CN113718183A - 无磁合金钢 - Google Patents
无磁合金钢 Download PDFInfo
- Publication number
- CN113718183A CN113718183A CN202111033596.1A CN202111033596A CN113718183A CN 113718183 A CN113718183 A CN 113718183A CN 202111033596 A CN202111033596 A CN 202111033596A CN 113718183 A CN113718183 A CN 113718183A
- Authority
- CN
- China
- Prior art keywords
- alloy steel
- magnetic alloy
- iron ball
- magnetic
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种无磁合金钢,按质量百分比计,C:0.15%、Si:0.01%、Mn:13~17%、P:0.01~0.05%、Ni:3~6%、Cr:15%、Cu:3.5%、N:0.01%、杂质:1%以下,余量由Fe组成。该无磁合金钢在硬度HV250以下,无磁性,磁铁不能吸附,可以通过检针直径0.8铁球测试,在硬度HV250‑350无磁性,磁铁不能吸附,可以通过检针直径1.0铁球测试。
Description
本申请是申请日为2017年06月10日、申请号为201710434980.X、发明名称为《合金钢》的发明专利的分案申请。
技术领域
本发明涉及金属材料技术领域,特别是涉及一种无磁合金钢。
背景技术
目前的无磁性材料主要用于代替铜带或铝带。目前有无磁性要求的主要使用铜带和铝带,铜带铝带价格较不锈钢高50%至一倍以上,其产品成本较高,且铜带铝带制作的产品在空气中表面易于氧化变色,产生锈斑及氧化斑点,不宜长期保存,而且其强度及硬度及使用寿命较低只有不锈钢的10%至30%。
普通不锈钢SUS301,SUS304在硬度HV250以下会有弱磁性或微磁性,可以用磁铁吸附,不能通过检针机直径0.8铁球测试,冲压成型后会产生强磁性,可以用磁铁吸附,不能通过检针机直径1.0铁球测试。在硬度HV250-350有磁性,可以用磁铁吸附,不能通过检针机直径1.0铁球测试。
发明内容
针对普通不锈钢存在的上述问题,本发明提供了一种无磁合金钢,在硬度HV250以下,无磁性,磁铁不能吸附;可以通过检针直径0.8铁球测试,冲压成型后可以通过检针机直径1.0铁球测试。在硬度HV250-350无磁性,磁铁不能吸附;可以通过检针直径1.0铁球测试。
一种无磁合金钢,按质量百分比计,
C:0.15%、Si:0.01%、Mn:13~17%、P:0.01~0.05%、Ni:3~6%、Cr:15%、Cu:3.5%、N:0.01%、杂质:1%以下,余量由Fe组成。
所述杂质选自下述(A)~(B)所示的元素组中的一种以上的元素,及S为0.05%以下,
(A)选自Mo、Ti、V和Nb中的一种以上:合计为0.95%以下;
(B)Ca和/或Mg:合计为0.01%以下。
本发明提供了一种无磁合金钢。本发明提供的无磁合金钢可代替铜带和铝带以及普通不锈钢(SUS301,SUS304等)的无磁不锈钢带,其无磁性可达到其产品的使用要求。本发明提供的无磁合金钢在硬度HV250以下,无磁性,磁铁不能吸附;可以通过检针直径0.8铁球测试,冲压成型后可以通过检针机直径1.0铁球测试。在硬度HV250-350无磁性,磁铁不能吸附;可以通过检针直径1.0铁球测试。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂,下面对本发明的具体实施方式做详细的说明。在下面的描述中阐述了很多具体细节以便于充分理解本发明。但是本发明能够以很多不同于在此描述的其它方式来实施,本领域技术人员可以在不违背本发明内涵的情况下做类似改进,因此本发明不受下面公开的具体实施例的限制。
一种合金钢,按质量百分比计,
C:0.01~0.15%、Si:0.01~1%、Mn:13~17%、P:0.01~0.05%、Ni:3~6%、Cr:15~18%、Cu:0.01~3.5%、N:0.01~0.5%、杂质:1%以下,余量由Fe组成。
上述合金钢,本产品在硬度HV250以下,无磁性,磁铁不能吸附;可以通过检针直径0.8铁球测试,冲压成型后可以通过检针机直径1.0铁球测试。在硬度HV250-350无磁性,磁铁不能吸附;可以通过检针直径1.0铁球测试。
优选的,按质量百分比计,
C:0.15%、Si:1%、Mn:17%、P:0.05%、Ni:6%、Cr:18%、Cu:3.5%、N:0.5%、杂质:1%,余量由Fe组成。
优选的,按质量百分比计,
C:0.01%、Si:0.01%、Mn:13%、P:0.01%、Ni:3%、Cr:15%、Cu:0.01%、N:0.01%、杂质:0.01%,余量由Fe组成。
优选的,按质量百分比计,
C:0.1%、Si:0.5%、Mn:14%、P:0.03%、Ni:5%、Cr:16%、Cu:2%、N:0.25%、杂质:0.5%,余量由Fe组成。
优选的,所述杂质选自下述(A)~(C)所示的元素组中的一种以上的元素,及S为0.05%以下,
(A)选自Mo、Ti、V和Nb中的一种以上:合计为0.95%以下;
(B)Ca和/或Mg:合计为0.01%以下。
以上所述实施例的各技术特征可以进行任意的组合,为使描述简洁,未对上述实施例中的各个技术特征所有可能的组合都进行描述,然而,只要这些技术特征的组合不存在矛盾,都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。因此,本发明专利的保护范围应以所附权利要求为准。
Claims (1)
1.一种无磁合金钢,其特征在于,按质量百分比计,
C:0.15%、Si:0.01%、Mn:13~17%、P:0.01~0.05%、Ni:3~6%、Cr:15%、Cu:3.5%、N:0.01%、杂质:1%以下,余量由Fe组成;
所述杂质选自下述(A)~(B)所示的元素组中的一种以上的元素,及S为0.05%以下,
(A)选自Mo、Ti、V和Nb中的一种以上:合计为0.95%以下;
(B)Ca和/或Mg:合计为0.01%以下。