KR101015120B1 - Complex waterproof structure and constructing method of complex waterproof using membrane waterproof stuff and self-adhesive rubberized asphalt sheet - Google Patents

Complex waterproof structure and constructing method of complex waterproof using membrane waterproof stuff and self-adhesive rubberized asphalt sheet Download PDF

Info

Publication number
KR101015120B1
KR101015120B1 KR1020100074529A KR20100074529A KR101015120B1 KR 101015120 B1 KR101015120 B1 KR 101015120B1 KR 1020100074529 A KR1020100074529 A KR 1020100074529A KR 20100074529 A KR20100074529 A KR 20100074529A KR 101015120 B1 KR101015120 B1 KR 101015120B1
Authority
KR
South Korea
Prior art keywords
self
weight
coating material
waterproof
sheet
Prior art date
Application number
KR1020100074529A
Other languages
Korean (ko)
Inventor
강충모
손문세
Original Assignee
강충모
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강충모 filed Critical 강충모
Priority to KR1020100074529A priority Critical patent/KR101015120B1/en
Application granted granted Critical
Publication of KR101015120B1 publication Critical patent/KR101015120B1/en

Abstract

PURPOSE: An asphalt sheet using membrane waterproof stuff and self-adhesive rubberized asphalt sheets and a complex waterproof construction method thereof are provided to improve waterproof performance and the service life of a waterproof layer. CONSTITUTION: An asphalt sheet using membrane waterproof stuff and self-adhesive rubberized asphalt sheets comprises a concrete base(10), a primer(21), a waterproof coating material(22) for base adjustment, and a self-adhesive rubberized asphalt sheet(23). The primer is applied on the top of the concrete base. The waterproof coating material for base adjustment is applied on the top of the primer in order to make concrete base flat. The self-adhesive rubberized asphalt sheet is attached on the top of the waterproof coating material for the base adjustment.

Description

바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조 및 이를 시공하는 복합방수공법{Complex waterproof structure and constructing method of complex waterproof using membrane waterproof stuff and self-adhesive rubberized asphalt sheet}Complex waterproof structure and constructing method of complex waterproof using membrane waterproof stuff and self-adhesive rubberized asphalt sheet}

본 발명은 방수구조 및 복합방수공법에 관한 것으로, 더욱 상세하게는, 콘크리트 바탕면에 프라이머 처리를 한 후, 그 상부에 평탄한 바탕면을 형성하기 위한 바탕조정용 방수도막재를 도포한 다음, 그 상부에 자착식 고무화 아스팔트시트를 접착시켜 시트가 바탕조정용 방수도막재와 일체화되어 접착함으로써 방수성능이 현저하게 향상된 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조 및 이를 시공하는 복합방수공법에 관한 것이다.
The present invention relates to a waterproof structure and a composite waterproofing method, and more particularly, after the primer treatment on the concrete base surface, and then applying a base coating waterproof coating material to form a flat base surface on the top, and then the top Self-adhesive rubberized asphalt sheet is adhered to and the sheet is integrally bonded with the waterproofing coating material for background adjustment, and the waterproof structure using ground-adjusting waterproofing coating material and self-adhesive rubberized asphalt sheet with improved waterproofing performance and composite waterproofing It is about public law.

콘크리트 구조물의 방수공사에서 가장 먼저 고려해야 할 사안은 구조물의 어느 부위에 시공할 것인지와 거기에 맞는 적절한 방수재료 및 방수공법의 적용이라고 할 수 있다. 일반적으로 방수시트를 사용하여 콘크리트 바탕면에 방수층을 형성하는 시공방법은 크게 밀착공법과 절연공법으로 나누어지는데, 밀착공법은 방수시트를 콘크리트 바탕면에 밀착시키는 시공법으로, 만일 시공후 콘크리트 바탕면에 크랙이 발생하면 접착층의 두께가 얇기 때문에 바탕면에 접착된 방수시트가 크랙을 흡수해 줄 수가 없어서 방수시트가 바탕면의 크랙과 함께 파단되어 방수층으로서의 기능을 상실하게 된다는 심각한 문제가 있고, 절연공법은 방수시트와 콘크리트 바탕면 사이가 접착되지 않고 떠 있기 때문에 바탕면에 크랙이 발생하더라도 방수시트에는 문제가 없지만 바탕면에 누수가 생기면 누수 개소를 찾기 위하여 방수시트 전체를 뜯어내고 찾아야 한다는 문제가 있다.
The first issue to be considered in the waterproofing of concrete structures is the application of appropriate waterproofing materials and waterproofing methods to which part of the structure to be installed. In general, a method of forming a waterproof layer on a concrete base surface using a waterproof sheet is largely divided into a close contact method and an insulation method. A close contact method is a method of closely contacting a waterproof sheet to a concrete base surface. When cracks occur, the thickness of the adhesive layer is so thin that the waterproof sheet adhered to the base cannot absorb the cracks, and the waterproof sheet breaks along with the crack on the base and loses its function as a waterproof layer. Since there is no problem between the waterproof sheet and the concrete base surface, it is not a problem with the waterproof sheet even if there is a crack on the base surface, but if there is a leak on the base surface, the entire waterproof sheet must be removed and searched for a leak location. .

또, 방수시트의 하부가 일반적인 아스팔트로 되어 있어서 방수시트를 시공할 때는 시트끼리의 접합부를 열기구를 이용하여 열융착 방식으로 접착시켜 시공하기 때문에 시트에 열이 과도하게 전달되었을 때에는 시트 표면이 손상되거나 변형되고, 또한 미열이 가해진 부분은 용융되지 않은 채 접착되기 때문에 접착력이 약화되어 결국에는 들뜸 및 박리 등의 하자가 발생하여 누수가 발생하게 되고, 다른 한편으로는 접합부의 열융착 작업을 위하여 토치램프, 가스통, 가스관 등의 부수적인 장비가 필요하므로 불편할 뿐더러 화재의 위험성과 작업자가 화상을 입을 염려가 많아 안전 및 작업능률이 저하되는 문제가 있다.
In addition, since the lower part of the waterproof sheet is made of general asphalt, when the waterproof sheet is constructed, the joints of the sheets are bonded by heat fusion using a hot air balloon, so when the heat is excessively transferred to the sheet, the surface of the sheet may be damaged or Since the deformed and unheated parts are bonded without melting, the adhesive strength is weakened, and eventually, defects such as lifting and peeling occur, which causes water leakage, and on the other hand, the torch lamp for thermal fusion operation of the joint. In addition to the need for additional equipment, such as gas cylinders and gas pipes, there is a problem that the safety and work efficiency are deteriorated due to the inconvenience of fire and the risk of a fire.

