CN117887175A - 一种汽车内饰用高耐候抗黄变的pp/ps合金材料 - Google Patents
一种汽车内饰用高耐候抗黄变的pp/ps合金材料 Download PDFInfo
- Publication number
- CN117887175A CN117887175A CN202311803030.1A CN202311803030A CN117887175A CN 117887175 A CN117887175 A CN 117887175A CN 202311803030 A CN202311803030 A CN 202311803030A CN 117887175 A CN117887175 A CN 117887175A
- Authority
- CN
- China
- Prior art keywords
- resistance
- alloy material
- yellowing
- high weather
- weather resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种汽车内饰用高耐候抗黄变的PP/PS合金材料,其包括按照重量百分比的如下配方:聚丙烯30‑70%,相容剂10‑30%,聚苯乙烯30‑60%,抗黄变剂0.2‑2%,耐刮擦剂0.2‑2%,抗氧剂0.2‑2%,光稳定剂0.2‑2%,其他添加剂0‑3%。采用上述技术方案得到的高耐候抗黄变的PP/PS合金材料具有高耐候性、抗黄变性,同时兼顾综合力学性能、耐光照以及耐刮擦的PP/PS合金材料。
Description
技术领域
本发明涉及一种聚丙烯与聚苯乙烯的合金材料,具体为具有长效耐候性能,抗黄变性能,同时兼顾综合力学性能、耐光照以及耐刮擦的PP/PS合金材料,属于高分子复合材料领域。
背景技术
PP(聚丙烯)具有耐酸、碱、盐液及多种有机溶剂的腐蚀等特点,具有良好的耐化学性、耐热性、电绝缘性。但也有耐磨性差、低温下的抗冲击性能差、耐候性不佳等缺点。PS(聚苯乙烯)具有具有优良的绝热、绝缘和透明性等特点,但也有性脆,冲击强度低,易出现应力开裂等缺点,目前在汽车领域应用受限。聚丙烯和聚苯乙烯通过相容剂进行复合,兼有聚丙烯和聚苯乙烯的优点,材料耐磨性,常、低温冲击性能都有明显提升,同时可兼顾材料的综合力学性能、低散发、耐光照等性能,从而得到一种高耐候抗黄变的汽车内饰用聚丙烯/聚苯乙烯合金材料。
发明内容
本发明提供一种汽车内饰用高耐候抗黄变的PP/PS合金材料,高耐候性,抗黄变性,同时兼顾综合力学性能、耐光照以及耐刮擦的PP/PS合金材料。
本发明可以通过以下技术方案实施完成。
一种汽车内饰用高耐候抗黄变的PP/PS合金材料,其包括按照重量百分比的如下配方:聚丙烯30-70%,相容剂10-30%,聚苯乙烯30-60%,抗黄变剂0.2-2%,耐刮擦剂0.2-2%,抗氧剂0.2-2%,光稳定剂0.2-2%,其他添加剂0-3%。
所述的聚丙烯为共聚聚丙烯,优选高抗冲共聚聚丙烯。
所述的相容剂为任何合适的嵌段共聚物,包括苯乙烯-丁二烯-苯乙烯(SBS)、苯乙烯-乙烯/丁烯-苯乙烯(SEBS)、苯乙烯-乙烯/丙烯二嵌段共聚物(SEP)与苯乙烯-乙烯/丙烯-苯乙烯(SEPS)等中的一种或两种以上的组合物,优选SEBS。
所述聚苯乙烯树脂为通用级聚苯乙烯(GPPS)或抗冲击级聚苯乙烯(HIPS),优选通用级聚苯乙烯(GPPS)。
所述的抗黄变剂为硫代二丙酸二烷基酯。
所述的耐刮擦剂为芥酸酰胺、油酸酰胺、硬脂基芥酸酰胺中的一种或者组合物。
所述的抗氧剂包括主抗氧剂和辅助抗氧剂,其中主抗氧剂为受阻酚或硫酯类抗氧剂,包括但不限于1330(1,3,5-三甲基-2,4,6-(3,5-二叔丁基-4-羟基苯甲基)苯)、1076(化学名称为β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯)、DSTP(化学名称为硫代二丙酸硬脂醇酯)中的一种或以上的组合物;辅助抗氧剂为亚磷酸盐或酯类抗氧剂,包括但不限于618(化学名称为双十八烷基季戊四醇双亚磷酸酯)、168(化学名称为亚磷酸三(2,4-二叔丁基苯)酯)中的一种或两种组合。
所述的光稳定剂为受阻胺类光稳定剂770(双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯)、紫外线吸收剂4050H(N,N'-双(2,2,6,6-四甲基-4-哌啶基)-N,N'-二醛基己二胺)、紫外线吸收剂327(2-(3,5-二叔丁基-2-羟苯基)-5-氯苯并三唑)中的一种或以上的组合物。
所述的其它添加剂包括本领域技术人员认为所需的着色剂、成核剂、发泡剂、表面活性剂、增塑剂、偶联剂、阻燃剂、光稳定剂、加工助剂、抗静电助剂、抗微生物助剂、润滑剂中的一种或以上的组合物。
由本发明方案得到的一种汽车内饰用高耐候抗黄变的PP/PS合金材料,高耐候性,抗黄变性,同时兼顾综合力学性能、耐光照以及耐刮擦的PP/PS合金材料。
具体实施方式
下面结合具体实施方式,进一步阐述本发明。应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。此外还应理解,在阅读了本发明讲述的内容后,本领域技术人员可以对本发明作改动或修改,这些等价形式同样落于本申请所附权利要求书所限制的范围。
本发明实施例所用原料:
聚丙烯:熔指为2.5g/10min(230℃,2.16Kg)的共聚丙烯,浙石化公司。
相容剂:苯乙烯含量为30%的SEBS,李长荣化学工业公司。
聚苯乙烯:熔指为9.0g/10min(200℃,5Kg)的聚苯乙烯,道达尔能源公司。
