CN1203019C - 强吸收紫外和红外的绿色玻璃 - Google Patents

强吸收紫外和红外的绿色玻璃 Download PDF

Info

Publication number
CN1203019C
CN1203019C CN 03117080 CN03117080A CN1203019C CN 1203019 C CN1203019 C CN 1203019C CN 03117080 CN03117080 CN 03117080 CN 03117080 A CN03117080 A CN 03117080A CN 1203019 C CN1203019 C CN 1203019C
Authority
CN
China
Prior art keywords
glass
content
colorant
transmissivity
total iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN 03117080
Other languages
English (en)
Other versions
CN1451621A (zh
Inventor
李亮佐
徐国平
李志进
汤旭初
曹百灵
周始民
陆黎鹤
许兵
朱占东
赵长海
陈雄
邹裕忠
赵沈安
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Huadong Yaopi Glass Co ltd
Original Assignee
Yaohua-Pierjindun Glass Co Ltd Shanghai
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yaohua-Pierjindun Glass Co Ltd Shanghai filed Critical Yaohua-Pierjindun Glass Co Ltd Shanghai
Priority to CN 03117080 priority Critical patent/CN1203019C/zh
Publication of CN1451621A publication Critical patent/CN1451621A/zh
Application granted granted Critical
Publication of CN1203019C publication Critical patent/CN1203019C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明提供一种能够强吸收紫外和红外的绿色玻璃，其是在普通钠钙硅平板玻璃成份中，添加着色剂，着色剂的配比是：着色剂中总铁含量(Fe2O3)在0.5～0.9%之间，其中总铁中的亚铁(Fe2+)含量在18～28%，TiO2的含量为0.2～0.7%，CeO2的含量为0.05～0.15%。这种玻璃的颜色为深绿色，其优点是，紫外线透过率不超过17%，红外线透过率不超过28%，可见光的透过率在70%以上。

Description

强吸收紫外和红外的绿色玻璃
技术领域
本发明涉及一种在普通浮化玻璃成份中，添加着色剂，使该玻璃能够吸收强紫外线和红外线，其颜色为绿色。
背景技术
随着人们对节能降耗认识的不断提高，以及汽车工业的不断发展，新型的节能降耗产品越来越被汽车行业所采用，射进汽车内的太阳光，一方面增加汽车内的温度，另一方面太阳光中的紫外线，又加速车内的塑料、皮革等装饰材料的侵蚀，目前市场上汽车用玻璃，不能阻挡强紫外线和红外线，尤其是在夏季，对人体健康不利。
发明内容
本发明的目的是提供一种向玻璃本体内掺入几种金属离子，使玻璃能对太阳光线有选择地吸收，对紫外线的吸收率达80％，对红外线的吸收率达70％以上，而同时，该玻璃又具有70％以上的透光率，其是在普通钠钙硅平板玻璃成份中，添加着色剂，着色剂占玻璃含量的重量配比是：
着色剂中总铁含量(Fe2O3)在0.5～0.9％之间，其中总铁中的亚铁(Fe2+)含量在18～28％；TiO2的含量为0.2～0.7％，CeO2的含量为0.05～0.15％。这种玻璃的颜色为深绿色，其优点是，对4mm厚度玻璃，紫外线透过率不超过17％，红外线透过率不超过28％，可见光的透过率在70％以上。
具体实施方式
1、按照上述配合料成分，普通透明玻璃配合料为基础称量1～2公斤(含不同浓度着色剂的生料)，生料的称量精度保持在1克以内，着色剂的称量精度在0.001克。
2、用1550℃以上的温度在电炉中进行熔化，同时，澄清时间不能低于4个小时。为解决条纹问题，在玻璃熔化以后，要间隔一定的时间进行搅拌，通常每15～30分钟搅拌一次，每次搅拌3～5圈，连续搅拌4次以上。
3、采用模具进行成型，因此，必须事先对模型进行加热，模具的加热温度为300～500度。玻璃熔化并澄清后将模具从加热炉中取出，然后将澄清好的玻璃倒入模具中，并迅速成型。
4、当玻璃成型好后，迅速将玻璃移入退火炉中进行退火，根据浮法玻璃的性质，退火温度控制在500～600度左右，在此温度下保持0.5～1小时，然后让玻璃随炉自然冷却，当炉温低于300度时微微开启炉门，加速冷却速度，当温度低于100度后将炉门完全打开，60度左右便将玻璃从退火炉中取出。
5、采用抛磨设备对玻璃进行处理，使玻璃成品的光洁度完全满足测量要求。

Claims (1)

1.一种强吸收紫外和红外的绿色玻璃，其特征在于：在普通钠钙硅平板玻璃成份中，添加着色剂，着色剂占玻璃含量的重量配比是：
着色剂中总铁含量Fe2O3在0.5～0.9％之间，其中总铁中的亚铁Fe2+含量在18～28％；TiO2的含量为0.2～0.7％，CeO2的含量为0.05～0.15％。
CN 03117080 2003-05-22 2003-05-22 强吸收紫外和红外的绿色玻璃 Expired - Lifetime CN1203019C (zh)