CN118256814A - 一种无磁合金钢 - Google Patents
一种无磁合金钢 Download PDFInfo
- Publication number
- CN118256814A CN118256814A CN202410356816.1A CN202410356816A CN118256814A CN 118256814 A CN118256814 A CN 118256814A CN 202410356816 A CN202410356816 A CN 202410356816A CN 118256814 A CN118256814 A CN 118256814A
- Authority
- CN
- China
- Prior art keywords
- alloy steel
- nonmagnetic
- mass
- nonmagnetic alloy
- percentage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及金属材料技术领域，特别是涉及一种无磁合金钢，按质量百分比计，其成分包括：C：0.01～0.15％、Si：0.01～1％、Mn：8～20％、P：0.01～0.05％、Ni：1～6％、Cr：10～20％、Cu：0.01～3.5％、N：0.01～0.5％、Co：0.01～0.3％、杂质：1％以下，余量由Fe组成。本发明通过对合金成分进行优化设计，开发除了一种具有优异性能的无磁合金钢，解决了普通不锈钢具有弱磁性或微磁性的问题。
Description
技术领域
本发明涉及金属材料技术领域，特别是涉及一种无磁合金钢。
背景技术
目前的无磁性材料主要用于代替铜带或铝带。目前有无磁性要求的主要使用铜带和铝带，铜带铝带价格较不锈钢高50％至一倍以上，其产品成本较高，且铜带铝带制作的产品在空气中表面易于氧化变色，产生锈斑及氧化斑点，不宜长期保存，而且其强度及硬度及使用寿命较低只有不锈钢的10％至30％。
针对目前这种现象，我公司研发了可代替铜带和铝带以及普通不锈钢(SUS301，SUS304等)的无磁不锈钢带，其无磁性可达到其产品的使用要求。
普通不锈钢SUS301，SUS304在硬度HV250以下会有弱磁性或微磁性，可以用磁铁吸附，不能通过检针机直径0.8铁球测试，冲压成型后会产生强磁性，可以用磁铁吸附，不能通过检针机直径1.0铁球测试。在硬度HV250-350有磁性，可以用磁铁吸附，不能通过检针机直径1.0铁球测试。
发明内容
有鉴于此，本发明的目的在于提供一种无磁合金钢，以解决普通不锈钢具有弱磁性或微磁性的问题。
本发明提供了一种无磁合金钢，按质量百分比计，其成分包括：C：0.01～0.15％、Si：0.01～1％、Mn：8～20％、P：0.01～0.05％、Ni：1～6％、Cr：10～20％、Cu：0.01～3.5％、N：0.01～0.5％、Co：0.01～0.3％、杂质：1％以下，余量由Fe组成。
优选的，按质量百分比计，所述无磁合金钢的成分包括：C：0.01％、Si：0.01％、Mn：8％、P：0.01％、Ni：1％、Cr：10％、Cu：0.01％、N：0.01％、Co：0.01％、杂质：0.01％，余量由Fe组成。
优选的，按质量百分比计，所述无磁合金钢的成分包括：C：0.15％、Si：1％、Mn：20％、P：0.05％、Ni：6％、Cr：20％、Cu：3.5％、N：0.5％、Co：0.3％、杂质：1％，余量由Fe组成。
优选的，按质量百分比计，所述无磁合金钢的成分包括：C：0.1％、Si：0.5％、Mn：15％、P：0.03％、Ni：4％、Cr：15％、Cu：2％、N：0.25％、Co：0.15％、杂质：0.5％以下，余量由Fe组成。
优选的，所述杂质为Mo、Ti、V、Nb、Ca、Mg和S中的一种或多种。
优选的，所述Mo、Ti、V和Nb在无磁合金钢中的合计质量百分含量为0.95％以下。
优选的，所述Ca和Mg在无磁合金钢中的合计质量百分含量为0.01％以下。
优选的，所述S在无磁合金钢中的质量百分含量为0.05％以下。
