CN1355051A - 水固化聚氨酯绷带及其制备方法 - Google Patents
水固化聚氨酯绷带及其制备方法 Download PDFInfo
- Publication number
- CN1355051A CN1355051A CN00132041.6A CN00132041A CN1355051A CN 1355051 A CN1355051 A CN 1355051A CN 00132041 A CN00132041 A CN 00132041A CN 1355051 A CN1355051 A CN 1355051A
- Authority
- CN
- China
- Prior art keywords
- parts
- bandage
- described water
- water solidified
- solidified polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种水固化聚氨酯绷带及其制造方法。其特点是将聚氨酯预聚体涂覆在绷带基材上制成矫形绷带。聚氨酯预聚体由异氰酸酯、聚醚、催化剂、稳定剂、防潮剂、消泡剂等合成制得。该水固化聚氨酯矫形绷带具有重量轻、强度高、保存期长、模塑性好、价廉、操作方便等优点。其中防潮剂氧化钙在吸水后作催化剂,从而可降低催化剂的用量;而选用的催化剂易于得到,价格便宜,有利于大规模生产。
Description
本发明涉及一种医用外科治疗材料，具体而言，它是一种水固化聚氨酯绷带及其制备方法。
美国专利4376438提出在织物上浸渍水固化聚氨酯预聚体制成的绷带，用以代替骨折治疗中的石膏绷带，将这种水固化绷带浸水后在患者的患处包扎后，三十分钟以内固化，该方法已被广泛接受，但由于在包装过程中和制备预聚体过程中微量水份不易排除，使绷带保质期不长，大约有九个月保质期。美国专利4433680提出用(双-2-吗啉代二乙基)醚作为聚氨酯预聚体的催化剂，使绷带具有较好的固化时间，但催化剂不易得到，给大规模生产到来一定的困难。EP522826提出在使用水固化聚氨酯绷带前，先将亲水性材料，如聚乙烯基吡咯烷酮，涂在操作者的手套上，避免使用绷带时，绷带和手套粘接，但该方法增加了操作步骤，对于医生而言不太方便。
本发明的目的是针对现有技术的不足而提供一种水固化聚氨酯绷带及其制备方法，其特点是在水固化聚氨酯预聚体中引入有效的催化剂、稳定剂、防粘剂、防潮剂和消泡剂等原料。水固化聚氨酯绷带具有固化时间短，绷带质地柔软，易于拉开和不粘接操作者手套，长期贮存不变质等特点。
本发明的目的由以下技术措施实现的：
水固化聚氨酯绷带的制备
一、聚氨酯预聚体的制备
聚氨酯预聚体起始原料的配方组分(按重量计)为：
异氰酸酯(可用二苯基甲烷二异氰酸酯(MDI)，含碳化二亚胺的二苯基二异氰酸酯(液化MDI)，二环己基甲烷二异氰酸酯(HMDI)或/和六甲基二异氰酸酯中至少一种) 100份
聚醚多元醇(可用分子量从600到3000的聚氧化丙烯二醇、氧化丙烯三醇、聚四氢呋喃二醇、四氢呋喃-氧化丙烯共聚二醇或/和聚氧化乙烯醚中至少一种)
75～150份
催化剂(可用二甲基乙醇胺，三亚乙基二胺，三乙醇胺，三乙胺，双-(二甲基氨基)乙基醚，N-乙基吗啉，二月桂酸二丁基锡，辛酸亚锡，碳酸钾或/和碳酸钠中至少一种) 4～10份
