CN117980358A - 聚合物和增粘剂及其制备方法以及钻井液 - Google Patents
聚合物和增粘剂及其制备方法以及钻井液 Download PDFInfo
- Publication number
- CN117980358A CN117980358A CN202280059130.5A CN202280059130A CN117980358A CN 117980358 A CN117980358 A CN 117980358A CN 202280059130 A CN202280059130 A CN 202280059130A CN 117980358 A CN117980358 A CN 117980358A
- Authority
- CN
- China
- Prior art keywords
- formula
- linear
- polymer
- hydrogen
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚合物,一种增粘剂及其制备方法以及一种钻井液。所述聚合物含有式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元,其中,R1、R2、R3、R4、R5、R6、R7和R8各自独立地为氢或C1‑C10的直链或支链烷基;X为C1‑C10的直链或支链亚烷基;Y为式(4)或C1‑C10的直链或支链亚烷基;M为氢或碱金属,A1、A2和A3各自独立地为键或C1‑C3的直链或支链亚烷基。该聚合物能够在高温、高钙环境下仍保持优异的增粘性能。
Description
本发明涉及油田钻井液技术领域,具体涉及一种聚合物、一种增粘剂及其制备方法以及一种钻井液。
钻井液中的粘土及重晶石等大量固相是导致油气层损害、造成产能降低的重要因素之一,而无固相钻井液体系可有效解决钻井液中固相对储层的伤害。无固相钻井液体系一般是指不含粘土和不溶固体加重材料的钻井液体系,其密度可以通过可溶性盐调整,体系其它性能则可以通过加入配套的处理剂来实现。根据使用的可溶性盐不同,无固相钻井液体系大体可分为无机盐类无固相钻井液和有机盐类无固相钻井液两大类。无机盐主要有NaCl、CaCl
2、KCl、NaBr、BaBr
2和磷酸盐等,有机盐主要为甲酸盐,例如NaCOOH、KCOOH和CsCOOH等。其它配伍处理剂主要为增粘剂、提切剂、降滤失剂、润滑剂、缓蚀剂以及缓冲剂等。
其中,在增粘剂中,聚合物类增粘剂是无固相钻井液的常用助剂之一,也是保证整个体系悬浮和携带岩屑性能的关键因素,钻井液体系中聚合物分子间相互缠绕形成空间网架结构,从而携带和悬浮岩屑,并最终将岩屑运移出井。现有技术中应用于无固相钻井液体系的聚合物增粘剂主要有三类,一类是以改性淀粉、改性纤维素为代表的天然改性聚合物,例如CN102127401A中公开了一种无固相钻井液用抗高温增粘剂,其以淀粉、瓜尔胶、碱性氢氧化物、环氧化物和醇类溶剂为主要成分,在淡水中可抗温150℃,在盐水中可抗温120℃;第二类是以丙烯酰胺、2-丙烯酰胺基-2-甲基丙磺酸为单体的水溶性共聚物,例如CN104650827A中公开了一种具有抗温增粘和抗盐性能的无固相钻井液用增粘剂,其由丙烯酰胺、2-甲基-2-丙烯酰胺基丙磺酸、N-乙烯基己内酰胺、二乙烯基苯为单体聚合而成,在水中经165℃老化16h前后均具有较好的增粘效果;第三类是水溶性疏水缔合聚合物,例如CN107235863A中公开了一种由含苯环疏水单体和N-乙烯基吡咯烷酮聚合而得的疏水缔合聚合物,在150℃老化16小时后仍具有较好的悬浮稳定性。再如CN107235862A中公开了一种无固相钻井液聚合物增粘剂,其分子中引入了同时含苯环和长氟碳链的疏水基团,通过疏水分子相互缔合而显著增加溶液粘度,抗温高达150℃。
如上所述的现有聚合物类增粘剂虽然具有较好的抗温性能(抗温可达150-165℃),然而无法兼顾抗钙性能。
目前我国大部分油田处于中后期开发,未动用地质储量多集中在高温地层,这便对具有良好储层保护性能的无固相钻井液提出了更高的要求。尤其是塔里木盆地的超深井, 其储层埋藏较深,深度一般大于6500m,井底温度高达150-180℃,且其地层水型为钙型地层水,钙离子浓度可高达15000mg/L。因此,迫切需要研发一种具有较好抗温能力,同时抗钙性能优异的高分子聚合物作为无固相钻井液的增粘剂,以保证高温和高钙环境下的悬浮性能。
发明内容
本发明的目的是为了克服现有技术存在的无固相钻井液无法兼顾抗温和抗钙性能等问题,提供一种聚合物、一种增粘剂及其制备方法和一种钻井液,该聚合物能够在高温、高钙环境下仍保持优异的增粘性能,非常适合用作无固相钻井液的增粘剂。
本发明的发明人经过大量研究发现,通过在以丙烯酰胺作为骨架结构的聚合物中引入含有磺酸基团的结构单元和含有-C(A
1COOH)(A
2COOH)(A
3COOH)的结构单元,能够使得该聚合物在高温、高钙环境下仍保持优异的增粘性能,特别适合用作无固相钻井液的增粘剂,由此完成了本发明。
为此,本发明第一方面提供一种聚合物,该聚合物含有式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元,
其中,R
1、R
2、R
3、R
4、R
5、R
6、R
7和R
8各自独立地为氢或C1-C10的直链或支链烷基;
X为C1-C10的直链或支链亚烷基;
Y为
或C1-C10的直链或支链亚烷基;
M为氢或碱金属;
A
1、A
2和A
3各自独立地为键或C1-C3的直链或支链亚烷基。
本发明第二方面提供一种增粘剂,该增粘剂含有丙烯酰胺骨架结构,该增粘剂还含有磺酸基团和-C(A
1COOH)(A
2COOH)(A
3COOH),其中A
1、A
2和A
3各自独立地为键或C1-C3的直链或支链亚烷基,将该增粘剂以0.7重量%的添加量加入Ca
2+浓度为15000mg/L的无固相钻井液基浆中,并在180℃老化16h后的表观粘度为28mPa·s以上,优选为36mPa·s以上。
本发明第三方面提供一种增粘剂的制备方法,所述方法包括:在聚合反应条件下,在引发剂存在下,使式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中发生聚合反应,
其中,R
1、R
2、R
3、R
4、R
5、R
6、R
7和R
8各自独立地为氢或C1-C10的直链或支链烷基;
X为C1-C10的直链或支链亚烷基;
