CN1396137A - 秸杆碎丝水泥中空隔墙条板及其制备方法 - Google Patents

秸杆碎丝水泥中空隔墙条板及其制备方法 Download PDF

Info

Publication number
CN1396137A
CN1396137A CN02133600A CN02133600A CN1396137A CN 1396137 A CN1396137 A CN 1396137A CN 02133600 A CN02133600 A CN 02133600A CN 02133600 A CN02133600 A CN 02133600A CN 1396137 A CN1396137 A CN 1396137A
Authority
CN
China
Prior art keywords
cement
water
hollow partition
straw
broken silk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN02133600A
Other languages
English (en)
Other versions
CN1285535C (zh
Inventor
黄华大
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB021336008A priority Critical patent/CN1285535C/zh
Publication of CN1396137A publication Critical patent/CN1396137A/zh
Application granted granted Critical
Publication of CN1285535C publication Critical patent/CN1285535C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了秸杆碎丝水泥中空隔墙条板及其制备方法，它含有以下材料：秸杆碎丝10％～18％(干料重量百分比)，活性填充料20～30％，水泥45～55％，化学添加剂5～8％，减水剂0.2～0.5％，抗碱玻纤0.5～1％，利用本发明得到的中空隔墙条板的空心率大于55％，抗弯破坏载荷大于板自重的4倍以上；干缩值小于或等于0.75mm/M，工艺简单，成本较低，且具有优良的耐气候和耐久性，可大量应用于低、中、高层建筑的围护墙和内隔墙。

