CN1238296C - 聚苯乙烯泡沫颗粒保温砂浆 - Google Patents

聚苯乙烯泡沫颗粒保温砂浆 Download PDF

Info

Publication number
CN1238296C
CN1238296C CNB200410053031XA CN200410053031A CN1238296C CN 1238296 C CN1238296 C CN 1238296C CN B200410053031X A CNB200410053031X A CN B200410053031XA CN 200410053031 A CN200410053031 A CN 200410053031A CN 1238296 C CN1238296 C CN 1238296C
Authority
CN
China
Prior art keywords
insulation mortar
polystyrene foam
heat insulation
foam particle
particle heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB200410053031XA
Other languages
English (en)
Other versions
CN1587181A (zh
Inventor
陈兵
陈龙珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jiaotong University
Original Assignee
Shanghai Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jiaotong University filed Critical Shanghai Jiaotong University
Priority to CNB200410053031XA priority Critical patent/CN1238296C/zh
Publication of CN1587181A publication Critical patent/CN1587181A/zh
Application granted granted Critical
Publication of CN1238296C publication Critical patent/CN1238296C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种聚苯乙烯泡沫颗粒保温砂浆，用于建筑材料工程技术领域。其各组分及其重量百分比为：硅酸盐水泥40～45%，粉煤灰3～6%，微硅粉0～3%，聚苯乙烯泡沫颗粒1.3～2.8%，聚丙烯纤维0.1～0.2%，石英砂42～47%，硅氧烷乳液5～8%。本发明容重轻，干燥密度为300～480kg/m3；保温隔音性能好，导热系数为0.07～0.13W/m·k；在原材料中采用粉煤灰部分取代水泥，为废物利用，可减少对环境的污染，此外减少水泥用量，节省能源；物理性能稳定，不开裂、不空鼓，抗老化，使用寿命长，由于该产品加水就可应用，因此使用方便，可实现文明施工；粘结性能好，与墙面和楼板粘结牢固；产品无毒、无味，对人体无害，不污染环境，属于环保型保温节能材料。

