CN1259386C - 一种玻璃防雾剂的制备方法 - Google Patents
一种玻璃防雾剂的制备方法 Download PDFInfo
- Publication number
- CN1259386C CN1259386C CN 200410068037 CN200410068037A CN1259386C CN 1259386 C CN1259386 C CN 1259386C CN 200410068037 CN200410068037 CN 200410068037 CN 200410068037 A CN200410068037 A CN 200410068037A CN 1259386 C CN1259386 C CN 1259386C
- Authority
- CN
- China
- Prior art keywords
- solution
- hours
- glass
- preparation
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种玻璃防雾剂的制备方法，以聚乙烯醇(PVA)为原料，通过对它的改性和添加负载制成效果优良的防雾剂。将聚乙烯醇(PVA)溶于热水中至室温后加入异丙醇，盐酸及乙醛，搅拌4小时后再加入重铬酸钾，再搅拌8小时后制得A溶液；将硅酸乙酯、γ-缩水甘油醚基丙基三甲氧基硅烷(KH560)、盐酸、乙醇以一定体积混合，在60℃恒温下回流6小时制得B溶液；A和B溶液静置14天后，在搅拌下，把B溶液慢慢加入到A溶液中，得C溶液的玻璃防雾剂。本发明制得的玻璃防雾剂性质稳定、防雾效果好、安全、无污染、无害、成本低。
Description
技术领域：一种玻璃防雾剂的制备方法。
背景技术：玻璃防雾剂在目前的国际、国内市场上，主要的产品有以下三种：
1.甲基丙烯酸酯—乙烯基吡咯烷酮三元共聚物，以乙二醇乙醚(ECME)为溶剂，偶氮二异丁氰(AIBN)为引发剂合成α-甲基丙烯酸缩水甘油酯/α-甲基丙烯酸p-羟基乙酯/N-乙烯基α-吡咯烷酮(GME/HEMA/NVP)三元共聚物。此种材料防雾时间长，透明效果好等特点，但其表面硬度差，易燃烧，易发生危险反应，吸入其高浓度蒸汽会导致神志不清。
2.羧基聚丙烯酸酯——乳胶型互穿网络聚合物(LIPN)涂料，具有优良防雾性能，但吸水后，漆膜破裂，不能长期使用。
3.全氟丙烯酸酯类，具有良好的防水、防油性，化学惰性、耐候性、抗污性，有较好的耐热性、耐擦伤性，耐酸，硬度好。透明性亦好，抗紫外线。此类产品效果较好，但由于安全原因和其昂贵的价格，目前已经停产。
发明内容：本发明的目的在于提供一种防雾效果好、性质稳定、安全、无污染、生产简单、成本上有很大优势的玻璃防雾剂的制备方法。
本发明的玻璃防雾剂以聚乙烯醇(PVA)为原料，通过对它的改性和添加负载制成的玻璃防雾剂能使玻璃表面附着的水滴迅速扩散成均匀的水膜，表面不会产生会发生光散射的雾，可维持高度的透明性，不燃烧，使用安全。
本发明一种玻璃防雾剂的制备方法如下：
(1)A溶液的制备：将9-11g聚乙烯醇溶于350ml热水中，加热搅拌至全部溶解，然后冷却至室温后加入50ml异丙醇，10ml浓度为3mol/L盐酸及0.4-1ml质量百分浓度为40％的乙醛，搅拌4小时后再加入4-12mg重铬酸钾，搅拌8小时后制得A溶液；
(2)B溶液的制备：将8ml硅酸乙酯、8ml γ-缩水甘油醚基丙基三甲氧基
硅烷、0.8-1.6ml浓度为3mol/L盐酸、8-16ml乙醇混合，在60℃恒温下搅拌回流6小时制得B溶液；
(3)C溶液的制备：将A和B溶液静置14天后，在搅拌下，把0.1-0.6ml B溶液慢慢加入到50ml A溶液中，得到C溶液的玻璃防雾剂。
A溶液的制备是对聚乙烯醇的改性，经改性后的聚乙烯醇具有良好的耐水性和耐擦性，B溶液是为了制备黏结聚乙烯醇与玻璃表面的负载。
本发明的产品与现有产品相比具有如下优点：
