KR100924114B1 - Rubberized asphalt sheet, root isolation sheet, and constructing method of complex waterproof and root isolation layer structure - Google Patents

Rubberized asphalt sheet, root isolation sheet, and constructing method of complex waterproof and root isolation layer structure Download PDF

Info

Publication number
KR100924114B1
KR100924114B1 KR1020090033519A KR20090033519A KR100924114B1 KR 100924114 B1 KR100924114 B1 KR 100924114B1 KR 1020090033519 A KR1020090033519 A KR 1020090033519A KR 20090033519 A KR20090033519 A KR 20090033519A KR 100924114 B1 KR100924114 B1 KR 100924114B1
Authority
KR
South Korea
Prior art keywords
sheet
banggeun
weight
parts
chaksik
Prior art date
Application number
KR1020090033519A
Other languages
Korean (ko)
Inventor
박종욱
손문세
Original Assignee
주식회사 부일건화
주식회사 행림종합 건축사사무소
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 부일건화, 주식회사 행림종합 건축사사무소 filed Critical 주식회사 부일건화
Priority to KR1020090033519A priority Critical patent/KR100924114B1/en
Application granted granted Critical
Publication of KR100924114B1 publication Critical patent/KR100924114B1/en

Abstract

PURPOSE: A rubberized asphalt sheet and root isolation sheet and construction method of complex waterproof and root isolation layer structure are provided, which achieve construction in winter and high adhesion. CONSTITUTION: A rubberized asphalt sheet(10) includes a compound, non-woven fabric(12), polyester film(13), and release paper(14). The compound is prepared by mixing asphalt 30~40 wt.%, styrene-butadiene styrene 10~20 wt.%, butyl rubber 10~15 wt.%, Dioctyl phthalic acid 5~10 wt.%, Nitrile Butadiene Rubber 5~10 wt.%, calcium carbonate 5~15 wt.%, and special additive 5~15 wt.%. The non-woven fabric is equipped on the upper part of the compound. The polyester film is equipped on the upper part of the non-woven fabric. The release paper is adhered to the lower part of the compound.

Description

자착식 고무화 아스팔트시트 및 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법{Rubberized asphalt sheet, root isolation sheet, and constructing method of complex waterproof and root isolation layer structure} Here chaksik rubberized asphalt sheet and the chair chaksik construction method of a composite structure using a water-banggeun Chemistry AR sheet and the sheet banggeun {Rubberized asphalt sheet, root isolation sheet, and constructing method of complex waterproof and root isolation layer structure}

본 발명은 자착식 고무화 아스팔트시트 및 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법에 관한 것으로, 보다 상세하게는, 방수층을 형성하는 방수시트가 접착력이 우수할 뿐만 아니라 바닥면에 크랙이 생기더라도 이를 흡수할 수 있도록 고점착 연질형 고무화 아스팔트를 점착층으로 한 자착식 고무화 아스팔트시트를 사용하고, 그 상부에 내근성과 접착력이 탁월한 방근시트로 시공한 복합방수·방근구조의 시공방법에 관한 것이다. The invention party relates to chaksik rubberized asphalt sheet and the chair chaksik construction method of a composite water-banggeun structure using a screen AR sheet and banggeun sheet and, more particularly, as a waterproof sheet for forming the waterproof layer to the adhesive force is excellent not even the advent of the crack to the bottom surface using a character chaksik rubberized asphalt sheet of high adhesion, soft-type rubberized asphalt to absorb the adhesive layer it, and its upper portion to the inside spirit and adhesion excellent room composite construction myopia Trojan waterproof and relates to the construction method of banggeun structure.

최근 도시 생태계 및 도시 환경을 개선하기 위하여 건물의 옥상녹화 또는 실내정원을 조성하는 사업을 많이 하고 있는데, 이들 옥상녹화 및 실내정원은 토양 생태계의 복원, 냉난방 에너지 절약, 도시 열섬화 현상 완화, 도시 홍수 예방, 공기 정화, 수질 정화, 소음 경감, 도시 경관 향상, 건축물의 내구성 향상 등 환경적 측면과 경제적 측면 등에서 여러 가지 이점이 있는 관계로 권장되고 있음은 물론, 일정 규모 이상의 건축물에는 의무적으로 옥상 녹화 시설을 갖추도록 규정하고 있으며, 일부 지방자치단체에서는 옥상 녹화 시설을 설치하는데 자금도 지원해주고 있다. There are a lot of business to create a rooftop or indoor garden of the building to the recent improving the urban ecology and urban environment, these green roof and indoor garden is the restoration of soil ecosystems, air-conditioning energy conservation, urban yeolseomhwa reduction, urban flood prevention , air purification, water purification, noise reduction, urban landscape improvements, an increase in the durability of buildings, including environmental aspects and the economic and recommendations in relation with several benefits, etc. aspects, as well as with green roof is compulsory are at least a certain size building facilities and to equip and regulations, and some local governments to install a green roof facility haejugo funding support.

상기와 같은 옥상녹화의 많은 이점에도 불구하고 옥상녹화가 활성화되지 못하고 있는 데에는 여러 가지 이유가 있겠지만, 그중에서도 식물의 뿌리가 성장하여 건축물을 파손시키게 될 뿐만 아니라 방수층의 파손으로 건축물의 방수에 문제가 발생한다는 것이다. But despite the many benefits of a green roof as described above and a number of reasons why that rooftop did not Activate, notably problems with waterproofing of buildings caused not only thereby damage the building to grow the roots of plants to damage the waterproof layer is that. 즉, 옥상녹화 또는 실내정원을 조성하지 않았더라면 방수에 문제가 없었을 것인데, 옥상녹화 또는 실내정원을 조성함으로써 식물의 뿌리가 기존의 방수층은 쉽게 뚫고 들어가기 때문에 방근 뿐만 아니라 방수에도 문제가 발생한다는 것이다. In other words, geotinde had not creating a rooftop or indoor gardens not have been a problem with the water, is that the roots of the plants by creating a rooftop or indoor gardens that, as well as banggeun water problems caused by going through existing waterproof layer is easy.

