CN1313363A - 多性能装饰涂料 - Google Patents
多性能装饰涂料 Download PDFInfo
- Publication number
- CN1313363A CN1313363A CN 00113317 CN00113317A CN1313363A CN 1313363 A CN1313363 A CN 1313363A CN 00113317 CN00113317 CN 00113317 CN 00113317 A CN00113317 A CN 00113317A CN 1313363 A CN1313363 A CN 1313363A
- Authority
- CN
- China
- Prior art keywords
- parts
- ratio
- filler
- coating according
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
多性能装饰涂料,其原料的配方比例(重量份数比):白水泥分别为20~30份和55~60份;填料(细度模数380目~480目之间)分别为70~80份和40~45份;颜料0.1~0.3份;助剂0.3~0.8份。该涂料用于墙壁装饰、无毒、无异味、光洁度高。具有耐火阻燃、耐水防潮、耐高低温、耐磨耐洗、耐冲击、耐碱性、耐污染、耐老化等多种性能。
Description
本发明属于建筑涂料,适用于房屋室内外墙壁的装饰。
建筑涂料工业发展迅速,品种繁多。其中与本发明最为接连的产品是日本的室内外装饰用薄质涂料C。该产品属水泥质系,主要材料是:1、白水泥;2、集料(粒径为1.2~5mm);3、填料,包括石灰、白云石膏;4、颜料;5、助剂,包括防水剂、早强剂、水泥掺合用树脂。尽管该产品具有各种优异性能,但也有不少缺限,表现在:1、骨料过粗,作为装饰涂料,则欠缺光洁、细腻之感,施工操作较为困难;2、石灰用量过大,因为高石灰含量的涂料,容易产生泛碱、柝白的现象,影响装饰效果,这是日本“涂料C”的主要弱点。
本发明的目的是对以往的同类产品存在的一些缺陷,在原材料的配方和比例方面进行调整,从根本上改善水泥的使用性能,使涂料的装饰效果更好,使用寿命更长,性能更优异。其配方方案是:在确定比例的水泥用量下掺入一定量的集料(细度模数为380目~480目之间),减免石灰的使用,配合使用多种复合助剂,如减水剂、缓凝剂、分散剂等一系列助剂的同时,较大量地使用了一些特殊助剂,如极性聚合物来实现上述目的。
该产品的原材料配方(重量份数比):白水泥分别为20~30份和55~60份;填料分别为70~80份和40~45份;颜料0.1~0.3份;助剂0.3~0.8份。
普通型底层涂料的填料组成(重量份数比):轻质碳酸钙占70~80份;硅石粉、铸石粉、大理石粉、花岗石粉占20~30份;合成纤维2~5份。
普通型面层涂料的填料组成(重量份数比):轻质碳酸钙20-30份;硅石粉铸石粉、大理石粉、花岗石粉占70-80份。
耐热型涂料的填料组成(体积比):膨胀珍珠岩粉50份,膨胀蛭石粉25份,矿棉粉25份。
弹性型涂料的填料组成(体积比):塑料粉60份,石灰石粉40份。
按上述配比所制成的涂料用于墙壁装饰,无毒,无异味,光洁度高;具有耐火阻燃、耐水防潮、耐高低温、耐磨耐洗、耐冲击、耐碱性、耐污染、耐老化等多种性能。
本发明的产品,可采用弹、滚、抹、刷、喷、刮、压花等多种施工工艺。
Claims (5)
1、多性能装饰涂料,其特征在于原料配方比例(重量份数比):白水泥分别为20~30份和55~60份;填料(细度模数380目~480目之间)分别为70~80份和40~45份;颜料0.1~0.3份;助剂0.3~0.8份。
2、根据权利要求1所述的涂料,其特征在于普通型底层涂料的填料组成(重量份数比)为:轻质碳酸钙70~80份;硅石粉、铸石粉、大理石粉、花岗石粉占20~30份;合成纤维2~5份。
3、根据权利要求1所述的涂料,其特征在于普通型面层涂料的填料组成(重量份数比)为:轻质碳酸钙20~30份;硅石粉、铸石粉、大理石粉、花岗石粉占70~80份。
4、根据权利要求1所述的涂料,其特征在于耐热型涂料的填料组成(体积比)为:膨胀珍珠岩50份,膨胀蛭石粉25份,矿棉粉25份。
5、根据权利要求1所述的涂料,其特征在于弹性型涂料的填料组成(体积比)为:塑料粉60份,石灰石粉40份。