CN1566238A - Thermoplastic fast-dry traffic paint - Google Patents
Thermoplastic fast-dry traffic paint Download PDFInfo
- Publication number
- CN1566238A CN1566238A CNA031480691A CN03148069A CN1566238A CN 1566238 A CN1566238 A CN 1566238A CN A031480691 A CNA031480691 A CN A031480691A CN 03148069 A CN03148069 A CN 03148069A CN 1566238 A CN1566238 A CN 1566238A
- Authority
- CN
- China
- Prior art keywords
- toluene
- dimethylbenzene
- acrylic resin
- dioctyl phthalate
- dop
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a thermoplastic fast-dry traffic paint which is prepared from the following raw materials (by weight ratio), thermoplastic acrylic resin 45-50, 819 or 820 epoxy resin 2-3, light calcium powder 7-8, talcum powder 2, alta-mud 0.5, titanium dioxide 10, toluene 6-8, dimethylbenzene 12, and acetic acid ethyl ester 5, ultraviolet absorbent 0.5, dioctyl phthalate 2.0-2.8.
Description
Technical field
The present invention relates to the fast arterial highway of a kind of thermoplastics type marking lines lacquer, described marking paint is a kind of coating that is used for the Road safety sign, need not heat during use and can directly spray, and is rapidly dry.
Background technology
Road mark paint commonly used divides solvent-borne type and hot-melting type two big classes, and solvent based coating has a large amount of organic solvents volatilizations in producing and using, and contaminate environment influences healthyly, and coating emphasizes lowly, wears no resistance, work-ing life weak point.Hot-melting type coating has the advantage of fast dried, wear-resisting, long service life but the cost height is arranged, and need be heated to 200 ℃ during construction, construction is loaded down with trivial details, equipment is complicated, and construction environment worsens, and freeze-thaw resistance is poor, and is inapplicable in the cold district use of constructing.On cement pavement, use and easily come off.
Chinese patent 98121033.3 discloses a kind of thermal solvent type paint for road markers, the present invention is made up of film forming component, pigment, filler, softening agent, anti-sedimentation agent and mixed solvent, and its main component is toluene, industrial naptha, dioctyl phthalate (DOP), hot melt acrylic resin, titanium dioxide, process white, lime carbonate, ground silica, talcum powder.The coating of this patent still needs to spray under 40 ℃～80 ℃ moderate temperature.Therefore, need to propose the fast arterial highway of a kind of thermoplastics type marking lines lacquer.
Summary of the invention
The object of the present invention is to provide the fast arterial highway of a kind of thermoplastics type marking lines lacquer, this marking paint need not heat and can directly spray when using, and is rapidly dry, has characteristics such as good wear-resisting, weather-proof, anti-rainwater, acid and alkali-resistance.
The objective of the invention is to realize by following technical proposals: the fast arterial highway of a kind of thermoplastics type marking lines lacquer, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
Thermoplastic acrylic resin 45-50
819 or 820 Resins, epoxy 2-3
Light calcium carbonate powder 7-8
Talcum powder 2
Wilkinite 0.5
Titanium dioxide 10
Toluene 6-8
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.0-2.8.
Preparation method of the present invention is: the acrylic resin in the above-mentioned prescription is added mix the normal temperature still, add 819 or 820 Resins, epoxy, light calcium carbonate powder, titanium dioxide, talcum powder, powdery wilkinite, toluene, dimethylbenzene, ethyl acetate then, stir after the sand mill mesh-of-grind reaches 40 microns, add UV light absorber and dioctyl phthalate (DOP) subsequently and stir and to make the present invention.Need not heat when the present invention uses and directly to spray, but the 10-15 minute paint film in spraying back is with regard to complete drying.
The present invention compared with prior art has following advantage:
1, the present invention has characteristics such as good wear-resisting, weather-proof, anti-rainwater, acid and alkali-resistance.
2, strong, the shock resistance, good to pitch and concrete road surface sticking power of paint film adhesion of the present invention is difficult for phenomenons such as producing variable color, chap and peel off.
