CN117801531A - 一种家用菜板硅胶保护套及其加工工艺 - Google Patents
一种家用菜板硅胶保护套及其加工工艺 Download PDFInfo
- Publication number
- CN117801531A CN117801531A CN202410032348.2A CN202410032348A CN117801531A CN 117801531 A CN117801531 A CN 117801531A CN 202410032348 A CN202410032348 A CN 202410032348A CN 117801531 A CN117801531 A CN 117801531A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- protective sleeve
- chopping board
- gel protective
- household
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于家庭用具技术领域，提供了一种家用菜板硅胶保护套及其加工工艺，包括备料、原料初筛、原料混合、充模、硬化、脱模、后处理、检查和包装等步骤；本发明通过加入防水剂，可以使制备完成家用菜板硅胶保护套具备防水效果，可以减少菜板硅胶保护套在使用时被水侵蚀而产生腐蚀情况的方法，且加入减水剂，可以使制备的菜板硅胶保护套润滑度提高，增强了菜板硅胶保护套制备的效果，同时通过采用物料切割法可以将模具的物料进行切割，接着通过按压可以将模具物料中含有的气体进行去除，防止菜板硅胶保护套成品内部含有水分及空气，提高了成品的质量，进而延长了家用菜板硅胶保护套的使用寿命。
Description
技术领域
本发明属于家庭用具技术领域，具体地说是一种家用菜板硅胶保护套及其加工工艺。
背景技术
家用菜板硅胶保护套是一种用于保护菜板的物件，其通常由食品级硅胶制成，具有柔软、耐用、防滑等特点。家用菜板硅胶保护套的主要功能包括、防止划痕、增加稳定性、防止菜汁渗透、保护菜板寿命等优点。
目前的家用菜板硅胶保护套在进行制备时，往往生产的成品具有一些瑕疵，例如内部含有水分及空气，导致成品的质量降低，缩短了家用菜板硅胶保护套的使用寿命。
为此，本领域技术人员提出了一种家用菜板硅胶保护套及其加工工艺来解决背景技术提出的问题。
发明内容
为了解决上述技术问题，本发明提供一种家用菜板硅胶保护套及其加工工艺，以解决现有技术中家用菜板硅胶保护套在进行制备时，往往生产的成品具有一些瑕疵，例如内部含有水分及空气，导致成品的质量降低，缩短了家用菜板硅胶保护套的使用寿命等问题。
一种家用菜板硅胶保护套，所述家用菜板硅胶保护套包括如下重量百分比的原料：90-95％硅胶原料、5-10％硬化剂和辅助材料。
优选的，所述硅胶原料包括二氧化硅(S iO2)和有机硅；所述硬化剂为过氧化物和硼酸中的一种至多种，所述硬化剂是一种用于加速硅胶固化的物质；所述辅助材料包括颜色素、热稳定剂、防水剂和减水剂，颜色素用于染色、热稳定剂用于增强硅胶的耐热性、防水剂用于防水、减水剂用于增强硅胶的润滑效果。
优选的，一种家用菜板硅胶保护套的加工工艺，包括以下步骤：
S1、备料：首先选择适量的硅胶原料、硬化剂、颜色素、热稳定剂、防水剂和减水剂，要保证硅胶原料、硬化剂、颜色素、热稳定剂、防水剂和减水剂过量有剩余；
S2、原料初筛：将上述原料进行分别放在振动筛进行筛选，得到筛选后的原料；
S3、原料混合：按照一定比例将硅胶原料和硬化剂混合在一起，得到混合体，然后将混合体与颜色素、热稳定剂、防水剂和减水剂混合均匀得到混合料；
S4、充模：将混合料倒入硅胶模具中，采用模具一角进行倒料的方式进行倒入，并在倒料的同时进行物料轻微搅动处理，使物料充满整个模具；
S5、然后采用物料切割法对模具内原料进行处理将模具中的气泡作第一次去除；接着再采用振动机将模具中的气泡作第二次去除；
S6、硬化：将装有硅胶原料的模具放置在恒温器中进行硬化，所述恒温器的温度控制在100-120℃；
S7、脱模：硅胶经过硬化后，可以将其从模具中取出；
S8、后处理：将脱模后的硅胶保护套采用打磨器进行修整边缘，直至其表面整齐平滑。