Y为
或C1-C10的直链或支链亚烷基;
M为氢或碱金属;
A
1、A
2和A
3各自独立地为键或C1-C3的直链或支链亚烷基。
本发明第四方面提供一种钻井液,所述钻井液含有上述第一方面所述聚合物或第二方面所述增粘剂。
本发明提供的聚合物通过含有式(1)、式(2)和式(3)所示的三种结构单元,可以使得各结构单元既充分发挥各自的性能特点,又能够产生良好的协同作用,从而保证所述聚合物作为增粘剂应用于无固相钻井液时,在高温(180℃下老化16h)和高钙离子浓度(15000mg/L)的条件下仍具备优异的增粘性能(表观粘度为28mPa·s以上),非常适合作为无固相钻井液的增粘剂。
图1是实施例1制备得到的聚合物A1的红外谱图。
在本文中所披露的范围的端点和任何值都不限于该精确的范围或值,这些范围或值应当理解为包含接近这些范围或值的值。对于数值范围来说,各个范围的端点值之间、各个范围的端点值和单独的点值之间,以及单独的点值之间可以彼此组合而得到一个或多个新的数值范围,这些数值范围应被视为在本文中具体公开。
本发明中,所述无固相钻井液是指不含粘土和加重剂的钻井液,所述粘土为蒙脱石、 伊利石、高岭石和海泡石等中的一种或多种;所述加重剂为不溶固体加重剂,包括重晶石、铁矿粉、方铅矿粉和微锰等中的一种或多种。
本发明第一方面提供一种聚合物,该聚合物含有式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元,
其中,R
1、R
2、R
3、R
4、R
5、R
6、R
7和R
8各自独立地为氢或C1-C10的直链或支链烷基;
X为C1-C10的直链或支链亚烷基;
Y为
或C1-C10的直链或支链亚烷基;
M为氢或碱金属;
A
1、A
2和A
3各自独立地为键或C1-C3的直链或支链亚烷基。
本发明中,所述C1-C10的直链或支链烷基的实例例如可以为甲基、乙基、正丙基、异丙基、正丁基、仲丁基、异丁基、叔丁基、正戊基、异戊基、叔戊基、新戊基、正己基、异己基、正庚基、异庚基、2-甲基己基、2-乙基己基、1-甲基庚基、2-甲基庚基、正辛基、异辛基、正壬基、异壬基和3,5,5-三甲基己基中的任意一种。
本发明中,所述C1-C10的直链或支链亚烷基的实例例如可以为亚甲基、1,2-亚乙基、亚正丙基、亚异丙基、亚正丁基、亚异丁基、亚正戊基、亚异戊基、亚正己基、亚异己基、亚正庚基、亚异庚基、亚2-甲基己基、亚2-乙基己基、亚1-甲基庚基、亚2-甲基庚基、亚正辛基、亚异辛基和亚正壬基中的任意一种。
本发明中,所述碱金属的实例例如可以为Li、Na和K中的任意一种。
本发明中,所述C1-C3的直链或支链亚烷基的实例例如可以为亚甲基、1,2-亚乙基、亚正丙基和亚异丙基中的任意一种。
根据本发明,式(1)中,优选地,R
1和R
2各自独立地为氢或C1-C6的直链或支链烷基;更优选为氢或C1-C4的直链或支链烷基;进一步优选为氢、甲基或乙基。
在本发明一个特别优选的实施方式中,式(1)中的R
1和R
2均为氢,此时,式(1)所示的结构单元可以为来自丙烯酰胺的结构单元。
根据本发明,式(2)中,优选地,R
3、R
4、R
5和R
6各自独立地为氢或C1-C6的直链或支链烷基;更优选为氢或C1-C4的直链或支链烷基;进一步优选为氢、甲基或乙 基。
另外,式(2)中,优选地,X为C1-6的直链或支链亚烷基,更优选为C1-3的直链或支链亚烷基,进一步优选为亚甲基或1,2-亚乙基。
另外,式(2)中,优选地,M为氢或钠。
在本发明一个特别优选的实施方式中,式(2)中的R
3和R
4均为氢,R
5和R
6均为甲基,X为亚甲基,M为氢。此时,式(2)所示的结构单元可以为来自2-丙烯酰胺基-2-甲基丙磺酸的结构单元。
根据本发明,式(3)中,优选地,R
7和R
8各自独立地为氢或C1-C6的直链或支链烷基,更优选为氢或C1-C4的直链或支链烷基;进一步优选为氢、甲基或乙基。
另外,式(3)中,优选地,Y为
或C1-6的直链或支链亚烷基,更优选为
或C1-3的直链或支链亚烷基,进一步优选为
亚甲基或1,2-亚乙基。
另外,式(3)中,优选地,A
1、A
2和A
3各自独立地为键、亚甲基或1,2-亚乙基,更优选为键或亚甲基。
在本发明一个特别优选的实施方式中,式(3)中的R
7和R
8均为氢,Y为
A
1和A
2均为亚甲基,A
3为键,此时,式(3)所示的结构单元可以为来自2-丙烯酰氧基-1,2,3-三羧基丙烷的结构单元。
根据本发明,所述聚合物中,式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元的摩尔比可以在较大范围内变动,例如可以为10-80:10-60:1,优选为30-50:20-40:1。通过将上述三种结构单元的摩尔比限定在上述范围,能够进一步提高所述聚合物作为增粘剂应用于无固相钻井液时的抗温和抗钙性能,从而保证所述聚合物在无固相钻井液中在高温(180℃下老化16h)和高钙离子浓度(15000mg/L)的条件下仍具备优异的增粘性能(表观粘度为28mPa·s以上)。
本发明中,如无特别说明,各结构单元的摩尔比通过投料量计算得到。
根据本发明,所述聚合物的特性粘数为1200-2600mL/g,优选为1500-1900mL/g。
根据本发明,所述聚合物的粘均分子量为600万-1500万,优选为750万-1000万。根据本发明,将所述聚合物以0.7重量%的添加量加入Ca
2+浓度为15000mg/L的无固相钻井液基浆中,并在180℃老化16h后的表观粘度为28mPa·s以上,优选为36mPa·s以上。
本发明中,所述无固相钻井液基浆的配方为:在350mL水中加入130.9g甲酸钾、1.75g无水碳酸钠和3.5g碳酸氢钠,之后加入无水氯化钙至Ca
2+浓度为15000mg/L。
本发明中,所述特性粘数按照GB12005.1-89中所述的方法进行测定;所述粘均分子量按照GB12005.10-92中所述的方法,采用公式M=802[η]
1.25来进行计算,其中,M 为粘均分子量,[η]为特性粘数;所述表观粘度按照GB/T 16783.1中所述的方法进行测定。
根据本发明,所述聚合物的红外谱图在1403cm
-1和1573cm
-1附近存在COO-共轭体系伸缩振动峰,且在614cm
-1和1051cm
-1附近存在S=O特征振动峰,从而可以说明所述聚合物中含有式(2)所示结构单元和式(3)所示结构单元。
