CN1272492C - Wool-acrylic fiber cospinning pearl lint and manufacture process thereof - Google Patents
Wool-acrylic fiber cospinning pearl lint and manufacture process thereof Download PDFInfo
- Publication number
- CN1272492C CN1272492C CN 01135220 CN01135220A CN1272492C CN 1272492 C CN1272492 C CN 1272492C CN 01135220 CN01135220 CN 01135220 CN 01135220 A CN01135220 A CN 01135220A CN 1272492 C CN1272492 C CN 1272492C
- Authority
- CN
- China
- Prior art keywords
- pearl
- humidification
- wool
- product
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a wool acrylic blended pearl flannel and manufacturing technology thereof, and belongs to the field of textile products. The wool acrylic blended pearl flannel comprises a bottom yarn layer and a surface yarn layer which are weaved and combined into a whole. The present invention is characterized in that the surface yarn layer is in a curly type solid tuft structure with dense arrangement, and the surface yarn layer is positioned on one side of the bottom yarn layer; the curly type solid tufts are irregularly or regularly arranged on the surface of the wool acrylic blended pearl flannel. The present invention has a manufacture method that the moistening, curling, forming, shaping and drying process steps are added after a scalding and shearing process step on a grey cloth. The face fabric of the product manufactured by the present invention has strong cubic effect and low manufacture cost, the luster of the weaved cloth is stronger than that of the common acrylon fabric, and the heat insulating performance of the product is strong. Compared with real animal fur, the product can be washed, and the weight is light. The appearance of the product is similar to pearls inlaid on the surface of the cloth. The product is elegant and beautiful, is a fashionable cloth with novelty and uniqueness, and has large development and application space and market perspective. The present invention can be widely applied to fields of clothing, bags, scarves, footwear, toys, decorative clothes, etc.
Description
Technical field
The invention belongs to the textile product field, relate in particular to the textile product and the manufacturing technique thereof of a kind of mao of nitrile blending.
Background technology
The knitting circle cashmere shell-fabric that cuts of domestic production at present, its production technology be the weaving of veil and filling, grey cloth starching typing, bristle, scald and operation such as cut, product by this explained hereafter, if do not handle through deep processing, the veil layer fiber on its cloth surface is erectility, cloth outward appearance basically identical, unless through the color separation dyeing process, otherwise the cloth surface color is single, but use the color separation dyeing and printing process, need increase equipment and operation, increase production cost, make its range of application be subjected to certain restriction.
Summary of the invention
It is the three-dimensional suede of curling shape bunch of dense arrangement, wool-acrylic fiber cospinning pearl lint and the technology thereof that production cost is low that goal of the invention provides a kind of veil layer.
A kind of technology of wool-acrylic fiber cospinning pearl lint comprises the boiling hot operation of cutting of grey cloth, it is characterized in that setting up humidification, cans and typing drying process after grey cloth boiling hot cut operation;
Described humidification process temperature scope is 10～80 ℃, and the moisture content of grey cloth is 10～60% after the process humidification operation;
Described cans process temperature scope is 80～110 ℃, and humidity is 80～100%, and the time is 5～30min;
Described typing drying process temperature range is 80～130 ℃, and rate of drying is 5～30m/min.
The wool-acrylic fiber cospinning pearl lint of explained hereafter of the present invention is characterized in that the veil layer is the three-dimensional suede clustering architecture of curling shape of dense arrangement;
Described veil layer is positioned at the one side of filling layer;
The three-dimensional suede of described curling shape bunch is arranged in wool-acrylic fiber cospinning pearl lint material surface brokenly or regularly.
Compared with prior art, advantage of the present invention is:
1. because the fiber of veil layer is the three-dimensional suede clustering architecture of curling shape of dense arrangement, the lining third dimension is strong.
2. production technology is simple, low cost of manufacture.