稳定剂(可用甲基磺酸、丙酰氯、乙酰氯、苯甲酰氯或/和马来酐中至少一种) 0.5～2份
防粘剂(可用聚氧化乙烯或/和氧化乙烯与丙烯的共聚物至少一种)8～12份
防潮剂(可用氧化钙、分子筛或/和强吸水性树脂中至少一种) 8～12份
消泡剂(可用消泡硅油或/和聚乙二醇单月桂酸酯中至少一种) 1～3份
将异氰酸酯100份、稳定剂0.5～2份和消泡剂1～3份，加入带有温度计、搅拌器、加料口和氮气进出口的反应釜中，聚醚多元醇75～150份，用滴加法或直接加入法加入，在20～80℃温度下反应1～1.5小时，然后将预聚体降温到40℃以下，加入催化剂4～10份，防粘剂8～12份，防潮剂8～12份。在氮气的保护下放入容器中待用。
二、聚氨酯绷带的制备及应用
将聚氨酯预聚体加热到50℃，在空气湿含量低于10％的干燥环境下，采用双辊筒涂复法，经送布、涂复、收卷、剪切等工艺，将聚氨酯预聚体涂复在绷带基材上，然后装入铝塑复合袋中，同时在其中装入一小袋防潮剂，经抽真空，通氮气、热封而成。
开封后将绷带在25℃水中浸泡10秒左右后，测试固化时间为8分钟左右。也可以通过调节配方来调节固化时间，一般控制在30分钟以内。绷带质地柔软，易拉开，不粘操作者手套。将绷带缠绕在病人患处模塑成型良好。
将包装在铝塑复合袋中的绷带放入70℃的烘箱中，贮存三周未固化，这相当于在室温条件下可贮存两年以上。
实施例
下面通过实施例对本发明进行具体的描述，有必要在此指出的是以下实施例只用于对本发明进行进一步说明，不能理解为对本发明保护范围的限制，该领域的技术熟练人员可以根据本发明的上述内容作出一些非本质的改进和调整。
1.将含碳化二亚胺的二苯基二异氰酸酯1000g，丙酰氯15g，消泡硅油20g依次加入带有温度计、搅拌器、加料口和氮气进出口的反应釜中，滴加聚氧化丙二醇(分子量1000)750g，于温度60℃反应1.5小时后，将预聚物降温到40℃左右，加入二甲基乙醇胺20g，二月桂酸二丁基锡20g，氧化乙烯和丙烯共聚物100g，氧化钙100g，在氮气保护下放入容器中待用。
2.将含碳化二亚胺的二苯基二异氰酸酯1000g，丙酰氯15g，消泡硅油20g依次加入带有温度计、搅拌器、加料口和氮气进出口的反应釜中，滴加聚四氢呋喃二醇(分子量1000)1140g，于温度60℃反应1.5小时后，将预聚物降温到40℃左右，加入二甲基乙醇胺20g，碳酸钾60g，氧化乙烯和丙烯共聚物100g，分子筛100g，在氮气保护下放入容器中待用。
3.将二苯基二异氰酸酯1000g，甲基磺酸5g，聚四氢呋喃二醇1000g，聚氧化丙烯三醇70g，乙酰氯10g，消泡硅油25g，加入实施例1相同的设备中，于温度60℃，反应1小时，将预聚物降温至40℃左右，加入双-(二甲基氨基)乙基醚20g，氧化乙烯和丙烯共聚物100g，分子筛100g，在氮气保护下放入密闭容器中待用。
4.将二环乙基甲烷二异氰酸酯1000g，甲基磺酸5g，聚四氢呋喃二醇1000g，聚氧化丙烯三醇70g，马来酐10g，加入实施例1相同的设备中，于温度60℃，反应1小时，将预聚物降温至40℃左右，加入二月桂酸二丁基锡10g，氧化乙烯和丙烯共聚物100g，碳酸钾60g，氧化钙60g，在氮气保护下放入密闭容器中待用。