일반적으로 방수시트인 고무화 아스팔트시트는 대부분 부직포가 시트의 두께방향에서 중간에 위치해 있기 때문에 접착층의 두께가 얇다. The thickness of the adhesive layer is thin, because generally waterproof sheets of rubberized asphalt sheet is mostly non-woven fabric is properly located in the middle in the thickness direction of the sheet. 이러한 방수시트를 사용하여 콘크리트 바닥면에 방수층을 형성하는 시공방법은 크게 밀착공법과 절연공법으로 나누어지는데, 밀착공법은 방수시트를 콘크리트 바닥면에 밀착시키는 시공법으로 만일 콘크리트 바닥면에 크랙이 발생하면 바닥면에 접착된 방수시트가 접착층의 두께가 얇아서 그 균열을 흡수해 줄 수가 없기 때문에 방수시트도 바닥면과 함께 크랙이 발생하게 되어 방수층으로서의 기능을 상실하게 된다는 심각한 문제가 있고, 절연공법은 방수시트와 콘크리트 바닥면 사이가 접착되지 않고 떠 있기 때문에 바닥면에 크랙이 발생하더라도 방수시트에는 문제가 없지만 바닥면에 누수가 생기면 누수 개소를 찾기 위하여 방수시트 전체를 뜯어내고 찾아야 한다는 문제가 있다. Using these water resistant sheet divided into concrete construction method of forming a waterproof layer on the bottom surface is larger contact method and isolated process, if the adhesion process is a crack in ten thousand and one concrete floor surface caused by construction method for close contact with the waterproof sheet to the concrete floor a serious problem that the waterproof sheet adhered to a bottom surface that because the number of lines to absorb the crack thickness of the adhesive layer is thin becomes waterproof sheet cracks with the bottom side lose their waterproof layer as function and isolation process is waterproof even if a crack in the floor surface occurs because the concrete between the seat and the floor surface does not leave adhesive waterproof sheet has the problem that problem is not to find the bottom saenggimyeon a leak ripping the entire waterproof sheet to find the leak points.

또한, 일반적으로 방수시트를 시공할 때는 시트끼리의 접합부를 열융착방식으로 접착시키는데, 방수시트들은 열기구를 이용하여 시공하기 때문에 시트에 열이 과도하게 전달되었을 때에는 시트 표면이 손상되거나 변형되고, 또한 미열이 가해진 부분은 용융되지 않은 채 접착시킨 부분이 생기게 되어 접착력이 약화되게 되므로, 결국에는 들뜸 및 박리 등의 하자가 발생하여 누수가 발생하고 또, 접합부에서의 열융착 작업을 위하여 토치램프, 가스통, 가스관 등의 부수적인 장비가 필요하므로 화재 또는 화상을 입을 염려가 많아 안전 및 작업능률이 저하되는 문제가 있다. Further, a general When construction waterproof sheets sikineunde bonded to the joint that connects the seat to the thermal fusion method, waterproof sheets, when due to application using a hot air balloon is heat is excessively transmitted to the sheet surface of the sheet is damaged or deformed, and part dummy string is applied is a part adhered without being melted is causing because adhesion is to be weakened, and eventually torch to the heat seal operation of the lifting and peeling, etc. is generated occurs and again, the junction leak defect in, Gaston , it needs additional equipment such as gas pipes, so there is a problem that concerns the fire or chemical burn safety and work efficiency decreases a lot.

또, 방수시트의 하부가 일반적인 아스팔트로 되어 있어서 아스팔트가 고형화되고 나면 딱딱해지기 때문에, 시공이 끝난 방수층에 하중이나 충격이 가해지면 아스팔트 자체가 깨지거나 갈라져서 방수시트에 문제가 생기게 될 뿐만 아니라, 방수시트와 방수시트가 접합되는 접합부에서 방수시트의 두께만큼의 높이 차가 생기기 때문에 시트의 길이를 따라 시트와 시트의 접합부에 공극(즉, 시트의 접합부에서 시트의 단부를 따라 생긴 공극)이 생기게 되고, 그 공극이 물이 흐르는 수로(水路) 역할을 하게 되어, 결국에는 그 수로를 따라 물이 고이고 방수에 문제가 발생한다. In addition, because of the tarpaulin bottom being to stiff Once the asphalt has solidified in the Typical asphalt, when a load or impact is applied to the waterproof construction is completed the asphalt itself, broken or divided in not only the problem causing the waterproof sheets, waterproof due to occur at the joint is a sheet of the waterproofing sheets are bonded car height by the thickness of the waterproof sheet along the length of the sheet gap at the junction of the sheet with the sheet (that is, looking voids along the ends of the sheet at the junction of the seat) is causing, that gap is the number of (水路) role running water, and eventually to a problem with the water resistant goyigo occur along its waterways.

또한, 본 발명의 출원인이 등록받은 특허 제872127호의 방근시트는 상부가 PET 필름으로 되어 있어서 매끈매끈하기 때문에 방근층을 형성할 때, 방근시트가 겹치는 접합부의 상부에 PET 테이프를 부착시켜 시공하는 데도 시간이 지남에 따라 PET 테이프의 접착력이 약화되어 방근시트의 접합부에서 들뜸이나 박리형상이 일어나 나무 뿌리가 접합부 사이로 침투하여 방근층이 훼손되어 방근은 물론 방수에도 하자가 발생하게 되는 문제가 발생한다. Further, Patent No. 872 127 arc room myopia received applicant is registered according to the present invention teuneun also to the top is constructed for forming a room mp because in smooth is a PET film, to adhere the PET tape on top of the banggeun sheet overlap joint the adhesion of the PET tape over time, the weakness at the junction of banggeun sheet lifting or peeling shape up the tree roots are in this room mp damage to penetrate through the junction causes a problem that banggeun, as well as defects occur even waterproof.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은, 콘크리트 바닥면에 방수층을 형성하고 난 이후에 바닥면에 크랙이 생기더라도 방수층이 이를 흡수할 수 있도록 방수시트로 점착력이 강한 연질형 고무화 아스팔트를 점착층으로 시용한 자착식 고무화 아스팔트시트를 제공하기 위한 것이다. The present invention been made in view of the above problems, an object of the present invention, even after the I to form a waterproof layer on the concrete floor surface advent of cracking on the bottom surface adhesiveness with a waterproof sheet to waterproof layer can absorb them Irritant chaksik try out the strong, soft-type rubberized asphalt as an adhesive layer to provide a rubberized asphalt sheet.