3. the veil layer adopts hair nitrile blend fibre yarn, and the general acrylic fabric gloss of the cloth of weaving out is strong, and exploitation provides advantage to knit fabric.
4. the product warmth retention property is strong.
5. compare with real movement thing fur, can wash and in light weight.
Description of drawings
Fig. 1 is the cross-sectional view of product of the present invention.
Among the figure, 1. being the filling layer, 2. is the veil layer, and the filling layer is common stocking yarn, and the veil layer is a hair nitrile blend fibre yarn, and filling layer and veil layer are combined into one through weaving.
The specific embodiment
The purpose of carrying out the humidification operation is that grey cloth is carried out even humidification, makes fiber yielding; The purpose of carrying out the cans operation is to make the fiber crimp moulding; The cans operation also can repeat, to obtain better appearance effect.
Because the veil layer adopts hair nitrile blend fibre yarn, wool fibre wherein is different with the tinctorial yield of acrylic fiber, and after through humidification and cans operation, the veil layer of knitted cloth presents two kinds of different colors of the depth; Simultaneously, because the resistance to elevated temperatures of wool fibre and acrylic fiber there are differences, wool fibre produces different curling and contraction with acrylic fiber, after the cans operation, make the intensive cluster shape that curls, flocks together of fiber in the veil layer, the top of bunch shape is a wool fibre, and its bottom remains the mixing of wool fibre and acrylic fiber, promptly forms the three-dimensional suede clustering architecture of curling shape of intensive inhomogeneous arrangement on the surface of cloth.
Embodiment 3 veils adopt the hair nitrile blended yarn of 36S/2, and filling is the 200D polyester filament, and humidification temperature is 45～50 ℃, moisture content 30%; The cans temperature is 100～105 ℃, humidity 95～100%, and the time is 25～30min; 125～130 ℃ of typing baking temperatures, rate of drying is 29～30m/min, all the other are with embodiment 1.
Embodiment 4 veils adopt the hair nitrile blended yarn of 48S/2, and filling is 60 a public/bifilar cotton yarn, and humidification temperature is 40～45 ℃, moisture content 50%; The cans temperature is 80～85 ℃, humidity 80～85%, and the time is 26～30min; 80～85 ℃ of typing baking temperatures, rate of drying is 11～12.5m/min, all the other are with embodiment 1.
Embodiment 5 veils adopt the hair nitrile blended yarn of 48S/2, and filling is 48 a public/bifilar cotton yarn, and humidification temperature is 45～50 ℃, moisture content 48%; The cans temperature is 100～105 ℃, humidity 92～98%, and the time is 22～25min; 95～100 ℃ of typing baking temperatures, rate of drying is 28～28.5m/min, all the other are with embodiment 1.
Embodiment 6 veils adopt the hair nitrile blended yarn of 42S/2, and filling is 36 a public/bifilar polyester, and humidification temperature is 50～55 ℃, moisture content 28%; The cans temperature is 80～85 ℃, humidity 80～85%, and the time is 28～30min; 80～85 ℃ of typing baking temperatures, rate of drying is 8～9.5m/min, all the other are with embodiment 1.
Embodiment 7 veils adopt the hair nitrile blended yarn of 48S/2, and filling is 42 a public/bifilar cotton yarn, and humidification temperature is 30～35 ℃, moisture content 30%; The cans temperature is 95～100 ℃, humidity 85～90%, and the time is 18～20min; 80～85 ℃ of typing baking temperatures, rate of drying is 7～7.5m/min, all the other are with embodiment 1.
Embodiment 8 veils adopt the hair nitrile blended yarn of 48S/2, and filling is the 100D dacron elasticity silk, and humidification temperature is 40～45 ℃, moisture content 46%; The cans temperature is 100～105 ℃, humidity 80～85%, and the time is 18～22min; 95～100 ℃ of typing baking temperatures, rate of drying is 12～12.5m/min, all the other are with embodiment 1.
