CN1325586C - Thermoplastic fast-dry traffic paint - Google Patents
Thermoplastic fast-dry traffic paint Download PDFInfo
- Publication number
- CN1325586C CN1325586C CNB031485162A CN03148516A CN1325586C CN 1325586 C CN1325586 C CN 1325586C CN B031485162 A CNB031485162 A CN B031485162A CN 03148516 A CN03148516 A CN 03148516A CN 1325586 C CN1325586 C CN 1325586C
- Authority
- CN
- China
- Prior art keywords
- solvent
- powder
- borne type
- acrylic acid
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a thermoplastic high-strength rapid-drying traffic paint. The traffic paint is prepared from the raw materials of 410 acrylic resin, 450 acrylic resin, chlorinated rubber powder, titanium white powder, deposited barium sulphate, talcum powder, ground limestone powder, organic bentonite, chloroparaffin NO. 52, xylene, butyl acetate, dispersing agents, defoaming agents, levelling agents, anti-settling agents and antioxidants. When in use, the present invention can be directly sprayed without the need of heating, and has the characteristics of rapid drying, favorable wear resistance, weather resistance, rain resistance, resistance to acid and alkali, etc.
Description
Technical field
The present invention relates to the powerful rapid-curing cutback road mark paint of a kind of thermoplastics type, described marking paint is a kind of coating that is used for the Road safety sign, need not heat during use and can directly spray, and is rapidly dry.
Background technology
Chinese patent 98121033.3 discloses a kind of thermal solvent type paint for road markers, the present invention is made up of film forming component, pigment, filler, softening agent, anti-sedimentation agent and mixed solvent, and its main component is toluene, industrial naptha, dioctyl phthalate (DOP), hot melt acrylic resin, titanium dioxide, process white, lime carbonate, ground silica, talcum powder.The coating of this patent still needs to spray under 40 ℃～80 ℃ moderate temperature.Therefore, need to propose the powerful rapid-curing cutback road mark paint of a kind of thermoplastics type.
Summary of the invention
The object of the present invention is to provide the powerful rapid-curing cutback road mark paint of a kind of thermoplastics type, this marking paint need not heat and can directly spray when using, and is rapidly dry, has good wear-resisting, weather-proof, anti-rainwater, resistance to acids and bases.
The objective of the invention is to realize by following technical proposals: the powerful rapid-curing cutback road mark paint of thermoplastics type, form by following feedstock production, the weight ratio of described raw material is:
410 acrylic acid resins 14～16
450 acrylic acid resins 9～11
Chlorinated rubber powder 4～6
Titanium dioxide 10～15
Process white 4～6
Talcum powder 4～6
Dry powder 10～15
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 14～16
N-BUTYL ACETATE 9～11
Solvent-borne type dispersion agent 0.1
Solvent-borne type defoamer 0.1
Solvent-borne type flow agent 0.2
The anti-heavy agent 0.2 of solvent-borne type
Solvent-borne type oxidation inhibitor 0.2.
410 acrylic acid resins among the present invention, good weatherability, the intensity height can increase the sticking power and the intensity of paint; 450 acrylic acid resins, good weatherability, highly polished, film forming properties is good, can increase the sticking power and the glossiness of paint; Chlorinated rubber, acidproof, alkaline-resisting, water-fast, anti-efflorescence, can anti-rainwater, anticorrosive; Organobentonite, suspension property is good, and certain anti-heavy ability is arranged, and can avoid the powder body material precipitation; Clorafin 52# increases heavy ability of resisting of coating, can improve the flexibility and the weather resisteant of coating; N-BUTYL ACETATE is used to adjust the volatility of coating, makes it over-all properties and improves with imitating; Dispersion agent increases each dispersing of pigments performance; Flow agent is used to adjust the brushability minimizing brush mark of coating; Anti-heavy agent is used to increase coating suspension, anti-settling.
The present invention compared with prior art has following advantage:
1, the present invention has characteristics such as good wear-resisting, weather-proof, anti-rainwater, acid and alkali-resistance.
2, strong, the shock resistance, good to pitch and concrete road surface sticking power of paint film adhesion of the present invention is difficult for phenomenons such as producing variable color, chap and peel off.
3, the present invention is used for highway pavement and executes and draw vehicle lines, can directly spray or the roller coating moulding, and easy construction, rapidly dry, surface drying 3 minutes was done solid work 15 minutes, did not influence vehicle during construction and travelled.
4, the present invention can deposit 2-3 in envrionment temperature during greater than 30 ℃ and never degenerate.
Embodiment
Embodiment one:
The powerful rapid-curing cutback road mark paint of thermoplastics type is formed by following feedstock production, and the weight ratio of described raw material is:
410 acrylic acid resins 15
450 acrylic acid resins 10
Chlorinated rubber powder 5
Titanium dioxide 15
Process white 5
Talcum powder 5
Dry powder 15
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 15
N-BUTYL ACETATE 10
Solvent-borne type dispersion agent 0.1
Solvent-borne type defoamer 0.1
Solvent-borne type flow agent 0.2
The anti-heavy agent 0.2 of solvent-borne type
Solvent-borne type oxidation inhibitor 0.2.
