CN101666058B - 军用瓦楞纸箱防潮油剂的制备方法 - Google Patents

军用瓦楞纸箱防潮油剂的制备方法 Download PDF

Info

Publication number
CN101666058B
CN101666058B CN2009100754775A CN200910075477A CN101666058B CN 101666058 B CN101666058 B CN 101666058B CN 2009100754775 A CN2009100754775 A CN 2009100754775A CN 200910075477 A CN200910075477 A CN 200910075477A CN 101666058 B CN101666058 B CN 101666058B
Authority
CN
China
Prior art keywords
parts
add
stirring
warm water
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100754775A
Other languages
English (en)
Other versions
CN101666058A (zh
Inventor
刘振刚
齐香玲
李玉芬
宋建勋
王才宁
刘宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jihua 3502 Professional Garment Co Ltd
Original Assignee
Jihua 3502 Professional Garment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jihua 3502 Professional Garment Co Ltd filed Critical Jihua 3502 Professional Garment Co Ltd
Priority to CN2009100754775A priority Critical patent/CN101666058B/zh
Publication of CN101666058A publication Critical patent/CN101666058A/zh
Application granted granted Critical
Publication of CN101666058B publication Critical patent/CN101666058B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种军用瓦楞纸箱防潮油剂的制备方法,在容器内加水15份,加热沸腾后放入火碱1.3-1.5份,搅拌后加入硬脂酸1.2-1.4份,搅拌,使硬脂酸全部融化后加入松香5.5-6份,搅拌,使松香溶化的同时持续均匀加入40-50℃温水20份,然后再加入石蜡11-12份,搅拌使石蜡溶化后,再加入氧化聚乙烯蜡11-12份,搅拌溶化后继续加热并连续搅拌成粘稠状,同时加入40-50℃温水20份,继续加热搅拌雾化成粘稠状,再加入40-50℃温水20份,沸腾后呈粘稠状,继续加入40-50℃温水70份,均匀搅拌,过滤即制成。本发明涂刷在瓦楞纸箱外表四周,使箱体表面光亮透明、柔韧,且涂膜不溶于水,具有良好的抗水防潮效果。