S9、检查：对硅胶保护套进行质量检查，确保没有瑕疵和损坏。
S10、包装：最后可以根据需要进行包装，以便销售和运输。
优选的，在步骤S2中，所述振动筛的目数为20-40目。
优选的，在步骤S4中，所述硅胶模具表面进行涂层处理或加工处理，可以提高硅胶模具的耐腐蚀性和使用寿命，减少维护和更换成本，硅胶模具内外干净无杂质，且硅胶模具内部喷涂脱模剂。
优选的，在步骤S5中，所述物料切割法的操作步骤如下：
S51、首先选择适宜大小的切割刀；
S52、接着采用切割刀将模具的物料进行九宫格进行切割；
S53、然后将切割物料后的模具进行轻微按压，并往复重复几次。
优选的，在步骤S6中，所述硬化的时间为8-24小时。
优选的，在步骤S10中，所述包装采用抽真空包装，真空包装可以有效降低氧气的含量，减缓氧化反应的发生，从而延缓橡胶老化的过程。
与现有技术相比，本发明具有如下有益效果：
1、本发明通过加入防水剂，可以使制备完成家用菜板硅胶保护套具备防水效果，可以减少菜板硅胶保护套在使用时被水侵蚀而产生腐蚀情况的方法，且加入减水剂，可以使制备的菜板硅胶保护套润滑度提高，增强了菜板硅胶保护套制备的效果。
2、本发明通过采用模具一角进行倒料的方式进行倒入，并在倒料的同时进行物料轻微搅动处理，使物料充满整个模具，且在硅胶模具表面进行涂层处理或加工处理，可以提高硅胶模具的耐腐蚀性和使用寿命，减少维护和更换成本，硅胶模具内外干净无杂质，且硅胶模具内部喷涂脱模剂，便于后续的脱模处理。
3、本发明通过采用物料切割法可以将模具的物料进行切割，接着通过按压可以将模具物料中含有的气体进行去除，防止菜板硅胶保护套成品内部含有水分及空气，提高了成品的质量，进而延长了家用菜板硅胶保护套的使用寿命，同时通过往复操作，可以防止空气和水分的残留，提高了制备的实用性。
附图说明
图1为本发明的家用菜板硅胶保护套的加工工艺流程图。
具体实施方式
下面结合附图和实施例对本发明的实施方式作进一步详细描述。以下实施例用于说明本发明，但不能用来限制本发明的范围。
如附图1所示：
实施例：本发明提供一种家用菜板硅胶保护套，所述家用菜板硅胶保护套包括如下重量百分比的原料：90-95％硅胶原料、5-10％硬化剂和辅助材料。
具体的，所述硅胶原料包括二氧化硅(S iO2)和有机硅；所述硬化剂为过氧化物和硼酸中的一种至多种，所述硬化剂是一种用于加速硅胶固化的物质；所述辅助材料包括颜色素、热稳定剂、防水剂和减水剂，颜色素用于染色、热稳定剂用于增强硅胶的耐热性、防水剂用于防水、减水剂用于增强硅胶的润滑效果
由上可知，通过加入防水剂，可以使制备完成家用菜板硅胶保护套具备防水效果，可以减少菜板硅胶保护套在使用时被水侵蚀而产生腐蚀情况的方法，且加入减水剂，可以使制备的菜板硅胶保护套润滑度提高，增强了菜板硅胶保护套制备的效果。
一种家用菜板硅胶保护套的加工工艺，包括以下步骤：
S1、备料：首先选择适量的硅胶原料、硬化剂、颜色素、热稳定剂、防水剂和减水剂，要保证硅胶原料、硬化剂、颜色素、热稳定剂、防水剂和减水剂过量有剩余；
S2、原料初筛：将上述原料进行分别放在振动筛进行筛选，所述振动筛的目数为20-40目，得到筛选后的原料；
S3、原料混合：按照一定比例将硅胶原料和硬化剂混合在一起，得到混合体，然后将混合体与颜色素、热稳定剂、防水剂和减水剂混合均匀得到混合料；
S4、充模：将混合料倒入硅胶模具中，采用模具一角进行倒料的方式进行倒入，并在倒料的同时进行物料轻微搅动处理，使物料充满整个模具，所述硅胶模具表面进行涂层处理或加工处理，可以提高硅胶模具的耐腐蚀性和使用寿命，减少维护和更换成本，硅胶模具内外干净无杂质，且硅胶模具内部喷涂脱模剂，便于后续的脱模处理；
S5、然后采用物料切割法对模具内原料进行处理将模具中的气泡作第一次去除；接着再采用振动机将模具中的气泡作第二次去除；
S6、硬化：将装有硅胶原料的模具放置在恒温器中进行硬化，所述硬化的时间为8-24小时，所述恒温器的温度控制在100-120℃；
S7、脱模：硅胶经过硬化后，可以将其从模具中取出；
S8、后处理：将脱模后的硅胶保护套采用打磨器进行修整边缘，直至其表面整齐平滑。
S9、检查：对硅胶保护套进行质量检查，确保没有瑕疵和损坏。
