CN1297352C - Heating die centrifugal casting mold spraying process for grey cast iron pipe with flexible interface - Google Patents

Heating die centrifugal casting mold spraying process for grey cast iron pipe with flexible interface Download PDF

Info

Publication number
CN1297352C
CN1297352C CNB2004100030785A CN200410003078A CN1297352C CN 1297352 C CN1297352 C CN 1297352C CN B2004100030785 A CNB2004100030785 A CN B2004100030785A CN 200410003078 A CN200410003078 A CN 200410003078A CN 1297352 C CN1297352 C CN 1297352C
Authority
CN
China
Prior art keywords
spraying
casting mold
mold
coating
cast iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100030785A
Other languages
Chinese (zh)
Other versions
CN1557567A (en
Inventor
范英俊
刘明忠
杨彬
王黎晖
张鑫
金美余
李晓兵
张宏伟
闫玉凤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinxing Ductile Iron Pipes Co Ltd
Original Assignee
Xinxing Ductile Iron Pipes Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xinxing Ductile Iron Pipes Co Ltd filed Critical Xinxing Ductile Iron Pipes Co Ltd
Priority to CNB2004100030785A priority Critical patent/CN1297352C/en
Publication of CN1557567A publication Critical patent/CN1557567A/en
Application granted granted Critical
Publication of CN1297352C publication Critical patent/CN1297352C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The present invention relates to casting mold spraying technology of hot mould centrifugal casting of a flexible joint grey cast-iron pipe. The casting mold spraying technology comprises the steps that residual coating layers of a casting mold are removed; if a new casting mold is used, the new casting mold is first processed in the modes of oil removal and rust removal, and then the new casting mold is preheated; the casting mold which has appropriate temperature and a clean inner surface are transported to a spraying service station in time, and the casting mold driven by a rotating motor to rotate at high speed to make preparations for being sprayed; when the rotation speed of the casting mold achieves a requirement, a high-pressure gas-free spraying machine is started; a spraying trolley drives a spraying gun to carry out uniform spraying in the casting mold; the casting mold which is sprayed is transported to a centrifugal service position in time to cast molten iron in a centrifugal mode, and the molten iron is cooled into the grey cast-iron pipe; and when the temperature is appropriate, the grey cast-iron pipe is drawn, and the next circulation is recycled. The present invention has the advantages of small paint dissipation quantity, high coating layer compactness, high intensity, easy control of paint atomization and high productive efficiency.