Description

军用瓦楞纸箱防潮油剂的制备方法
技术领域
本发明涉及一种军用瓦楞纸箱防潮油剂的制备方法。
背景技术
军用瓦楞纸箱运输路途较远、仓储周期较长,其质量标准(国军标)高于普通瓦楞纸箱,其中,箱体外部四周需要涂刷一种防雨、防热、防潮、防霉变的油剂,而一般的防潮油剂存在着干燥速度慢、易粘连、干后易掉色,对纸箱油墨有影响,防潮效果差等弊病。
发明内容
本发明所要解决的技术问题是提供一种防雨、防热、防潮、防霉变效果好、适于远途运输和长时间储存的军用瓦楞纸箱防潮油剂的制备方法。
本发明采用如下技术方案:
本发明采用如下重量份数比组份:纯火碱1.3-1.5份、硬脂酸1.2--1.4份、松香5.5-6份、石蜡11-12份、氧化聚乙烯蜡11-12份、自来水15份、40-50℃温水130份,制备方法如下:在容器内加水15份,加热沸腾后,放入火碱1.3--1.5份,搅拌5--8分钟后加入硬脂酸1.2--1.4份,搅拌,使硬脂酸全部融化后加入松香5.5--6份,搅拌,使松香溶化的同时持续均匀加入40--50℃温水20份,然后再加入石蜡11-12份,搅拌使石蜡溶化后,再加入氧化聚乙烯蜡11-12份,搅拌溶化后继续加热并连续搅拌成粘稠状,同时加入40--50℃温水20份,继续加热搅拌雾化成粘稠状,再加入40--50℃温水20份,沸腾后呈粘稠状,继续加入40--50℃温水70份,均匀搅拌8-10分钟,关闭热源或压火降温,用过滤网过滤即制成。
本发明的有益效果:
本发明外观呈棕黄色黏稠状液体,无毒、无刺激性气味。固含量:20%~30%黏度(涂3-4杯/秒,25℃);干燥时间:6-8分钟;PH值:8.5-9,550±30秒。乳化剂与不溶于水的石蜡、氧化聚乙烯等树脂乳化后,将其乳液涂刷在瓦楞纸箱外表四周,使箱体表面光亮透明、柔韧。具有良好的上光作用,且涂膜不溶于水,具有良好的抗水防潮效果。
本发明军用瓦楞纸箱防潮油剂,克服了原有防油油剂产品存在的干燥速度慢、易粘连、干后易掉色、对纸箱油墨有影响以及防潮效果差等弊病。本发明防潮油剂不含有机溶剂,不易燃易爆、无毒、无刺激性气味、无腐蚀性,适用于任何瓦楞纸箱产品的防潮和上光,可以人工手刷,也可以机制涂刷一次完成。经本发明防潮油剂涂刷后的瓦楞纸箱,表面能抗划痕,箱体耐磨性增强,同时,增加了油墨的耐光性和箱体防热、防潮能力以及耐力强度,对纸箱起到美化及长期保护的作用。经军事代表检验检测,各项性能达标,验收合格并已经广泛大批量用于各种规格的军用瓦楞纸箱包装物品中。
具体实施方式
一、本发明加工防潮油剂制备所需设备:加热蒸汽罐和大口径不锈钢锅灶、不锈钢过滤网、搅拌用具。
二、主要原材料:纯火碱(NaOH)、硬脂酸(即十八烷酸、十八碳烷酸,分子式:C18H3602.)、松香(微黄色至黄色的透明固体)、石蜡(分子式:CxHy)、氧化聚乙烯蜡(淡黄色粉末状,分子式:(C2H4)n.)。
三、主要原材料的配比:
采用如下重量份数比组份:纯火碱1.3-1.5份、硬脂酸1.2--1.4份、松香5.5-6份、石蜡11-12份、氧化聚乙烯蜡11-12份、自来水15份、40-50℃温水130份。
四、生产工艺流程
水→烧碱溶液→硬脂酸(沸腾)→松香(溶化开)→加水(沸腾)→石蜡(溶化开)→氧化聚乙烯蜡(呈粘稠状)→加水→氧化聚乙烯蜡(呈粘稠状)→加水→氧化聚乙烯蜡(呈粘稠状)→加水→关闭蒸汽热源(火源)→降温过滤→成品。
五、加工方法步骤:
第一步:在大口径不锈钢锅容器内加水15份,用蒸汽罐或者火源加热沸腾后,放入火碱1.3--1.5份,不停地均匀搅拌,搅拌时间为5--8分钟;
第二步:加入硬脂酸1.2--1.4份,不断均匀搅拌10分钟,使硬脂酸全部融化;
第三步:加入松香5.5-6份,继续均匀搅拌10分钟使其溶化,同时持续均匀加入40-50℃温水20份;
第四步:加入石蜡11-12份,继续搅拌使其溶化,时间约5-6分钟;
第五步:加入氧化聚乙烯蜡11-12份,连续搅拌溶化开后,继续加热形成粘稠状,同时加入40--50℃温水20份,继续加热搅拌雾化成粘稠状,再加40--50℃温水20份,沸腾后呈粘稠状,继续加入40--50℃温水70份,均匀搅拌8-10分钟,关闭热源或压火降温,用过滤网过滤,盛入专门的容器中。成品在18-25℃时使用最佳。
实施例1:
本发明采用如下重量份数比组份:纯火碱1.3份、硬脂酸1.2份、松香6份、石蜡12份、氧化聚乙烯蜡11份、自来水15份、40℃温水130份,制备方法如下:在容器内加水15份,加热沸腾后,放入火碱1.5份,搅拌5分钟后加入硬脂酸1.2份,搅拌,使硬脂酸全部融化后加入松香5.5份,搅拌,使松香溶化的同时持续均匀加入50℃温水20份,然后再加入石蜡11份,搅拌使石蜡溶化后,再加入氧化聚乙烯蜡11份,搅拌溶化后继续加热并连续搅拌成粘稠状,同时加入40℃温水20份,继续加热搅拌雾化成粘稠状,再加入40-℃温水20份,沸腾后呈粘稠状,继续加入40℃温水70份,均匀搅拌8分钟,关闭热源或压火降温,用过滤网过滤即制成。
实施例2:
本发明采用如下重量份数比组份:纯火碱1.5份、硬脂酸1.3份、松香5.5份、石蜡11份、氧化聚乙烯蜡11.5份、自来水15份、45℃温水130份,制备方法如下:在容器内加水15份,加热沸腾后,放入火碱1.3份,搅拌7分钟后加入硬脂酸1.4份,搅拌,使硬脂酸全部融化后加入松香5.7份,搅拌,使松香溶化的同时持续均匀加入40℃温水20份,然后再加入石蜡12份,搅拌使石蜡溶化后,再加入氧化聚乙烯蜡12份,搅拌溶化后继续加热并连续搅拌成粘稠状,同时加入45℃温水20份,继续加热搅拌雾化成粘稠状,再加入45℃温水20份,沸腾后呈粘稠状,继续加入45℃温水70份,均匀搅拌9分钟,关闭热源或压火降温,用过滤网过滤即制成。
实施例3:
本发明采用如下重量份数比组份:纯火碱1.4份、硬脂酸1.4份、松香5.7份、石蜡11.5份、氧化聚乙烯蜡12份、自来水15份、50℃温水130份,制备方法如下:在容器内加水15份,加热沸腾后,放入火碱1.4份,搅拌8分钟后加入硬脂酸1.3份,搅拌,使硬脂酸全部融化后加入松香6份,搅拌,使松香溶化的同时持续均匀加入45℃温水20份,然后再加入石蜡11.5份,搅拌使石蜡溶化后,再加入氧化聚乙烯蜡11.5份,搅拌溶化后继续加热并连续搅拌成粘稠状,同时加入50℃温水20份,继续加热搅拌雾化成粘稠状,再加入50℃温水20份,沸腾后呈粘稠状,继续加入50℃温水70份,均匀搅拌10分钟,关闭热源或压火降温,用过滤网过滤即制成。

Claims (1)

1.一种军用瓦楞纸箱防潮油剂的制备方法,其特征在于采用如下重量份数比组份:纯火碱1.3-1.5份、硬脂酸1.2--1.4份、松香5.5-6份、石蜡11-12份、氧化聚乙烯蜡11-12份、自来水15份、40-50℃温水130份,制备方法如下:在容器内加水15份,加热沸腾后,放入火碱1.3--1.5份,搅拌5--8分钟后加入硬脂酸1.2--1.4份,搅拌,使硬脂酸全部融化后加入松香5.5-6份,搅拌,使松香溶化的同时持续均匀加入40--50℃温水20份,然后再加入石蜡11-12份,搅拌使石蜡溶化后,再加入氧化聚乙烯蜡11-12份,搅拌溶化后继续加热并连续搅拌成粘稠状,同时加入40--50℃温水20份,继续加热搅拌雾化成粘稠状,再加入40--50℃温水20份,沸腾后呈粘稠状,继续加入40--50℃温水70份,均匀搅拌8-10分钟,关闭热源或压火降温,用过滤网过滤即制成。
CN2009100754775A 2009-09-23 2009-09-23 军用瓦楞纸箱防潮油剂的制备方法 Expired - Fee Related CN101666058B (zh)