삭제 delete

본 발명의 또 다른 목적은, 콘크리트 바닥면에 점착력이 강한 연질형 고무화 아스팔트시트를 자착식으로 접착시키고, 시트와 시트 사이에 점착력이 강한 연질형 고무화 아스팔트와 동일한 재질의 도막재를 충전시켜 계면(界面)이 없는 동일한 재질의 방수층을 형성하고, 그 상부에 내근성과 접착력이 탁월한 자착식 방근시트로 방근층을 형성하는 복합방수·방근구조의 시공방법을 제공하기 위한 것이다. It is another object of the present invention, now the concrete stronger the adhesive strength on the bottom side a soft-type rubberized asphalt sheet was adhered to chaksik, to charge the coating material of the same material as the sheet and the strong, soft type adhesive force between the sheet rubberized asphalt forming a waterproof layer of the same material without the surfactant (界面), and to provide an adhesive force within the spirit and excellent chair chaksik room myopia Trojan room composite waterproof construction, the method of forming the structure banggeun mp thereon.

상기와 같은 기술 과제를 해결하기 위하여 본 발명에 따른 자착식 고무화 아 스팔트시트는, 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP(Dioctyl phthalic acid) 5∼10중량부, NBR(Nitrile Butadiene Rubber) 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드; Chemistry chair chaksik rubber according to the present invention to solve the technical problem described above Arsenal palteu sheet is 30 to 40 parts by weight of asphalt, 10 to 20 parts by weight of styrene butadiene styrene, butyl rubber, 10 to 15 parts by weight of DOP (Dioctyl phthalic acid) 5~10 parts by weight of NBR (Nitrile Butadiene Rubber) 5~10 parts by weight, 5 to 15 parts by weight of calcium carbonate, 5 to 15 parts by weight of a compound mixture a special additive; 상기 콤파운드 상부에 구비되는 부직포; Non-woven fabric provided in the upper part of the compound; 상기 부직포 상부에 구비되는 PE필름; PE film provided on the upper non-woven fabric; 상기 콤파운드의 하부에 부착된 이형지로 구성되는 것을 특징으로 한다. It characterized by consisting of a release liner attached to the lower portion of the compounds.

본 발명에 따른 자착식 방근시트는 PET(Polyethylene Terephthalate)필름, 상기 PET필름 상부에 구비되는 부직포, 상기 PET필름 하부에 구비되는 합성수지접착제, 상기 합성수지접착제 하부에 부착시킨 이형지로 구성되는 것을 특징으로 한다. Here chaksik room myopia according to the invention teuneun characterized by consisting of a non-woven fabric, a synthetic resin adhesive, the synthetic resin adhesive bottom having a release paper attached to which is provided on the PET film, the lower is provided with a PET (Polyethylene Terephthalate) film, the PET film, the upper .

본 발명에 따른 복합방수·방근구조의 시공방법은, 콘크리트 바닥층 상부에 자착식 고무화 아스팔트시트를 부착하여 방수층을 형성하는 단계; Water-resistant, composite construction method of banggeun structure according to the present invention includes the steps of attaching the chaksik rubberized asphalt sheet to form a waterproof layer on the chair concrete bottom layer thereon; 상기 방수층의 상부에 자착식 방근시트를 부착하여 방근층을 형성하는 단계를 거쳐서 시공하는데, 상기 자착식 고무화 아스팔트시트는 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP 5∼10중량부, NBR 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드로 점착층을 형성하고, 상기 콤파운드 상부에는 부직포와 PE필름을 구비하며, 상기 자착식 방근시트는 PET필름과, 상기 PET필름 상부에 부직포를 구비하고, 상기 PET필름 하부에는 합 성수지접착제를 구비한 것을 특징으로 한다. To attach the chaksik banggeun seat chair at an upper portion of the waterproof layer construction through the steps of forming a mp room, the self-chaksik asphalt rubberized asphalt sheet is 30 to 40 parts by weight of styrene butadiene styrene 10 to 20 parts by weight of butyl rubber 10 to 15 parts by weight of DOP 5~10 parts by weight of NBR 5~10 parts by weight, to form a pressure-sensitive adhesive layer to 5 to 15 parts by weight of calcium carbonate, a compound mixing special additives from 5 to 15 parts by weight, the compound has an upper non-woven fabric and provided with a PE film, the self-chaksik room myopia teuneun characterized in that it includes a nonwoven fabric and the PET film, the PET film, and the upper, provided with a synthetic resin adhesive is the lower PET film.

바람직하게는, 본 발명에 따른 복합방수·방근구조의 시공방법으로 형성되는 방수층은, 고무화 아스팔트시트를 일정 간격으로 바닥면에 접착시킨 다음, 시트와 시트 사이 이음부에는 상기 고무화 아스팔트시트의 콤파운드와 동일한 재질의 도막재를 충전시켜 시트끼리를 연결하고, 도막재의 상부에는 부틸고무테이프로 테이핑하여 형성하며, 방근층은, 방근시트를 일정 간격으로 겹쳐서 부착시킨 다음, 방근시트가 겹치는 접합부에는 FRP 또는 고경질 우레탄으로 도포하는 것을 특징으로 한다. Preferably, the present invention compound Water-resistant, in which a waterproof layer formed by the application method of banggeun structure, rubberized asphalt sheet adhered to the bottom surface at a predetermined interval, and then, the sheet and a sheet is the rubber between the joint asphalt sheet according to by charging the coating material of the same material as that of the compound connecting the sheets together, and the upper film material is to form by taping with a butyl rubber tape, room mp is, was rolled attaching banggeun sheet at a constant interval, and then, banggeun sheet overlap joint is characterized in that said FRP or coated with a rigid urethane.