Description

Flexible interface gray cast iron tube hot-die mould centrifugal casting mould spraying coating process
(1), technical field
The invention belongs to a kind of flexible interface gray cast iron tube hot-die mould centrifugal casting mould spraying coating process.
(2), background technology
At present, domestic flexible interface gray cast iron tube production technology has all been used gas blowout and has been coated with, and there have gas blowout to be coated with major defect to be as follows: (1), coating windage are big, two aspects influence: a is arranged, cause environmental pollution, easily causes anthraco-silicosis; B, paint waste are serious, by statistics, with this technology coating usage factor only 80~90%.(2), coating compactness is poor, intensity is low, two aspects influence: a is arranged, cause the percent defective height.Because at the high temperature liquid iron of 1450 ℃ of coating surface cast, pouring into a mould moment, strong heat exchange action causes coating shedding, forms slag inclusion, makes product rejection, this technology qualification rate is generally 80~85%; B, mold life-span are low.After coating is washed away by molten iron, molten iron will act directly on the mold inner surface, cause molten iron and mold bonding, or mould surface is washed into pit, and the mold life-span is reduced greatly.About 1000 of general cast of this technology mold life-span.(3), the coating atomizing is wayward.If compressed-air actuated air pressure instability, or nozzle wear all can have a strong impact on atomizing effect, causes the coating surface roughness big, causes that the product surface roughness is big.The general Ra10 of this artistic face roughness~20.(4), production efficiency is low.Because the application of compressed air atomised coating, quantity for spray is less, and when quantity for spray increased, atomization badness then, this technology spray time be generally at 2~3 minutes, so production efficiency is low, and 20~30 grey iron pipes of production in one hour.
(3), summary of the invention
In order to overcome the shortcoming of prior art, the invention provides a kind of flexible interface gray cast iron tube hot-die mould centrifugal casting mould spraying coating process, not only the coating windage is little for it, and coating compactness is good, the intensity height, and also the coating atomizing is easy to control, the production efficiency height.
The present invention solves the processing step that its technical problem takes: a, mold are cleared up remaining coating, after mold pours molten iron and gray cast iron tube is pulled out, the mold inner surface has the remaining coating of part, remaining coating being cleaned out before the spraying again, just can obtain the uniform coating of thickness; B, preheating, if use new mold, at first necessary degreasing and rust removal carries out preheating to mold again; C, the mold that temperature is suitable, inner surface is clean are in time delivered to spray station, drive bottom mold at electric rotating machine and rotate at a high speed, prepare spraying; D, after rotational speed of casting die reaches requirement, start high pressure airless spray equipment; E, spraying dolly drive spray gun evenly spraying in mold; F, the mold after will spraying are in time delivered to the centrifuge station, carry out the centrifugal casting molten iron, and molten iron is cooled to gray cast iron tube, after temperature is suitable, gets final product tube drawing, repeats next circulation behind the tube drawing.
The present invention is the following advantage of tool compared with prior art: (1), coating windage are little, have two aspect advantage: a, working environment to be greatly improved; B, paint waste reduce, by statistics, with this technology coating usage factor only more than 95%.(2), coating compactness is good, the intensity height has two aspect advantage: a, qualification rate height, this technology qualification rate is generally 95~98%; B, mold life-span improve greatly, about 2500~3000 of general cast of this technology mold life-span.(3), the coating atomizing is easy to control.Owing to use high pressure airless spray equipment, the coating atomizing is stable, make the coating surface roughness little, thereby the product surface roughness is little, the general Ra5 of this artistic face roughness~10.(4), production efficiency height.Because the applying high voltage airless sprayer, quantity for spray increases greatly, and spray time shortens, and this technology spray time is generally at 40~55 seconds, so the production efficiency height can be produced 50~55 grey iron pipes in one hour.
(4), description of drawings
Accompanying drawing is a process chart of the present invention.
(5), the specific embodiment
Processing step of the present invention is successively: a, mold are cleared up remaining coating: after mold pours molten iron and gray cast iron tube pulled out, the mold inner surface has the remaining coating of part, remaining coating being cleaned out before the spraying again, just can obtain the uniform coating of thickness.If b uses new mold, at first necessary degreasing and rust removal carries out preheating to mold again, and the preheat temperature of mold inner surface is 200~250 ℃.C, the mold that temperature is suitable, inner surface is clean are in time delivered to spray station, and the speed that drives bottom mold 700~800r/min at electric rotating machine is rotated at a high speed, prepare spraying, and d, after rotational speed of casting die reaches requirement starts high pressure airless spray equipment.E, spraying dolly drive spray gun evenly spraying in mold, and the pressure of spraying is 1~2Mpa, and the flow of nozzle is 0.3~1.7kg/min, and the walking speed of spray gun is 0.1~0.2m/s, and the thickness of coating is 0.2~0.4mm.F, the mold after will spraying are in time delivered to the centrifuge station, carry out the centrifugal casting molten iron, and molten iron is cooled to gray cast iron tube, after temperature is suitable, gets final product tube drawing, repeats next circulation behind the tube drawing.Process chart is seen accompanying drawing.

Claims (2)

1, a kind of flexible interface gray cast iron tube hot-die mould centrifugal casting mould spraying coating process, it is characterized in that: comprise that following processing step: a, mold clear up remaining coating, after mold pours molten iron and gray cast iron tube is pulled out, the mold inner surface has the remaining coating of part, remaining coating being cleaned out before the spraying again, just can obtain the uniform coating of thickness; B, mold is carried out preheating, preheat temperature is 200~250 ℃: c, mold is delivered to spray station, drive bottom mold at electric rotating machine and rotate at a high speed, rotating speed is 700~800r/min, prepares spraying; D, startup high pressure airless spray equipment, spraying dolly drive spray gun evenly spraying in mold, and the pressure of spraying is 1~2Mpa, and the flow of nozzle is 0.3~0.7kg/min, and the walking speed of spray gun is 0.1~0.2m/s, and the thickness of coating is 0.2~0.4mm; E, the mold after will spraying are delivered to the centrifuge station, carry out the centrifugal casting molten iron, and molten iron is cooled to gray cast iron tube, after temperature is suitable, gets final product tube drawing, repeats next circulation behind the tube drawing.
2, spraying coating process according to claim 1 is characterized in that: use new mold, carried out degreasing and rust removal and handle before preheating.
CNB2004100030785A 2004-01-18 2004-01-18 Heating die centrifugal casting mold spraying process for grey cast iron pipe with flexible interface Expired - Fee Related CN1297352C (en)