CN102108590A - Weaving method of non-split terylene plush cloth and non-split terylene plush cloth - Google Patents
Weaving method of non-split terylene plush cloth and non-split terylene plush cloth Download PDFInfo
- Publication number
- CN102108590A CN102108590A CN 201110028666 CN201110028666A CN102108590A CN 102108590 A CN102108590 A CN 102108590A CN 201110028666 CN201110028666 CN 201110028666 CN 201110028666 A CN201110028666 A CN 201110028666A CN 102108590 A CN102108590 A CN 102108590A
- Authority
- CN
- China
- Prior art keywords
- terylene
- low elastic
- silk
- polyester filament
- elastic polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a weaving method and terylene cloth, in particular relating to a weaving method of non-split terylene plush cloth and the non-split terylene plush cloth, wherein the weaving method of the non-split terylene plush cloth comprises the following steps: a) preparing materials: using 450D terylene low stretch yarns as surface yarns, using 150D terylene low stretch yarns and 32 counts of cotton as bottom yarns; b) sending materials: sending the prepared surface yarns and bottom yarns into a circular knitting machine, sending one 450D terylene low stretch yarn, one 150D terylene low stretch yarn and one 32 counts of cotton in each path, so that the 150D terylene low stretch yarns and 32 counts of cotton before being woven are arranged at intervals; c) weaving: weaving the 150D terylene low stretch yarns and 32 counts of cotton in each path into a bottom plate by the circular knitting machine, and weaving the 450D terylene low stretch yarns into surface yarns; and d) napping: cutting the surface yarns by the circular knitting machine so as to nap. The bottom plate is woven by the terylene low stretch yarns and the cotton so that the bottom plate is firm and tough with less possibility of cracking.
Description
Technical field
The present invention relates to a kind of weaving method and a kind of woven dacron, relate in particular to a kind of a kind of nothing cracking terylene TWEED of not having cracking terylene TWEED weaving method and utilizing it to be made into.
Background technology
Existing washing entirely during TWEED weaves generally adopted 150D polyester low stretch silk weaving base plate, 450D low elastic polyester filament surface of second order silk, perhaps adopts 100D polyester low stretch silk weaving base plate, 450D low elastic polyester filament surface of second order silk.Because terylene itself has certain oiliness, is a kind of very smooth fiber, base plate and face silk all are to be formed by the low elastic polyester filament braiding, cause bottom slab crack easily in follow-up typing, stentering flow process.
Therefore, how solving entirely, terylene TWEED base plate defective easy to crack in typing, stentering has become a technical barrier.
Summary of the invention
The invention provides a kind of nothing cracking terylene TWEED weaving method, utilize its a kind of nothing cracking terylene TWEED that is made into, have the solid indehiscent advantage of base plate.In order to realize the foregoing invention purpose, the present invention has adopted following technological means:
A kind of nothing cracking terylene TWEED weaving method may further comprise the steps:
A), get the raw materials ready: the 450D low elastic polyester filament is made the face silk, and 150D low elastic polyester filament and 32 polyester-cotton blend are done end silk;
B), feeding: ready silk and end silk are sent into circular knitting machine, and 1 450D low elastic polyester filament, 1 150D low elastic polyester filament and 1 32 polyester-cotton blend are sent in each road, and the preceding 150D low elastic polyester filament of braiding and 32 polyester-cotton blend are spaced;
C), braiding: circular knitting machine is woven into base plate with spaced 150D low elastic polyester filament and 32 polyester-cotton blend, and the 450D low elastic polyester filament is woven into the face silk;
D), napping: circular knitting machine cuts off the face silk, finishes napping.
Ready silk and end silk are sent into the braiding of 14 road circular knitting machines.
A kind of nothing cracking terylene TWEED comprises face silk and base plate, and described silk is low elastic polyester filament, knits and form fine hair on base plate; Described base plate is spaced braiding by low elastic polyester filament and polyester-cotton blend and forms.
Described silk is the 450D low elastic polyester filament; Described base plate is formed by 150D low elastic polyester filament and 32 polyester-cotton blend braidings.