5.将六次甲基二异氰酸酯500g，苯酰氯15g，消泡硅油25g，加入实施例1相同的设备中，滴加聚四氢呋喃二醇700g，聚氧化丙烯三醇200g，于温度60℃反应1小时，将预聚物降温至40℃左右，加入三亚乙基二胺5g，辛酸亚锡5g，氧化乙烯和丙烯共聚物100g，氧化钙60g，在氮气保护下放入密闭容器中待用。
6.将上述聚氨酯预聚体分别选取一种加热到50℃，在空气湿含量至少低于10％的干燥环境下，采用双辊筒涂复法，经过送布、涂复、收卷、剪切等工艺，将聚氨酯预聚体涂复在绷带基材上，然后装入铝塑复合袋中，同时在其中装入一小袋防潮剂，如生石灰，经抽真空、通氮气、热封而成。开封后将绷带在25℃水中浸泡10秒左右，测试固化时间为8分钟。绷带质地柔软，易拉开，不粘操作者手套，将绷带缠绕在病人患处，模型成型良好。将包装在铝塑复合袋中的绷带放入70℃的烘箱中，贮存三周未固化，这相当于在室温条件下可贮存两年以上。
本发明具有如下优点：
水固化聚氨酯绷带具有重量轻，强度高，保存期长，模塑性好，价廉，操作方便等优点。由于氧化钙的使用，既可作为防潮剂，也可在吸水后作为催化剂，从而降低催化剂的用量。选用的催化剂为通用型催化剂，易于得到，价格便宜，有利于大规模生产。
Claims (9)
1.一种水固化聚氨酯绷带，其特征在于该聚氨酯预聚体原料配方组分(按重量计)为：
异氰酸酯 100份
聚醚多元醇 75～150份
催化剂 4～10份
稳定剂 0.5～2份
防粘剂 8～12份
防潮剂 8～12份
消泡剂 1～3份
2.根据权利要求1所述水固化聚氨酯绷带，其中异氰酸酯为二苯基甲烷二异氰酸酯(MDI)，含碳化二亚胺的二苯基二异氰酸酯(液化MDI)，二环己基甲烷二异氰酸酯(HMDI)或/和六甲基二异氰酸酯中至少一种。
3.根据权利要求1所述水固化聚氨酯绷带，其中聚醚多元醇是分子量从600到3000的聚氧化丙烯二醇、氧化丙烯三醇、聚四氢呋喃二醇、四氢呋喃-氧化丙烯共聚二醇或/和聚氧化乙烯醚中至少一种。
4.根据权利要求1所述水固化聚氨酯绷带，其中催化剂为二甲基乙醇胺，三亚乙基二胺，三乙醇胺，三乙胺，双-(二甲基氨基)乙基醚，N-乙基吗啉，二月桂酸二丁基锡，辛酸亚锡，碳酸钾或/和碳酸钠中至少一种。
5.根据权利要求1所述水固化聚氨酯绷带，其中稳定剂为甲基磺酸、丙酰氯、乙酰氯、苯甲酰氯或/和马来酐中至少一种。
6.根据权利要求1所述水固化聚氨酯绷带，其中防粘剂为聚氧化乙烯或/和氧化乙烯和丙烯的共聚物中至少一种。
7.根据权利要求1所述水固化聚氨酯绷带，其中防潮剂为氧化钙，分子筛或/和强吸水性树脂中至少一种。
8.根据权利要求1所述水固化聚氨酯绷带，其中消泡剂为消泡硅油或/和聚乙二醇单月桂酸酯中至少一种。
9.按照权利要求1所述水固化聚氨酯绷带的制造方法，其特征在于：
a.聚氨酯预聚体的制备
将异氰酸酯100份、稳定剂0.5～2份和消泡剂1～3份，加入带有温度计、搅拌器、加料口和氮气进出口的反应釜中，聚醚多元醇75～150份，用滴加法或直接加入法加入，在20～80℃温度下反应1～1.5小时，然后将预聚体降温到40℃以下，加入催化剂4～10份，防粘剂8～12份，防潮剂8～12份，在氮气的保护下放入容器中待用，
b.聚氨酯水固化绷带的制造
将聚氨酯预聚体加热到50℃，在空气湿含量低于10％的干燥环境下，采用双辊筒涂复法，经过送布、涂复、收卷、剪切等工艺，将聚氨酯预聚体涂复在绷带基材上，然后装入铝塑复合袋中包装。