本发明中,所述聚合物的红外谱图采用美国赛默飞公司的Nicolet iS20红外光谱仪测得。
根据本发明一个优选的实施方式,所述聚合物中除含有上述式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元之外,还含有以下式(4)所示结构单元。
其中,R
9和R
10各自独立地为氢或C1-C10的直链或支链烷基,优选为氢或C1-C6的直链或支链烷基,更优选为氢或C1-C4的直链或支链烷基;进一步优选为氢、甲基或乙基;R
11和R
12各自独立地为C1-C6的直链或支链烷基,更优选为C1-C4的直链或支链烷基;进一步优选为甲基或乙基。
在本发明一个特别优选的实施方式中,式(4)所示结构单元中,R
9和R
10均为氢,R
11和R
12均为甲基。此时,式(4)所示的结构单元可以为来自N,N-二甲基丙烯酰胺的结构单元。
本发明的发明人发现,通过在上述聚合物中引入式(4)所示的结构单元,能够进一步提高聚合物的疏水缔合性能,与式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元相互协同作用,可以进一步提高聚合物的抗温抗钙性能。
此外,式(4)所示结构单元的含量可以根据式(1)所示结构单元的含量来确定,并且可以在较大范围内变动。例如,式(1)所示结构单元和式(4)所示结构单元摩尔比可以为10-100:1,优选为40-80:1。通过将式(4)所示结构单元的含量限定在上述范围,可以进一步提高所述聚合物的抗温抗钙性能。
此外,根据本发明又一个优选的实施方式,所述聚合物中除含有上述式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元以及选择性含有的式(4)所示结构单元之外,还含有以下式(5)所示结构单元。
其中,R
13和R
14各自独立地为氢或C1-C10的直链或支链烷基,优选为氢或C1-C6的直链或支链烷基,更优选为氢或C1-C4的直链或支链烷基;进一步优选为氢、甲基或乙基;R
15和R
16各自独立地为氢或C1-C6的直链或支链烷基,更优选为氢或C1-C4的直链或支链烷基,进一步优选为氢、甲基或乙基;Z为C1-C10的直链或支链亚烷基,优选为C1-C6的直链或支链亚烷基,更优选为C1-C4的直链或支链亚烷基,进一步优选为亚甲基或1,2-亚乙基。
在本发明一个特别优选的实施方式中,式(5)所示结构单元中,R
13为氢,R
14、R
15和R
16均为甲基,Z为1,2-亚乙基。此时,式(5)所示的结构单元可以为来自甲基丙烯酸二甲氨基乙酯的结构单元。
本发明的发明人发现,通过在上述聚合物中引入式(5)所示的结构单元,能够与式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元以及选择性含有的式(4)所示结构单元相互协同作用,从而进一步提高聚合物的分子量,由此能够进一步提高所述聚合物的粘度。并且通过各结构单元之间的相互协同作用,能够使得所述聚合物用于无固相钻井液的增粘剂时能够进一步提高抗温和抗钙性能。
此外,式(5)所示结构单元的含量可以根据式(1)所示结构单元的含量来确定,并且可以在较大范围内变动。例如,式(1)所示结构单元和式(5)所示结构单元的摩尔比可以为10-100:1,优选为30-80:1。通过将式(5)所示结构单元的含量限定在上述范围,可以进一步提高所述聚合物的抗温抗钙性能。
另外,在本发明一个特别优选的实施方式中,所述聚合物含有式(1)所述结构单元、式(2)所述结构单元、式(3)所述结构单元、式(4)所述结构单元和式(5)所示结构单元。包含上述结构单元的聚合物以0.7重量%的添加量加入Ca
2+浓度为15000mg/L的无固相钻井液基浆中,并在180℃老化16h后的表观粘度可高达28mPa·s以上,优选为36mPa·s以上,非常适合用作无固相钻井液的增粘剂使用。
本发明中,式(1)所示结构单元能够形成丙烯酰胺骨架结构,通过配合具有磺酸基团的式(2)所示结构单元和含有-C(A
1COOH)(A
2COOH)(A
3COOH)的式(3)所示结构单元,三者协同作用,能够显著提高所得聚合物的抗温和抗钙性能。
另外,通过进一步引入具有弱疏水作用的式(4)所示结构单元能够进一步提高聚合物的抗温抗盐性能,通过引入式(5)所示结构单元能起到扩链作用,从而最大限度地 提高聚合物的分子量,由此来提高所得聚合物的粘度。并且通过上述五种结构单元的相互协同作用,不仅能够发挥各结构单元各自的特性,而且可以最大限度地提高所述聚合物的抗温抗钙性能。
此外,本发明第一方面所述聚合物的制备方法没有特别的限定,例如可以在聚合反应条件下,在引发剂存在下,使上述结构单元对应的单体在溶剂中发生聚合反应从而制备得到所述聚合物,具体的制备方法可参见下述第三方面的增粘剂的制备方法进行,此处不再详述。
本发明第二方面提供一种增粘剂,所述增粘剂含有丙烯酰胺骨架结构,所述增粘剂还含有磺酸基团和-C(A
1COOH)(A
2COOH)(A
3COOH),其中A
1、A
2和A
3各自独立地为键或C1-C3的直链或支链亚烷基,优选为键、亚甲基或1,2-亚乙基,更优选为键或亚甲基。
在本发明一个特别优选的实施方式中,所述增粘剂含有磺酸基团和-C(CH
2COOH)
2(COOH)。
通过在丙烯酰胺骨架结构中引入磺酸基团和-C(A
1COOH)(A
2COOH)(A
3COOH),尤其是引入磺酸基团和-C(CH
2COOH)
2(COOH),能够使得将该增粘剂以0.7重量%的添加量加入Ca
2+浓度为15000mg/L的无固相钻井液基浆中,并在180℃老化16h后的表观粘度高达28mPa·s以上,优选为36mPa·s以上。
此外,根据本发明的第二方面,所述增粘剂中磺酸基团和-COOH的摩尔比可以为3-20:1,优选为6-14:1,由此,可以进一步保证所述增粘剂的抗温和抗钙性能。
另外,根据本发明的第二方面,优选地,所述增粘剂中-COOH的含量不低于2mol%,更优选为不低于3.2mol%,进一步优选为不低于4mol%。由此,可以进一步保证所述增粘剂的抗温和抗钙性能。
本发明中,所述磺酸基团和-COOH的摩尔比以及所述-COOH的含量按照投料比计算得到。
本发明第三方面提供一种增粘剂的制备方法,所述方法包括:在聚合反应条件下,在引发剂存在下,使式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中发生聚合反应,
其中,R
