CN1295172C - Method for producing dull cowboy glaze - Google Patents

Method for producing dull cowboy glaze Download PDF

Info

Publication number
CN1295172C
CN1295172C CNB2004100470588A CN200410047058A CN1295172C CN 1295172 C CN1295172 C CN 1295172C CN B2004100470588 A CNB2004100470588 A CN B2004100470588A CN 200410047058 A CN200410047058 A CN 200410047058A CN 1295172 C CN1295172 C CN 1295172C
Authority
CN
China
Prior art keywords
glaze
dull
cowboy
unglazed
metal oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100470588A
Other languages
Chinese (zh)
Other versions
CN1648088A (en
Inventor
潘俊明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN TAIXIN CERAMICS CO Ltd
Original Assignee
HUNAN TAIXIN CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN TAIXIN CERAMICS CO Ltd filed Critical HUNAN TAIXIN CERAMICS CO Ltd
Priority to CNB2004100470588A priority Critical patent/CN1295172C/en
Publication of CN1648088A publication Critical patent/CN1648088A/en
Application granted granted Critical
Publication of CN1295172C publication Critical patent/CN1295172C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a method for manufacturing dull cowboy glaze. The present invention is characterized in that the glaze is prepared by a given recipe; the glaze comprises dull orchid and dull brown which respectively contain univalent metal oxides, divalent metal oxide, trivalent metal oxide and tetravalent metal oxide with required quantity; the dull orchid takes CoO as a colorant, while the dull brown takes Fe2O3 and MnO2 as colorants; the materials are milled by balls by a wet method, are filtered, and are prepared into slurry according to the concentration of 25 to 35 Baume degrees; the porcelain blank with specific surface characteristic is doped with glaze, and is put in a kiln, and is fast fired in an oxidizing atmosphere at the temperature of 1180 to 1200DEGC. The color of the surface enamel layer of the finished porcelain is similar to the color of the cowboy clothes, the surface enamel layer has natural spot patterns, and the decorating effect is strong.

Description

The making method of unglazed cowboy's glaze
Technical field
The present invention relates to the making method of unglazed cowboy's glaze.
Background technology
Jean is well-known with the assorted decorative pattern of its unique style and colour of clothes and natural spot.Can it be borrowed in the porcelain industry, in the hope of obtaining unexpected effect?
Summary of the invention
Purpose of the present invention will be burnt till on the porcelain base substrate exactly near the assorted decorative pattern of the natural spot of cowboy's style and colour of clothes, its color look that should get close to nature, and have stronger decorative effect.
The process for calcining of the so-called unglazed cowboy's glaze of the present invention is characterized in that: (1) is by following chemical constitution per-cent batching---A, unglazed blue prescription Na 2O 2～8, and K2O 5～10, and CaO 25～40, Al 2O 316～18, SiO 217～20, BaO 6～8, and MgO 4～5, and ZnO 4～12, C 0O 0.8～2; Perhaps B, unglazed palm fibre prescription Na 2O 2～8, K 2O 5～10, and CaO 25～40, Al 2O 316～18, SiO 217～20, BaO 6～8, and MgO 4～5, and ZnO 4～12, Fe 2O 32～7, MnO 20.5～2; (2) by material: ball: water equals to carry out wet ball grinding 20 hour at 1: 2: 0.6; (3) glaze behind the ball milling is crossed 250 mesh sieves, is made into the slurry of 25～35 degree Beaume again; (4) get the pockmark of the regular distribution of appearance or bright and clean porcelain base substrate and soak glaze and go into to burn till fast roller kiln, under 1180～1200 ℃ oxidizing atmosphere, fire and form.
Embodiment
Example one is by the unglazed blue glaze of following formulated (all raw materials all are technical grade): Na 2O 5% (weight percent, down together), K 2O 7%, and CaO 35%, Al 2O 316%, SiO 218%, BaO 6%, and MgO 5%, and ZnO 6.5%, C 0O 1.5%; Carry out wet ball grinding, sieve, make the slurry of concentration 25～35 U.S. degree according to the present invention regulation, get the pockmark of the regular distribution of appearance or bright and clean porcelain base substrate and soak glaze and go into kiln, kiln is fired under 1180～1200 ℃ oxidizing atmosphere for burning till roller kiln fast.All pockmarks bottom glaze layer colors of gained finished product porcelain tool surface are the darkest, and rest part then color and luster is very shallow, and glaze this in burning till, also form mottled effect of decorative patterns, thereby first and last be mottled naturally decorative pattern as the jean, color sensation is pressed close to self colour.
Example two is according to the unglazed brown glaze of following formulated (all raw materials all are technical grade): Na 2O 8% (weight percent, down together), K 2O 5%, and CaO 33.5%, Al 2O 316%, SiO 218%, BaO 6%, and MgO 4%, and ZnO 4%, Fe 2O 35%, MnO 21.5%; Carry out ball milling after sieve according to the inventive method, be deployed into the slurry of 25～35 degree Beaume concentration, go into to burn till fast roller kiln after the porcelain base substrate of getting outer watchband rule distribution pockmark soaks glaze, under 1180～1200 ℃ oxidizing atmosphere, fire.All pockmark bottom glaze layer colors of its surface of gained finished product porcelain are the darkest, and other parts then color and luster are more shallow, and first and last color is mottled, and decorative effect is fine; Even glazing also can reach effect same on bright and clean level and smooth base substrate, thus the glaze kind this in burn till and process of cooling in can nature form mottled floral designs.

Claims (1)

1, the making method of unglazed cowboy's glaze is characterized in that:
(1) by following chemical constitution per-cent preparation---
A, unglazed blue prescription
Na 2O 2～8
K 2O 5～10
CaO 25～40
Al 2O 3 16～18
SiO 2 17～20
BaO 6～8
MgO 4～5
ZnO 4～12
CoO 0.8～2
Perhaps
B, unglazed palm fibre prescription
Na 2O 2～8
K 2O 5～10
CaO 25～40
Al 2O 3 16～18
SiO 2 17～20
BaO 6～8
MgO 4～5
ZnO 4～12
Fe 2O 3 2～7
MnO 2 0.5～2
(2) wet ball grinding is 20 hours, selected material: ball: water=1: 2: 0.6;
(3) glaze behind the ball milling is crossed 250 mesh sieves, again the slurry of furnishing concentration 25～35 degree Beaume;
(4) get the pockmark of the regular distribution of appearance or bright and clean porcelain base substrate and soak glaze and go into to burn till fast roller kiln, under 1180～1200 ℃ oxidizing atmosphere, fire.
CNB2004100470588A 2004-12-16 2004-12-16 Method for producing dull cowboy glaze Expired - Fee Related CN1295172C (en)