한편, 상기와 같은 방수시트에 의한 시트방수공법 외에 도막 방수공법이 사용되고 있는데, 도막 방수공법은 콘크리트 바탕면에 요철이 있는 경우 액상의 방수재가 오목하게 들어간 부분은 두껍게 도포되고 볼록하게 튀어나온 부분은 액상의 방수재가 흘러 내려 얇게 도포되기 때문에 바닥면 전체를 일정한 두께로 방수층을 형성하는 것이 불가능하게 되며, 바탕면 자체가 경사진 곳에서는 액상의 방수재가 윗부분에서 아랫부분으로 흘러 내려 방수층이 윗부분은 얇고 아랫부분은 두껍게 형성된다는 문제가 있다.
On the other hand, in addition to the sheet waterproofing method by the waterproof sheet as described above, the coating film waterproofing method is used, the coating film waterproofing method when the concave-convex on the concrete base surface, the part where the liquid waterproofing material is concave thickly coated and protruding convex portion Because the liquid waterproof material flows down and is applied thinly, it is impossible to form a waterproof layer with a certain thickness on the entire floor surface.In the place where the base surface itself is inclined, the liquid waterproof material flows from the upper part to the lower part and the waterproof layer is thin There is a problem that the lower part is formed thick.

이와 같이 방수시트를 사용한 방수공법은 시트 상호간의 접합부에서의 접합 불량 및 파단에 따른 방수성능의 저하가 가장 큰 문제이고, 도막 방수공법은 전체적으로 균일한 두께의 방수층을 형성하기 어렵다는 문제가 있기 때문에, 시트간 연결부위의 접착성 및 방수재료의 층간 접착성이 우수할 뿐만 아니라 콘크리트 바탕면과의 접착력이 좋고 유연성이 우수하여 모서리 부위 및 요철 부위에서 들뜸이나 박리 현상이 발생하지 않는 복합 방수재 및 복합 방수공법의 개발이 절실히 요구된다고 하겠다.
As such, the waterproofing method using the waterproof sheet is the biggest problem of deterioration of the waterproofing performance due to poor bonding and breakage at the joints between the sheets, and the coating film waterproofing method has a problem that it is difficult to form a waterproof layer of uniform thickness as a whole. Composite waterproofing material and composite waterproofing that does not cause lifting or peeling at corners and uneven areas due to its excellent adhesion to the concrete base surface and excellent flexibility as well as excellent adhesion between the sheets and the interlayer of the waterproofing material. The development of public methods is urgently needed.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 목적은, 콘크리트 바탕면에 프라이머 처리를 한 후에, 평탄한 바탕면을 형성하기 위한 바탕조정용 방수도막재를 도포한 다음, 그 상부에 자착식 고무화 아스팔트시트를 접착시켜, 시트가 바탕조정용 방수도막재와 일체화되어 접착함으로써 방수성능이 현저하게 향상된 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조 및 이를 시공하는 복합방수공법을 제공하기 위한 것이다.
The present invention has been made to solve the above problems, an object of the present invention, after the primer treatment on the concrete base surface, after applying the base coating waterproof coating material for forming a flat base surface, and then the top Self-adhesive rubberized asphalt sheet is adhered to the sheet, and the sheet is integrated with the waterproofing coating material for background adjustment. To provide a waterproof method.

상기와 같은 기술 과제를 해결하기 위하여 본 발명에 따른 바탕 조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조는, 콘크리트 바탕면 상부에 도포된 프라이머; 상기 프라이머 상부에 도포되어 콘크리트 바탕면을 평탄하게 만들어 주는 바탕조정용 방수도막재; 상기 바탕조정용 방수도막재 상부에 접착되는 자착식 고무화 아스팔트 시트로 구성되며, 상기 바탕조정용 방수도막재는, 아스팔트 40∼50 중량부, PVA-SBR(styrene-butadien copolymer) 합성고무 20∼35 중량부, 유화제 2∼3 중량부, 소포제 0.1∼1 중량부, 접착강화제 5∼10 중량부, 점도조절제 0.1∼1 중량부, 물 10∼25 중량부로 구성되는 것을 특징으로 한다.
In order to solve the technical problem as described above, the waterproof structure using the waterproofing coating material and the self-adhesive rubberized asphalt sheet according to the present invention, the primer applied to the upper surface of the concrete; A waterproofing coating material for base adjustment applied to the primer to make the concrete base surface flat; It is composed of a self-adhesive rubberized asphalt sheet adhered to the upper surface of the waterproof coating material, the ground adjustment waterproof coating material is 40 to 50 parts by weight of asphalt, 20 to 35 parts by weight of PVA-SBR (styrene-butadien copolymer) synthetic rubber , 2 to 3 parts by weight of an emulsifier, 0.1 to 1 part by weight of an antifoaming agent, 5 to 10 parts by weight of an adhesive strengthening agent, 0.1 to 1 part by weight of a viscosity modifier, and 10 to 25 parts by weight of water.

