CN1222441A - 超高分子量聚乙烯托辊制造工艺 - Google Patents
超高分子量聚乙烯托辊制造工艺 Download PDFInfo
- Publication number
- CN1222441A CN1222441A CN 98122155 CN98122155A CN1222441A CN 1222441 A CN1222441 A CN 1222441A CN 98122155 CN98122155 CN 98122155 CN 98122155 A CN98122155 A CN 98122155A CN 1222441 A CN1222441 A CN 1222441A
- Authority
- CN
- China
- Prior art keywords
- molecular weight
- weight polyethylene
- polypropylene
- idler
- superhigh molecular
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
超高分子量聚乙烯托辊制造工艺,将玻璃纤维和偶联剂在加热式混料机内混合,然后把聚丙烯粉加入已偶联的玻璃纤维中,把搅拌好的料放入注塑机中制成聚丙烯内套辊体2;将玻璃纤维和偶聚剂在加热式混料机内混合,再加入超高分子量聚乙烯,把搅拌好的料放入模具中制成超高分子量聚乙烯外套1;最后将上述内套辊体2和外套1以过盈配合装在一起制成超高分子量聚乙烯托辊。
Description
本发明涉及超高分子量聚乙烯托辊制造工艺技术领域。
目前在冶金、矿山、煤矿、港口、建材和化工等领域的固体物料输送中使用的铸石托辊虽然耐磨性较好，但强度差，不耐冲击，易粘辊，使用寿命短。
本发明的目的是发明一种超高分子量聚乙烯托辊制造工艺，由该工艺制成的托辊其内套辊体为聚丙烯材料，外套为超高分子量聚乙烯材料使该托辊各项性能指标大大提高。
本发明是这样实现的：将玻璃纤维和偶联剂在加热式混料机内混合，然后把聚丙烯粉加入已偶联的玻璃纤维中，把搅拌好的料放入注塑机中注塑成型为聚丙烯内套辊体2；将玻璃纤维和偶联剂在加热式混料机内混合，然后再加入超高分子量聚乙烯、脱模剂和炭黑继续搅拌，把搅拌好的料称重放入模具中加温，在一定压力下保压直至冷却到室温出模制成超高分子量聚乙烯外套1；把聚丙烯内套辊体2和超高分子量聚乙烯外套1接触面涂上粘合剂以过盈配合装在一起制成超高分子量聚乙烯托辊。
本发明的优点是：制造工艺简单，由该工艺制成的托辊耐磨性好，韧性强耐冲击，自润滑性能好不粘附，比生轻，噪音小，防腐性能好。
下面结合附图，用实施例对本发明做进一步说明；
该附图为本发明结构示意图。
附图中：1、超高分子量聚乙烯外套，2、聚丙烯内套辊体。
将玻璃纤维0.9公斤和偶联剂5克在加热式混料机内混合，搅拌30分钟，温度为60℃，然后把聚丙烯粉9公斤加入已偶联的玻璃纤维中搅拌30分钟，把搅拌好的料放入注塑机中注塑成型为聚丙烯内套辊体2；将玻璃纤维0.2公斤和偶联剂2克在加热式混料机内混合，搅拌时间30分钟，温度60℃，然后再加入超高分子量聚乙烯4公斤、脱模剂20克和炭黑1.32克继续搅拌30分钟，把搅拌好的料放入模具中加热至230℃，加压直至冷却到室温制成超高分子量聚乙烯外套1；把制成的聚丙烯内套辊体2和超高分子量聚乙烯外套1接触面涂上粘合剂以过盈配合装在一起制成Φ133×1400规格的超高分子量聚乙烯托辊。
Claims (1)
1．超高分子量聚乙烯托辊制造工艺，其特征是：将玻璃纤维和偶联剂在加热式混料机内混合，然后把聚丙烯粉加入已偶联的玻璃纤维中，把搅拌好的料放入注塑机中注塑成型为聚丙烯内套辊体(2)；将玻璃纤维和偶联剂在加热式混料机内混合，然后再加入超高分子量聚乙烯、脱模剂和炭黑继续搅拌，把搅拌好的料称重放入模具中加温，在一定压力下保压直至冷却到室温出模制成超高分子量聚乙烯外套(1)；把聚丙烯内套辊体(2)和超高分子量聚乙烯外套(1)接触面涂上粘合剂以过盈配合装在一起制成超高分子量聚乙烯托辊。