CN109536026A - Complex waterproof layer and its construction method - Google Patents
Complex waterproof layer and its construction method Download PDFInfo
- Publication number
- CN109536026A CN109536026A CN201710652989.8A CN201710652989A CN109536026A CN 109536026 A CN109536026 A CN 109536026A CN 201710652989 A CN201710652989 A CN 201710652989A CN 109536026 A CN109536026 A CN 109536026A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- layer
- self
- adhesive glue
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to architectural waterproof material fields, and in particular to a kind of complex waterproof layer and its construction method.Complex waterproof layer includes self-adhesive glue layer and waterproof sheet layer, and self-adhesive glue layer material is uncured rubber asphalt waterproof coating;Uncured rubber asphalt waterproof coating includes following raw material: asphalt, softening agent, styrene-butadiene block copolymer, tackifying resin, shoddy, filler and surfactant.The present invention adapts to that base's deformability is strong, bond effect is good, prevents channeling water, drainage, solves existing waterproof coiled material construction and is easy to produce the high disadvantage of hollowing, disengagement, repair rate;The present invention also provides its construction methods, self-adhesive glue layer of being constructed by the way of spraying or blade coating in base;It is laid with waterproof sheet layer on the surface of the self-adhesive glue layer for completion of having constructed, waterproof sheet layer edge sealing is sealed using self-adhesive glue layer;Environmental protection, conveniently, securely and reliably, construction operation can be carried out at -10 DEG C~-20 DEG C, meet construction period.
Description
Technical field
The invention belongs to architectural waterproof material fields, and in particular to a kind of complex waterproof layer and its construction method.
Background technique
Roof waterproof form generallys use waterproof roll and is affixed directly on concrete base layer at present, and coiled material adapts to base and becomes
The ability of shape is poor, and bond effect is general, is very easy to generate disengagement, hollowing, channeling water and other issues, is easy to cause leakage,
Maintenance rate is high, and common coiled material is to will cause unnecessary fire and personnel in construction application by hot melt application
By injuring the generation of casualty accident, and it will cause environmental pollution.
Uncured rubber asphalt waterproof coating is a kind of creepage type water-repellent paint, it is not water paint, nor solvent
Type or reactive type of coating, but one-component creepage type coating that is solvent-free, not forming a film, with metal, nonmetallic and coagulation great soil group
Equal substrates have good cementitiousness, the double effects with waterproof, anti-corrosion of metal.
Summary of the invention
In view of the deficiencies of the prior art, the object of the present invention is to provide a kind of complex waterproof layers, adapt to base's deformability
By force, bond effect is good, prevents channeling water, drainage, solves existing waterproof coiled material construction and is easy to produce hollowing, disengagement, repair rate
High disadvantage;The present invention also provides its construction method, environmental protection, conveniently, securely and reliably can construct at -10 DEG C~-20 DEG C
Operation meets construction period.
Complex waterproof layer of the present invention, including self-adhesive glue layer and waterproof sheet layer, self-adhesive glue layer material are uncured
Rubber asphalt waterproof coating;Uncured rubber asphalt waterproof coating includes following raw material: asphalt, softening agent, styrene-fourth
Diene block copolymer, tackifying resin, shoddy, filler and surfactant.
Wherein:
Waterproof sheet layer material is in asphalt water-proof coiled material, modified-high polymer waterproof roll material or synthetic polymeric waterproofing material
It is one or more.
Uncured rubber asphalt waterproof coating of the present invention, the raw material including following parts by weight: asphalt 35-
65 parts, 5-25 parts of softening agent, 2-10 parts of styrene-butadiene block copolymer, 5-20 parts of tackifying resin, 5-25 parts of shoddy,
5-20 parts of filler, 0.5-3 parts of surfactant.
As a kind of perferred technical scheme, uncured rubber asphalt waterproof coating of the present invention, including it is following heavy
Measure the raw material of number: 40-60 parts of asphalt, 8-20 parts of softening agent, 3-8 parts of styrene-butadiene block copolymer, thickening is set
5-15 parts of rouge, 10-25 parts of shoddy, 10-20 parts of filler, 1-3 parts of surfactant.
