CN1354717A - 包括具有低捻度系数和改进压缩模量的有机纤维的复合材料 - Google Patents
包括具有低捻度系数和改进压缩模量的有机纤维的复合材料 Download PDFInfo
- Publication number
- CN1354717A CN1354717A CN00808578A CN00808578A CN1354717A CN 1354717 A CN1354717 A CN 1354717A CN 00808578 A CN00808578 A CN 00808578A CN 00808578 A CN00808578 A CN 00808578A CN 1354717 A CN1354717 A CN 1354717A
- Authority
- CN
- China
- Prior art keywords
- goods
- cord
- fabric thread
- cord fabric
- carcass plies
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
对比帘子线 | 起始PEN帘子线 | 聚合物 | 帘子线结构(纱旦尼尔/所用纱的数目#) | 捻度(tpi×tpi) | 捻度系数 | 初始拉伸模量(g/den) | 在1%应变下的应力(g/den) | 初始压缩模量(g/den) |
A | 芳族聚酰胺 | 1500/2 | 0×0 | 0 | 466 | 4 | 4.5 | |
B | 芳族聚酰胺 | 1500/2 | 3×3 | 164 | 441 | 4 | 4.1 | |
C | 芳族聚酰胺 | 1500/2 | 6.7×6.7 | 450 | 257 | 1.9 | 2.7 | |
D | PET | 1000/2 | 0×0 | 0 | 97 | 0.89 | 10.4 | |
E | PET | 1000/2 | 0×3 | 164 | 86 | 0.88 | n.a.1 | |
F | PET | 1000/2 | 7×7 | 313 | n.a. | n.a. | 7.1 | |
G | PET | 1000/2 | 9.5×9.5 | 425 | 87 | 0.74 | n.a. | |
1 | PEN | 1000/1 | 0×0 | 0 | 251 | 2.4 | 12 | |
2 | PEN | 1000/4 | 0×1 | 63 | 216 | 2.1 | n.a. | |
3 | PEN | 1000/2 | 3.5×3.5 | 157 | 210 | 2 | 11.1 | |
4 | PEN | 1000/2 | 4.5×4.5 | 201 | 198 | 1.9 | n.a. | |
5 | PEN | 1000/2/3 | 4×4 | 310 | 173 | 1.7 | 10.2 | |
6 | PEN | 1000/2 | 8×8 | 358 | 182 | 1.7 | 9.5 |
对比实施例 | 本发明实施例 | 帘布贴合角度 | 相对面内剪切模量1 | 相对拉伸模量1 |
A | 0° | 0.14 | n.d. | |
1 | 23° | 0.52 | 1.75 | |
2 | 25° | 0.72 | 1.09 | |
3 | 26° | 0.85 | 0.91 | |
4 | 30° | 1.01 | 0.61 | |
5 | 35° | 1.07 | 0.5 | |
6 | 45° | 1.07 | 0.14 |
对比和本发明实施例 | 增强帘子线 | 帘布的层数# | 帘布贴合角度 | EPI/每层帘布 | 固化的复合材料厚度(in) | 最大负荷(lbf) | 拉伸模量(lbf/in) | 面内剪切模量(lbf/in) | 面外弯曲模量(107达因/厘米×厘米宽度) | 疲劳(到破坏时的周期数#) |
B | 钢丝 | 2 | ±23° | 22 | 0.098 | 768 | 4187 | 1406 | 2.36 | 2500 |
1 | PEN | 2 | ±23° | 21 | 0.108 | 686 | 7234 | 731 | 2.08 | 3600 |
7 | PEN | 2 | ±28° | 26 | 0.087 | 342 | 2941 | 1388 | n.d. | n.d. |
8 | PEN | 4 | 外±23°内±45° | 外:21内:4 | 0.13 | 580 | 5700 | 1106 | 2.51 | n.d. |