Embodiment 9 veils adopt the hair nitrile blended yarn of 48S/2, and filling is the 100D polyester filament, 65～70 ℃ of humidification temperatures, moisture content 35%; 90～95 ℃ of cans temperature, humidity 90～95%, the time is 20～25min; 95～100 ℃ of typing baking temperatures, rate of drying is 28～28.5m/min, all the other are with embodiment 1.
Embodiment 10 veils adopt the hair nitrile blended yarn of 42S/2, and filling is 42 a public/bifilar polyester, 35～40 ℃ of humidification temperatures, moisture content 21%; 95～100 ℃ of cans temperature, humidity 94～96%, the time is 12～15min; 105～110 ℃ of typing baking temperatures, rate of drying is 15～15.5m/min, all the other are with embodiment 1.
Embodiment 11 veils adopt the hair nitrile blended yarn of 36S/2, and filling is the 150D dacron elasticity silk, 40～45 ℃ of humidification temperatures, moisture content 30%; 95～100 ℃ of cans temperature, humidity 90～95%, the time is 20～25min; 110～115 ℃ of typing baking temperatures, rate of drying is 20～21.5m/min, all the other are with embodiment 1.
Embodiment 12 veils adopt the hair nitrile blended yarn of 36S/2, and filling is 30 a public/bifilar polyester, 75～80 ℃ of humidification temperatures, moisture content 28%; 105～110 ℃ of cans temperature, humidity 90～95%, the time is 19～21min; 92～98 ℃ of typing baking temperatures, rate of drying is 16～16.5m/min, all the other are with embodiment 1.
Embodiment 13 veils adopt the hair nitrile blended yarn of 42S/2, and filling is 36 a public/bifilar polyester, 10～15 ℃ of humidification temperatures, moisture content 10%; 105～110 ℃ of cans temperature, humidity 95～100%, the time is 25～30min; 100～105 ℃ of typing baking temperatures, rate of drying is 28.5～30m/min, all the other are with embodiment 1.
Embodiment 14 veils adopt the hair nitrile blended yarn of 48S/2, and filling is 60 a public/bifilar polyester, 20～25 ℃ of humidification temperatures, moisture content 28%; 80～85 ℃ of cans temperature, humidity 95～100%, the time is 15～18min; The typing baking temperature is at 80～85 ℃, and rate of drying is 12～12.5m/min, and all the other are with embodiment 1.
Embodiment 15 veils adopt the hair nitrile blended yarn of 24S/2, and filling is 30 a public/bifilar cotton yarn, 75～80 ℃ of humidification temperatures, moisture content 20%; 92～98 ℃ of cans temperature, humidity 90～95%, the time is 25～30min; 115～120 ℃ of typing baking temperatures, rate of drying is 5～5.5m/min, all the other are with embodiment 1.
Embodiment 16 veils adopt the hair nitrile blended yarn of 24S/2, and filling is 30 a public/bifilar polyester, 75～80 ℃ of humidification temperatures, moisture content 50%; 105～110 ℃ of cans temperature, humidity 80～85%, the time is 28～30min; 125～130 ℃ of typing baking temperatures, rate of drying is 10～11.5m/min, all the other are with embodiment 1.
Embodiment 17 veils adopt the hair nitrile blended yarn of 24S/2, and filling is 24 a public/bifilar cotton yarn, 35～40 ℃ of humidification temperatures, moisture content 32%; 105～110 ℃ of cans temperature, humidity 95～100%, the time is 25～30min; 125～130 ℃ of typing baking temperatures, rate of drying is 9.5～10m/min, all the other are with embodiment 1.
Embodiment 18 veils adopt the hair nitrile blended yarn of 42S/2, and filling is the 100D dacron elasticity silk, 25～30 ℃ of humidification temperatures, moisture content 38%; 80～85 ℃ of cans temperature, humidity 90～95%, the time is 25～30min; 115～120 ℃ of typing baking temperatures, rate of drying is 25.5～26m/min, all the other are with embodiment 1.
