CN1259493A - 机立窑生产超早强高标号硅酸盐水泥熟料的方法 - Google Patents

机立窑生产超早强高标号硅酸盐水泥熟料的方法 Download PDF

Info

Publication number
CN1259493A
CN1259493A CN 99109068 CN99109068A CN1259493A CN 1259493 A CN1259493 A CN 1259493A CN 99109068 CN99109068 CN 99109068 CN 99109068 A CN99109068 A CN 99109068A CN 1259493 A CN1259493 A CN 1259493A
Authority
CN
China
Prior art keywords
clinker
portland cement
early strength
machine shaft
shaft kiln
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 99109068
Other languages
English (en)
Inventor
王书煜
张兴堂
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 99109068 priority Critical patent/CN1259493A/zh
Publication of CN1259493A publication Critical patent/CN1259493A/zh
Pending legal-status Critical Current

Abstract

本发明涉及用机立窑生产超早强高标号硅酸盐水泥熟料,由石灰石65—75%,高铝粘土7—9%,粉煤灰2—5%,高炉矿渣2—5%,铁矿石1—2%,无烟煤8—11%和矿化剂2—5%,经配料、粉磨在机立窑内煅烧而成。本发明的优点在于,能够使机立窑熟料具有超早期强度和高标号,由该熟料磨制的水泥安定性合格和凝结时间正常,能大幅度提高机立窑熟料产量及掺入大量混合材料生产高标号水泥。

Description

机立窑生产超早强高标号硅酸盐水泥熟料的方法
本发明涉及机立窑生产硅酸盐水泥熟料的方法，特别是超早强高标号硅酸盐水泥熟料的生产方法。
现有机立窑水泥熟料，主要是普通硅酸盐水泥熟料，其特点是早、后期强度低，机立窑的台时产量低，烧成煤耗高，不能稳定生产高标号水泥，用机立窑熟料磨制的水泥，安定性合格率低，存放期长，混合材料掺加量少，生产成本高等不足之处。
本发明的目的是提出一种能够使机立窑硅酸盐熟料具有超高早期和后期强度的生产方法，使机立窑硅酸盐熟料能够稳定生产优质的高标号水泥，降低机立窑熟料的烧成煤耗，提高机立窑硅酸盐熟料的台时产量，确保用立窑硅酸盐熟料磨制的水泥安定性合格，并可掺入大量混合材料生产425号水泥，降低生产成本。
通过下述技术方案，可实现本发明的目的，用机立窑生产超早强高标号硅酸盐水泥熟料的原料包括：石灰石、粘土、粉煤灰、高炉矿渣、无烟煤和矿化剂(包括萤石、石膏、铅锌矿或磷渣)。其特征是(按重量百分比)石灰石65-75％、粘土6-9％、粉煤灰2-5％、高炉矿渣2-5％、铁矿石1-2％、无烟煤8-11％和矿化剂2-5％。上述物料按重量配比配料，粉磨至细度≤10％(0.08mm方孔筛)，经成球盘成出球径为3-5mm的料球后，送入机立窑内在氧化气氛和1250℃下煅烧，即可获得以C3S、C2S和C4A3s-为主要矿物的超早强高标号机立窑硅酸盐水泥熟料。
该机立窑超早强高标号硅酸盐水泥熟料的工艺流程是：将石灰石、粘土、粉煤灰、高炉矿渣、铁矿石、矿化剂、无烟煤分别烘干后，按重量配比配料，再经生料磨粉磨和成球盘成球后，分别送入机立窑内煅烧。
由本发明技术方法煅烧出的机立窑硅酸盐水泥熟料，具有超高的早强强度，三天强度可达45Mpa，二十八天强度可达71.8Mpa，安定性合格，凝结时间正常，并能提高机立窑熟料台时产量和降低烧成煤耗，可用该熟料生产高标号水泥。
本发明与现有机立窑硅酸盐熟料的生产技术相比，其优点和效果在于：
1、能够大幅度提高机立窑熟料的早、后期强度，使机立窑熟料能够稳定生产高标号水泥。
2、用该机立窑熟料磨制的水泥安定性合格，解决了长期以来机立窑熟料安定性合格率低，存放时间长，影响企业资金周转的问题。
3、用该发明技术方法可提高机立窑熟料的产量15-30％，降低烧成煤耗15-25％。
4、可掺入大量混合材料(40-65％)生产425号水泥，大幅度降低生产成本。
下面，结合实施例对本发明进一步阐述。
实施例采用的原燃材料化学成份和煤的工业分析结果示于表1、表2。
                 原燃材料化学分析结果
                         表1
                       煤的工业分析结果表2
    Mar     Mad     Aad    Vad     FCad    Qnet.ar
    9.5     0.3     22.93     6.64     70.13    23021
实施例，将上述表1和表2中的原燃材料按石灰石71.21％，高铝土8.45％，铁矿石1.42％，粉煤灰2.86％，高炉矿渣2.86，矿化剂3.22％(萤石1％、石膏2.22％)，无烟煤9.98％，通过配料并粉磨至细度合格入库均化后，物料经成球进入机立窑内煅烧而成的超早强高标号硅酸盐水泥熟料，其物理性能示于表3。
棋盘井水泥厂应用该技术方法前后结果对比表3
  凝结时间(h∶min)          抗折强度(Mpa)            抗压强度(Mpa)
初凝 终凝 三天 七天 二十八天 三天 七天 二十八天
应用该技术方法前 3∶40 5∶26 5.2 6.3 7.5 32.0 41.7 55.2
应用该技术方法后 1∶25 3∶16 6.7 7.9 9.3 45.0 56.1 71.8
本发明技术在机立窑内生产超早强高标号硅酸盐水泥熟料，必须在低煤耗氧化气氛和1250℃条件下煅烧。

Claims (4)

1、一种机立窑生产超早强高标号硅酸盐水泥熟料的方法，其特征在于原料包括石灰石65-75％，粘土6-9％，粉煤灰2-5％，高炉矿渣2-5％，铁矿石1-2％，无烟煤8-11％和矿化剂2-5％，经配料、粉磨在机立窑内煅烧而成。
2、根据权利要求1机立窑生产超早强高标号硅酸盐水泥熟料的方法，其特征是粉煤灰中Al2O3含量≥29％。
3、根据权利要求1机立窑生产超早强高标号硅酸盐水泥熟料的方法，其特征是矿化剂是萤石和石膏，萤石CaF2含量≥70％。
4、根据权利要求1机立窑生产超早强高标号硅酸盐水泥熟料的方法，其特征是高炉矿渣中的CaO≥20％，SiO2≥50％。
CN 99109068 1999-06-17 1999-06-17 机立窑生产超早强高标号硅酸盐水泥熟料的方法 Pending CN1259493A (zh)