CN1305964C - Water-proof coiled material - Google Patents
Water-proof coiled material Download PDFInfo
- Publication number
- CN1305964C CN1305964C CNB2004100400246A CN200410040024A CN1305964C CN 1305964 C CN1305964 C CN 1305964C CN B2004100400246 A CNB2004100400246 A CN B2004100400246A CN 200410040024 A CN200410040024 A CN 200410040024A CN 1305964 C CN1305964 C CN 1305964C
- Authority
- CN
- China
- Prior art keywords
- water
- present
- parts
- coiled material
- proof coiled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a water-proof coiled material which contains styrene-butadiene-styrene block copolymer and/or atactic polypropelene and filling materials. The present invention is characterized in that the water-proof coiled material also contains rosin and vegetable oil, and all the components have the following proportion measured by parts by weight: 30 to 60 parts of rosin, 15 to 45 parts of vegetable oil, 10 to 35 parts of styrene-butadiene-styrene block copolymer and/or atactic polypropelene and 5 to 25 parts of filling material. The water-proof coiled material of the present invention adopts the rosin and the vegetable oil instead of raw materials for traditional asphalt water-proof coiled materials and also overcomes the problem of environment pollution in the processes of production, construction and use of water-proof coiled materials in the prior art. The present invention has the characteristic of environmental protection and simultaneously maintains the properties of resistance to high and low temperature, compression resistance, strong aging resistance, high stretching resistance, etc. of the existing coiled material; therefore, the present invention is a novel water-proof material.
Description
Technical field
The present invention relates to a kind of water-proof material, specifically, relate to a kind of waterproof roll.
Background technology
In the water-proof material industry, existing very many water-proof material products, but at vinylbenzene-divinyl-styrene block copolymer, be called for short " SBS ", Atactic Polypropelene is called for short in " APP " waterproof roll, all adopts pitch or tar to carry out modification.Disclosed as on January 21st, 2004, notification number is CN1468929A, the Chinese invention patent prospectus that name is called " a kind of waterproof roll and production method thereof " discloses a kind of waterproof roll, contain waste butyl rubber, oil building asphalt and filler, it is characterized in that also containing styrene-butadiene rubber(SBR) and/or vinylbenzene-divinyl-styrene block copolymer, ratio is by weight: vinylbenzene-divinyl-styrene block copolymer 5-30 part, waste butyl rubber 10-50 part, oil building asphalt 5-20 part, filler 10-60 part.
In the production process of above-mentioned waterproof roll, during the pitch heating for dissolving, can produce the unpleasant irritating smell that has, severe contamination production site surrounding enviroment, and the production operation workman had very big harm, this material construction is in building roof or toilet and other life and work places, to long-time life and work people therein, has certain toxicity, infringement people's health.
Summary of the invention
Goal of the invention of the present invention is to overcome above-mentioned deficiency, and a kind of asphalt free waterproof roll is provided.
Waterproof roll of the present invention contains rosin, vegetables oil, vinylbenzene-divinyl-styrene block copolymer and/or Atactic Polypropelene, stopping composition, and in weight part, concrete ratio is as follows:
Rosin 30-60 part
Vegetables oil 15-45 part
Vinylbenzene-divinyl-styrene block copolymer and/or Atactic Polypropelene 10-35 part
Stopping composition 5-25 part
Wherein vegetables oil can be tung oil, soybean oil, the young oil of dish, peanut wet goods, and stopping composition can be talcum powder, lime powder, terra alba etc.
Under the situation of above-mentioned component, can also contain essence 5-10 part or/and pigment 5-10 part, to produce fragrance or/and various color.
The production process of waterproof roll of the present invention is: use thermal oil equipment to heat.Add rosin earlier, be heated to 160 degrees centigrade to 200 degrees centigrade dissolvings, add vegetables oil in proportion, stir, the insulation dehydration, add vinylbenzene-divinyl-styrene block copolymer and/or Atactic Polypropelene properties-correcting agent and stir, adding stopping composition, pigment, essence stir, and promptly get waterproof roll of the present invention.As produce the coiled material ointment, carry out cooling packing.If the production coiled material is made the tire base with polyester non-woven fabric or glass Compound Fabric and carried out dip-coating, through roll-in, multiple film or sand again, produce this product use equipment and adopt the production modified bituminous pitch coiled material production line can produce the coiled material of different thickness through operations such as cooling, rollings.
Constructional method: identical with the modified bituminous pitch coiled material constructional method, specific as follows,
1, buildings keeps smooth smooth, dry, no-sundries;
2, scrape one to two road ointment;
3, the sticking coiled material in shop is roasting sticking with spray;
4, overlap vertical 10-12 centimetre, laterally 8-10 centimetre;
5, floating lap side seam is promptly finished the construction of waterproof roll of the present invention.
Waterproof roll of the present invention has subzero 15 degrees centigrade to the 18 degrees centigrade flawlesses of low temperature, high temperature does not trickle for 90 degrees centigrade to 110 degrees centigrade, resistance to compression, anti-aging strong, and stretching resistance is high, meets national existing modified asphalt waterproof standard of materials.Waterproof roll of the present invention, adopt rosin, vegetables oil to substitute traditional asphalt water-proof coiled material raw material, overcome the problem of environmental pollution of prior art waterproof roll in production, construction and use, characteristics with environmental protection, simultaneously, kept high-low temperature resistant, the resistance to compression, anti-aging strong of existing coiled material, performances such as stretching resistance height are the water-proof materials of a new generation.
Embodiment
Below in conjunction with specific embodiment, waterproof roll of the present invention is described in further detail.
Following table is the situation (in weight part) and the performance index detection case of the concrete proportioning of several enforcement products.
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | ||
| Component | Rosin | 30 | 40 | 60 | 50 | 30 |
| Vegetables oil | 45 | 15 | 30 | 20 | 40 | |
| SBS is or/and APP | 10 | 35 | 25 | 20 | 10 | |
| Stopping composition | 20 | 5 | 20 | 10 | 15 | |
| Pigment | 0 | 0 | 0 | 5 | 10 | |
| Essence | 0 | 0 | 0 | 10 | 5 | |
| Performance | Low temperature-18 ℃ | Flawless | Flawless | Flawless | Flawless | Flawless |
| 110 ℃ of high temperature | Do not trickle | Do not trickle | Do not trickle | Do not trickle | Do not trickle |
As can be seen from the above table, waterproof roll of the present invention can substitute the water-proof material made from pitch at present fully, is new generation of green environment-friendly type waterproof roll.
Waterproof roll of the present invention is not limited to the scope of embodiment, and present embodiment just helps to understand the present invention, and all utilize innovation and creation that the present invention conceives all at the row of protection.
Claims (2)
1. a waterproof roll contains styrene-butadiene-styrene block copolymer and/or Atactic Polypropelene, stopping composition, it is characterized in that also containing rosin, vegetables oil, and in weight part, concrete ratio is as follows:
Rosin 30-60 part
Vegetables oil 15-45 part
Styrene-butadiene-styrene block copolymer 10-35 part
Stopping composition 5-25 part.
2. according to claims 1 described waterproof roll, it is characterized in that also containing essence 5-10 part or/and pigment 5-10 part.