1、R
2、R
3、R
4、R
5、R
6、R
7和R
8各自独立地为氢或C1-C10的直链或支 链烷基;
X为C1-C10的直链或支链亚烷基;
Y为
或C1-C10的直链或支链亚烷基;
M为氢或碱金属;
A
1、A
2和A
3各自独立地为键或C1-C3的直链或支链亚烷基。
本发明第三方面所述的C1-C10的直链或支链烷基的实例、C1-C10的直链或支链亚烷基的实例、碱金属的实例以及C1-C3的直链或支链亚烷基的实例等可以与本发明第一方面所述的相同,此处不再赘述。
根据本发明,式(A)中,R
1和R
2的优选取代基与本发明第一方面式(1)中对应的R
1和R
2相同,并且在本发明一个特别优选的实施方式中,式(A)中的R
1和R
2均为氢,也即,式(A)所示单体为丙烯酰胺。
根据本发明,式(B)中,R
3、R
4、R
5、R
6、X和M的优选取代基与本发明第一方面式(2)中对应的R
3、R
4、R
5、R
6、X和M相同,并且在本发明一个特别优选的实施方式中,式(B)中的R
3和R
4均为氢,R
5和R
6均为甲基,X为亚甲基,M为氢。也即,式(B)所示单体为2-丙烯酰胺基-2-甲基丙磺酸。
根据本发明,式(C)中,R
7、R
8、Y以及A
1、A
2和A
3的优选取代基与本发明第一方面式(3)中对应的R
7、R
8、Y以及A
1、A
2和A
3相同,并且在本发明一个特别优选的实施方式中,式(C)中的,R
7和R
8均为氢,Y为
A
1和A
2均为亚甲基,A
3为键,也即,式(C)所示单体为2-丙烯酰氧基-1,2,3-三羧基丙烷。
本发明中,式(A)所示单体、式(B)所示单体和式(C)所示单体的摩尔比可以在较大范围内变动,例如可以为10-80:10-60:1;优选为30-50:20-40:1。通过将上述三种单体的摩尔比限定在上述范围,能够进一步提高制备得到的聚合物作为增粘剂应用于无固相钻井液时的抗温性能和抗钙性能。
另外,本发明中,所述增粘剂的制备方法还包括:使式(D)所示单体和/或式(E)所示单体与式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中一起发生聚合反应。
根据本发明,式(D)中,R
9、R
10、R
11和R
12的优选取代基与本发明第一方面式 (4)中对应的R
9、R
10、R
11和R
12相同,并且在本发明一个特别优选的实施方式中,式(D)中的R
9和R
10均为氢,R
11和R
12均为甲基,也即,式(D)所示单体为N,N-二甲基丙烯酰胺。
本发明的发明人发现,通过式(A)所示单体、式(B)所示单体和式(C)所示单体的基础上引入式(D)所示的单体,能够进一步提高聚合物的疏水缔合性能,可以与式(A)所示单体、式(B)所示单体和式(C)所示单体相互协同作用,能够进一步提高由此制备得到的增粘剂的抗温抗钙性能。
此外,式(D)所示单体的用量可以根据式(A)所示单体的用量来进行选择,并且可以在较大范围内变动。例如,式(A)所示单体和式(D)所示单体的摩尔比可以为10-100:1,优选为40-80:1。通过将式(D)所示单体的含量限定在上述范围,可以进一步提高所述增粘剂的抗温抗钙性能。
根据本发明,式(E)中,R
13、R
14、R
15、R
16和Z的优选取代基与本发明第一方面式(5)中对应的R
13、R
14、R
15、R
16和Z相同,并且在本发明一个特别优选的实施方式中,式(E)中的R
13为氢,R
14、R
15和R
16均为甲基,Z为1,2-亚乙基,也即,式(E)所示单体为甲基丙烯酸二甲氨基乙酯。
本发明的发明人发现,通过在式(A)所示单体、式(B)所示单体、式(C)所示单体以及可选的式(D)所示单体的基础上引入式(E)所示单体,能够与式(A)所示单体、式(B)所示单体和式(C)所示单体相互协同作用,从而进一步提高增粘剂的分子量,由此能够进一步提高所述增粘剂的粘度。并且通过上述各单体之间的相互协同作用,能够使得由此制备得到的增粘剂应用于无固相钻井液时能够进一步提高抗温和抗钙性能。
此外,式(E)所示单体的用量可以根据式(A)所示单体的用量来进行选择,并且可以在较大范围内变动。例如,式(A)所示单体和式(E)所示单体的摩尔比可以为10-100:1,优选为30-80:1。通过将式(E)所示单体的含量限定在上述范围,可以进一步提高制备得到的聚合物的抗温抗钙性能。
通过使式(D)所示单体或式(E)所示单体与式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中一起发生聚合反应,尤其是通过使式(D)所示单体和式(E)所示单体与式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中一起发生聚合反应,能够进一步提高制备得到的增粘剂的抗温抗钙性能,使得所得增粘剂在高温高钙环境下仍然能够保持优异的粘度。
另外,本发明中,所述引发剂可以为本领域常见的能够引发所述单体发生聚合反应的各种引发剂,例如,所述引发剂可以选自偶氮类引发剂和氧化还原类引发剂中的至少一种。优选地,所述引发剂为偶氮类引发剂和氧化还原类引发剂的混合物。
本发明中,所述偶氮类引发剂没有特别的限定,例如可以为偶氮二异丁腈、偶氮二 咪唑啉基丙烷二盐酸盐、2,2’-偶氮(2-脒基丙烷)二盐酸盐、4,4’-偶氮双(4-氰基戊酸)和2,2’-偶氮二异丁基脒盐酸盐中的至少一种,优选为2,2’-偶氮二异丁基脒盐酸盐、2,2’-偶氮(2-脒基丙烷)二盐酸盐和偶氮二咪唑啉基丙烷二盐酸盐中的至少一种。
本发明中,所述氧化还原类引发剂没有特别地限定,包括氧化剂和还原剂。其中,所述氧化剂例如可以为过硫酸铵、过硫酸钾、过硫酸钠和过氧化氢中的至少一种,优选为过硫酸铵和/或过硫酸钾。
另外,本发明中,所述还原剂可以选自无机还原剂和有机还原剂中的至少一种。
其中,所述无机还原剂例如可以为亚硫酸氢钠、亚硫酸钠、硫酸亚铁、硫代硫酸钠和尿素中的至少一种,优选为亚硫酸氢钠和/或亚硫酸钠。
其中,所述有机还原剂例如可以为N,N-二甲基乙醇胺、N,N-二甲基丙醇胺、N,N-二甲基哌嗪、N,N’-二甲基哌嗪、四甲基脲素、N,N-二甲基脲素、N,N,N’,N’-四甲基乙二胺、N,N’-二甲基乙二胺、N,N’-二甲基-1,3-丙二胺、3-甲氨基丙胺和N,N-二甲基乙二胺中的至少一种,优选为N,N’-二甲基-1,3-丙二胺或N,N,N’,N’-四甲基乙二胺,更优选为N,N,N’,N’-四甲基乙二胺。
