CN1304616C - 人造板大型木工刨切机刀片材料及生产方法 - Google Patents
人造板大型木工刨切机刀片材料及生产方法 Download PDFInfo
- Publication number
- CN1304616C CN1304616C CNB200510016727XA CN200510016727A CN1304616C CN 1304616 C CN1304616 C CN 1304616C CN B200510016727X A CNB200510016727X A CN B200510016727XA CN 200510016727 A CN200510016727 A CN 200510016727A CN 1304616 C CN1304616 C CN 1304616C
- Authority
- CN
- China
- Prior art keywords
- blade material
- annealing
- vanadium
- manganese
- tungsten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种人造板大型木工刨切机刀片材料及生产方法，属于金属材料制造技术领域，取碳、硅、锰、铬、钨、钒、钼，混合投入到电炉中，浇铸电极坯，退火再放入重熔炉中，退火，开坯，退火，制成。本发明材料制成的刀具耐用程度高，可以连续工作29小时，性能安全可靠，稳定性好，废品率低，生产成本低。
Description
技术领域：
本发明属于金属材料制造技术领域，涉及一种人造板刨切机刀片材料，以及生产人造板刨切机刀片材料的方法。
背景技术：
目前木国外生产的人造板刨切机刀片材料售价非常高，造成刨切机器设备造价高，制造的刀具，可连续工作24小时左右。
发明内容：
本发明要解决的技术问题是公开一种使用寿命较长，生产成本较低的人造板刨切机刀片材料。
本发明的解决技术问题的方案是采用下述化学元素材料制成，其
组分用重量份数比表示
碳 85-95 硅 80-150 锰 20-40 铬 380-440
钨 420--520 钼 180-200 钒 130-170
本材料的优选重量份数配比为
碳 88-93 硅 90-130 锰 25-35 铬 400-420
钨 470--500 钼 185-195 钒 140-160
本材料的最佳重量份数配比为
碳 90 硅 120 锰 30 铬 410 钨 470
钼 190 钒 150
生产方法为：
将上述原材料混合投入到电炉中，加热温度为1550℃，加热时间2小时，浇铸电极坯，退火，880℃均温2小时，再放入重熔炉中，加热温度为1600℃，加热时间1小时，退火，开坯，退火，制成刨切机刀片材料。
本发明材料制成的刀具耐用程度高，可以连续工作29小时，性能安全可靠，稳定性好，废品率低，生产成本低。
具体实施方式：
取碳90公斤、硅120公斤、锰30公斤、铬410公斤、钨470公斤、钼190公斤、钒150公斤，混合投入到电炉中，加热温度为1550℃，加热时间2小时，浇铸电极坯，退火，880℃均温2小时，再放入重熔炉中，加热温度为1600℃，加热时间1小时，退火，开坯，退火，制成刨切机刀片材料。在混合原料的同时可加入微量的磷、硫。
Claims (3)
1、一种人造板大型木工刨切机刀片材料，其特征在于采用下述重量份数比化学元素材料制成
碳85-95 硅80-150 锰20-40 铬380-440
钨420--520 钼180-200 钒130-170
其中制备方法为将上述原材料混合投入到电炉中，加热温度为1550℃，加热时间2小时，浇铸电极坯，退火，880℃均温2小时，再放入重熔炉中，加热温度为1600℃，加热时间1小时，退火，开坯，退火，制成刨切机刀片材料。
2、根据权利要求1所述的人造板刨切机刀片材料，其特征在于：材料的重量份数配比为
碳88-93 硅90-130 锰25-35 铬400-420
钨470--500 钼185-195 钒140-160。
3、根据权利要求2所述的人造板刨切机刀片材料，其特征在于：本材料的重量份数配比为
碳90 硅120 锰30 铬410 钨470
钼190 钒150。