본 발명에 따른 바탕 조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조를 시공하는 복합방수공법은, 콘크리트 바탕면 상부에 프라이머를 도포하는 단계; 콘크리트 바탕면을 평탄하게 하기 위하여 상기 프라이머 상부에 바탕조정용 방수도막재를 도포하는 단계; 상기 바탕조정용 방수도막재 상부에 자착식 고무화 아스팔트시트를 접착시키는 단계를 거쳐서 시공하며, 상기 바탕조정용 방수도막재는, 아스팔트 40∼50 중량부, PVA-SBR(styrene-butadien copolymer) 합성고무 20∼35 중량부, 유화제 2∼3 중량부, 소포제 0.1∼1 중량부, 접착강화제 5∼10 중량부, 점도조절제 0.1∼1 중량부, 물 10∼25 중량부로 구성되는 것을 특징으로 한다. 또한 상기 자착식 고무화 아스팔트시트와 시트 사이 이음부에는 바탕조정용 방수도막재 또는 자착식 고무화 아스팔트시트의 콤파운드와 동일한 재질의 도막재로 보강함으로써 시트끼리 연결한다.
The composite waterproof method for constructing a waterproof structure using a waterproofing coating material and a self-adhesive rubberized asphalt sheet for ground adjustment according to the present invention comprises the steps of: applying a primer on the concrete base surface; Applying a waterproofing coating material for surface adjustment on the primer to flatten the concrete base surface; The construction is performed through the step of adhering the self-adhesive rubberized asphalt sheet to the upper surface of the waterproofing coating material for adjustment, the waterproofing coating material for the ground adjustment, 40 to 50 parts by weight of asphalt, 20 to 30 parts of PVA-SBR (styrene-butadien copolymer) It is characterized by consisting of 35 parts by weight, emulsifier 2-3 parts by weight, antifoaming agent 0.1-1 parts by weight, 5-10 parts by weight of the adhesive strengthening agent, 0.1-1 parts by weight of viscosity modifier, 10-25 parts by weight of water. In addition, the joint between the self-adhesive rubberized asphalt sheet and the sheet is connected to each other by reinforcing with a coating material of the same material as the compound of the waterproofing coating material or self-adhesive rubberized asphalt sheet.

삭제delete

바람직하게는, 자착식 고무화 아스팔트 시트는, 자착식 고무화 아스팔트와, 그 상부에 부착된 부직포 및 그 하부에는 이형지가 부착되어 구성되며, 자착식 고무화 아스팔트는, 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP(Dioctyl phthalic acid) 5∼10중량부, NBR(Nitrile Butadiene Rubber) 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드로 구성된다.
Preferably, the self-adhesive rubberized asphalt sheet is composed of a self-adhesive rubberized asphalt, a nonwoven fabric attached to the upper portion and a release paper attached to the lower portion thereof, and the self-adhesive rubberized asphalt is 30 to 40 parts by weight of asphalt, 10-20 parts by weight of styrene butadiene styrene, 10-15 parts by weight of butyl rubber, 5-10 parts by weight of DOP (Dioctyl phthalic acid), 5-10 parts by weight of NBR (Nitrile Butadiene Rubber), 5-15 parts by weight of calcium carbonate, special It consists of a compound which mixed 5-15 weight part of additives.

상기와 같은 특징을 갖는 본 발명에 따른 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용하여 시공한 방수구조는, 콘크리트 바탕면을 평탄하게 한 바탕조정용 방수도막재가 1차 방수 기능을 하고, 그 위에 일체로 접착된 자착식 고무화 아스팔트시트가 2차로 방수 기능을 하기 때문에 방수 성능이 현저하게 상승되고, 바탕조정용 방수도막재가 콘크리트 바탕면을 요철이 없는 평탄한 면으로 만들어 주기 때문에 자착식 고무화 아스팔트시트와 바탕면 사이가 들뜨거나 박리되지 않아서 방수 성능뿐만 아니라 방수층의 수명도 오래간다.
The waterproof structure constructed by using the waterproofing coating material and the self-adhesive rubberized asphalt sheet according to the present invention having the characteristics as described above, the waterproofing coating material for flattening the concrete base surface has a primary waterproofing function, Self-adhesive rubberized asphalt sheet bonded together thereon has a second waterproofing function, which significantly increases the waterproofing performance, and the self-adhesive rubberization because the waterproofing coating material for ground adjustment makes the concrete base surface a flat surface without irregularities. As the asphalt sheet and the base surface are not lifted or peeled off, the waterproofing performance and the life of the waterproofing layer are long.

또한, 자착식 고무화 아스팔트시트는 접착력이 강하기 때문에 토치램프 등에 의한 열기나 불꽃을 전혀 사용하지 않고 접착하는 자착식이어서 시공이 간편할 뿐만 아니라 접착력이 강한 연질형이기 때문에 기온이 낮은 겨울에도 시공이 가능하고 콘크리트 바닥에 가해지는 충격도 잘 흡수해 주며, 콘크리트 바탕면에 크랙이 발생했을 때도 바탕조정용 방수도막재와 함께 크랙의 폭만큼 늘어나면서 크랙을 흡수해 주기 때문에 콘크리트 바탕면에 크랙이 생기더라도 누수에 문제가 발생하지 않는다.
In addition, the self-adhesive rubberized asphalt sheet is a self-adhesive type that adheres without using any heat or flame by a torch lamp because it has a strong adhesive force, and is easy to install. It absorbs the impact on the concrete floor and absorbs the crack as the width of the crack increases along with the waterproofing coating material for the ground even when the crack occurs on the concrete floor. Leakage does not occur.

도 1은 종래의 일반적인 방수시트를 사용한 방수공법을 설명하기 위한 도면이다.
도 2는 본 발명에 따른 방수구조를 설명하기 위한 도면이다.
도 3은 본 발명에 사용되는 자착식 고무화 아스팔트시트를 도시한 도면이다.
도 4는 본 발명에 따른 방수구조의 접합부 및 복합방수공법을 설명하기 위한 단면도이다.1 is a view for explaining a waterproof method using a conventional general waterproof sheet.
2 is a view for explaining a waterproof structure according to the present invention.
3 is a view showing a self-adhesive rubberized asphalt sheet used in the present invention.
4 is a cross-sectional view for explaining a joint and a composite waterproof method of the waterproof structure according to the present invention.