1.本发明的产品的性能优于甲基丙烯酸酯——乙烯基吡咯烷酮与羧基聚丙烯酸酯——乳胶型互穿网络聚合物(LIPN)涂料，前者存在表面硬度差、易燃烧、易老化等缺点，后者吸水，漆膜破裂，不能长期使用。而本发明产品性质稳定，具有足够的表面强度。
2.本发明的产品清洁无害，绝不会对人畜造成任何伤害，而甲基丙烯酸酯——乙烯基吡咯烷酮及全氟丙烯酸酯类产品的化学活性大，故其毒性也较大，在安全性能上无法替代本发明的产品，而且价格远高于本发明的产品。
3.本发明的产品使用简单，防雾效果好，且持续有效时间长达半年以上。
4.本发明的产品制作工艺简单，对环境无污染，在成本上也有很大的优势，目前市售防雾剂的价格大致在200元/平方米的水平，而本发明的产品其价格将远低于此。
具体实施方式：
实施例1：
将10g聚乙烯醇(PVA)溶于350ml热水中，加热搅拌至全部溶解，然后冷却至室温后加入50ml异丙醇，10ml盐酸(3mol/L)及0.6ml质量百分浓度为40％的乙醛，搅拌4小时后再加入重铬酸钾10mg，搅拌8小时后制得A溶液；将8ml硅酸乙酯、8ml γ-缩水甘油醚基丙基三甲氧基硅烷(KH560)、1.3ml盐酸(3mol/L)、10ml乙醇混合，在60℃恒温下回流6小时制得B溶液；将A和B溶液静置14天后，在搅拌下，把0.4ml B溶液慢慢加入到50ml A溶液中，得到C溶液的玻璃防雾剂。将玻璃洗净后，涂上C溶液，经吹干后，把该玻璃放在冰箱冷冻若干分钟后取出，观察此玻璃具有良好的防雾效果，能持续半年有效。用抹布擦和水冲洗对涂层均无影响。
实施例2：
将10g聚乙烯醇(PVA)溶于350ml热水中，加热搅拌至全部溶解，然后冷却至室温后加入50ml异丙醇，10ml盐酸(3mol/L)及0.8ml质量百分浓度为40％的乙醛，搅拌4小时后再加入重铬酸钾6mg，搅拌8小时后制得A溶液；将8ml硅酸乙酯、8mlγ-缩水甘油醚基丙基三甲氧基硅烷(KH560)、1.3ml盐酸(3mol/L)、10ml乙醇混合，在60℃恒温下回流6小时制得B溶液；将A和B溶液静置14天后，在搅拌下，把0.4ml B溶液慢慢加入到50ml A溶液中，得到C溶液的玻璃防雾剂。将玻璃洗净后，涂上C溶液，经吹干后，把该玻璃放在冰箱冷冻若干分钟后取出，观察此玻璃具有良好的防雾效果，能持续半年有效。用抹布擦和水冲洗对涂层均无影响。
实施例3：
将10g聚乙烯醇(PVA)溶于350ml热水中，加热搅拌至全部溶解，然后冷却至室温后加入50ml异丙醇，10ml盐酸(3mol/L)及0.7ml质量百分浓度为40％的乙醛，搅拌4小时后再加入重铬酸钾8mg，搅拌8小时后制得A溶液；将8ml硅酸乙酯、8mlγ-缩水甘油醚基丙基三甲氧基硅烷(KH560)、1.3ml盐酸(3mol/L)、10ml乙醇混合，在60℃恒温下回流6小时制得B溶液；将A和B溶液静置14天后，在搅拌下，把0.4ml B溶液慢慢加入到50ml A溶液中，得到C溶液的玻璃防雾剂。将玻璃洗净后，涂上C溶液，经吹干后，把该玻璃放在冰箱冷冻若干分钟后取出，观察此玻璃具有良好的防雾效果，能持续半年有效。用抹布擦和水冲洗对涂层均无影响。
Claims (1)
1.一种玻璃防雾剂的制备方法，其特征在于制备方法如下：
(1)A溶液的制备：将9-11g聚乙烯醇溶于350ml热水中，加热搅拌至全部溶解，然后冷却至室温后加入50ml异丙醇，10ml浓度为3mol/L盐酸及0.4-1m1质量百分浓度为40％的乙醛，搅拌4小时后再加入4-12mg重铬酸钾，搅拌8小时后制得A溶液；
(2)B溶液的制备：将8ml硅酸乙酯、8ml γ-缩水甘油醚基丙基三甲氧基硅烷、0.8-1.6ml浓度为3mol/L盐酸、8-16ml乙醇混合，在60℃恒温下搅拌回流6小时制得B溶液。
(3)C溶液的制备：将A和B溶液静置14天后，在搅拌下，把0.1-0.6mlB溶液慢慢加入到50ml A溶液中，得到C溶液的玻璃防雾剂。