CN1225908A - 一种β-萘磺酸甲醛缩合物季铵盐型混凝土外加剂 - Google Patents
一种β-萘磺酸甲醛缩合物季铵盐型混凝土外加剂 Download PDFInfo
- Publication number
- CN1225908A CN1225908A CN 99116049 CN99116049A CN1225908A CN 1225908 A CN1225908 A CN 1225908A CN 99116049 CN99116049 CN 99116049 CN 99116049 A CN99116049 A CN 99116049A CN 1225908 A CN1225908 A CN 1225908A
- Authority
- CN
- China
- Prior art keywords
- beta
- naphthalenesulfonic
- formaldehyde condensation
- acid formaldehyde
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种萘磺酸甲醛缩合物季铵盐型水泥混凝土聚合物添加剂。在水泥混凝土中掺入少量外加剂便可显著改善水泥混凝土的力学性能、工作性能和耐久性能,从而满足不同工程对水泥混凝土的特殊要求。为此,研制性能优异的水泥混凝上外加剂一直是国内外研究的热点。本发明采用离子交换手段制备了六种不同季铵阳离子对应的β-萘磺酸甲醛缩合物盐。它们作为水泥混凝土添加剂,具有显著的分散能力和减水增强早强功能。
Description
本发明涉及一种β-萘磺酸甲醛缩合物季铵盐型混凝土外加剂。
聚合物添加剂在水泥混凝土材料中占有重要地位,只要掺入少量这类添加剂就可显著提高混凝土材料的力学强度、工作性能和耐久性能。因而可以实现机械化施工,满足不同工程对水泥混凝上的特殊要求。国内外常见的水泥混凝土聚合物添加剂主要有如下几类:(1)木质素磺酸盐及其衍生物;(2)萘磺酸甲醛缩合物;(3)多环芳烃磺酸盐甲醛缩合物;(4)聚氧乙烯醚及其衍生物;(5)三聚氰胺磺酸盐甲醛缩合物;(6)丙烯酸及其衍生物的均聚物或共聚物;(7)马来酸盐及其衍生物的均聚物或共聚物。随着国内外经济的发展,现代建筑业对水泥混凝土材料的要求越来越高,因此研制新型高性能水泥混凝土添加剂一直是世界各国在本研究领域的热门课题。
M=CH3N+(C2H5)3,CH3N+(CH2CH2OH)3,CH3N+(n-C4H9)3,
C6H5CH2N+(CH2CH3)3,(CH3)3N+CH2CH2N+(CH3)3,CH3(CH2)15N+(CH3)3化学结构式中的M有六种不同型式,因型式不同而有不同的分子量:M为CH3N+(C2H5)3时,分子量为1663~4343;M为CH3N+(CH2CH2OH)3时,分子量为1903~4967;M为CH3N+(n-C4H9)3时,分子量为2083~5435;M为C6H5CH2N+(CH2CH3)3时,分子量为2043~5331;M为(CH3)3N+CH2CH2N+(CH3)3时,分子量为1451~3795;M为CH3(CH2)15N+(CH3)3时,分子量为2503~6527。M的不同型式就形成了六种不同化学结构的β-萘磺酸甲醛缩合物季铵盐混凝土外加剂,它们是以萘磺酸甲醛缩合物钠盐为原料,通过离子交换方法制备的,本发明所提供的混凝土外加剂使用效果见表1:
表1六种β-萘磺酸甲醛缩合物季铵盐对水泥的性能影响
样品号 | 掺量(%) | 水泥净浆流动度(mm) | 水泥净浆抗压强度(MPa) | ||||
水灰比 | 流动度 | 水灰比 | 3d | 7d | 28d | ||
空白 | 0 | 0.35 | 163 | 0.4 | 16.7 | 31.1 | 45.3 |
A | 0.25 | 0.35 | 206 | 0.32 | 44.4 | 53.6 | 75.5 |
0.75 | 0.35 | 227 | 0.29 | 50.3 | 55.8 | 87.4 | |
B | 0.25 | 0.35 | 194 | 0.32 | 47.8 | 58.4 | 83.3 |
0.75 | 0.35 | 190 | 0.29 | 43.0 | 62.1 | 85.3 | |
C | 0.25 | 0.35 | 220 | 0.32 | 53.8 | 61.3 | 76.9 |
0.75 | 0.35 | 265 | 0.29 | 52.9 | 70.9 | 80.8 | |
D | 0.25 | 0.35 | 188 | 0.32 | 42.1 | 51.4 | 74.8 |
0.75 | 0.35 | 190 | 0.29 | 37.6 | 49.5 | 76.2 | |
E | 0.25 | 0.35 | 206 | 0.32 | 56.7 | 66.6 | 80.0 |
0.75 | 0.35 | 275 | 0.29 | 62.9 | 72.1 | 93.1 | |
F | 0.25 | 0.35 | 223 | 0.32 | 52.2 | 57.5 | 76.6 |
0.75 | 0.35 | 290 | 0.29 | 60.1 | 71.4 | 90.0 |
注1:上表中掺量为添加剂占水泥重量的百分比
注2:A:β-萘磺酸甲醛缩合物CH3N+(C2H5)3盐
B:β-萘磺酸甲醛缩合物CH3N+(n-C4H9)3盐
C:β-萘磺酸甲醛缩合物CH3N+(CH2CH2OH)3盐
D:β-萘磺酸甲醛缩合物C6H5CH2N+(CH2CHO3)3盐
E:β-萘磺酸甲醛缩合物(CH3)3N+CH2CH2N+(CH3)3盐
F:β-萘磺酸甲醛缩合物CH3(CH2)15N+(CH3)3盐
水泥净浆流动度按照JGJ56-84中所示的方法测定;水泥净浆固结体抗压强度按照GB119-88所示方法测定。
从表中数据可以看出,本发明提供的六种不同化学结构的季铵附离子型β-萘磺酸甲醛缩合物作为水泥添加剂能明显提高水泥净浆的流动性能和抗压强度,另外还具有早强功能。
实施例1.