본 발명에 따른 방수구조는 콘크리트 바탕면(10)과, 그 상부에 도포되는 프라이머(21)와, 바탕조정용 방수도막재(22) 및 그 상부에 접착되는 자착식 고무화 아스팔트 시트(23)를 기본적인 구성으로 포함한다.
The waterproof structure according to the present invention has a concrete base surface 10, a primer 21 applied to the upper portion, a waterproofing coating material 22 for ground adjustment and the self-adhesive rubberized asphalt sheet 23 adhered to the upper portion Include in basic configuration.

프라이머는 아스팔트와 휘발성이 높은 용제(solvent)를 혼합 제조하여, 콘크리트 바탕면에 도포되어 피막을 형성하고 바탕면의 표면정리 및 방수시트와의 접착력을 강화시키기 위해 사용되는 제품이다. 그런데 도 1에서 보는 바와 같이, 대부분의 콘크리트 바탕면(1)은 거칠고 요철 부위가 많아 프라이머(2)를 도포하더라도 바탕면이 평탄하지 못하고 불균일하기 때문에 방수시트(3)를 접착시켜도 바탕면과 방수시트 사이가 완전히 밀착되지 못하고 떠 있는 부분이 생기게 되어 접착력이 떨어져 방수층의 부풀음, 박리, 국부적인 파단 등의 하자가 발생하게 되어, 결국에는 방수에 하자가 발생하게 된다. 따라서 이와 같은 문제를 근원적으로 없애기 위하여 본 발명에서는 프라이머 상부에 액상의 바탕조정용 방수도막재를 도포한 것이다.
Primer is a product used to mix and manufacture asphalt and a highly volatile solvent, and is applied to the concrete base surface to form a coating, to enhance the surface cleanup and adhesion to the waterproof sheet. By the way, as shown in Figure 1, most of the concrete base surface (1) is rough and there are a lot of irregularities, even if the primer (2) is applied because the base surface is not flat and non-uniform, even if the waterproof sheet (3) bonded to the base surface and waterproof The floating parts are not completely adhered to each other and the floating parts are formed, resulting in poor adhesion, thereby causing defects such as swelling, peeling, and local breakage of the waterproof layer. Therefore, in order to fundamentally eliminate such a problem, in the present invention, the waterproofing coating material for liquid phase adjustment is applied on the primer.

바탕조정용 방수도막재(22)는, 콘크리트 바탕면(10) 상부에 도포된 프라이머(21) 상부에 도포되면 일정한 두께를 갖는 피막이 되어 콘크리트 바탕면을 요철이 없는 평탄한 면으로 만들어 주고, 바탕조정용 방수도막재 자체가 방수 기능을 할 뿐만 아니라 그 상부에 접착되는 자착식 고무화 아스팔트시트(23)와의 접착력을 증대시켜 주기 때문에 시트의 들뜸 현상이나 박리 등이 발생하지 않아 장기간 동안 방수층의 방수 성능을 유지하게 해준다.
When the waterproofing coating material 22 for ground adjustment is applied to the primer 21 applied on the concrete base surface 10, the film becomes a film having a constant thickness, thereby making the concrete ground surface a flat surface without irregularities, and waterproofing the ground adjustment. As the coating material itself not only provides a waterproof function, but also increases the adhesive strength with the self-adhesive rubberized asphalt sheet 23 adhered to the upper part thereof, no lifting or peeling of the sheet occurs, thereby maintaining the waterproof performance of the waterproof layer for a long time. Let's do it.

바탕조정용 방수도막재(22)는, 용제로 물을 사용하고 주원료로는 아스팔트와 PVA(poly vinyl alcohol) 및 SBR(styrene butadien copolymer)을 사용하며, 첨가제로는 유화제, 소포제, 접착강화제 및 점도조절제를 사용한 것인데, 구체적으로는 아스팔트 40∼50 중량부, PVA-SBR 합성고무 20∼35 중량부, 유화제 2∼3 중량부, 소포제 0.1∼1 중량부, 접착강화제 5∼10 중량부, 점도조절제 0.1∼1 중량부, 물 10∼25 중량부로 구성된다.
Waterproofing coating material 22 for the ground adjustment uses water as a solvent and asphalt and PVA (poly vinyl alcohol) and SBR (styrene butadien copolymer) as main ingredients, and as an additive, an emulsifier, an antifoaming agent, an adhesive strengthening agent and a viscosity adjusting agent. Specifically, 40 to 50 parts by weight of asphalt, 20 to 35 parts by weight of PVA-SBR synthetic rubber, 2 to 3 parts by weight of emulsifier, 0.1 to 1 part by weight of antifoaming agent, 5 to 10 parts by weight of adhesive strengthening agent, and viscosity regulator 0.1 It consists of -1 weight part and 10-25 weight part of water.

물에 아스팔트와 유화 중합으로 제조된 SBR 라텍스를 믹싱(mixing)한 상태에서 용융시킨 PVA를 가하게 되면 안정화되어 방수도막재가 안정화된 콜로이드 상태로 존재하게 되며, 장기간 방치하더라도 응집이나 침전되지 않고 완전한 분산상으로 존재하게 된다. 이러한 방수도막재를 시공하게 되면 공기 중에서 용제인 물이 증발하게 되고 아스팔트와 SBR 및 PVA가 하나로 응집되면서 경화되어 하나의 고상으로 존재하게 된다.
When the molten PVA is added to the water while mixing SBR latex made by asphalt and emulsion polymerization, the water is stabilized and the waterproof coating material is in a stabilized colloidal state. It will exist. When the waterproof coating material is constructed, water, which is a solvent, is evaporated in the air, and the asphalt, SBR, and PVA agglomerate and harden to exist as one solid phase.