Asphalt is 70# 90# bi tumenf orr oad.
Softening agent is catalytic cracked oil pulp, and catalytic cracked oil pulp is oil plant catalytic cracked oil pulp.
Styrene-butadiene block copolymer is linear SBS.
Tackifying resin is in coumarone indene resin, terpene resin, rosin resin, C 5 petroleum resin or C 9 petroleum resin
One or more of mixtures.
Shoddy is 60-120 mesh waste-tyre rubber-powder.
Filler is flyash.
Surfactant is one in stearic acid polyoxyethylene ether, fatty alcohol polyoxyethylene ether or alkyl phenol polyoxyethylene ether
Kind or several mixtures.
The preparation method of uncured rubber asphalt waterproof coating of the present invention, includes the following steps:
(1) asphalt and softening agent are mixed, is heated to 150-160 DEG C, moderate-speed mixer 20-40min, moderate-speed mixer speed
Degree is 2000-3000r/min;
(2) styrene-butadiene block copolymer is added in the mixture obtained to step (1), is heated to 170-190
DEG C, moderate-speed mixer 30-60min, moderate-speed mixer speed is 2000-3000r/min;
(3) tackifying resin, shoddy, surfactant and filler are sequentially added in the mixture obtained to step (2), dropped
For temperature to 140-160 DEG C, high-speed stirred 30-60min, high-speed stirred speed is 5000-6000r/min, is then down to room temperature to obtain the final product.
The construction method of complex waterproof layer of the present invention, comprising the following steps:
(1) it is constructed self-adhesive glue layer by the way of spraying or blade coating in base;
(2) it is laid with waterproof sheet layer on the surface of the self-adhesive glue layer for completion of having constructed, waterproof sheet layer edge sealing uses self-adhesion
Glue-line is sealed.
Base is cleared up before self-adhesive glue layer of constructing, with tool that the laitance of base and building sundries cleaning is dry
Only.Phenomena such as base of waterproof layer should sufficiently conserve, and accomplish that surface is firm, smooth, clean, no peeling, dusting, base is preferably dry
It is dry to there is bright water or moisture content to reach saturation state.
Wherein:
The self-adhesive glue layer breadth that paves is 95-105mm bigger than waterproof sheet layer.
The construction temperature of self-adhesive glue layer is 145-165 DEG C, and spraying or blade coating are with a thickness of 1-2.5mm, the i.e. thickness of self-adhesive glue layer
Degree is 1-2.5mm.
Compared with prior art, the invention has the following advantages that
(1) complex waterproof layer of the present invention bonds waterproof using the excellent cementitiousness of uncured rubber asphalt waterproof coating
Coiled material forms the double-deck waterproof, secure bond, uncured rubber-asphalt coating not still waterproof layer and be buffer layer and adhesive layer,
After base course crack, dope layer waterproof absorbs crack stress, closes base's pore, protects waterproof roll not to be pulled off, effectively
It prevents the channeling water between complex waterproof layer and base and drainage, solves existing waterproof coiled material construction and be easy to produce sky
Drum disengages, the disadvantage that repair rate is high.
(2) the present invention also provides its construction method, complex waterproof layer not only saves the ring that waterproof coiled material construction needs to heat
Section so that construction is more environmentally-friendly, conveniently, securely and reliably, and can carry out construction operation at -10 DEG C~-20 DEG C, greatly meet
Construction period.
(3) present invention adaptation base's deformability is strong, bond effect is good, construction environment friendly convenient.
Specific embodiment
Below with reference to embodiment, the present invention will be further described.
Embodiment 1
A kind of complex waterproof layer, construction method are as follows:
1. clearing up base, the laitance of base and building sundries are cleaned out with tool.The base of waterproof layer should sufficiently support
Phenomena such as shield, and accomplishes that surface is firm, smooth, clean, no peeling, dusting, base's preferably drying must not have bright water or moisture content to reach
To saturation state.
2. the uncured rubber asphalt waterproof coating for above-mentioned preparation of being constructed by the way of spraying, blade coating in base.