本发明的发明人在研究中发现,当所述还原剂采用无机还原剂和有机还原剂的混合物时,不仅能够最大限度地在保证聚合物高分子量的前提下使得单体完全转化,并且能够进一步提高聚合得到的增粘剂的抗温抗钙性能。因此,本发明中,优选地,所述还原剂为无机还原剂和有机还原剂的混合物。
此外,本发明中,所述引发剂的用量没有特别的限定,只要能够引发所述聚合反应即可,可以根据参与聚合反应的单体的量来决定。例如,以聚合单体总重量(式(A)所示单体、式(B)所示单体、式(C)所示单体以及任选的式(D)所示单体和任选的式(E)所示单体的总量)为100重量份计,所述引发剂的总用量可以为0.1-1重量份,优选为0.3-0.6重量份。通过将所述引发剂的用量限定在上述范围,不仅可以保证聚合反应更加顺利地进行,并且可以调控聚合反应,从而进一步确保制备得到的增粘剂具备良好的抗温抗钙性能。
本发明中,当所述引发剂为偶氮类引发剂和氧化还原类引发剂的混合物时,所述氧化还原类引发剂的用量可以为引发剂总用量的30-90重量%,优选为60-80重量%,余量为所述偶氮类引发剂。
本发明中,在所述氧化还原类引发剂中,所述还原剂的用量可以为氧化剂和还原剂总用量的40-80重量%,优选为50-70重量%,余量为所述氧化剂。
此外,本发明中,当所述还原剂为所述无机还原剂和有机还原剂的混合物时,所述有机还原剂的用量可以为还原剂总用量的30-90重量%,优选为60-80重量%,余量为无机还原剂。由此,不仅可以进一步促进聚合反应的顺利进行,并且可以进一步提高制备得到的增粘剂的抗温抗钙性能。
另外,根据本发明,所述溶剂可以为本领域进行聚合反应的常规溶剂,没有特别的限定。例如可以为水,优选为去离子水。
此外,所述溶剂的用量没有特别的限定,可以根据所述聚合单体的总重量(式(A)所示单体、式(B)所示单体、式(C)所示单体以及任选的式(D)来决定,例如,所述溶剂的用量可以为聚合单体总重量的2-6倍,优选为3-5倍。通过将所述溶剂的用量控制在上述范围,不仅可以保证聚合反应更加顺利地进行,并且可以确保制备得到的增粘剂具备良好的抗温抗钙性能。
另外,本发明中,可以将所述单体、引发剂和溶剂等同时加入反应装置中并搅拌混合均匀;也可以首先将所述单体与所述溶剂混合,再加入所述引发剂引发反应;还可以首先将所述引发剂与所述溶剂混合,再向其中加入所述单体。
本发明中,优选地,首先将所述单体与所述溶剂混合,再加入所述引发剂引发反应。
根据本发明的第三方面,所述聚合反应的条件没有特别的限制,只要可以使得所述单体发生聚合即可。优选地,所述聚合反应的条件包括:温度为-10℃至15℃,优选为-10℃至0℃,更优选为-10℃至-5℃;时间为1-20小时,优选为5-10小时,更优选为8-10小时。由此可以进一步保证聚合反应快速且完全地进行。
此外,本发明中,所述聚合反应可以在pH为4-12的条件下进行,优选pH为5-10,更优选pH为6-9。
另外,所述聚合反应优选在惰性气体的存在下进行,所述惰性气体例如可以为氮气、氩气和氦气等,没有特别的限定。
本发明中,所述增粘剂的制备方法进一步包括:聚合反应结束后,将聚合反应所得产物进行造粒,接着与无机碱混捏后进行水解,得到水解产物,再将所得水解产物进行造粒、干燥和粉碎。
本发明中,对所述无机碱没有特别的限定,例如可以氢氧化钠、氢氧化钾和碳酸钠中的一种或多种,优选为氢氧化钠和/或氢氧化钾。
此外,本发明中,所述无机碱的用量没有特别的限定,例如,以聚合单体总重量(式(A)所示单体、式(B)所示单体、式(C)所示单体以及任选的式(D)所示单体和任选的式(E)所示单体的总量)为100重量份计,所述无机碱的用量可以为5-30重量份,优选为20-30重量份。
此外,本发明中,对所述水解的温度和时间等条件没有特别的限定,例如可以为40-100℃,优选为60-90℃,更优选为80-85℃;所述水解的时间例如可以为0.5-6h,优选为1-4h,更优选为2-3h。
本发明中,为了得到颗粒均匀的所述增粘剂,进一步地,所述制备方法还包括将粉碎后的产物进行筛分。
本发明中,所述造粒、干燥、粉碎和筛分等操作的方法均无特殊限定,可以采用本 领域常规或已知的方法进行,此处不再赘述。
根据本发明的第三方面所述方法制备得到的聚合物的红外谱图中,在1653cm
-1附近未发现存在C=C伸缩振动峰,且在3017cm
-1附近未发现存在双键的C-H伸缩振动峰,由此可以表明上述聚合反应进行充分,不存在未反应的残留单体。
另外,本发明第三方面制备得到的增粘剂具有本发明第一方面所述聚合物和本发明第二方面所述增粘剂的性能,此处不再赘述。
本发明第四方面提供一种钻井液,所述钻井液含有本发明第一方面所述聚合物或本发明第二方面所述增粘剂。并且优选地,所述钻井液为无固相钻井液,即所述钻井液中不含所述粘土和所述加重剂。
根据本发明第四方面,所述钻井液中,所述聚合物或所述增粘剂的含量可以为0.1-3重量%,优选为0.5-1.5重量%,由此,可以进一步提高所述钻井液的悬浮和携带岩屑性能。
此外,本发明所述钻井液的密度可以为1.01-2.30g/cm
3,优选为1.10-1.80g/cm
3。
为了更好地说明本发明,下面结合实施例和对比例来进一步说明本发明的作用和效果,但本发明的范围不只局限于这些实施例。
以下实施例和对比例中,如无特别说明,所用材料均为常规市售品。
以下实施例和对比例中,粘均分子量根据GB12005.10-92中规定的方法测定,即,采用公式M=802[η]
1.25来计算聚合物的粘均分子量,其中,[η]为特性粘数,其按照GB12005.1-89所述方法测得。
表观粘度按照GB/T 16783.1中规定的方法测定。
以下实施例中使用的2-丙烯酰氧基-1,2,3-三羧基丙烷按照下述方法制备得到:
1)在单口烧瓶中加入19.2g的柠檬酸和80mL的N,N'-二甲基甲酰胺(DMF),之后搅拌至柠檬酸完全溶解;
2)用恒压滴液漏斗缓慢滴加20mL丙烯酰氯的DMF溶液(其中丙烯酰氯的含量为0.45g/mL),反应12h后,减压蒸馏除去DMF,得到产物,通过核磁共振分析可知所得产物即为2-丙烯酰氧基-1,2,3-三羧基丙烷。
实施例1
1)在配料釜中加入2840kg(40kmol)丙烯酰胺、6210kg(30kmol)2-丙烯酰胺基-2-甲基丙磺酸、246kg(1kmol)2-丙烯酰氧基-1,2,3-三羧基丙烷、66kg(0.67kmol)N,N-二甲基丙烯酰胺、125.6kg(0.8kmol)甲基丙烯酸二甲氨基乙酯以及重量为上述单体总重量4倍的去离子水,在搅拌状态下,用冷冻盐水控制溶液温度为-7℃,加入氢氧化钠 调节pH至7,得到混合单体溶液;