与现有技术相比，本发明提供了提供一种无磁合金钢，按质量百分比计，其成分包括：C：0.01～0.15％、Si：0.01～1％、Mn：8～20％、P：0.01～0.05％、Ni：1～6％、Cr：10～20％、Cu：0.01～3.5％、N：0.01～0.5％、Co：0.01～0.3％、杂质：1％以下，余量由Fe组成。本发明通过对合金成分进行优化设计，开发除了一种具有优异性能的无磁合金钢，实验结果表明：本发明提供的合金钢在硬度HV250以下时，无磁性，磁铁不能吸附，可以通过检针直径0.8铁球测试，冲压成型后可以通过检针机直径1.0铁球测试；在硬度HV250～350时，无磁性，磁铁不能吸附，可以通过检针直径1.0铁球测试；合金钢的熔点可达1200℃以上，具有良好的耐高温性能。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供了一种无磁合金钢，按质量百分比计，其成分包括：C：0.01～0.15％、Si：0.01～1％、Mn：8～20％、P：0.01～0.05％、Ni：1～6％、Cr：10～20％、Cu：0.01～3.5％、N：0.01～0.5％、Co：0.01～0.3％、杂质：1％以下，余量由Fe组成。
在本发明提供的一个实施例中，按质量百分比计，所述无磁合金钢的成分包括：C：0.01％、Si：0.01％、Mn：8％、P：0.01％、Ni：1％、Cr：10％、Cu：0.01％、N：0.01％、Co：0.01％、杂质：0.01％，余量由Fe组成。
在本发明提供的一个实施例中，按质量百分比计，所述无磁合金钢的成分包括：C：0.15％、Si：1％、Mn：20％、P：0.05％、Ni：6％、Cr：20％、Cu：3.5％、N：0.5％、Co：0.3％、杂质：1％，余量由Fe组成。
在本发明提供的一个实施例中，按质量百分比计，所述无磁合金钢的成分包括：C：0.1％、Si：0.5％、Mn：15％、P：0.03％、Ni：4％、Cr：15％、Cu：2％、N：0.25％、Co：0.15％、杂质：0.5％以下，余量由Fe组成。
在本发明提供的一个实施例中，所述杂质优选为Mo、Ti、V、Nb、Ca、Mg和S中的一种或多种。
在本发明提供的一个实施例中，所述Mo、Ti、V和Nb在无磁合金钢中的合计质量百分含量优选为0.95％以下。
在本发明提供的一个实施例中，所述Ca和Mg在无磁合金钢中的合计质量百分含量优选为0.01％以下。
在本发明提供的一个实施例中，所述S在无磁合金钢中的质量百分含量优选为0.05％以下。
本发明通过对合金成分进行优化设计，开发除了一种具有优异性能的无磁合金钢，实验结果表明：本发明提供的合金钢在硬度HV250以下时，无磁性，磁铁不能吸附，可以通过检针直径0.8铁球测试，冲压成型后可以通过检针机直径1.0铁球测试；在硬度HV250～350时，无磁性，磁铁不能吸附，可以通过检针直径1.0铁球测试；合金钢的熔点可达1200℃以上，具有良好的耐高温性能。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种无磁合金钢，其特征在于，按质量百分比计，其成分包括：C：0.01～0.15％、Si：0.01～1％、Mn：8～20％、P：0.01～0.05％、Ni：1～6％、Cr：10～20％、Cu：0.01～3.5％、N：0.01～0.5％、Co：0.01～0.3％、杂质：1％以下，余量由Fe组成。
2.根据权利要求1所述的无磁合金钢，其特征在于，按质量百分比计，其成分包括：C：0.01％、Si：0.01％、Mn：8％、P：0.01％、Ni：1％、Cr：10％、Cu：0.01％、N：0.01％、Co：0.01％、杂质：0.01％，余量由Fe组成。
3.根据权利要求1所述的无磁合金钢，其特征在于，按质量百分比计，其成分包括：C：0.15％、Si：1％、Mn：20％、P：0.05％、Ni：6％、Cr：20％、Cu：3.5％、N：0.5％、Co：0.3％、杂质：1％，余量由Fe组成。
4.根据权利要求1所述的无磁合金钢，其特征在于，按质量百分比计，其成分包括：C：0.1％、Si：0.5％、Mn：15％、P：0.03％、Ni：4％、Cr：15％、Cu：2％、N：0.25％、Co：0.15％、杂质：0.5％以下，余量由Fe组成。
5.根据权利要求1所述的无磁合金钢，其特征在于，所述杂质为Mo、Ti、V、Nb、Ca、Mg和S中的一种或多种。
6.根据权利要求5所述的无磁合金钢，其特征在于，所述Mo、Ti、V和Nb在无磁合金钢中的合计质量百分含量为0.95％以下。
7.根据权利要求5所述的无磁合金钢，其特征在于，所述Ca和Mg在无磁合金钢中的合计质量百分含量为0.01％以下。
8.根据权利要求5所述的无磁合金钢，其特征在于，所述S在无磁合金钢中的质量百分含量为0.05％以下。