1 is characterized in that: stainless steel is the martensite type stainless steel.
3, the preparation method of environment protection type stainless steel oil well pump according to claim 2 is characterized in that: the trade mark of martensite type stainless steel is 3Cr13Mo, 9Cr18Mo, 7Cr17,8Cr17 or 11Cr17.
4, the preparation method of environment protection type stainless steel oil well pump according to claim 1 is characterized in that: quenching liquid is polyvinyl alcohol water solution or emulsified liquid.
5, the preparation method of environment protection type stainless steel oil well pump according to claim 1 is characterized in that: the diameter of quenching liquid spray orifice is that 1.2～2mm, spray angle are that 35～45 °, pitch-row are 3～5mm.
6, the preparation method of environment protection type stainless steel oil well pump according to claim 1 is characterized in that: inductor is high frequency or intermediate frequency inductor.