유화제는 유성인 아스팔트와 수성인 합성고무 라텍스가 잘 섞이게 하는 역할로 에멀젼 상태의 연장과 안정화를 유지시켜 이들의 분리를 방지하는 물질인데, 유화제로는 음이온 유화제인 올레인산카리를 사용하는 것이 바람직하며 pH는 약 11 정도이다. 점도조절제는 점착성과 보수성을 좋게 해주는 역할을 하는데, 수용성 메틸셀룰로우즈를 사용하는 것이 바람직하다. 또한 소포제로는 실리콘 소포제를 사용하는데, 실리콘 소포제는 그 성상에 따라 오일형, 변성유형, 용액형, 분말형, 에멀젼형 등 여러 종류가 있으나, 희석안정성이 양호한 에멀젼형을 사용하는 것이 바람직하다.
The emulsifier is a material that mixes oily asphalt and aqueous synthetic rubber latex to maintain the extension and stabilization of the emulsion state and prevents their separation.Emulsifier is preferably an anionic emulsifier. Is about 11 or so. Viscosity modifiers serve to improve the adhesion and water retention, it is preferable to use a water-soluble methyl cellulose. In addition, a silicone antifoaming agent is used as the antifoaming agent, but silicone antifoaming agent may be of various types such as oil type, modified type, solution type, powder type, and emulsion type, but it is preferable to use an emulsion type having good dilution stability.

자착식 고무화 아스팔트 시트(23)는 바탕조정용 방수도막재(22) 상부에 접착되는데, 자착식 고무화 아스팔트(232)와, 그 상부에 부착된 부직포(233) 및 그 하부에 부착되며 시공시 떼어내는 이형지(231)로 구성된다.
The self-adhesive rubberized asphalt sheet 23 is bonded to the upper surface of the waterproof coating material 22, the self-adhesive rubberized asphalt 232, the non-woven fabric 233 attached to the upper portion and the bottom of the construction It consists of release paper 231 which is peeled off.

자착식 고무화 아스팔트(232)는, 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP(Dioctyl phthalic acid) 5∼10중량부, NBR(Nitrile Butadiene Rubber) 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드로 구성되는데, 특수첨가제는 자착식 고무화 아스팔트에 여러 가지 기능을 부여하기 위하여 첨가하는데, 예를 들면 점착력 및 접착력 강화와 흘러내림 방지를 위한 검로진과 같은 것이다.
The self-adhesive rubberized asphalt 232 includes 30 to 40 parts by weight of asphalt, 10 to 20 parts by weight of styrene butadiene styrene, 10 to 15 parts by weight of butyl rubber, 5 to 10 parts by weight of DOP (Dioctyl phthalic acid), and NBR (Nitrile Butadiene). Rubber) 5-10 parts by weight, 5-15 parts by weight of calcium carbonate, and 5-15 parts by weight of special additives. A special additive is added to give various functions to self-adhesive rubberized asphalt. For example, it is the same as gum rosin for enhancing adhesion and adhesion and preventing falling.

여기서 '자착식'이란 시트의 접착방법이 토치램프나 버너 등을 이용한 열기나 불꽃으로 가열하거나 접착용 용제를 사용하지 않고, 방수시트의 이형지를 떼어내고 점착층이 갖고 있는 접착성을 이용하여 부착면(본 발명에서는 바탕조정용 방수도막재를 지칭함)에 시트를 부착시키는 방식을 말한다.
Here, the 'self-adhesive' means that the sheet is bonded by heat or flame using a torch lamp or burner, or without using an adhesive solvent, peeling off the release paper of the waterproof sheet and attaching it using the adhesive property of the adhesive layer. It refers to a method of attaching the sheet on the surface (in the present invention refers to the waterproofing coating material for the background adjustment).

본 발명의 자착식 고무화 아스팔트시트에 사용된 점착력이 강한 연질형 콤파운드는, 본 발명의 발명자가 개발해서 방근시트에 적용하여 특허 제872127호로 등록받은 점착력이 강한 연질형 고무화 아스팔트를 방수시트에 맞게 더욱 개량한 것인데, 상기 특허 등록받은 점착력이 강한 연질형 고무화 아스팔트는 기후 변화와 충격 흡수 및 콘크리트 바탕면에서 발생하는 크랙에 대응함에 있어 미비한 점이 있어서, 본 발명에서는 기후 변화에 잘 견디며 충격이 가해지더라도 잘 흡수해 주고, 콘크리트 바닥면에 크랙이 발생하더라도 크랙을 흡수해 줄 수 있어서 방수시트에 적합하도록 더욱 개량한 것이다.
The strong adhesive soft compound used in the self-adhesive rubberized asphalt sheet of the present invention is developed by the inventor of the present invention and applied to a weatherproof sheet, and has a strong adhesive soft rubberized asphalt registered in patent 872127 to a waterproof sheet. According to the present invention, the patented high-strength soft rubberized asphalt is inadequate in responding to climate change, shock absorption, and cracks occurring on the concrete base surface. It absorbs well even if it is applied, and even if a crack occurs on the concrete floor, it can absorb the cracks, which is further improved to be suitable for the waterproof sheet.

본 발명의 점착력이 강한 연질형 자착식 고무화 아스팔트시트에 사용한 콤파운드는 부틸고무를 합성한 것인데, 부틸고무는 내후성이 탁월하여 -30℃의 저온에서도 물리적 성질을 그대로 유지할 수 있어서 겨울철과 같은 저온의 환경에서도 작업이 가능하게 된다. 특히 부틸고무는 본 발명의 콤파운드에 사용된 다른 재료와 혼합되어 내산화성, 내오존성, 낮은 수분투과성, 저온 유연성의 물리적 성질을 나타내므로 동절기 시공이 가능하고, 부착면에 시트를 접착시킬 때에도 접착제나 열기구를 전혀 사용하지 않고 자착식 시트의 접착력만으로 시공이 가능하다.
The compound used in the high-adhesive soft self-adhesive rubberized asphalt sheet of the present invention is synthesized with butyl rubber, but butyl rubber has excellent weather resistance and can maintain physical properties even at low temperatures of -30 ° C. Work in the environment is possible. In particular, butyl rubber is mixed with other materials used in the compound of the present invention and exhibits physical properties such as oxidation resistance, ozone resistance, low water permeability, and low temperature flexibility, so that it can be applied in winter. It can be installed only by the adhesive force of the self-adhesive sheet without using any hot air balloon.