2)将步骤1)所得混合单体溶液泵入聚合釜中,通高纯氮气除氧0.5h后,依次加入14.12kg的N,N,N’,N’-四甲基乙二胺、6.04kg亚硫酸氢钠、13.44kg过硫酸铵和14.4kg的2,2’-偶氮(2-脒基丙烷)二盐酸盐,在-7℃下静置聚合反应10h,得到聚合物凝胶;
3)打开反应釜底球阀,用0.3MPa压缩空气将步骤2)得到的聚合物凝胶压出,通过造粒机造粒成4-6毫米的胶粒,之后取1500kg胶粒与400kg氢氧化钠粒颗粒捏合接触,在温度85℃下水解2h,经二次造粒后,在75℃热风条件下干燥2h后粉碎筛分至20-80目,得到聚合物A1。
聚合物A1的特性粘数和粘均分子量如表1所示。
聚合物A1的红外谱图如图1所示,通过图1可知,聚合物A1在1403cm
-1和1573cm
-1附近存在COO-共轭体系伸缩振动峰,在614cm
-1和1051cm
-1附近存在S=O特征振动峰,且在1192cm
-1附近存在叔胺C-N的特征振动峰,由此可以说明单体2-丙烯酰胺基-2-甲基丙磺酸、2-丙烯酰氧基-1,2,3-三羧基丙烷和甲基丙烯酸二甲氨基乙酯成功聚合。
此外,聚合物A1的红外谱图中,在1653cm
-1附近未发现存在C=C伸缩振动峰,且在3017cm
-1附近未发现存在双键的C-H伸缩振动峰。由此可以说明聚合反应充分,不存在未反应的残留单体。
实施例2
1)在配料釜中加入3550kg(50kmol)丙烯酰胺、4140kg(20kmol)2-丙烯酰胺基-2-甲基丙磺酸、246kg(1kmol)2-丙烯酰氧基-1,2,3-三羧基丙烷、61.88kg(0.625kmol)N,N-二甲基丙烯酰胺、98.12kg(0.625kmol)甲基丙烯酸二甲氨基乙酯以及重量为上述单体总重量3倍的去离子水,在搅拌状态下,用冷冻盐水控制溶液温度为-5℃,加入氢氧化钠调节pH至8,得到混合单体溶液;
2)将步骤1)所得混合单体溶液泵入聚合釜中,通高纯氮气除氧0.5h后,依次加入12.2kg的N,N,N’,N’-四甲基乙二胺、8.2kg亚硫酸氢钠、8.7kg过硫酸铵和19.4kg的2,2’-偶氮(2-脒基丙烷)二盐酸盐,在-5℃下静置聚合反应9h,得到聚合物凝胶;
3)打开反应釜底球阀,用0.3MPa压缩空气将步骤2)得到的聚合物凝胶压出,通过造粒机造粒成4-6毫米的胶粒,之后取1500kg胶粒与400kg氢氧化钠颗粒捏合接触,在温度85℃下水解2h,经二次造粒后,在75℃热风条件下干燥2h后粉碎筛分至20-80目,得到聚合物A2。
聚合物A2的特性粘数和粘均分子量如表1所示。
聚合物A2的红外谱图与聚合物A1相似。
实施例3
1)在配料釜中加入2130kg(30kmol)丙烯酰胺、8280kg(40kmol)2-丙烯酰胺基-2-甲基丙磺酸、246kg(1kmol)2-丙烯酰氧基-1,2,3-三羧基丙烷、74.25kg(0.75kmol)N,N-二甲基丙烯酰胺、157kg(1kmol)甲基丙烯酸二甲氨基乙酯以及重量为上述单体总重量5倍的去离子水,在搅拌状态下,用冷冻盐水控制溶液温度为-10℃,加入氢氧化钠调节pH至9,得到混合单体溶液;
2)将步骤1)所得混合单体溶液泵入聚合釜中,通高纯氮气除氧0.5h后,依次加入10.4kg的N,N,N’,N’-四甲基乙二胺、2.6kg亚硫酸氢钠、13kg过硫酸铵和6.5kg的2,2’-偶氮(2-脒基丙烷)二盐酸盐,在-10℃下静置聚合反应8h,得到聚合物凝胶;
3)打开反应釜底球阀,用0.3MPa压缩空气将步骤2)得到的聚合物凝胶压出,通过造粒机造粒成4-6毫米的胶粒,之后取1500kg胶粒与400kg氢氧化钠粒碱捏合接触,在温度85℃下水解2h,经二次造粒后,在75℃热风条件下干燥2h后粉碎筛分至20-80目,得到聚合物A3。
聚合物A3的特性粘数和粘均分子量如表1所示。
聚合物A3的红外谱图与聚合物A1相似。
实施例4
按照与实施例1相同的方法进行,不同的是,
步骤1)中,在配料釜中加入5680kg(80kmol)丙烯酰胺、2070kg(10kmol)2-丙烯酰胺基-2-甲基丙磺酸、246kg(1kmol)2-丙烯酰氧基-1,2,3-三羧基丙烷、79.2kg(0.8kmol)N,N-二甲基丙烯酰胺、125.6kg(0.8kmol)甲基丙烯酸二甲氨基乙酯以及重量为上述单体总重量4倍的去离子水;
步骤2)中,依次加入12kg的N,N,N’,N’-四甲基乙二胺、5.2kg亚硫酸氢钠、11.5kg过硫酸铵和12.3kg的2,2’-偶氮(2-脒基丙烷)二盐酸盐。
得到聚合物A4。
聚合物A4的特性粘数和粘均分子量如表1所示。
聚合物A4的红外谱图与聚合物A1相似。
实施例5
按照实施例1所述方法进行,不同的是,步骤1)中,
不加入甲基丙烯酸二甲氨基乙酯,得到聚合物A5。
聚合物A5的特性粘数和粘均分子量如表1所示。
在聚合物A5的红外谱图中,在1403cm
-1和1573cm
-1附近存在COO-共轭体系伸缩振动峰,在614cm
-1和1051cm
-1附近存在S=O特征振动峰,由此可以说明单体2-丙烯 酰胺基-2-甲基丙磺酸和2-丙烯酰氧基-1,2,3-三羧基丙烷成功聚合。
此外,聚合物A5的红外谱图中,在1653cm
-1附近未发现存在C=C伸缩振动峰,且在3017cm
-1附近未发现存在双键的C-H伸缩振动峰。由此可以说明聚合反应充分,不存在未反应的残留单体。
实施例6
按照实施例1所述方法进行,不同的是,步骤1)中,
不加入N,N-二甲基丙烯酰胺,得到聚合物A6。
聚合物A6的特性粘数和粘均分子量如表1所示。
在聚合物A6的红外谱图中,在1403cm
-1和1573cm
-1附近存在COO-共轭体系伸缩振动峰,在614cm
-1和1051cm
-1附近存在S=O特征振动峰,并且在1192cm
-1附近存在叔胺C-N的特征振动峰,由此可以说明单体2-丙烯酰胺基-2-甲基丙磺酸、2-丙烯酰氧基-1,2,3-三羧基丙烷和甲基丙烯酸二甲氨基乙酯成功聚合。
此外,聚合物A6的红外谱图中,在1653cm
-1附近未发现存在C=C伸缩振动峰,且在3017cm
-1附近未发现存在双键的C-H伸缩振动峰。由此可以说明聚合反应充分,不存在未反应的残留单体。
实施例7
按照实施例1所述方法进行,不同的是,步骤1)中,
不加入N,N-二甲基丙烯酰胺和甲基丙烯酸二甲氨基乙酯,得到聚合物A7。