Beneficial effect of the present invention is: because base plate adopts low elastic polyester filament and polyester-cotton blend to be made into, low elastic polyester filament and polyester-cotton blend are spaced before braiding, so the base plate of the terylene TWEED after being made into is thin low elastic polyester filament and polyester-cotton blend be spaced the braiding form, and polyester-cotton blend is terylene and cotton BLENDED FABRIC, the style of existing terylene has the strong point of COTTON FABRIC again, and is more coarse, the terylene TWEED base plate that is formed by polyester-cotton blend and low elastic polyester filament mixed weaving, firmly tough and tensile, not easy to crack.
Description of drawings
Fig. 1 does not have the structural representation of cracking terylene TWEED for the present invention is a kind of.
The specific embodiment
Below in conjunction with accompanying drawing, do not have cracking terylene TWEED weaving method and utilize its a kind of preferred implementation of not having the cracking TWEED that is made into to make detailed description the present invention is a kind of:
The weaving method of this nothing cracking TWEED adopts the braiding of 14 road circular knitting machines, carries out according to following steps: a, get the raw materials ready: the low elastic polyester filament of preparing 14 450D makes the low elastic polyester filament of face silk, 150D and 32 each 14 of polyester-cotton blend are made end silk; B, feeding: the low elastic polyester filament of the low elastic polyester filament of 1 450D, 1 150D and 1 32 polyester-cotton blend are sent in each road, and the low elastic polyester filament of the preceding 150D of braiding and 32 polyester-cotton blend are spaced; C, braiding: with weft-knitted method the low elastic polyester filament of spaced 150D and 32 polyester-cotton blend are woven into base plate, the low elastic polyester filament of 450D are woven in make the face silk on the base plate; D, napping: large circle machine cuts off the face silk, and the face silk erects and is the fine hair shape.
As shown in Figure 1, a kind of nothing cracking terylene TWEED that weaves according to above-mentioned weaving method, comprise face silk 1 and base plate 2, face silk 1 is the low elastic polyester filament of 450D, base plate 2 is made into by the low elastic polyester filament 21 of 150D and 32 polyester-cotton blend 22 mixing weft knittings, low elastic polyester filament 21 and polyester-cotton blend 22 are spaced, and face silk 1 towers and form lint on base plate 2.
Such nothing cracking TWEED, owing to its base plate 2 is formed by coarse polyester-cotton blend 22 and smooth low elastic polyester filament 21 interval weft knittings,, not easy to crack so the sliding style of its existing woven dacron silk has the solid characteristics of COTTON FABRIC again.
Claims (4)
1. one kind is not had cracking terylene TWEED weaving method, it is characterized in that: may further comprise the steps:
A), get the raw materials ready: the 450D low elastic polyester filament is made the face silk, and 150D low elastic polyester filament and 32 polyester-cotton blend are done end silk;
B), feeding: ready silk and end silk are sent into circular knitting machine, and 1 450D low elastic polyester filament, 1 150D low elastic polyester filament and 1 32 polyester-cotton blend are sent in each road, and the preceding 150D low elastic polyester filament of braiding and 32 polyester-cotton blend are spaced;
C), braiding: circular knitting machine is woven into base plate with spaced 150D low elastic polyester filament and 32 polyester-cotton blend, and the 450D low elastic polyester filament is woven into the face silk;
D), napping: circular knitting machine cuts off the face silk, finishes napping.
2. a kind of nothing cracking TWEED weaving method according to claim 1 is characterized in that: ready silk and end silk are sent into the braiding of 14 road circular knitting machines.
3. one kind is not had cracking terylene TWEED, comprises face silk (1) and base plate (2), and described silk (1) is low elastic polyester filament, knits at base plate (2) and goes up formation fine hair; It is characterized in that: described base plate (2) is spaced braiding by low elastic polyester filament (21) and polyester-cotton blend (22) and forms.
4. a kind of nothing cracking terylene TWEED according to claim 3, it is characterized in that: described silk (1) is the 450D low elastic polyester filament; Described base plate (2) is formed by 150D low elastic polyester filament (21) and 32 polyester-cotton blend (22) braiding.