이와 같이 자착식 고무화 아스팔트시트를 콘크리트 바탕면에 직접 부착시킴으로써 바탕면과의 접합 안정성이 증대되며, KS F4934에서 규정하고 있는 신장률 이상의 탁월한 신장률을 가지고 있기 때문에 콘크리트 바탕면에 크랙이 발생하더라도 방수시트인 자착식 고무화 아스팔트시트의 접착력이 강한 연질형 콤파운드가 크랙의 폭만큼 신장되면서 크랙을 흡수해주므로 방수시트가 파단되지 않는다.
By directly attaching the self-adhesive rubberized asphalt sheet to the concrete base surface, the bonding stability with the base surface is increased, and since it has an excellent elongation rate higher than that specified in KS F4934, even if a crack occurs in the concrete base surface, the waterproof sheet Since the soft compound with strong adhesion of the self-adhesive rubberized asphalt sheet is stretched by the width of the crack, the crack is absorbed so that the waterproof sheet does not break.

또한, 본 발명의 자착식 고무화 아스팔트 시트(23)는 최상부에 인장강도와 내열성이 우수한 부직포(233)를 부착시켰기 때문에 바탕면의 균열 및 지속적인 인장력에 의해 크리프(creep) 현상이 발생하여 방수층이 파단되는 것을 방지할 수 있으며, 부직포는 표면이 까칠까칠하여 표면적이 크기 때문에 시트 상호간 이음부에 도막재로 보강시킬 때 접착력을 극대화시킬 수 있게 된다.
In addition, since the self-adhesive rubberized asphalt sheet 23 of the present invention adheres a nonwoven fabric 233 having excellent tensile strength and heat resistance at the top thereof, creep phenomenon occurs due to cracking of the base surface and continuous tensile force, resulting in a waterproof layer. The fracture can be prevented, and the nonwoven fabric has a large surface area because the surface is rough, so that the adhesive force can be maximized when reinforced with the coating material on the joints between the sheets.

이하에서는 본 발명에 따른 방수구조를 시공하는 복합방수공법에 대하여 설명한다. 본 발명의 복합방수공법은 콘크리트 바탕면 상부에 프라이머를 도포하는 단계, 콘크리트 바탕면을 평탄하게 하기 위하여 상기 프라이머 상부에 바탕조정용 방수도막재를 도포하는 단계 및 상기 바탕조정용 방수도막재 상부에 자착식 고무화 아스팔트시트를 접착시키는 단계를 기본적으로 거쳐서 시공한다.
Hereinafter, a composite waterproof method for constructing a waterproof structure according to the present invention will be described. The composite waterproof method of the present invention is a step of applying a primer on the concrete base surface, the step of applying a base coating waterproof coating material on the primer to flatten the concrete base surface and the self-adhesive on top of the waterproof coating material for ground adjustment Basically, the step of bonding the rubberized asphalt sheet is performed.

또한, 도 4에 도시된 바와 같이, 자착식 고무화 아스팔트시트(23)를 맞댐하여 바탕조정용 방수도막재(22) 상부에 접착시킨 다음, 시트와 시트 사이 이음부에는 바탕조정용 방수도막재(22) 또는 자착식 고무화 아스팔트시트(23)의 콤파운드와 동일한 재질의 도막재(30)를 덧바름하여 보강함으로써 시트끼리 연결시켜 시공한다.
In addition, as shown in FIG. 4, the self-adhesive rubberized asphalt sheet 23 is bonded to the upper surface of the waterproofing coating material 22 for adjustment of the ground, and then the waterproofing coating material for the adjustment of the ground is formed on the joint between the sheet and the sheet. Or by coating and reinforcing the coating material 30 of the same material as the compound of the self-adhesive rubberized asphalt sheet 23, the construction is connected to each other.

본 발명에서는 시트와 시트 사이에 덧바름하여 보강하는 도막재를 자착식 고무화 아스팔트시트의 콤파운드와 동일한 재질이거나, 또는 바탕조정용 도막방수재와 주재료(아스팔트와 PVA-SBR 합성고무)가 같은 재질을 사용한다.
In the present invention, the coating material for reinforcing and reinforcing between the sheet and the sheet is the same material as the compound of the self-adhesive rubberized asphalt sheet or the same material as the base waterproofing material and the main material (asphalt and PVA-SBR synthetic rubber) are used. do.

도막재를 자착식 고무화 아스팔트시트의 콤파운드와 동일한 재질을 사용할 경우에는, 콤파운드가 반고체화 된 상태로 제품화 되어 있기 때문에 시공할 때는 작업현장에서 가열수단에 넣고 150∼200℃ 정도로 가열하여 액상으로 만든 다음, 자착식 고무화 아스팔트시트 설치 후 맞댐한 시트 사이에 도막재를 덧바름하면 시트와 일체화되면서 곧바로 굳게 된다. 또한 도막재를 바탕조정용 도막방수재의 주재료와 동일한 재질을 사용할 경우에는, 바탕조정용 도막방수재가 액상상태의 제품이기 때문에 자착식 고무화 아스팔트시트 설치 후 시트 사이에 도막재를 도포하는 것만으로 시공이 완료되며, 도막재가 수용성이고 시트 상부 표면에 부직포가 있으므로 도막재와 시트 표면의 접착력도 매우 강하여 시공성이 아주 양호하다. 이렇게 간단하게 시공이 가능한 이유는, 도막재의 재질과 자착식 고무화 아스팔트시트의 콤파운드 또는 바탕조정용 도막방수재의 주재료가 동일하기 때문이다.
If the coating material is made of the same material as the self-adhesive rubberized asphalt sheet, the compound is manufactured in a semi-solidified state. Next, after the self-adhesive rubberized asphalt sheet is installed, when the coating material is applied between the sheets to be bonded together, the sheet is solidified as soon as it is integrated with the sheet. In addition, when using the same material as the main material of the base waterproofing waterproofing material, since the grounding waterproofing material is a liquid product, the construction is completed by simply applying the coating material between the sheets after the self-adhesive rubberized asphalt sheet is installed. Since the coating material is water-soluble and there is a nonwoven fabric on the upper surface of the sheet, the adhesion between the coating material and the surface of the sheet is also very strong, so that the workability is very good. This simple construction is possible because the material of the coating material and the main material of the compound of the self-adhesive rubberized asphalt sheet or the coating material waterproofing material for ground adjustment are the same.