聚合物A7的特性粘数和粘均分子量如表1所示。
聚合物A7的红外谱图中,在1403cm
-1和1573cm
-1附近存在COO-共轭体系伸缩振动峰,在614cm
-1和1051cm
-1附近存在S=O特征振动峰,由此可以说明单体2-丙烯酰胺基-2-甲基丙磺酸和2-丙烯酰氧基-1,2,3-三羧基丙烷成功聚合。
此外,在聚合物A7的红外谱图中,在1653cm
-1附近未发现存在C=C伸缩振动峰,且在3017cm
-1附近未发现存在双键的C-H伸缩振动峰。由此可以说明聚合反应充分,不存在未反应的残留单体。
实施例8
按照实施例1所述方法进行,不同的是,步骤2)中,
将N,N,N’,N’-四甲基乙二胺替换为相同重量的亚硫酸氢钠,得到聚合物A8。
聚合物A8的特性粘数和粘均分子量如表1所示。
聚合物A8的红外谱图与A1相似。
实施例9
按照实施例1所述方法进行,不同的是,步骤2)中,
将亚硫酸氢钠替换为相同重量的N,N,N’,N’-四甲基乙二胺,得到聚合物A9。
聚合物A9的特性粘数和粘均分子量如表1所示。
聚合物A9的红外谱图与A1相似。
对比例1
按照实施例1所述方法进行,不同的是,步骤1)中,
不加入2-丙烯酰氧基-1,2,3-三羧基丙烷,得到聚合物D1。
聚合物D1的特性粘数和粘均分子量如表1所示。
对比例2
按照实施例1所述方法进行,不同的是,步骤1)中,
2-丙烯酰氧基-1,2,3-三羧基丙烷由相同摩尔羧基量的甲基丙烯酸代替,得到聚合物D2。
聚合物D2的特性粘数和粘均分子量如表1所示。
对比例3
采用雪佛龙菲利普斯化工有限公司(Chevron Phillips Chemical)生产的聚合物增粘剂
150作为聚合物D3。
聚合物D3的特性粘数和粘均分子量如表1所示。
对比例4
按照实施例1所述方法进行,不同的是,步骤1)中,
将所述5种单体替换为与上述5种单体总重量相同的2-丙烯酰氧基-1,2,3-三羧基丙烷,得到聚合物D4。
聚合物D4的特性粘数和粘均分子量如表1所示。
将聚合物D4与聚合物D1按照重量比1:1混合,得到聚合物D5。
表1:共聚物的特性粘数和粘均分子量结果
聚合物 | 特性粘数(mL/g) | 粘均分子量(10 4) |
A1 | 1679 | 862 |
A2 | 1761 | 915 |
A3 | 1606 | 816 |
A4 | 2406 | 1352 |
A5 | 1696 | 873 |
A6 | 1710 | 882 |
A7 | 1741 | 902 |
A8 | 1552 | 781 |
A9 | 1524 | 764 |
D1 | 1807 | 945 |
D2 | 1687 | 867 |
D3 | 1512 | 756 |
D4 | 482 | 181 |
测试例1
表观粘度测试
1)向350mL去离子水中加入130.9g甲酸钾,得到甲酸钾水溶液;
2)向步骤1)所得甲酸钾水溶液中加入1.75g无水碳酸钠和3.5g碳酸氢钠,搅拌均匀后在25℃±3℃的温度下密闭养护24h,之后向其中加入无水氯化钙并搅拌溶解,使得Ca
2+浓度为15000mg/L,得到无固相钻井液基浆;
3)取350g步骤2)所得无固相钻井液基浆,向其中边搅拌边缓慢加入2.45g聚合物样品,再用电动搅拌器搅拌溶解30min后,测定所得钻井液的密度为1.15g/cm
3,接着在高温滚子炉中180℃恒温滚动16h,冷却后搅拌5min,测定其对应的表观粘度AV,其结果如表2。
表2:表观粘度测定结果
聚合物 | AV/mPa·s |
A1 | 38 |
A2 | 37 |
A3 | 36 |
A4 | 28 |
A5 | 32 |
A6 | 31 |
A7 | 29 |
A8 | 33 |
A9 | 32 |
D1 | 21 |
D2 | 23 |
D3 | 17 |
D4 | 4 |
D5 | 12 |
通过表2的结果可以看出,在含钙无固相钻井液中加入本发明的聚合物作为增粘 剂,并在180℃下高温老化16h后的表观粘度可高达38mPa·s,远远优于目前国外同类产品
150(对比例3)的表观粘度,表明本发明所述聚合物具有较好的增粘性、抗温性能以及抗钙性能,能够有效改善无固相钻井液在高温、高钙环境下的流变性。
通过上述聚合物A1-A3和A4的测试结果可以看出,通过将各个单体的用量控制在本发明所述优选范围内,可以进一步提高所得聚合物的抗温抗钙性能。
通过上述聚合物A1和A5-A7的测试结果可以看出,通过在式(A)所示单体、式(B)所示单体和式(C)所示单体的基础上进一步加入式(D)所示单体和/或式(E)所示单体,可以进一步提高所得聚合物的抗温抗钙性能。
此外,通过上述聚合物A1、A8和A9的测试结果可以看出,采用同时含有无机还原剂和有机还原剂的引发剂制备所述聚合物时,能够进一步提高制备得到的聚合物的抗温抗钙性能。
以上详细描述了本发明的优选实施方式,但是,本发明并不限于此。在本发明的技术构思范围内,可以对本发明的技术方案进行多种简单变型,包括各个技术特征以任何其它的合适方式进行组合,这些简单变型和组合同样应当视为本发明所公开的内容,均属于本发明的保护范围。
Claims (17)
- 一种聚合物,其特征在于,该聚合物含有式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元,其中,R 1、R 2、R 3、R 4、R 5、R 6、R 7和R 8各自独立地为氢或C1-C10的直链或支链烷基;X为C1-C10的直链或支链亚烷基;Y为 或C1-C10的直链或支链亚烷基;M为氢或碱金属;A 1、A 2和A 3各自独立地为键或C1-C3的直链或支链亚烷基。
- 根据权利要求1所述的聚合物,其中,R 1、R 2、R 3、R 4、R 5、R 6、R 7和R 8各自独立地为氢或C1-C4的直链或支链烷基,优选为氢、甲基或乙基;优选地,R 1、R 2、R 3、R 4、R 7和R 8各自独立地为氢;优选地,R 5和R 6各自独立地为甲基;优选地,X为C1-3的直链或支链亚烷基,更优选为亚甲基或1,2-亚乙基,进一步优选为亚甲基;优选地,Y为 或C1-3的直链或支链亚烷基,更优选为 亚甲基或1,2-亚乙基,进一步优选为优选地,M为氢或钠,更优选为氢;优选地,A 1、A 2和A 3各自独立地为键、亚甲基或1,2-亚乙基,更优选为键或亚甲基,进一步优选地,A 1和A 2均为亚甲基,A 3为键。