상기와 같은 특징을 갖는 본 발명에 따른 고무화 아스팔트시트는 콘크리트 바닥면에 접착되는 점착층이 점착력이 강한 연질형 고무화 아스팔트이기 때문에 토치램프 등에 의한 열기나 불꽃을 전혀 사용하지 않고 접착하는 자착식이어서 시공이 간편할 뿐만 아니라 점착력이 강한 연질형이기 때문에 기온이 낮은 겨울에도 시공이 가능하고 바닥에 가해지는 충격도 잘 흡수해 주며, 콘크리트 바닥에 크랙이 발생했을 때도 점착력이 강한 연질형의 점착층이 크랙의 폭만큼 늘어나면서 크랙을 흡수해 주기 때문에 콘크리트 바닥면에 크랙이 생기더라도 누수에 문제가 발생하지 않는다. Rubberized asphalt sheet according to the invention having the characteristics as described above jachak expression of bonding without using a heat or flame due torch because the adhesive layer the adhesive strength is strong, soft-type rubberized asphalt is bonded to concrete surface Come gives to construction is in the low temperature in winter construction is possible because not only easy to be a cohesive strong, soft-type well absorption impact on the ground, when cracks in the concrete floor when the adhesive strength adhesive for a strong, soft-type layer because they absorb the growing number cracking as the width of the crack is not a problem with leaks, even the advent of cracks in the concrete floor.

또한, 방수층을 형성할 때, 시트와 시트 사이의 이음부를 처리함에 있어서 점착력이 강한 연질형 아스팔트시트의 점착층을 이루는 콤파운드의 재질과 동일한 재질의 도막재를 충전시킴으로써, 구체적으로 설명하면 반고체상태의 콤파운드를 현장에서 핫멜트기 등과 같은 가열장치를 이용하여 액상으로 녹인 다음 접착시킴으로써 방수시트의 점착층과 방수시트 사이의 이음부에 충전된 도막재가 동일한 재질로 형성되게 되어 재질 간의 계면층(界面層)이 발생하지 않아 바닥 전체가 동일한 재질로 된 하나의 방수층으로 형성되기 때문에 방수에 전혀 문제가 발생하지 않는다. Further, when forming the waterproof layer, the way, described in detail by filling the film material of the same material as the material of the compound forming the adhesive layer of a strong, soft-type asphalt sheet cohesive semi-solid state in processing a joint between the sheet and the sheet to be presented by using a heating device such as a hot melt based on the spot formed by a coating material identical to material is filled in joints between dissolved in the liquid phase, and then bonded by the adhesive layer of the waterproof sheet and the waterproof sheet interface layer between the material compound (界面 層) this does not occur in the entire floor is not a problem at all in water occurs are formed as a waterproof layer of the same material.

방수층의 상부에 형성되는 방근층은, 방근시트의 최상부에 부직포를 배치한 방근시트를 사용했기 때문에 시트와 시트의 접합부를 FRP 또는 고경질 우레탄으로 도포하여 시공하고 나서 장기간이 지나더라도 접합부에서 들뜸이나 박리현상이 발생하지 않는다. Room mp formed on the waterproof layer is, since using the banggeun seat arrangement is a non-woven fabric on the top of the banggeun sheet to the junction of the sheet and the sheet FRP or that after the construction is coated with a hard polyurethane, even if a long period of time is past excitation, or at the junction It does not cause delamination. 이와 같은 구조를 갖는 방근시트 사용으로 일반적인 방근시트의 가장 취약점인 방근시트의 접합부에서의 우수한 내근성과 수밀성을 확보할 수 있다. The sheet used as banggeun having the structure can be secured within the spirit and excellent water tightness at the most vulnerabilities in general banggeun sheet banggeun sheet joints.

본 발명에 따른 자착식 고무화 아스팔트시트(10)는 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌(Stylene Butadiene Stylene) 10∼20중량부, 부틸고무 10∼15중량부, DOP(Dioctyl phthalic acid) 5∼10중량부, NBR(Nitrile Butadiene Rubber) 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합 및 가열한 콤파운드로 점착층(11)을 형성하고, 상기 콤파운드 상부에는 부직포(12)를, 상기 부직포(12)의 상부에 PE필름(13)을 구비하며, 상기 콤파운드의 하부에는 사용시 떼어내는 이형지(14)를 부착시킨 것을 구성적 특징으로 하며, 상기 콤파운드에 혼합되는 특수첨가제로는 점착력 및 접착력 강화와 흘러내림 방지를 위한 검로진을 사용하는 것이 바람직하다. Now according to the invention chaksik rubberized asphalt sheet (10) is 30 to 40 parts by weight of asphalt, styrene butadiene styrene (Stylene Butadiene Stylene) 10~20 parts by weight of butyl rubber 10 to 15 parts by weight of DOP (Dioctyl phthalic acid) 5 to 10 parts by weight of NBR (Nitrile Butadiene Rubber), 5~10 parts by weight, to form a calcium carbonate from 5 to 15 parts by weight, the adhesive layer 11 to the special additives from 5 to 15 parts by weight of a compound mixture and heating, above the compound in the nonwoven fabric 12, and that is adhered to PE film, a release paper (14) (13) that includes, and removed when using the lower portion of the compound has a at an upper side of the nonwoven fabric 12 with the constructive features, mixed with the compound with special additives, it is preferable to use a binary geomro for preventing falling flow and enhance the adhesive strength and adhesion.

여기서 '자착식'이란 시트의 접착방법이 토치램프나 버너 등을 이용한 열기나 불꽃으로 가열하거나 접착용 용제를 사용하지 않고, 방수시트의 이형지를 떼어내고 점착층이 갖고 있는 접착성을 이용하여 콘크리트 바닥면에 시트를 부착시키는 방식을 말한다. The 'character chaksik' bonding method is the sheet is not heated by heat or flame with such torch or burner or by using the adhesive solvent, to detach the release sheet of the waterproof sheet using an adhesive having an adhesive layer of concrete It refers to a method for attaching the sheet to the bottom surface.