3. SBS modified asphalt waterproof coiled material is laid on the uncured rubber asphalt waterproof coating surface for completion of having constructed,
Coiled material edge sealing is sealed using uncured rubber-asphalt coating.
Uncured rubber asphalt waterproof coating used, the raw material including following parts by weight: 70# bi tumenf orr oad 55
Part, 15 parts of catalytic cracked oil pulp, 1,301 6 parts of SBS, 10 parts of coumarone indene resin, 80 20 parts of mesh shoddies, 15 parts of flyash, NP-
10 2.5 parts.
Uncured rubber asphalt waterproof coating preparation method the following steps are included:
(1) asphalt and softening agent are mixed, is heated to 150 DEG C, moderate-speed mixer 40min, moderate-speed mixer speed is
2000r/min;
(2) styrene-butadiene block copolymer is added in the mixture obtained to step (1), is heated to 170 DEG C, in
Speed stirring 60min, moderate-speed mixer speed are 2000r/min;
(3) tackifying resin, shoddy, surfactant and filler are sequentially added in the mixture obtained to step (2), dropped
For temperature to 140 DEG C, high-speed stirred 60min, high-speed stirred speed is 6000r/min, is then down to room temperature to obtain the final product.
Embodiment 2
A kind of complex waterproof layer, construction method are as follows:
1. clearing up base, the laitance of base and building sundries are cleaned out with tool.The base of waterproof layer should sufficiently support
Phenomena such as shield, and accomplishes that surface is firm, smooth, clean, no peeling, dusting, base's preferably drying must not have bright water or moisture content to reach
To saturation state.
2. the uncured rubber asphalt waterproof coating for above-mentioned preparation of being constructed by the way of spraying, blade coating in base.
3. being laid with polyethylene polypropylene fiber waterproof coiled material on the uncured rubber asphalt waterproof coating surface for completion of having constructed, roll up
Material edge sealing is sealed using uncured rubber-asphalt coating.
Uncured rubber asphalt waterproof coating used, the raw material including following parts by weight: 70# bi tumenf orr oad 50
Part, 20 parts of catalytic cracked oil pulp, 5 parts of SBS1301,12 parts of terpene resin, 60 15 parts of mesh shoddies, 20 parts of flyash, MOA-9
1.5 part.
Uncured rubber asphalt waterproof coating the preparation method comprises the following steps:
(1) asphalt and softening agent are mixed, is heated to 155 DEG C, moderate-speed mixer 30min, moderate-speed mixer speed is
3000r/min;
(2) styrene-butadiene block copolymer is added in the mixture obtained to step (1), is heated to 180 DEG C, in
Speed stirring 40min, moderate-speed mixer speed are 3000r/min;
(3) tackifying resin, shoddy, surfactant and filler are sequentially added in the mixture obtained to step (2), dropped
For temperature to 150 DEG C, high-speed stirred 50min, high-speed stirred speed is 5000r/min, is then down to room temperature to obtain the final product.
Embodiment 3
A kind of complex waterproof layer, construction method are as follows:
1. clearing up base.The laitance of base and building sundries are cleaned out with specific purpose tool.The base of waterproof layer should fill
Phenomena such as point maintenance, and accomplishes that surface is firm, smooth, clean, no peeling, dusting, base's preferably drying must not have bright water or aqueous
Rate reaches saturation state.
2. the uncured rubber-asphalt waterproof coating for above-mentioned preparation of being constructed by the way of spraying, blade coating in base.
3. APP modified asphalt waterproof coiled material is laid on the uncured rubber-asphalt waterproof coating surface for completion of having constructed,
Coiled material edge sealing is sealed using uncured rubber-asphalt coating.
Uncured rubber asphalt waterproof coating used, the raw material including following parts by weight: 90# bi tumenf orr oad 45
Part, 16 parts of catalytic cracked oil pulp, 7 parts of SBS1301,15 parts of C 5 petroleum resin, 100 10 parts of mesh shoddies, 15 parts of flyash,
2 parts of SG-40.Uncured rubber asphalt waterproof coating preparation method is same as Example 1.