Present embodiment is a kind of marking paint of white, in the present embodiment:
410 acrylic acid resins and 450 acrylic acid resins are main base-materials of traffic paint, can increase sticking power, intensity and the glossiness of paint;
Chlorinated rubber adopts pulvis, can increase the anti-rainwater of paint, erosion resistance;
Titanium dioxide is as main pigment, and pigment is assisted in zinc sulfide white, dry powder, conduct, can improve whiteness, covering performance and the chalking resistance energy of present embodiment;
Process white adopts pulvis and talcum powder together as filler, can improve the hardness of present embodiment;
Organobentonite, suspension property is good, as antisettling agent, avoids the powder body material precipitation;
Clorafin 52# increases the material agent, increases the anti-heavy ability of coating, improves the flexibility of coating;
N-BUTYL ACETATE and dimethylbenzene are used to adjust the volatility of coating, make it over-all properties and improve with imitating;
The dispersion agent model is 170, increases each dispersing of pigments performance.
The defoamer model is optional 550, and the flow agent model is optional 3306, and anti-heavy agent model is optional 118, the optional triphenyl phosphite of oxidation inhibitor.
The production technique of present embodiment is:
1, dimethylbenzene, N-BUTYL ACETATE weighing is good, pour into then in the high-speed stirring still, add chlorinated rubber after starting slow rotation, stirred 10-15 minute.
2, powder, pigment and the organobentonite in the adding prescription under middling speed stirs.
3, add acrylic acid resin and auxiliary agent then, stirred 10-15 minute
4, pour the above-mentioned liquid slurry that stirs into sand mill, add grinding bead and start and grind, after grinding in 30-60 minute, the fineness of measuring material reaches 50 microns and can make the present invention.
5, the material filtering discharging after will grinding with 100 purpose filtering nets then, barrelling.
Need not heat when the present invention uses and directly to spray, but the 10-15 minute paint film in spraying back is with regard to complete drying.150 microns of total coating thickness can adopt 2-3 spraying operation to realize.
Embodiment two:
The powerful rapid-curing cutback road mark paint of thermoplastics type is formed by following feedstock production, and the weight ratio of described raw material is:
410 acrylic acid resins 15
450 acrylic acid resins 10
Chlorinated rubber powder 5
Titanium dioxide 10
Medium chrome yellow medium yellow powder 5
Process white 5
Talcum powder 5
Zinc sulfide white 5
Dry powder 10
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 15
N-BUTYL ACETATE 10
Solvent-borne type dispersion agent 0.1
Solvent-borne type defoamer 0.1
Solvent-borne type flow agent 0.2
The anti-heavy agent 0.2 of solvent-borne type
Solvent-borne type oxidation inhibitor 0.2.
Present embodiment is a kind of xanchromatic marking paint, and the production technique of present embodiment and embodiment one are basic identical, do not describe in detail at this.
Embodiment three:
Present embodiment is to add light reflecting material to form on the basis of embodiment two, and the weight ratio of described raw material is:
410 acrylic acid resins 14
450 acrylic acid resins 9
Chlorinated rubber powder 4
Titanium dioxide 15
Medium chrome yellow medium yellow powder 5
Process white 6
Talcum powder 6
Zinc sulfide white 5
Dry powder 15
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 14
N-BUTYL ACETATE 11
Dispersion agent 170 0.1
Defoamer 550 0.1
Flow agent 3,306 0.2
Anti-heavy agent 118 0.2
Triphenyl phosphite 0.2
High-refraction glass bead 20
Present embodiment is a kind of yellow reflecting roads sign lacquer, and its production technique and embodiment two are basic identical.
The present invention also can add light reflecting material and make the white reflection marking paint on the basis of embodiment one.
Claims (3)
1, the powerful rapid-curing cutback road mark paint of a kind of thermoplastics type, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
410 acrylic acid resins 14～16
450 acrylic acid resins 9～11
Chlorinated rubber powder 4～6
Titanium dioxide 10～15
Process white 4～6
Talcum powder 4～6
Dry powder 10～15
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 14～16
N-BUTYL ACETATE 9～11
Solvent-borne type dispersion agent 0.1
Solvent-borne type defoamer 0.1
Solvent-borne type flow agent 0.2
The anti-heavy agent 0.2 of solvent-borne type
Solvent-borne type oxidation inhibitor 0.2.
2, the powerful rapid-curing cutback road mark paint of thermoplastics type according to claim 1, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
410 acrylic acid resins 15
450 acrylic acid resins 10
Chlorinated rubber powder 5
Titanium dioxide 10
Medium chrome yellow medium yellow powder 5
Process white 5
Talcum powder 5
Zinc sulfide white 5
Dry powder 10
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 15
N-BUTYL ACETATE 10
Solvent-borne type dispersion agent 0.1
Solvent-borne type defoamer 0.1
Solvent-borne type flow agent 0.2
The anti-heavy agent 0.2 of solvent-borne type
Solvent-borne type oxidation inhibitor 0.2.
3, the powerful rapid-curing cutback road mark paint of thermoplastics type according to claim 2, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
410 acrylic acid resins 14
450 acrylic acid resins 9
Chlorinated rubber powder 4
Titanium dioxide 15
Medium chrome yellow medium yellow powder 5
Process white 6
Talcum powder 6
Zinc sulfide white 5
Dry powder 15
Organobentonite 2
Clorafin 52# 2.5
Dimethylbenzene 14
N-BUTYL ACETATE 11
Dispersion agent 170 0.1
Defoamer 550 0.1
Flow agent 3,306 0.2
Anti-heavy agent 118 0.2
Triphenyl phosphite 0.2
High-refraction glass bead 20.