본 발명의 고무화 아스팔트시트에 사용된 점착력이 강한 연질형 콤파운드는, 본 발명의 출원인이 개발해서 방근시트에 적용하여 특허 제872127호로 등록받은 점착력이 강한 연질형 고무화 아스팔트를 방수시트에 맞게 더욱 개량한 것인데, 상기 특허 등록받은 점착력이 강한 연질형 고무화 아스팔트는 기후 변화와 충격 흡수 및 콘크리트 바탕면에서 발생하는 크랙에 대응함에 있어 미비한 점이 있어서, 본 발명에서는 기후 변화에 잘 견디며 충격이 가해지더라도 잘 흡수해 주고, 콘크리트 바닥면에 크랙이 발생하더라도 크랙을 흡수해 줄 수 있어서 방수시트에 적합하도록 더욱 개량한 것이다. Soft-type compound the adhesive force using a rubberized asphalt sheet of the present invention strong will, according to the present invention the applicant has developed, by applying the banggeun sheet even for a soft-type rubberized asphalt strong cohesive received registration arcs Patent No. 872 127 in the waterproof sheet geotinde an improvement, in point insufficient the patent registration has a strong, soft-type rubberized asphalt adhesive strength received is in corresponding to the crack generated in the surface of climate change and shock-absorbers, concrete basis, the present invention can withstand well the climate change impact even if the applied give it absorbs well, but a further improvement, even if cracks occur in the concrete floor surface to be in line to absorb the cracks suitable for waterproofing sheet.

본 발명의 점착력이 강한 연질형 고무화 아스팔트시트에 사용한 콤파운드는 부틸고무를 합성한 것인데, 부틸고무는 내후성이 탁월하여 -30℃의 저온에서도 물리적 성질을 그대로 유지할 수 있어서 겨울철과 같은 저온의 환경에서도 작업이 가능하게 된다. Compound is used in a strong, soft rubberized asphalt sheet-shaped adhesion of the present invention geotinde synthesize butyl rubber, a butyl rubber is superior in weather resistance even at low temperatures of -30 ℃ according to keep the physical properties as in the low-temperature environment such as winter this action is possible. 특히 부틸고무는 본 발명의 콤파운드에 사용된 다른 재료와 혼합되어 내산화성, 내오존성, 낮은 수분투과성, 저온 유연성의 물리적 성질을 나타내므로 동절기 시공이 가능하고, 콘크리트 표면에 시트를 접착시킬 때에도 접착제나 열기구를 전혀 사용하지 않고 자착식 시트의 접착력만으로 시공이 가능하다. In particular, the adhesive when butyl rubber is to and exhibits the physical properties of the blend with another material oxidation resistance, ozone resistance, low moisture permeability, low temperature flexibility using the compounds of the present invention in winter construction is possible, adhering the sheets to the concrete surface, or Now without using a hot-air balloon construction it is possible only chaksik adhesion of the sheet.

이와 같이 자착식 고무화 아스팔트시트를 콘크리트 바닥면에 직접 부착시킴으로써 바닥면과의 접합 안정성이 증대되며, KS F4934에서 규정하고 있는 신장률 이상의 탁월한 신장률을 가지고 있기 때문에 콘크리트 바닥면에 크랙이 발생하더라도 방수시트인 자착식 고무화 아스팔트시트의 점착력이 강한 연질형 콤파운드가 크랙의 폭만큼 신장되면서 크랙을 흡수해주므로 방수시트가 파단되지 않는다. In this way characters by directly attaching the chaksik rubberized asphalt sheet on the concrete floor surface and increase the bonding stability of the floor surface, even if the crack in the concrete floor surface occurs due to its excellent elongation than the elongation as required by the KS F4934 waterproof sheet as the chair is chaksik rubberized adhesive force strong, soft-type compound of the asphalt sheet height as the width of the crack because it does not absorb the crack resistant sheet is broken.

본 발명의 방수시트인 자착식 고무화 아스팔트시트는 상기와 같이 특성이 개선된 점착력이 강한 연질형 콤파운드를 점착층(11)으로 사용함으로써, 방수층을 형성하고 난 후에 콘크리트 바닥면에 크랙이 발생하더라도 바닥면에 접착된 점착력이 강한 연질형의 점착층(11)이 바닥면에 생긴 크랙을 흡수해 줄 수 있을 뿐만 아니라 점착층(11)이 점착력이 강한 연질형이기 때문에 여름철은 물론 겨울철에도 방수층 형성 작업이 가능하고, 방수층을 형성하고 난 후에 방수층 상부에 하중이나 충격이 가해지더라도 이를 흡수할 수 있어서 아스팔트시트가 깨지거나 갈라지지 않아서 방수층에 문제가 없게 된다. Waterproof sheets of characters chaksik rubberized asphalt sheet of the present invention even by using a soft-type compound the adhesion of characteristics are improved as the strong as the adhesive layer 11, after forming the waterproof layer, cracks occurring in the concrete floor since only the adhesive layer 11 of the strong, soft type adhesive strength attached to the bottom surface is to be able to absorb the crack occurs in the bottom surface as the adhesive layer 11, the adhesive strength is strong, soft type in summer as well as in winter waterproof layer formed operation is possible, after forming the waterproof layer is a load or shock, even if applied to the upper waterproof layer to be able to absorb this, because the support sheet is broken or cracked asphalt is no problem with the waterproof layer.

본 발명에 따른 자착식 방근시트는, PET(Polyethylene Terephthalate)필름(21)과, 상기 PET필름(21) 상부에 구비되는 부직포(24)와, 상기 PET필름(21) 하부에 구비되는 점착성이 강한 합성수지접착제(22)와, 상기 합성수지접착제(22)의 하부에는 사용시 떼어내는 이형지(25)를 부착시켜 구성되며, 상기 PET필름(21)과 합성수지접착제(22) 사이에는 보강코팅층(24)을 더 형성할 수도 있다. Now according to the invention chaksik room myopia teuneun, PET (Polyethylene Terephthalate) film 21, and the nonwoven fabric 24 is provided on the PET film 21, an upper, a strong adhesive is provided on the lower the PET film 21 between the resin adhesive 22, and is configured by adhering a release paper (25) lower part detaching using the resin adhesive 22, the PET film 21 and the resin adhesive 22 is further reinforced coating layer 24 It may be formed.