It is applied to house roof, basement as waterproof layer according to the construction method of embodiment 1-3.After construction respectively into
Row detection, discovery complex waterproof layer waterproof effect is good, equal ne-leakage water phenomenon, also occurs without disengagement, hollowing, channeling water phenomenon.
Embodiment 1-4 is prepared according to uncured rubber-asphalt coating professional standard publicity original text in 2014 uncured
Rubber asphalt waterproof coating does performance test, and test result is shown in Table 1.
The uncured rubber asphalt waterproof coating testing result of table 1
It can be seen from Table 1 that uncured rubber asphalt waterproof coating heat resistance, low temperature flexibility and extensibility all reach
Quality standard, while being also equipped with and being not easy to solidify, the features such as flexibility is good and self-healing property is strong, at low cost.
Claims (10)
1. a kind of complex waterproof layer, it is characterised in that: including self-adhesive glue layer and waterproof sheet layer, self-adhesive glue layer material is uncured
Rubber asphalt waterproof coating;Uncured rubber asphalt waterproof coating includes following raw material: asphalt, softening agent, styrene-fourth
Diene block copolymer, tackifying resin, shoddy, filler and surfactant.
2. complex waterproof layer according to claim 1, it is characterised in that: waterproof sheet layer material be asphalt water-proof coiled material,
One of modified-high polymer waterproof roll material or synthetic polymeric waterproofing material are a variety of.
3. complex waterproof layer according to claim 1, it is characterised in that: uncured rubber asphalt waterproof coating includes following
The raw material of parts by weight: 35-65 parts of asphalt, 5-25 parts of softening agent, 2-10 parts of styrene-butadiene block copolymer, increase
5-20 parts of viscosity resin, 5-25 parts of shoddy, 5-20 parts and surfactant 0.5-3 parts of filler.
4. complex waterproof layer according to claim 3, it is characterised in that: asphalt is the drip of 70# 90# road petroleum
It is green;Softening agent is catalytic cracked oil pulp;Styrene-butadiene block copolymer is linear SBS.
5. complex waterproof layer according to claim 3, it is characterised in that: tackifying resin be coumarone indene resin, terpene resin,
The mixture of one or more of rosin resin, C 5 petroleum resin or C 9 petroleum resin.
6. complex waterproof layer according to claim 3, it is characterised in that: shoddy is 60-120 mesh waste-tyre rubber-powder;
Filler is flyash;Surfactant is stearic acid polyoxyethylene ether, fatty alcohol polyoxyethylene ether or alkyl phenol polyoxyethylene ether
One or more of mixture.
7. -6 any complex waterproof layer according to claim 1, it is characterised in that: uncured rubber asphalt waterproof coating
Preparation method includes the following steps:
(1) asphalt and softening agent are mixed, is heated to 150-160 DEG C, moderate-speed mixer 20-40min, moderate-speed mixer speed is
2000-3000r/min;
(2) styrene-butadiene block copolymer is added in the mixture obtained to step (1), is heated to 170-190 DEG C, in
Speed stirring 30-60min, moderate-speed mixer speed are 2000-3000r/min;
(3) tackifying resin, shoddy, surfactant and filler are sequentially added in the mixture obtained to step (2), be cooled to
140-160 DEG C, high-speed stirred 30-60min, high-speed stirred speed is 5000-6000r/min, is then down to room temperature to obtain the final product.
8. a kind of construction method of any complex waterproof layer of claim 1-6, it is characterised in that: the following steps are included:
(1) it is constructed self-adhesive glue layer by the way of spraying or blade coating in base;
(2) it is laid with waterproof sheet layer on the surface of the self-adhesive glue layer for completion of having constructed, waterproof sheet layer edge sealing uses self-adhesive glue layer
It is sealed.
9. the construction method of complex waterproof layer according to claim 8, it is characterised in that: self-adhesive glue layer paves breadth than anti-
The big 95-105mm of water sheet layer.
10. the construction method of complex waterproof layer according to claim 8, it is characterised in that: the construction temperature of self-adhesive glue layer
It is 145-165 DEG C, spraying or blade coating are with a thickness of 1-2.5mm.