3, the present invention is used for highway pavement and executes and draw vehicle lines, can directly spray or the roller coating moulding, and easy construction, rapidly dry, surface drying 3 minutes was done solid work 15 minutes, did not influence vehicle during construction and travelled.
4, the present invention can deposit 2-3 in envrionment temperature during greater than 30 ℃ and never degenerate.
Embodiment
Embodiment one:
The fast arterial highway of thermoplastics type marking lines lacquer is formed by following feedstock production, and the weight ratio of described raw material is:
Thermoplastic acrylic resin 50
819 or 820 Resins, epoxy 2.5
Light calcium carbonate powder 7.5
Talcum powder 2.0
Wilkinite 0.5
Titanium dioxide 10
Toluene 8
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.0.
Preparation method of the present invention is: the acrylic resin in the above-mentioned prescription is added mix the normal temperature still, add 819 or 820 Resins, epoxy, light calcium carbonate powder, titanium dioxide, talcum powder, powdery wilkinite, toluene, dimethylbenzene, ethyl acetate then, stir after the sand mill mesh-of-grind reaches 40 microns, add UV light absorber and dioctyl phthalate (DOP) subsequently and stir and to make the present invention.The model of the UV light absorber of using in the present embodiment is UV237.
Need not heat when the present invention uses and directly to spray, but the 10-15 minute paint film in spraying back is with regard to complete drying.150 microns of total coating thickness of the present invention can adopt 2-3 spraying operation to realize.
Embodiment two:
The fast arterial highway of thermoplastics type marking lines lacquer is formed by following feedstock production, and the weight ratio of described raw material is:
Thermoplastic acrylic resin 50
819 Resins, epoxy 2.5
Light calcium carbonate powder 7
Talcum powder 2.0
Wilkinite 0.5
Medium chrome yellow medium yellow 10
Toluene 6
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.
The preparation method of present embodiment is: the acrylic resin in the above-mentioned prescription is added mix the normal temperature still, add 819 Resins, epoxy, light calcium carbonate powder, powdery medium chrome yellow medium yellow, talcum powder, powdery wilkinite, toluene, dimethylbenzene, ethyl acetate then, stir after the sand mill mesh-of-grind reaches 40 microns, add UV light absorber and dioctyl phthalate (DOP) subsequently and stir and to make the present invention.
Embodiment three:
Present embodiment is to add light reflecting material on the basis of embodiment two, and the weight ratio of described raw material is:
Thermoplastic acrylic resin 45
819 Resins, epoxy 3
Light calcium carbonate powder 7
Talcum powder 2.0
Wilkinite 0.5
Medium chrome yellow medium yellow 10
Toluene 6
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.8
High-refraction glass bead 20.
Present embodiment is a kind of yellow reflecting roads sign lacquer, and its production technique and embodiment two are basic identical.
The present invention also can add light reflecting material and make the white reflection marking paint on the basis of embodiment one.
Claims (3)
1, the fast arterial highway of a kind of thermoplastics type marking lines lacquer, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
Thermoplastic acrylic resin 45-50
819 or 820 Resins, epoxy 2-3
Light calcium carbonate powder 7-8
Talcum powder 2
Wilkinite 0.5
Titanium dioxide 10
Toluene 6-8
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.0-2.8.
2, the fast arterial highway of thermoplastics type according to claim 1 marking lines lacquer, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
Thermoplastic acrylic resin 50
819 Resins, epoxy 2.5
Light calcium carbonate powder 7
Talcum powder 2
Wilkinite 0.5
Medium chrome yellow medium yellow 10
Toluene 6
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.
3, the fast arterial highway of thermoplastics type according to claim 2 marking lines lacquer, it is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
Thermoplastic acrylic resin 45
819 Resins, epoxy 3
Light calcium carbonate powder 7
Talcum powder 2
Wilkinite 0.5
Medium chrome yellow medium yellow 10
Toluene 6
Dimethylbenzene 12
Ethyl acetate 5
UV light absorber 0.5
Dioctyl phthalate (DOP) 2.8
High-refraction glass bead 20.