- 根据权利要求1或2所述的聚合物,其中,式(1)所示结构单元、式(2)所示结构单元和式(3)所示结构单元的摩尔比为10-80:10-60:1;优选为30-50:20-40:1。
- 根据权利要求1-3中任意一项所述的聚合物,其中,所述聚合物还含有式(4)所示结构单元和/或式(5)所示结构单元,其中,R 9、R 10、R 13和R 14各自独立地为氢或C1-C10的直链或支链烷基,优选为氢或C1-C4的直链或支链烷基,更优选为氢、甲基或乙基;R 11和R 12各自独立地为C1-C6的直链或支链烷基,优选为C1-C4的直链或支链烷基,更优选为甲基或乙基;R 15和R 16各自独立地为氢或C1-C6的直链或支链烷基,优选为氢或C1-C4的直链或支链烷基,更优选为氢、甲基或乙基;优选地,R 9、R 10和R 13各自独立地为氢;优选地,R 11、R 12、R 14、R 15和R 16各自独立地为甲基;Z为C1-C10的直链或支链亚烷基,优选为C1-C4的直链或支链亚烷基,更优选为亚甲基或1,2-亚乙基,进一步优选为1,2-亚乙基;优选地,式(1)所示结构单元和式(4)所示结构单元摩尔比为10-100:1,更优选为40-80:1;优选地,式(1)所示结构单元和式(5)所示结构单元的摩尔比为10-100:1,更优选为30-80:1。
- 根据权利要求1-4中任意一项所述的聚合物,其中,所述聚合物的特性粘数为1200-2600mL/g,优选为1500-1900mL/g;优选地,所述聚合物的粘均分子量为600万-1500万,更优选为750万-1000万。
- 根据权利要求1-5中任意一项所述的聚合物,其中,将所述聚合物以0.7重量%的添加量加入Ca 2+浓度为15000mg/L的无固相钻井液基浆中,并在180℃老化16h后的表观粘度为28mPa·s以上,优选为36mPa·s以上。
- 根据权利要求1-6中任意一项所述的聚合物,其中,所述聚合物的红外谱图在 1403cm -1和1573cm -1附近存在COO-共轭体系伸缩振动峰,且在614cm -1和1051cm -1附近存在S=O特征振动峰。
- 一种增粘剂,该增粘剂含有丙烯酰胺骨架结构,其特征在于,该增粘剂还含有磺酸基团和-C(A 1COOH)(A 2COOH)(A 3COOH),其中A 1、A 2和A 3各自独立地为键或C1-C3的亚烷基,将该增粘剂以0.7重量%的添加量加入Ca 2+浓度为15000mg/L的无固相钻井液基浆中,并在180℃老化16h后的表观粘度为28mPa·s以上,优选为36mPa·s以上。
- 根据权利要求8所述的增粘剂,其中,磺酸基团和-COOH的摩尔比为3-20:1,优选为6-14:1,优选地,-COOH的含量不低于2mol%,更优选为不低于3.2mol%。
- 一种增粘剂的制备方法,其特征在于,所述方法包括:在聚合反应条件下,在引发剂存在下,使式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中发生聚合反应,其中,R 1、R 2、R 3、R 4、R 5、R 6、R 7和R 8各自独立地为氢或C1-C10的直链或支链烷基;X为C1-C10的直链或支链亚烷基;Y为 或C1-C10的直链或支链亚烷基;M为氢或碱金属;A 1、A 2和A 3各自独立地为键或C1-C3的直链或支链亚烷基。
- 根据权利要求10所述的方法,其中,R 1、R 2、R 3、R 4、R 5、R 6、R 7和R 8各自独立地为氢或C1-C4的直链或支链烷基,优选为氢、甲基或乙基;优选地,R 1、R 2、R 3、R 4、R 7和R 8各自独立地为氢;优选地,R 5和R 6各自独立地为甲基;优选地,X为C1-3的直链或支链亚烷基,更优选为亚甲基或1,2-亚乙基,进一步优选为亚甲基;优选地,Y为 或C1-3的直链或支链亚烷基,更优选为 亚甲基或1,2-亚乙基,进一步优选为优选地,M为氢或钠,更优选为氢;优选地,A 1、A 2和A 3各自独立地为键、亚甲基或1,2-亚乙基,更优选为键或亚甲基,进一步优选地,A 1和A 2均为亚甲基,A 3为键。
- 根据权利要求10或11所述的方法,其中,式(A)所示单体、式(B)所示单体和式(C)所示单体的摩尔比为10-80:10-60:1;优选为30-50:20-40:1。
- 根据权利要求10-12中任意一项所述的方法,其中,所述方法还包括:使式(D)所示单体和/或式(E)所示单体与式(A)所示单体、式(B)所示单体和式(C)所示单体在溶剂中发生聚合反应,其中,R 9、R 10、R 13和R 14各自独立地为氢或C1-C10的直链或支链烷基,优选为氢或C1-C4的直链或支链烷基,更优选为氢、甲基或乙基;R 11和R 12各自独立地为C1-C6的直链或支链烷基,优选为C1-C4的直链或支链烷基,更优选为甲基或乙基;R 15和R 16各自独立地为氢或C1-C6的直链或支链烷基,优选为氢或C1-C4的直链或支链烷基,更优选为氢、甲基或乙基;优选地,R 9、R 10和R 13各自独立地为氢;优选地,R 11、R 12、R 14、R 15和R 16各自独立地为甲基;Z为C1-C10的直链或支链亚烷基,优选为C1-C4的直链或支链亚烷基,更优选为亚甲基或1,2-亚乙基,进一步优选为1,2-亚乙基;优选地,式(A)所示单体和式(D)所示单体的摩尔比为10-100:1,更优选为40-80:1;优选地,式(A)所示单体和式(E)所示单体的摩尔比为10-100:1,更优选为30-80:1。
- 根据权利要求10-13中任意一项所述的方法,其中,所述引发剂含有氧化还原体类引发剂,优选地,所述氧化还原体类引发剂中的还原剂为无机还原剂和有机还原剂的混合物;优选地,所述无机还原剂和有机还原剂的混合物中,所述有机还原剂的用量为30-90重量%,更优选为60-80重量%。
- 根据权利要求10-14中任意一项所述的方法,其中,所述聚合反应的条件包括:温度为-10℃至15℃,优选为-10℃至0℃;时间为1-20小时,优选为5-10小时;pH为4-12,优选为5-10。
- 一种钻井液,其特征在于,所述钻井液含有权利要求1-7中任意一项所述的聚合物或者权利要求8或9所述的增粘剂;优选地,所述钻井液为无固相钻井液。
- 根据权利要求16所述的钻井液,其中,所述钻井液中所述聚合物或所述增粘剂的含量为0.1-3重量%,优选为0.5-1.5重量%;优选地,所述钻井液的密度为1.01-2.30g/cm 3,优选为1.10-1.80g/cm 3。