Description

秸杆碎丝水泥中空隔墙条板及其制备方法
                      所属领域
本发明涉及秸杆碎丝水泥中空隔墙条板及其制备方法。
                      背景技术
在现有技术中，有关秸秆与水泥制成板材的情况一般以制成单板为多，如中国专利ZL92104363.5“植物纤维水泥复合板”、“麦秸水泥刨花板”一般以秸秆为填料，水泥为胶结料，采用液压机冷压加工锁模养护而成，工艺十分繁杂，而且要复合后才能成隔墙板。
                      发明内容
针对上述只有秸秆水泥单板和加工养护工艺复杂的缺陷，本发明提供一种秸杆碎丝水泥中空隔墙条板及其制备方法，是以秸秆碎丝为填料，普通水泥为胶结料，加入活性填充料和化学添加剂，在常温常压下挤压成型，养护而成一种环保轻质隔墙板，其空心率＞55％，抗弯破坏荷载大于板自重的4倍以上；干缩值小于等于0.75mm/M，工艺简单，成本较低，且具有优良的耐气候和耐久性，是用于低、中、高层建筑极好的围护材料和隔墙材料。
本发明的技术内容是：利用秸秆碎丝和普通水泥制成中空隔墙条板，含有秸杆碎丝10％～18％(干料重量百分比)；活性填充料20～30％；水泥45～55％，化学添加剂5～8％；减水剂0.2～0.5％；抗碱玻纤0.5~1％，利用本发明得到的中空隔墙条板的空心率＞55％，抗弯破坏载荷大于板自重的4倍以上；干缩值小于或等于0.75mm/M。
上述隔墙条板的制备方法，包括：
a.按水灰比0.4-0.55的要求，称取所需要的水量；
b.称取总干料重的5～8％化学添加剂，加入步骤a的水中搅拌均匀成水溶液；
c.按秸秆碎丝10～18％(重量百分比)；活性填充料20～30％；水泥45～55％，减水剂0.2～0.5％，抗碱玻纤0.5～1％的比例，称取上述各种材料，先将秸秆碎丝和步骤b的水溶液加入搅拌机内搅拌3～4分钟，然后加入水泥、活性填充料、减水剂、玻纤丝等物料再在搅拌机内充分混合成均匀混合料浆；
d、混合料浆送入模具或专用成型机，加工成中空隔墙条板的板坯，再进行养护硬化得到成品。本发明的具体内容是：
秸杆碎丝水泥中空隔墙条板，含有以下组分：秸杆碎丝10％～18％(干料重量百分比)，活性填充料20～30％，水泥45～55％，化学添加剂5～8％，减水剂0.2～0.5％，抗碱玻纤0.5~1％。优选的是由下列组分与水配制而成：秸杆碎丝10％～18％(干料重量百分比)，活性填充料20～30％，水泥45～55％，化学添加剂5～8％，减水剂0.2～0.5％，抗碱玻纤0.5~1％。其中，水灰比为0.4-0.55，水泥为普通建筑水泥，优选的是强度等级为32.5R、42.5R的普通硅酸盐水泥，秸杆碎丝长度＜1.5cm，并且优选的秸杆碎丝是麦秸碎丝。化学添加剂是水玻璃和下列一种或多种成分制成：氯化钙、硫酸铝、氯化镁，优选的是氯化钙和水玻璃。玻璃碎丝是抗碱玻璃碎丝短切丝或抗碱玻璃网格布。活性填充料由粉煤灰与下列一种或多种组分配制而成：石英砂，硅灰、矿渣、炉渣、膨胀珍珠岩，优选的是粉煤灰和石英砂。优选的减水剂为木钙粉。上述隔墙条板的制备方法，包括：
a.按0.4-0.55的水灰比，称取所需要的水量；
b.称取总干料重的5～8％化学添加剂，加入步骤a的水中搅拌均匀成水溶液；
c.按秸秆碎丝10～15％(干料重量百分比)；活性填充料20～30％；水泥45～55％，减水剂0.2～0.5％，耐碱玻纤短切丝0.5～1％的比例，称取上述各种材料，先将秸秆碎丝和步骤b的水溶液在搅拌机内搅拌3～4分钟，然后加入水泥、活性填充料、减水剂、玻纤丝等物料再在搅拌机内充分混合成均匀混合料浆；
d、将混合料浆送入模具加工成中空隔墙条板的板坯，再进行养护硬化得到成品。
下面通过实施例对本发明作进一步说明。
实施例一
1.称取水50kg，加入3kg氯化钙，3.0kg硫酸铝，7kg水玻璃，混合搅拌成均匀水溶液
2.称取120kg水泥，20kg石膏粉，20kg粉煤灰，20kg石英砂，25kg秸秆碎丝，0.5kg木钙粉，1.5kg抗碱玻纤丝，先将秸秆碎丝和步骤1的水溶液在搅拌机内搅拌3～4分钟然后加入水泥、石膏粉、粉煤灰，石英砂，木钙粉，在搅拌机内充分搅拌成均匀混合料浆；
3.将混合料浆及抗碱玻纤丝送入模具加工成中空隔墙条板，静养6-8小时，即可脱去模具，放置养护28天，即得产品。检测结果：1、空心率68％
2、干缩值：0.68mm/M
3、抗弯破坏荷载：板自重的4.4倍。
实施例二
1.称取水50kg并加入3kg氯化钙，1.5kg硫酸铝，1.5kg氯化镁，7kg水玻璃，混合搅拌成均匀水溶液；
2.取100kg水泥，20kg粉煤灰，20kg石英砂，25kg秸秆碎丝，0.5kg木钙粉，1.5kg抗碱玻纤丝及步骤1中的所有水溶液，先将秸秆碎丝和水溶液在搅拌机内搅拌3～4分钟然后加入水泥、粉煤灰、石英砂，木钙粉，在搅拌机内充分搅拌成均匀混合料浆；
3.混合料浆及抗碱玻纤放送入专用中空轻质隔墙条板平模模具内加工成中空隔墙条板，静养6～8小时，即可脱去模具，放置养护28天后即为产品。
检测结果：1、空心率68％
2、干缩值：0.68mm/M
3、抗弯破坏荷载：板自重的4.2倍。
实施例三
1.称取水50kg，加入6kg氯化钙，7kg水玻璃，混合搅拌成均匀水溶液
2.称取95kg水泥，25kg粉煤灰，25kg硅灰，20kg秸秆碎丝，0.5kg木钙粉，1.5kg耐碱玻纤及步骤1中的所有水溶液，先将秸秆碎丝和水溶液在搅拌机内搅拌3～4分钟然后加入水泥、粉煤灰、硅灰，木钙粉，在搅拌机内充分搅拌成均匀混合料浆；
3.将混合料浆送入专用挤板机内挤出中空板坯，并按所需长度切割，并用钢托板托住板坯，送入养护设备养护一定时间即成产品。检测结果：1、空心率58％
2、干缩值：0.72mm/M
3、抗弯破坏荷载：板自重的4.4倍。
实施例四
1.称取水50kg，加入4kg氯化钙，2kg氯化镁，7kg水玻璃，混合搅拌均匀。
2.称取100kg 32.5R水泥，25kg粉煤灰，20kg矿渣，25kg麦秸碎丝，0.5kg木钙粉，1.5kg抗碱玻纤短切丝及上述水溶液，先湿拌麦秸碎丝3～4分钟，然后加入水泥、粉煤灰，矿渣，木钙粉，抗碱玻纤短切丝充分搅拌成混合料浆。
3.将混合料送入专用挤板机内挤出中空板坯，按所需长度切割，并用钢托板托住板坯送入养护设备(或场地)养护一定时间即成产品。(也用于中空平模模具生产)
检测结果：1、空心率58％
          2、干缩值：0.69mm/M
          3、抗弯破坏荷载：板自重的4.3倍
实施例五
1.称取水45kg，加入3kg氯化钙，3kg硫酸铝，7kg水玻璃，混合搅拌均匀。
2.称取100kg水泥，25kg秸秆粉，10kg粉煤灰，10kg石英砂，25kg矿渣，0.5kg木钙粉，1.5kg抗碱玻纤短切丝及上述水溶液，先湿拌秸秆碎丝3～4分钟，然后加入水泥、粉煤灰，石英砂，矿渣，木钙粉，抗碱玻纤短切丝充分搅拌成混合料浆。
3.料送入专用挤板机内挤出中空板坯，按所需长度切割，并用钢托板托住板坯送入养护设备(或场地)养护一定时间即成产品。
检测结果：1、空心率58％
          2、干缩值：0.68mm/M
          3、抗弯破坏荷载：板自重的4.5倍
实施例五
1.称取水50kg，加入6kg氯化钙，7kg水玻璃，混合搅拌均匀。
2.称取100kg 42.5R水泥，25kg麦秸碎丝，20kg粉煤灰，20kg石英砂，0.5kg木钙粉、1.5kg抗碱玻纤短切丝及上述水溶液，先将麦秸碎丝和步骤1的水溶液混合搅拌3～4分钟，然后加入水泥、粉煤灰，石英砂，木钙粉充分搅拌成混合料浆。
3.将混合料浆和抗碱玻纤网格布送入专用中空轻质条板平模内，采用铺网抹浆法成型成中空条板，静养6-8小时即脱去模具再放置养护28天即得到产品。
检测结果：1、空心率68％
          2、干缩值：0.69mm/M
          3、抗弯破坏荷载：板自重的4.8倍