抗黄变剂:Irganox PS 800,德国BASF公司。
耐刮擦剂:硬脂基芥酸酰胺,英国禾大。
抗氧剂:1076(受阻酚类抗氧剂),168(磷酸酯类抗氧剂),DSTP(硫化酯类抗氧剂)市售。
光稳定剂:Tinuvin 770,Uvinul 5050H,德国BASF公司。
其他添加剂:钛白粉,市售。
产品性能测试方法:
拉伸强度:按ISO 527方法,试样规格:1A样条。
弯曲强度/弯曲模量:按ISO 178方法,试样规格:80*10*4mm。
悬臂梁缺口冲击强度:按ISO 180方法,试样规格:80*10*4mm。
氙灯加速老化:按SAE J2412标准,能量值:1050KJ/m2,测量色差ΔE值。
气味:按PV 3900标准,80℃,2h。
总碳:按PV 3341标准。
把共聚丙烯、SEBS、聚苯乙烯、Irganox PS 800、硬脂基芥酸酰胺、抗氧剂1076/168/DSTP、Tinuvin 770/Uvinul 5050H、钛白粉等按表1中所组成比例混合均匀后经双螺杆挤出机(螺杆直径35mm,长径比L/D=40)主机筒中,主机筒分10段控制温度(从加料口至机头出口)为150℃、220℃、210℃、215℃、215℃、205℃、205℃、205℃、205℃、200℃,双螺杆转速为300转/分钟,经多级真空抽提有害气体,挤出料条经过水槽冷却后切粒得到产品。产品切粒完成后需要批混。将上述产品用塑料注射成型机注塑成标准样条和标准光板(150*100*3.2mm),注塑温度210℃。注塑好的样条和光板立即放入玻璃干燥器中在室温放置至少24小时后进行性能和光照测试。测试结果见表1。
表1聚丙烯/聚苯乙烯组合物的组成和性能
从表1中对比例1-2以及实施例1-3中可以看出,未添加抗黄变剂Irganox PS 800和光稳定剂进行复配,材料因易发生黄变而导致灰度等级不达标,通过光稳定剂和抗黄变剂复配,光照试验后灰度等级可以做到≥4级。同时,多级真空对气味和总碳有明显贡献,可以满足汽车内饰材料的要求。而且以上实施例能够实现优异的机械性能。
本发明提供一种汽车内饰用高耐候抗黄变的PP/PS合金材料,兼有聚丙烯和聚苯乙烯的优点,材料耐磨性,常、低温冲击性能都有明显提升,同时可兼顾材料的综合力学性能、低散发、耐光照等性能,从而得到一种高耐候抗黄变的汽车内饰用聚丙烯/聚苯乙烯合金材料。
Claims (10)
1.一种汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:其包括按照重量百分比的如下配方:
聚丙烯30-70%;
相容剂10-30%;
聚苯乙烯30-60%;
抗黄变剂0.2-2%;
耐刮擦剂0.5-2%;
抗氧剂0.2-2%;
光稳定剂0.2-2%;
其他添加剂0-3%。
2.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述的聚丙烯为高抗冲共聚聚丙烯。
3.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述相容剂为嵌段共聚物,包括苯乙烯-丁二烯-苯乙烯(SBS)、苯乙烯-乙烯/丁烯-苯乙烯(SEBS)、苯乙烯-乙烯/丙烯二嵌段共聚物(SEP)与苯乙烯-乙烯/丙烯-苯乙烯(SEPS)等中的一种或两种以上的组合物。
4.如权利要求3所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述相容剂为SEBS。
5.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述聚苯乙烯树脂为通用级聚苯乙烯(GPPS)或抗冲击级聚苯乙烯(HIPS),优选通用级聚苯乙烯(GPPS)。
6.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述抗黄变剂为硫代二丙酸二烷基酯。
7.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述耐刮擦剂为芥酸酰胺、油酸酰胺、硬脂基芥酸酰胺中的一种或者组合物。
8.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述所述抗氧剂包括主抗氧剂和辅助抗氧剂,其中主抗氧剂为受阻酚或硫酯类抗氧剂,包括但不限于1330(1,3,5-三甲基-2,4,6-(3,5-二叔丁基-4-羟基苯甲基)苯)、1076(化学名称为β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯)、DSTP(化学名称为硫代二丙酸硬脂醇酯)中的一种或以上的组合物;辅助抗氧剂为亚磷酸盐或酯类抗氧剂,包括但不限于618(化学名称为双十八烷基季戊四醇双亚磷酸酯)、168(化学名称为亚磷酸三(2,4-二叔丁基苯)酯)中的一种或两种组合。
9.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述光稳定剂为受阻胺类光稳定剂770(双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯)、紫外线吸收剂4050H(N,N'-双(2,2,6,6-四甲基-4-哌啶基)-N,N'-二醛基己二胺)、紫外线吸收剂327(2-(3,5-二叔丁基-2-羟苯基)-5-氯苯并三唑)中的一种或以上的组合物。
10.如权利要求1所述的汽车内饰用高耐候抗黄变的PP/PS合金材料,其特征在于:所述其它添加剂包括本领域技术人员认为所需的着色剂、成核剂、发泡剂、表面活性剂、增塑剂、偶联剂、阻燃剂、光稳定剂、加工助剂、抗静电助剂、抗微生物助剂、润滑剂中的一种或以上的组合物。