Description

聚苯乙烯泡沫颗粒保温砂浆
技术领域
本发明涉及一种建筑砂浆，具体是一种聚苯乙烯泡沫颗粒保温砂浆。用于建筑材料工程技术领域。
背景技术
目前，国家正在大力发展提倡环保、节能建筑结构。实施建筑节能必须大幅度提高外围护结构，尤其是外墙的热工性能。但是，短期内要在我国长江流域和南方地区普遍采用复合节能墙体材料是不现实的。而且，用于砌筑这些保温轻质墙体材料大都采用普通水泥或混合砌筑砂浆，这类砂浆的表观密度一般为1600～1 800kg/m3，导热系数为0.8～1.0W/(m·K)，而轻质保温砌块的表观密度一般为450～950kg/m3，导热系数为0.15W～0.35W/(m·K)，由于两者导热系数差距较大，致使整个砌体存在“冷桥”现象，由砌筑灰缝引起的能量损失达到25％左右，严重影响建筑节能效果。因此，发展具有保温绝热节能功能型的抹面和砌筑砂浆显得十分必要。
经对现有技术的文献检索发现，伊立在《粉煤灰》第4期2002，P12-15撰文《高性能粉煤灰复合保温砂浆的研制》，该文提出采用掺加漂珠和膨胀珍珠岩对砂浆进行改性，达到保温隔热效果。研究结果表明这种保温砂浆保温效果较好，其导热系数达到0.1742W/m·k。但该文提出的复合保温砂浆价格偏高，施工复杂，而且很难解决施工后发生的裂缝、空鼓等问题。在功能上比较单一，无法满足现代建筑对保温砂浆其它建筑性能的要求，如隔音、环保和轻质等。
发明内容
本发明的目的在于针对现有技术中的不足和缺陷，提供一种聚苯乙烯泡沫颗粒保温砂浆，使其具有导热系数低、容重轻、不开裂、不空鼓、保温、隔音效果好、节省能源、生产成本低、无毒无污染、便于施工的绝热、隔音等特点。
本发明是通过以下技术方案实现的，本发明各组分及其重量百分比为：
硅酸盐水泥          40～45％
粉煤灰                   3～6％
微硅粉                   0～3％
聚苯乙烯泡沫颗粒         1.4～2.8％
聚丙烯纤维               0.1～0.2％
石英砂                   42～47％
硅氧烷乳液(固含量)       5～8％
本发明由聚苯乙烯泡沫颗粒、硅酸盐水泥、粉煤灰、微硅粉、硅氧烷乳液，聚丙烯纤维和石英砂按一定比例混合均匀袋装而成。主要是利用硅氧烷乳液首先对聚苯乙烯泡沫颗粒表面进行改性，提高其与水泥浆体界面粘结强度，同时采用微硅粉和粉煤灰部分取代水泥以改善砂浆拌和物的流动性和保水性。为防止砂浆抹面后出现开裂和空鼓，在砂浆拌和物中掺入一定体积含量的微细聚丙烯纤维。它既有较高的粘结强度，又有广的施工适应性，同时由于掺有聚苯乙烯泡沫颗粒，从而达到保温、隔音、隔热等多种功能。
本发明采用的原材料：水泥宜选用42.5强度等级的硅酸盐水泥，粉煤灰宜选用II级粉煤灰；石英砂细度控制在20～50目，聚苯乙烯泡沫颗粒粒径选为1.5～3.0mm，聚丙烯纤维长度宜控制为5～15mm，直径为30～50um。各组分的自由水分含量控制在0.5％以下。
按配方比例称取各种原材料，首先将硅氧烷乳液加入聚苯乙烯泡沫颗粒，搅拌均匀，将该混合物烘干，然后加入微硅粉、硅酸盐水泥、粉煤灰、石英砂和聚丙烯纤维进行充分搅拌均匀形成产品，进行装袋。
本发明与其它保温材料相比优点在于：容重轻，干燥密度为300～480kg/m3；保温隔音性能好，导热系数为0.07～0.13W/m·k；在原材料中采用粉煤灰部分取代水泥，为废物利用，可减少对环境的污染，此外减少水泥用量，节省能源；物理性能稳定，不开裂、不空鼓，抗老化，使用寿命长，由于该产品加水就可应用，因此使用方便，可实现文明施工；粘结性能好，与墙面和楼板粘结牢固；产品无毒、无味，对人体无害，不污染环境，属于环保型保温节能材料。
具体实施方式
以下结合本发明内容提供以下实施例：
聚苯乙烯泡沫颗粒保温砂浆，按配方比例称取各种原材料，首先将硅氧烷乳液加入聚苯乙烯泡沫颗粒，搅拌均匀，将该混合物烘干，然后加入微硅粉、硅酸盐水泥、粉煤灰、石英砂和聚丙烯纤维进行充分搅拌均匀形成产品，进行装袋。根据工程应用需要，通过调整发明配方，可以获得所需要的性能。在具体实施过程中，各组分重量百分比为：
上述组分按前述工艺制备得聚苯乙烯泡沫颗粒保温砂浆干粉，加入适量水，使砂浆拌和物稠度达到80mm，按标准要求成型试样。砂浆的稠度、分层度、容重、抗压强度按JGJ 70-90《建筑砂浆基本性能的测试方法》进行；砂浆的粘结强度参照JGJ 110-98《建筑工程饰面砖粘结强度检验标准进行》，砂浆的导热系数参照JGJ51-90《轻集料混凝土技术规程》测定，试件自然养护28d，烘干至恒重，用热脉冲法测量导热系数装置进行测定。其测试参数性能指标见下表。
                    聚苯乙烯泡沫颗粒保温砂浆性能
实施例   稠度(mm)   分层度(mm)   干容重(kg/m3)   导热系数(W/m·k)   抗压强度(MPa)   粘结强度(MPa)
 实施例1   82.0   100   450   0.103   7.5   1.2
 实施例2   80.0   105   350   0.095   5.0   1.4
 实施例3   82.0   110   480   0.115   7.0   1.1
 实施例4   80.0   105   360   0.090   5.5   1.5

Claims (7)

1、一种聚苯乙烯泡沫颗粒保温砂浆，其特征在于，各组分及其重量百分比为：
硅酸盐水泥                        40～45％
粉煤灰                            3～6％
微硅粉                            0～3％
聚苯乙烯泡沫颗粒                  1.4～2.8％
聚丙烯纤维                        0.1～0.2％
石英砂                            42～47％
硅氧烷乳液                        5～8％。
2、权利要求1所述的聚苯乙烯泡沫颗粒保温砂浆，其特征是，所述的石英砂细度控制在20～50目。
3、权利要求1所述的聚苯乙烯泡沫颗粒保温砂浆，其特征是，所述的聚苯乙烯泡沫颗粒粒径为1.5～3.0mm。
4、权利要求1所述的聚苯乙烯泡沫颗粒保温砂浆，其特征是，所述的聚丙烯纤维长度为5～15mm，直径为30～50um。
5、权利要求1所述的聚苯乙烯泡沫颗粒保温砂浆，其特征是，所述的硅酸盐水泥选用42.5强度等级的硅酸盐水泥。
6、权利要求1所述的聚苯乙烯泡沫颗粒保温砂浆，其特征是，所述的粉煤灰选用II级粉煤灰。
7、权利要求1所述的聚苯乙烯泡沫颗粒保温砂浆，其特征是，各组分的自由水分含量控制在0.5％以下。
CNB200410053031XA 2004-07-22 2004-07-22 聚苯乙烯泡沫颗粒保温砂浆 Expired - Fee Related CN1238296C (zh)