Claims (10)

1.秸杆碎丝水泥中空隔墙条板，其特征在于它含有以下组分：秸杆碎丝10％～18％(干料重量百分比)，活性填充料20～30％，水泥45～55％，化学添加剂5～8％，减水剂0.2～0.5％，抗碱玻纤0.5～1％。
2.根据权利要求1所述的秸杆碎丝水泥中空隔墙条板，其特征在于它由下列组分与水配制而成：秸杆碎丝10％～18％(干料重量百分比)，活性填充料20～30％，水泥45～55％，化学添加剂5～8％，减水剂0.2～0.5％，抗碱玻纤0.5～1％。
3.根据权利要求1或2所述的中空隔墙条板，其特征在于：水泥为普通建筑水泥，优选的是强度等级为32.5R、42.5R的普通硅酸盐水泥。
4.根据权利要求1或2所述的中空隔墙条板，其特征在于：秸杆碎丝长度＜1.5cm，并且优选的秸杆碎丝是麦秸碎丝。
5.根据权利要求1或2所述的中空隔墙条板，其特征在于：化学添加剂由水玻璃和下列一种或多种成分配制而成：氯化钙、硫酸铝、氯化镁，优选的是氯化钙和水玻璃。
6.根据权利要求1或2所述的中空隔墙条板，其特征在于：抗碱玻纤是抗碱玻璃纤维短切丝或抗碱玻璃网格布。
7.根据权利要求1或2所述的中空隔墙条板，其特征在于，活性填充料由粉煤灰与下列一种或多种组分配制而成：石英砂，硅灰、矿渣、炉渣、膨胀珍珠岩，优选的是粉煤灰和石英砂。
8.根据权利要求1或2所述的中空隔墙条板，其特征在于：优选的减水剂为木钙粉。
9.根据权利要求1或2所述的中空隔墙条板，其特征在于：水灰比为0.4～0.55。
10.如权利要求1或2所述的中空隔墙条板的制备方法，包括：
a.按0.4-0.55的水灰比要求，称取所需要的水量；
b.称取总干料重的5～8％化学添加剂，加入步骤a的水中搅拌均匀成水溶液；
c.按秸秆碎丝10～18％(干料重量百分比)；活性填充料20～30％；水泥45～55％，减水剂0.2～0.5％，抗碱玻纤0.5～1％的比例，称取上述各种材料，先将秸秆碎丝和步骤b的水溶液加入搅拌机内搅拌3～4分钟，然后再加入水泥、活性填充料、减水剂、玻纤丝等物料充分混合成均匀混合料浆；
d.将混合料浆送入模具或专用成型机中加工成中空隔墙条板的板坯，再进行养护硬化得到成品。
CNB021336008A 2002-08-12 2002-08-12 秸杆碎丝水泥中空隔墙条板及其制备方法 Expired - Fee Related CN1285535C (zh)