S10、包装：最后可以根据需要进行包装，所述包装采用抽真空包装，以便销售和运输。
由上可知，通过备料、原料初筛、原料混合、充模、硬化、脱模、后处理、检查和包装步骤，增强了菜板硅胶保护套制备效果，适合大面积的推广与应用。
具体的，所述物料切割法的操作步骤如下：
S51、首先选择适宜大小的切割刀；
S52、接着采用切割刀将模具的物料进行九宫格进行切割；
S53、然后将切割物料后的模具进行轻微按压，并往复重复几次。
由上可知，通过采用物料切割法可以将模具的物料进行切割，接着通过按压可以将模具物料中含有的气体进行去除，防止菜板硅胶保护套成品内部含有水分及空气，提高了成品的质量，进而延长了家用菜板硅胶保护套的使用寿命，同时通过往复操作，可以防止空气和水分的残留，提高了制备的实用性。
应用例
选择20例采用实施例制备方法制备的家用菜板硅胶保护套进行检测(实验组)，然后选择20例目前常规制备方法制备的家用菜板硅胶保护套进行检测(对照组)，检测的项目为：防水性能(％)、耐腐蚀性(％)、稳定性(％)、抗划性(％)，得到下表：
| 组别 | 防水性能(％) | 耐腐蚀性(％) | 稳定性(％) | 抗划性(％) |
| 实验组 | 79.6 | 56.4 | 88.6 | 73.5 |
| 对照组 | 67.1 | 40.6 | 72.5 | 59.4 |
由上表可知，该实施例的家用菜板硅胶保护套的防水性能、耐腐蚀性、稳定性、抗划性显著优于对照组，可以有效延长了家用菜板硅胶保护套的使用寿命。
本发明的实施例是为了示例和描述起见而给出的，尽管上面已经示出和描述了本发明的实施例，可以理解的是，上述实施例是示例性的，不能理解为对本发明的限制，本领域的普通技术人员在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。
Claims (8)
1.一种家用菜板硅胶保护套，其特征在于：所述家用菜板硅胶保护套包括如下重量百分比的原料：90-95％硅胶原料、5-10％硬化剂和辅助材料。
2.如权利要求1所述一种家用菜板硅胶保护套，其特征在于：所述硅胶原料包括二氧化硅(SiO2)和有机硅；所述硬化剂为过氧化物和硼酸中的一种至多种，所述硬化剂是一种用于加速硅胶固化的物质；所述辅助材料包括颜色素、热稳定剂、防水剂和减水剂。
3.如权利要求1-2任意一项所述一种家用菜板硅胶保护套的加工工艺，其特征在于：包括以下步骤：
S1、备料：首先选择适量的硅胶原料、硬化剂、颜色素、热稳定剂、防水剂和减水剂；
S2、原料初筛：将上述原料进行分别放在振动筛进行筛选，得到筛选后的原料；
S3、原料混合：按照一定比例将硅胶原料和硬化剂混合在一起，得到混合体，然后将混合体与颜色素、热稳定剂、防水剂和减水剂混合均匀得到混合料；
S4、充模：将混合料倒入硅胶模具中，使物料充满整个模具；
S5、然后采用物料切割法对模具内原料进行处理将模具中的气泡作第一次去除；接着再采用振动机将模具中的气泡作第二次去除；
S6、硬化：将装有硅胶原料的模具放置在恒温器中进行硬化；
S7、脱模：硅胶经过硬化后，可以将其从模具中取出；
S8、后处理：将脱模后的硅胶保护套进行修整边缘，直至其表面整齐平滑。
S9、检查：对硅胶保护套进行质量检查，确保没有瑕疵和损坏。
S10、包装：最后可以根据需要进行包装，以便销售和运输。
4.如权利要求1所述一种家用菜板硅胶保护套的加工工艺，其特征在于：在步骤S2中，所述振动筛的目数为20-40目。
5.如权利要求1所述一种家用菜板硅胶保护套的加工工艺，其特征在于：在步骤S4中，所述硅胶模具表面进行涂层处理或加工处理，且硅胶模具内外干净无杂质，且硅胶模具内部喷涂脱模剂。
6.如权利要求1所述一种家用菜板硅胶保护套的加工工艺，其特征在于：在步骤S5中，所述物料切割法的操作步骤如下：
S51、首先选择适宜大小的切割刀；
S52、接着采用切割刀将模具的物料进行九宫格进行切割；
S53、然后将切割物料后的模具进行轻微按压，并往复重复几次。
7.如权利要求1所述一种家用菜板硅胶保护套的加工工艺，其特征在于：在步骤S6中，所述硬化的时间为8-24小时。
8.如权利要求1所述一种家用菜板硅胶保护套的加工工艺，其特征在于：在步骤S10中，所述包装采用抽真空包装。