Embodiment 19 veils adopt the hair nitrile blended yarn of 48S/2, and filling is 42 a public/bifilar polyester, 60～65 ℃ of humidification temperatures, moisture content 32.5%; 95～100 ℃ of cans temperature, humidity 90～95%, the time is 24～26min; 75～80 ℃ of typing baking temperatures, rate of drying is 15～16.5m/min, all the other are with embodiment 1.
Embodiment 20 veils adopt the hair nitrile blended yarn of 36S/2, and filling is the 150D dacron elasticity silk, 75～80 ℃ of humidification temperatures, moisture content 42%; 90～95 ℃ of cans worker temperature, humidity 80～85%, the time is 22～25min; 110～115 ℃ of typing baking temperatures, rate of drying is 15.5～16m/min, all the other are with embodiment 1.
Embodiment 21 veils adopt the hair nitrile blended yarn of 24S/2, and filling is 36 a public/bifilar cotton yarn, 35～40 ℃ of humidification temperatures, moisture content 35%; 105～110 ℃ of cans temperature, humidity 90～95%, the time is 26～28min; 125～130 ℃ of typing baking temperatures, rate of drying is 16～17.5m/min, all the other are with embodiment 1.
Embodiment 22 veils adopt the hair nitrile blended yarn of 42S/2, and filling is the 150D polyester filament, 60～65 ℃ of humidification temperatures, moisture content 45%; 90～95 ℃ of cans temperature, humidity 80～85%, the time is 10～12min; 90～95 ℃ of typing baking temperatures, rate of drying is 26～26.5m/min, all the other are with embodiment 1.
Embodiment 23 veils adopt the hair nitrile blended yarn of 18S/2, and filling is the 150D dacron elasticity silk, 35～40 ℃ of humidification temperatures, moisture content 35%; 105～110 ℃ of cans temperature, humidity 90～95%, the time is 26～28min; 125～130 ℃ of typing baking temperatures, rate of drying is 8～8.5m/min, all the other are with embodiment 1.
Embodiment 24 veils adopt the hair nitrile blended yarn of 10S, and filling is the 150D polyester filament, 60～65 ℃ of humidification temperatures, moisture content 45%; 100～105 ℃ of cans temperature, humidity 80～85%, the time is 28～30min; 90～95 ℃ of typing baking temperatures, rate of drying is 4～4.5m/min, all the other are with embodiment 1.
The data of the embodiment of the invention are not limited only to the above-mentioned data of giving, and all technological parameters in claim scope of the present invention are claimed scope.
The present invention is after actual manufacturing is finished, and product appearance is embedded in the cloth surface like a pearl, and is elegant and poised, elegant in appearance, is a kind of new and original fashion lining, and very big exploitation, application space and market prospects are arranged.
Product with manufacturing of the present invention can be widely used in fields such as clothes, case and bag, scarf, footwear, toy, bunting.
Claims (2)
1. the technology of a wool-acrylic fiber cospinning pearl lint comprises the boiling hot operation of cutting of grey cloth, it is characterized in that setting up humidification, cans and typing drying process after grey cloth boiling hot cut operation;
Described humidification process temperature scope is 10～80 ℃, and the moisture content of grey cloth is 10～60% after the process humidification operation;
Described cans process temperature scope is 80～110 ℃, and humidity is 80～100%, and the time is 5～30min;
Described typing drying process temperature range is 80～130 ℃, and rate of drying is 5～30m/min.
2. according to the wool-acrylic fiber cospinning pearl lint of the described explained hereafter of claim 1, it is characterized in that the veil layer is the three-dimensional suede clustering architecture of curling shape of dense arrangement;
Described veil layer is positioned at the one side of filling layer;
The three-dimensional suede of described curling shape bunch is arranged in wool-acrylic fiber cospinning pearl lint material surface brokenly or regularly.