掺入占水泥量0.25%的萘磺酸甲醛缩合物CH3N+(C2H5)3盐,水灰比为0.35的水泥净浆流动度达206mm,水灰比为0.32的水泥净浆28d抗压强度达75.5Mpa,与空白水泥净浆28d抗压强度45.3MPa相比,提高了66.7%。
实施例2.
掺入占水泥量0.25%的萘磺酸甲醛缩合物CH3N+(n-C4H9)3盐,水灰比为0.35的水泥净浆流动度达194mm,水灰比为0.32的水泥净浆28d抗压强度达83.3MPa,与空白水泥净浆28d抗压强度45.3MPa相比,提高了83.9%。
实施例3.
掺入占水泥量0.25%的萘磺酸甲醛缩合物CH3N+(CH2CH2OH)3盐,水灰比为0.35的水泥净浆流动度达220mm,水灰比为0.32的水泥净浆28d抗压强度达76.9MPa,与空白水泥净浆28d抗压强度45.3MPa相比,提高了69.8%。
实施例4.
掺入占水泥量0.25%的萘磺酸甲醛缩合物C6H5CH2N+(CH2CH3)3盐,水灰比为0.35的水泥净浆流动度达188mm,水灰比为0.32的水泥净浆28d抗压强度达74.8MPa,与空白水泥净浆28d抗压强度45.3MPa相比,提高了65.1%。
实施例5.
掺入占水泥量0.25%的萘磺酸甲醛缩合物(CH3)3N+CH2CH2N+(CH3)3盐,水灰比为0.35的水泥净浆流动度达206mm,水灰比为0.32的水泥净浆28d抗压强度达80.0MPa,与空白水泥净浆28d抗压强度45.3MPa相比,提高了76.6%。
实施例6.
掺入占水泥量0.25%的萘磺酸甲醛缩合物CH3(CH2)15N+(CH3)3盐,水灰比为0.35的水泥净浆流动度达223mm,水灰比为0.32的水泥净浆28d抗压强度达76.6MPa,与空白水泥净浆28d抗压强度45.3MPa相比,提高了69.1%。
Claims (2)
1.一种β-萘磺酸甲醛缩合物季铵盐型混凝土外加剂,以β-萘磺酸甲醛缩合物钠盐为原料,通过离子交换方法制备,其特征在于它们的组成包括如下的阳离子:CH3N+(C2H5)3,CH3N+(CH2CH2OH)3,CH3N+(n-C4H9)3,C6H5CH2N+(CH2CH3)3,(CH3)3N+CH2CH2N+(CH3)3,CH3(CH2)15N+(CH3)3,其化学结构式为:聚合度n=5~13式中M分别为CH3N+(CH2CH2OH)3,C6H5CH2N+(CH2CH3)3,(CH3)3NCH2CH2N+(CH3)3,CH3(CH2)15N+(CH3)3,CH3N+(C2H5)3。CH3N+(n-C4H9)3
2.根据权利要求书1中所述的外加剂,其特征在于结构式中M有六种型式,因型式不同而有不同的分子量:
M为CH3N+(C2H5)3时,分子量为1663~4343;
M为CH3N+(CH2CH2OH)3时,分子量为1903~4967;
M为CH3N+(n-C4H9)3时,分子量为2083~5435;
M为C6H5CH2N+(CH2CH3)3时,分子量为2043~5331;
M为(CH3)3N+CH2CH2N+(CH3)3时,分子量为1451~2795;
M为CH3(CH2)15N+(CH3)3时,分子量为2503~6527。