PET필름(21)은 텔레프탈산에 에틸렌글리콜을 축합반응시켜 만든 것으로, 인장강도와 압축강도 및 굽힘강도 등 기계적 강도가 강하며 식물 뿌리에 대한 내근성과 내구성, 내약품성 및 내부패성이 우수하다. PET film 21 has to be made by the condensation reaction of ethylene glycol in the tele acid, the mechanical strength such as tensile strength and compression strength and flexural strength steel and is excellent in spirit and durability, chemical resistance and resistance to spoilage of the plant roots. 또한 PET필름(21)의 상부에는 라미네이트된 부직포(22)를 부착하여 후술하는 방근층 형성시 방근시트(20)의 조인트 처리 즉 시트 연결의 씰링 처리가 용이하도록 하고, 하부에는 점착성이 강한 합성수지접착제(22)를 도포하여 방수층과의 접착성을 좋게 하였다. In addition, and to facilitate the PET film 21, the upper part sealing process of attaching a laminated non-woven fabric 22, a joint processing of the room mp formed during banggeun sheet 20 to be described later that is sheet connection, the lower portion of a strong adhesive synthetic resin adhesive applying (22) to improve the adhesion to the waterproof layer.

본 발명의 출원인이 등록받은 특허 제872127호의 방근시트는 상부가 PET 필름으로 되어 있어서 매끈매끈하기 때문에 방근층을 형성할 때 방근시트가 겹치는 접합부의 상부에 PET 테이프를 부착시켜 시공하더라도, 시간이 지남에 따라 PET 테이프의 접착력이 약화되어 방근시트의 접합부에서 들뜸이나 박리가 일어나 나무 뿌리가 접합부 사이로 침투하여 방근층이 훼손되는 문제가 있었다. Patent No. 872 127 arc room myopia received applicant is registered according to the present invention teuneun even if the upper is constructed by attaching a PET tape on top of the banggeun sheet overlap joint to form a room mp because smooth in the PET film, over time, depending on the adhesion of the PET tape was weakened by problems of infiltration in the joint banggeun sheet lifting up or separation between the junction tree roots that room mp damage. 그러나 본 발명에 따른 방근시트는 최상부에 PET 필름이 아닌 부직포를 배치함으로써 최상부가 매끈 매끈하지 않기 때문에, 접합부를 처리함에 있어 FRP 또는 고경질 우레탄을 도포하여 도포층을 형성하고 시간이 지나더라도 접합부에서 접착력이 약화되지 않기 때문에 들뜸이나 박리현상이 나타나지 않는다. However, at the joint room myopia teuneun even when forming a coating layer FRP or high coating a rigid polyurethane it as it does not uppermost is smooth by arranging the non-woven non-PET film to the top, handles the junction and over time in accordance with the present invention this does not appear lifting or peeling phenomenon because the adhesion is not impaired.

방근시트(20)의 PET필름(21)과 합성수지접착제(22) 사이에 보강코팅층(24)을 형성하는 경우에는, 보강코팅층의 재료로는 열가소성 수지에 열안정제, 산화방지제, 착색제, 대전 방지제 중 하나 이상을 혼합하여 코팅 처리해 줌으로써 방근시트의 열적 안정이나 산화방지 등과 같은 여러 가지 기능이 보강된다. Banggeun sheet 20 from the PET film 21 and the resin adhesive 22 in the case of forming the reinforced coating layer 24 in between, the material of the reinforced coating layer is a heat stabilizer in the thermoplastic resin, an antioxidant, a colorant, an antistatic agent mixing one or more by a number of features such as the coating process by giving thermal stability or oxidation prevention of banggeun sheet is reinforced.

이하에서는 도 3을 참조하여 본 발명에 따른 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법에 대하여 설명한다. Hereinafter reference to Figure 3 will be described with respect to the construction method of a composite water-banggeun structured chair chaksik rubber according to the invention with asphalt sheet and banggeun sheet. 본 발명에 따른 복합방수·방근구조의 시공방법은 위에서 설명했던 자착식 고무화 아스팔트시트와 방근시트의 구성을 갖는 시트를 사용하여, 콘크리트 바닥층 상부에 자착식 고무화 아스팔트시트(10)를 부착하여 방수층을 형성하는 단계와, 상기 방수층의 상부에 자착식 방근시트(20)를 부착하여 방근층을 형성하는 단계를 거쳐서 시공된다. Construction method of a composite water-banggeun structure according to the invention flower rubber character chaksik described in above by using the sheet having the configuration of the asphalt sheet and banggeun sheet, characters on a concrete bottom layer upper by attaching chaksik rubberized asphalt sheet 10 forming a waterproof layer, chair at an upper portion of the waterproof layer by attaching a chaksik banggeun sheet 20 is constructed through the forming chamber mp.

방수층을 형성하기 위해서는 먼저, 자착식 고무화 아스팔트시트(10)를 일정 간격으로 바닥면에 접착시킨 다음, 시트와 시트 사이 이음부에는 상기 고무화 아스팔트시트(10)의 콤파운드와 동일한 재질의 고무화 아스팔트로 된 도막재(30)를 충전시켜 시트끼리를 연결하고, 그 상부에는 부틸고무테이프(40)로 테이핑하여 방수 층을 형성한다. In order to form a waterproof layer, first, characters chaksik rubberized asphalt sheet 10, the rubber of the same material as the compound of which adhered to the bottom surface at a predetermined interval, and then screen the rubber, the part between the seat and the seat joint asphalt sheet 10. Chemistry by charging the coating material 30 to the asphalt connection between the sheet and its upper part forms a waterproof layer by taping with a butyl rubber tape 40.