종래에 사용하던 공법은 도막재의 재질과 방수시트의 재질이 서로 달랐기 때문에 도막재가 굳고 난 다음에는 재질의 상이함에 따른 계면층(界面層)이 발생하여 시간이 지남에 따라 계면층이 누수의 원인이 되었다. 하지만, 본 발명에서는 도막재를 자착식 고무화 아스팔트시트의 콤파운드 재질과 같은 재질을 사용하거나 또는 바탕조정용 도막방수재와 주재료가 같은 재질의 도막재로 시트간 조인트 상부에 보강하여 방수층 전체를 동일한 재질로 된 하나의 방수층으로 형성함으로써, 공사현장의 조건, 계절적 또는 기후적 요인, 바탕면의 상태, 바탕면의 형상, 일반시트의 접착력 미확보 등에 의한 기존의 일반방수시트의 들뜸 및 박리 문제를 해결하였고, 시트방수층의 접합부에서의 취약점을 근본적으로 보완하였다.
In the conventional method, since the material of the coating material and the material of the waterproof sheet are different from each other, after the coating material is hardened, an interfacial layer occurs due to the difference of the materials, and as a result, the interfacial layer leaks over time. It became. However, in the present invention, the coating material is made of the same material as the compound of the self-adhesive rubberized asphalt sheet, or the base material waterproofing material and the main material are made of the same material as the coating material, and the entire waterproof layer is made of the same material. By forming a single waterproof layer, it solved the problem of lifting and peeling of the existing general waterproof sheet due to the condition of the construction site, seasonal or climatic factors, the state of the base surface, the shape of the base surface, and the inability to secure the adhesion of the general sheet. The weakness at the junction of the sheet waterproof layer is fundamentally compensated.

이와 같이 본 발명에 따른 복합방수공법은, 일반시트를 사용한 밀착공법이 바탕면 요철로 인한 접착력 감소와 국부적인 들뜸이나 박리 및 균열이 발생한다는 단점과, 절연공법이 시트가 바탕면에서 떠 있고 조인트 부분만 바탕면에 붙어 있어서 시트의 열변형 등으로 인한 모든 응력이 시트와 시트 사이의 조인트 부분으로 집중되기 때문에 조인트 안정성이 떨어진다는 단점을 근본적으로 없애고, 밀착공법이 조인트의 안정성이 좋다는 장점과, 절연공법이 바탕면의 균열에 의한 시트의 파단이 없다는 장점을 살린 가장 이상적인 공법으로서, 시트와 도막 재료와의 재질적 이질성으로 인해 복합층의 열변형 및 구조체의 거동에 따라 이질재의 계면(界面)이 분리되는 문제를 근원적으로 해결하면서 공사기간단축 및 공사비를 절감할 수 있는 효과가 있다.
As described above, the composite waterproof method according to the present invention has the disadvantage that the adhesion method using the general sheet reduces the adhesive force due to irregularities of the base surface, and local lifting or peeling and cracking occur. Since only the part is attached to the base surface, all stresses due to heat deformation of the sheet are concentrated in the joint part between the sheet and the sheet, thereby essentially eliminating the disadvantage of poor joint stability, and the close contact method has the advantage of good joint stability. It is the most ideal method that utilizes the advantage that the sheet is not broken by the crack of the base surface, and due to the material heterogeneity between the sheet and the coating material, the interface of the dissimilar materials due to the thermal deformation of the composite layer and the behavior of the structure. While fundamentally solving this separation problem, there is an effect that can reduce the construction period and construction costs.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로, 본 발명이 속하는 기술 분야에서 통상의 지식을 갖는 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서 본 발명에 게시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이런 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호범위는 아래의 청구범위에 의하여 해석되어야하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
The above description is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains may make various modifications and changes without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention but to describe the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The protection scope of the present invention should be interpreted by the following claims, and all technical ideas within the equivalent scope should be interpreted as being included in the scope of the present invention.

10 : 콘크리트 바탕면
20 : 방수층 21 : 프라이머
22 : 바탕조정용 방수도막재 23 : 자착식 고무화 아스팔트시트
231 : 이형지 232 : 자착식 고무화 아스팔트
233 : 부직포
30 : 도막재10: concrete ground surface
20: waterproof layer 21: primer
22: waterproofing coating material for ground adjustment 23: self-adhesive rubberized asphalt sheet
231: release paper 232: self-adhesive rubberized asphalt
233: nonwoven fabric
30: coating material

Claims (11)