9 | PEN | 4 | 外±23°内±45° | 外:21内:8 | 0.140 | 541 | 4900 | 1213 | 2.61 | 2700 |
10 | PEN | 3 | 外±30°内~0° | 外:21内:4 | 0.14 | 499 | 4538 | 1291 | 2.39 | 21,100 |
11 | PEN | 3 | 外±30°内~0° | 外:21内:16 | 0.124 | 720 | 7071 | 1461 | n.d. | 19,644 |
对比和本发明实施例 | 增强帘子线 | 帘布层数# | 帘布贴合角度 | EPI/每层帘布 | 缝合图案 | 缝合帘子线的实际旦尼尔 | 固化的复合材料厚度(in) | IPSM(lbf/in) | OPBM(107达因/厘米*厘米宽度) | 最大负荷(lbf) | 拉伸模量(lbf/in) | 疲劳(到破坏时的周期数#) |
B | 钢丝 | 2 | ±23° | 22 | n.s. | n.s. | 0.098 | 1406 | 2.36 | 768 | 4,187 | 2,500 |
1 | PEN | 2 | ±23° | 21 | n.s. | n.s. | 0.108 | 731 | 2.08 | 686 | 7,234 | 3,600 |
12 | PEN | 2 | ±23° | 21 | 连续链 | 6500d | 0.11 | 938 | 1.80 | 613 | 8,445 | n.d. |
13 | PEN | 2 | ±23° | 21 | 十字缝合 | 6500d | 0.139 | 850 | 1.81 | 542 | 5,744 | 5,611 |
14 | PEN | 2 | ±23° | 21 | Z形 | 6500d | 0.135 | 869 | 1.49 | 502 | 5,287 | 6,584 |
15 | PEN | 2 | ±23° | 21 | Z形 | 2400d | 0.130 | 869 | 1.76 | 536 | 5,293 | n.d. |
对比实施例 | 本发明实施例 | 增强帘子线类型 | 帘子线结构 | EPI/每层帘布 | 帘布层数# | 帘布贴合角度 |
B | 钢丝 | (~14,000旦尼尔轮胎帘子线) | ~22 | 2 | 23° | |
3 | PEN | 1000/2/3 4×4 | 21 | 2 | 26° | |
16 | PEN | 1000/2/3 4×4 | 21 | 2 | 26° | |
4 | PEN | 1000/2/3 4×4 | 21 | 2 | 30° | |
17 | PEN | 1000/2/3 4×4 | 21 | 2 | 30° | |
18 | PEN | 1000/2/3 4×4 | 14 | 4 | 30° | |
19 | PEN | 1000/2/3 4×4 | 21 | 2 | 30° |
对比实施例 | 本发明实施例 | 拉伸模量(lbf/in) | 最大负荷(lbf) | IPSM(lbf/in) | OPBM(107达因/厘米×厘米宽度) | 疲劳(到破坏为止的周期数#) |
B | 4,187 | 768 | 1406 | 2.36 | 2,500 | |
3 | 3802 | 479 | 1197 | 1.69 | 14,600 | |
16 | 18,584 | 2,027 | n.d. | 1.34 | >130,000(没有破坏) | |
4 | 2,536 | 363 | 1417 | 1.52 | 3,157 | |
17 | 5,952 | 1,804 | 1063 | 1.0 | >130,000(没有破坏) | |
18 | 10,455 | 2,463 | 1306 | 3.98 | 37,841 | |
19 | 7340 | 2170 | 833 | 2.32 | 15,625 |
实施例 | 在带束帘布层中帘子线的重量(lb) | 在胎冠缓冲层中帘子线的重量(lb) | 帘子线因缝合带来的重量(lb) | 在实施例中总的帘子线重量(lb) | 与钢丝增强带束相比的重量减少百分比(%) |
对比实施例B | 2.36 | 0.41 | 0 | 2.77 | - |
本发明实施例8 | 0.98 | 0 | 0 | 0.98 | 65% |
本发明实施例10 | 0.98外帘布层和0.39内帘布层 | 0 | 0 | 1.37 | 51% |
本发明实施例11 | 0.98主要帘布层和0.2中间帘布层 | 0 | 0 | 1.18 | 57% |
本发明实施例12 | 0.98 | 0 | 0.14 | 1.12 | 60% |
Claims (28)