도막재(30)는 고무화 아스팔트시트(10)의 점착층을 이루는 콤파운드와 동일한 재질의 것을 사용하는 것이 바람직하며, 이와 같은 도막재는 반고체화 된 상태로 제품화 되어 있기 때문에 시공을 할 때는 작업 현장에서 핫멜트기 등과 같은 가열수단에 넣고 150∼200℃ 정도로 가열하여 액상으로 만든 다음, 고무화 아스팔트시트(10)의 시트와 시트 사이에 충전시키고 나면 고무화 아스팔트시트와 일체화되면서 곧바로 다시 굳게 된다. Coating material 30 is preferably to use the same material as that forming the adhesive layer of rubberized asphalt sheet (10) compound, when the construction because it is commercialized in a semi-cured state material such a coated film on the shop floor into a heating means such as hot melt as heat exchanger and then made after the liquid phase, it was charged between the sheet and the sheet rubberized asphalt sheet 10 integrated with the rubberized asphalt sheet so 150~200 ℃ is firmly straight back. 기존에 사용하던 도막재는 모두 수용성이기 때문에 도막재를 시트 사이에 충전시키고 난 다음에도 몇 시간이 지난 후에 도막재가 굳었기 때문에 작업에 많은 지장을 주었었고, 또한 도막재의 재질과 방수시트에 구비된 점착층의 재질이 서로 달랐기 때문에 도막재가 굳고 난 다음에는 재질의 상이함에 따른 재질 간의 계면층(界面層)이 발생하여 시간이 지남에 따라 계면층이 누수의 원인이 되었으나, 본 발명에서는 도막재와 점착층(11)에 동일한 재질을 사용함으로써 방수층 전체를 동일한 재질로 된 하나의 방수층으로 형성함으로써 이러한 문제를 완전히 해결한 것이다. Was because then was charged coating material between the sheet I since all coating material previously used water soluble Fig group few hours before the coating film material is hardened gave much interfere with the work, and the adhesive provided on the film material the material and waterproof sheet coating material is firm and I followed, but the cause of the surface layer is a leak over time, to generate the interface layer (界面 層) between the material resulting from the differences in the material, in the present invention, coating material and adhesive because of the material of the layer dalratgi each other by using the same material as the layer 11 it is fully resolved this problem by forming the entire one waterproof layer as a waterproof layer of the same material.

부틸고무 테이프(40)는 이소부틸렌과 소량의 이소프렌을 낮은 온도에서 액체상태로 이온중합한 부틸고무(42)의 상부에 PE필름(41)을 부착시키고, 하부에는 사용할 때 떼어내는 이형지(43)를 부착한 것인데, 이와 같은 부틸고무 테이프(40)를 방수시트인 고무화 아스팔트시트(10) 사이의 도막재(30)가 충전된 이음부분 상부에 부착시키게 되면, 점착력이 강한 연질형 고무화 아스팔트시트와 시트 사이에 충전된 도막재가 계면(界面)이 없는 동일한 재질의 방수층을 형성하기도 하지만, 방수시트의 상부는 접합부에 상관없이 모두 같은 재질의 PE필름층을 갖게 되어 하자의 원인이 훨씬 줄어든다. Butyl rubber tape 40 is isobutylene and the upper part of a small amount of isoprene at a temperature lower by ion polymerization butyl liquid rubber 42 and attaching the PE film 41, a release liner lower portion detaching when used (43 ) the geotinde attached, on the other when the same butyl rubber tape 40 waterproof sheets of rubberized asphalt sheet 10, the coating film material 30 is thereby attached to the top-filled joints between, the adhesion is strong, soft-type rubberized cause also forms a waterproof layer of the same material without the coating material surface (界面) filled between asphalt sheets and sheet let but the upper portion of the waterproof sheet is has a PE film layer of the same material, regardless to the junction is much less .

방근시트(20)는 일정 간격으로 겹쳐서 시공하는데, 방근시트(20)가 겹치는 접합부에는 FRP(Fiber Reinforced Plastics) 또는 고경질 우레탄을 도포하여 도포층(50)을 형성함으로써 물성과 수축 및 변형 등이 적고 크랙을 방지할 수 있어서 수밀성과 경도를 향상시킬 수 있다. By banggeun sheet 20 is in rolled-up construction at regular intervals, joints are banggeun sheet 20 overlaps, the formation of the coating layer 50 by coating a (Fiber Reinforced Plastics) FRP or a high hard urethane such as physical properties and the shrinkage and deformation in less it can prevent cracks can improve the water tightness and hardness. 또한 접합부를 더욱 보강하기 위하여 방근시트(20)가 겹치는 접합부에 FRP 또는 고경질 우레탄을 도포한 다음, 유리강화섬유를 적층시킨 후 그 위에 다시 FRP 또는 고경질 우레탄을 도포을 도포하여 도포층(50)을 형성할 수도 있다. In addition, in order to further reinforce the joint banggeun sheet 20, the FRP or that the application of the rigid urethane and then, after laminating the glass reinforcing fibers again FRP or a high coating layer 50 by coating dopoeul the rigid urethane thereon in overlapping joints a may form.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로, 본 발명이 속하는 기술 분야에서 통상의 지식을 갖는 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. The above description is only to be mentioned that the technical idea of ​​the present invention by way of example, if the character of ordinary skill in the art that various modifications, additions and substitutions will be possible without departing from the essential characteristics of the present invention. 따라서 본 발명에 게시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이런 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. Therefore, the embodiment posted to the invention is for illustrative and not intended to limit the technical idea of ​​the present invention, but the scope of the technical idea of ​​the present invention by this embodiment is not limited. 본 발명의 보호범위는 아래의 청구범위에 의하여 해석되어야하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되 는 것으로 해석되어야 할 것이다. The scope of protection of the invention is to be interpreted by the following claims, all spirits within a scope equivalent will be construed as being included in the scope of the present invention.

도 1은 본 발명에 따른 자착식 고무화 아스팔트시트의 단면도이다. 1 is a cross-sectional view of the chair chaksik rubberized asphalt sheet according to the present invention.

도 2는 본 발명에 따른 방근시트의 단면도이다. 2 is a cross-sectional view of banggeun sheet according to the present invention.

도 3은 본 발명에 따른 복합방수·방근구조의 시공방법을 설명하기 위한 단면도이다. 3 is a sectional view for explaining a construction method of a composite water-banggeun structure according to the present invention.