콘크리트 바탕면 상부에 도포된 프라이머;
상기 프라이머 상부에 도포되어 콘크리트 바탕면을 평탄하게 만들어 주는 바탕조정용 방수도막재;
상기 바탕조정용 방수도막재 상부에 접착되는 자착식 고무화 아스팔트 시트;
로 구성되며,
상기 바탕조정용 방수도막재는, 아스팔트 40∼50 중량부, PVA-SBR(styrene-butadien copolymer) 합성고무 20∼35 중량부, 유화제 2∼3 중량부, 소포제 0.1∼1 중량부, 접착강화제 5∼10 중량부, 점도조절제 0.1∼1 중량부, 물 10∼25 중량부로 구성되는 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조.
A primer applied on the concrete base surface;
A waterproofing coating material for base adjustment applied to the primer to make the concrete base surface flat;
Self-adhesive rubberized asphalt sheet is bonded to the upper surface of the waterproof coating material for adjustment;
Lt; / RTI >
The ground coating waterproofing coating material is 40 to 50 parts by weight of asphalt, 20 to 35 parts by weight of PVA-SBR (styrene-butadien copolymer), 2 to 3 parts by weight of emulsifier, 0.1 to 1 part by weight of antifoaming agent, and 5 to 10 adhesive strengthening agent. A waterproof structure using a waterproofing coating material for ground adjustment and a self-adhesive rubberized asphalt sheet, comprising a weight part, a viscosity modifier 0.1 to 1 part by weight, and water 10 to 25 parts by weight.
삭제delete 제1항에 있어서,
상기 자착식 고무화 아스팔트 시트는, 자착식 고무화 아스팔트와, 그 상부에 부착된 부직포로 구성된 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조.
The method of claim 1,
The self-adhesive rubberized asphalt sheet is a waterproof structure using a self-adhesive rubberized asphalt and a non-woven fabric attached to the upper portion of the waterproofing coating material and the self-adhesive rubberized asphalt sheet.
제3항에 있어서,
상기 자착식 고무화 아스팔트는, 아스팔트 30∼40중량부, 스틸렌 부타디엔 스틸렌 10∼20중량부, 부틸고무 10∼15중량부, DOP(Dioctyl phthalic acid) 5∼10중량부, NBR(Nitrile Butadiene Rubber) 5∼10중량부, 탄산칼슘 5∼15중량부, 특수첨가제 5∼15중량부를 혼합한 콤파운드로 구성된 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조.
The method of claim 3,
The self-adhesive rubberized asphalt, 30 to 40 parts by weight asphalt, 10 to 20 parts by weight of styrene butadiene styrene, 10 to 15 parts by weight of butyl rubber, 5 to 10 parts by weight of DOP (Dioctyl phthalic acid), NBR (Nitrile Butadiene Rubber) 5-10 parts by weight, 5-15 parts by weight of calcium carbonate, 5-15 parts by weight of special additives, characterized in that the compound consisting of a waterproof coating material and self-adhesive rubberized asphalt sheet, characterized in that the waterproof structure.
제4항에 있어서,
상기 특수첨가제는, 점착력 및 접착력 강화와 흘러내림 방지를 위한 검로진인 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조.
The method of claim 4, wherein
The special additive is a waterproof structure using a waterproofing coating material and a self-adhesive rubberized asphalt sheet for ground adjustment, characterized in that the gumjin for strengthening the adhesion and adhesion and preventing the fall.
콘크리트 바탕면 상부에 프라이머를 도포하는 단계;
콘크리트 바탕면을 평탄하게 하기 위하여 상기 프라이머 상부에 바탕조정용 방수도막재를 도포하는 단계;
상기 바탕조정용 방수도막재 상부에 자착식 고무화 아스팔트시트를 접착시키는 단계;
를 거쳐 시공하며,
상기 바탕조정용 방수도막재는, 아스팔트 40∼50 중량부, PVA-SBR(styrene-butadien copolymer) 합성고무 20∼35 중량부, 유화제 2∼3 중량부, 소포제 0.1∼1 중량부, 접착강화제 5∼10 중량부, 점도조절제 0.1∼1 중량부, 물 10∼25 중량부로 구성되어 있는 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조를 시공하는 복합방수공법.
Applying a primer on the concrete base surface;
Applying a waterproofing coating material for surface adjustment on the primer to flatten the concrete base surface;
Adhering a self-adhesive rubberized asphalt sheet to the upper surface of the waterproofing coating material;
Construction through
The ground coating waterproofing coating material is 40 to 50 parts by weight of asphalt, 20 to 35 parts by weight of PVA-SBR (styrene-butadien copolymer), 2 to 3 parts by weight of emulsifier, 0.1 to 1 part by weight of antifoaming agent, and 5 to 10 adhesive strengthening agent. A composite waterproof method for constructing a waterproof structure using a waterproofing coating material for ground adjustment and a self-adhesive rubberized asphalt sheet, comprising a weight part, a viscosity modifier 0.1 to 1 part by weight and water 10 to 25 parts by weight.
제6항에 있어서.
상기 자착식 고무화 아스팔트시트를 맞댐한 후, 시트와 시트의 맞댐부위 상부에는 도막재를 덧바름하여 보강하는 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조를 시공하는 복합방수공법.
The method of claim 6.
After abutting the self-adhesive rubberized asphalt sheet, construct a waterproof structure using a waterproofing coating material for self-adhesive rubberized asphalt sheet, characterized in that the coating layer is reinforced by reinforcing the sheet material on top of the sheet-to-butt portion of the sheet. Composite waterproofing method.
제7항에 있어서.
상기 도막재는, 상기 자착식 고무화 아스팔트시트의 콤파운드와 동일한 재질인 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조를 시공하는 복합방수공법.
The method of claim 7.
The coating material is a composite waterproof method for constructing a waterproof structure using a waterproof coating material for ground adjustment and a self-adhesive rubberized asphalt sheet, characterized in that the same material as the compound of the self-adhesive rubberized asphalt sheet.
제7항에 있어서.
상기 도막재는, 상기 바탕조정용 방수도막재의 주재료로 동일한 재질인 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조를 시공하는 복합방수공법.
The method of claim 7.
The coating material is a composite waterproof method for constructing a waterproof structure using the waterproofing coating material and the self-adhesive rubberized asphalt sheet for grounding, characterized in that the same material as the main material of the waterproofing coating material for grounding.
삭제delete 제6항에 있어서.
상기 자착식 고무화 아스팔트 시트는, 자착식 고무화 아스팔트와, 그 상부에 부착된 부직포로 구성된 시트인 것을 특징으로 하는 바탕조정용 방수도막재와 자착식 고무화 아스팔트 시트를 사용한 방수구조를 시공하는 복합방수공법.The method of claim 6.
The self-adhesive rubberized asphalt sheet is a composite comprising a waterproof structure using a waterproofing coating material and a self-adhesive rubberized asphalt sheet, characterized in that the sheet consisting of a self-adhesive rubberized asphalt and a non-woven fabric attached to the upper portion. Waterproof method.
KR1020100074529A 2010-08-02 2010-08-02 Complex waterproof structure and constructing method of complex waterproof using membrane waterproof stuff and self-adhesive rubberized asphalt sheet KR101015120B1 (en)