** 도면의 주요 부분에 대한 부호의 설명 ** Description of the drawings ** **

10 : 고무화 아스팔트시트 11 : 점착층 10: rubberized asphalt sheet 11: pressure-sensitive adhesive layer

12 : 부직포 13 : PE필름 12: non-woven fabric 13: PE film

14 : 이형지 14: release liner

20 : 방근시트 21 : PET필름 20: banggeun sheet 21: PET film

22 : 합성수지접착제 23 : 보강코팅층 22: synthetic resin adhesive 23: reinforcing coating layer

24 : 부직포 25 : 이형지 24: Non-woven 25: release liner

30 : 도막재 30: coating material

40 :부틸고무 테이프 41 : PE필름 40: butyl rubber tape 41: PE film

42 : 부틸고무 43 : 이형지 42: butyl rubber, 43: release paper

50 : 도포층 50: coating layer

Claims (9)

  1. 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP(Dioctyl phthalic acid) 5∼10중량부, NBR(Nitrile Butadiene Rubber) 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드; Asphalt 30 to 40 parts by weight of styrene butadiene styrene 10 to 20 parts by weight of butyl rubber 10 to 15 parts by weight of DOP (Dioctyl phthalic acid) 5~10 parts by weight of NBR (Nitrile Butadiene Rubber) 5~10 parts by weight of calcium carbonate 5 to 15 parts by weight of a compound mixture 5 to 15 parts by weight of special additive;
    상기 콤파운드 상부에 구비되는 부직포; Non-woven fabric provided in the upper part of the compound;
    상기 부직포 상부에 구비되는 PE필름; PE film provided on the upper non-woven fabric;
    상기 콤파운드의 하부에 부착된 이형지; A release paper attached to the lower portion of the compound;
    로 구성되는 것을 특징으로 하는 자착식 고무화 아스팔트시트. Here, characterized in that consisting of chaksik rubberized asphalt sheet.
  2. 제1항에 있어서, According to claim 1,
    상기 특수첨가제는, 점착력 및 접착력 강화와 흘러내림 방지를 위한 검로진인 것을 특징으로 하는 자착식 고무화 아스팔트시트. The special additives are, characters, it characterized in that the adhesive force and adhesive strength for geomro jinin enhanced and bleeding prevention chaksik rubberized asphalt sheet.
  3. 삭제 delete
  4. 콘크리트 바닥층 상부에 자착식 고무화 아스팔트시트를 부착하여 방수층을 형성하는 단계; A step of attaching the chaksik rubberized asphalt sheet to form a waterproof layer on the chair concrete bottom layer thereon;
    상기 방수층의 상부에 자착식 방근시트를 부착하여 방근층을 형성하는 단계; Chaksik step of attaching the sheet to form a room banggeun mp chair at an upper portion of the waterproof layer;
    를 거쳐서 시공하고, 상기 자착식 고무화 아스팔트시트는 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP 5∼10중량부, NBR 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드로 점착층을 형성하고, 상기 콤파운드 상부에는 부직포와 PE필름을 구비하며, 상기 자착식 방근시트는 PET필름과, 상기 PET필름 상부에 부직포를 구비하고, 상기 PET필름 하부에는 합성수지접착제를 구비한 것을 특징으로 하는 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법. Through the construction, and the self-chaksik asphalt rubberized asphalt sheet is 30 to 40 parts by weight of styrene butadiene styrene 10 to 20 parts by weight, 10 to 15 parts by weight of butyl rubber, 5~10 parts by weight of DOP, 5~10 parts by weight of NBR , further comprising 5 to 15 parts by weight of calcium carbonate, 5 to 15 parts by weight of special additive to form an adhesive layer with a mixture of compounds, wherein the compound has an upper non-woven and PE film, the self-chaksik room myopia teuneun PET film and the PET comprising a non-woven fabric on the upper film and the PET film has a lower construction method of a composite structure using a water-banggeun chair chaksik rubberized asphalt sheet and banggeun sheet comprising the synthetic resin adhesive.
  5. 제4항에 있어서, 5. The method of claim 4,
    상기 고무화 아스팔트시트를 일정 간격으로 바닥면에 접착시킨 다음, 시트와 시트 사이 이음부에는 상기 고무화 아스팔트시트의 콤파운드와 동일한 재질의 도막재를 충전시켜 시트끼리 연결하고, 그 상부에는 부틸고무테이프로 테이핑하여 방수 층을 형성하는 것을 특징으로 하는 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법. The inspired Chemistry bond the asphalt sheet on the bottom surface at a predetermined interval, and then part between the seat and the seat joint have to charge the coating material of the same material as the compound of the rubberized asphalt sheet connection between the sheet and the upper portion of the butyl rubber tape construction method of a composite structure using a water-banggeun chair chaksik rubberized asphalt sheet and banggeun sheet, characterized in that by forming a waterproof layer in taping.
  6. 제5항에 있어서, 6. The method of claim 5,
    상기 고무화 아스팔트시트와 시트 사이에 충전되는 도막재는 액상으로 녹여서 충전시키는 것을 특징으로 하는 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법. The rubberized asphalt sheet and the construction method of a composite structure using a water-banggeun chair chaksik rubberized asphalt sheet and banggeun sheet, comprising a step of dissolving liquid charged to the coating material to be filled in between the sheets.
  7. 제4항에 있어서, 5. The method of claim 4,
    상기 방근시트는 일정 간격으로 겹쳐서 시공하는 것을 특징으로 하는 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법. The room myopia teuneun construction method of a composite structure using a water-banggeun chair chaksik rubberized asphalt sheet and banggeun sheet characterized in that the rolled-up construction at a predetermined interval.
  8. 제7항에 있어서, The method of claim 7,
    상기 방근시트가 겹치는 접합부의 상부에는 FRP(Fiber Reinforced Plastics) 또는 고경질 우레탄을 도포하여 도포층을 형성하는 것을 특징으로 하는 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법. The banggeun how the sheet is constructed of a composite water-banggeun structure using a character chaksik rubberized asphalt sheet and banggeun sheet as to form a coating layer to the upper part of the overlapping joint, the application of FRP (Fiber Reinforced Plastics) or a high rigid urethane .
  9. 제8항에 있어서, The method of claim 8,
    상기 도포층의 상부에 유리강화섬유를 적층시킨 후, 그 위에 다시 FRP 또는 고경질 우레탄을 도포하는 것을 특징으로 하는 자착식 고무화 아스팔트시트와 방근시트를 이용한 복합방수·방근구조의 시공방법. After laminating the glass reinforcing fibers on top of the coated layer, the above re-FRP or a high way construction of the composite structure using a water-banggeun chair chaksik rubberized asphalt sheet and banggeun sheet, characterized in that for applying the rigid urethane.
KR1020090033519A 2009-04-17 2009-04-17 Rubberized asphalt sheet, root isolation sheet, and constructing method of complex waterproof and root isolation layer structure KR100924114B1 (en)