CN1176766C - 非预热铝碳锆质浸入式水口及其制造方法 - Google Patents
非预热铝碳锆质浸入式水口及其制造方法 Download PDFInfo
- Publication number
- CN1176766C CN1176766C CNB02100062XA CN02100062A CN1176766C CN 1176766 C CN1176766 C CN 1176766C CN B02100062X A CNB02100062X A CN B02100062XA CN 02100062 A CN02100062 A CN 02100062A CN 1176766 C CN1176766 C CN 1176766C
- Authority
- CN
- China
- Prior art keywords
- aluminium carbon
- immersion type
- preheating
- carbon zirconium
- type sprue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本发明提供一种非预热铝碳锆质浸入式水口及其制造方法，作为浸入式水口的铝碳锆材质由以下按重量百分数计的组份组成：鳞片石墨10-35%，碳化硅1-10%，赛隆5-15%，电熔锆莫来石5-15%，白刚玉35-50%，其余为低导热系数的耐火材料。本发明的浸入式水口具有良好的热震稳定性、抗冲击性，不需预热即可安全使用，提高了使用寿命，大大提高了连续铸钢的作业效率，并且降低了成本。
Description
技术领域
本发明涉及一种无机非金属耐火材料产品，尤其是涉及在连续铸钢生产中使用的一种非预热铝碳锆质浸入式水口。
背景技术
目前国内外生产的普通铝碳质、铝碳锆质浸入式水口，在使用前必须均匀加热至1100-1200℃才能正常使用，如果预热不当，升温过快或达不到预热温度，浸入式水口在开浇或拉钢过程中就会出现炸裂，影响正常连续生产；另外如果保温时间过长，就会在高温状态下使铝碳锆材质氧化，缩短浸入式水口的使用寿命，直接影响连续铸钢生产的效率。
发明内容
本发明的目的是提供一种可以不经过预热直接使用、具有良好的热震稳定性、抗热冲击性，而且安全可靠，使用寿命长的浸入式水口。
本发明另一目的是提供一种上述浸入式水口的制造方法。
为了克服现有技术中的缺点，本发明人经过深入研究，发现了本发明的非预热铝碳锆质浸入式水口。
本发明是采用下述方法实现的。
本发明铝碳锆质浸入式水口的特征是作为浸入式水口的铝碳锆材质由以下组份组成(按重量百分数计，以下同)：鳞片石墨10-35％，碳化硅1-10％，赛隆(sialon)5-15％，电熔锆莫来石5-15％，白刚玉35-50％，其余为低导热系数的耐火材料。
上述的低导热系数的耐火材料为氧化铝空心球或氧化锆空心球或漂珠。
上述原材料均可以在市场上买到。
上述铝碳锆材质优选由以下组份组成：鳞片石墨25％，碳化硅5％，赛隆5％，电熔锆莫来石10％，白刚玉48％，氧化铝空心球7％。
上述铝碳锆材质还优选由以下组份组成：鳞片石墨23％，碳化硅5％，赛隆7％，电熔锆莫来石10％，白刚玉47％，氧化锆空心球8％。
上述铝碳锆材质还优选由以下组份组成：鳞片石墨22％，碳化硅5％，赛隆10％，电熔锆莫来石10％，白刚玉48％，漂珠5％。
为了制造本发明的非预热浸入式水口，将上述无机非金属材料均匀混合，往其中加入上述组份重量之合10％的酚醛树脂结合剂，使用高速造粒机将原料造粒，造粒料经流动烘干床烘干，使挥发份满足成型要求，使用冷等静压机在120-150MPa下成型，成型产品在梭式窑炉中于1200-1300℃及还原气氛下烧制，烧成产品经过立式仿型车床加工，产品表面再涂敷防氧化涂层，烘干后即制成非预热浸入式水口。
和现有技术的产品比较，本发明的产品具有突出的特点和显著的优点：由于本发明采用了抗热震性高，膨胀系数小，化学稳定性高的赛隆，锆莫来石，白刚玉及低导热系数的耐火材料，使浸入式水口具有良好的热震稳定性、抗冲击性，不需预热即可安全使用，在渣线的抗侵蚀性及使用寿命方面提高了20-33％，大大提高了连续铸钢的作业效率，由于节约了烘烤能源，避免了因烘烤可能引起的质量事故，因此降低了成本，并且改善了操作条件，降低了工人劳动强度。
具体实施方式
实施例1
铝碳锆材质的各组份为：
鳞片石墨 25Kg；
碳化硅 5Kg；
赛隆 5Kg；
电熔锆莫来石 10Kg；
白刚玉 48Kg；
氧化铝空心球 7Kg。
将以上组份均匀混合，加入10Kg酚醛树脂结合剂，按照前文所述的方法制造成浸入式水口。
实施例2
铝碳锆材质的各组份为：
鳞片石墨 23Kg；
碳化硅 5Kg；
赛隆 7Kg；
电熔锆莫来石 10Kg；
白刚玉 47Kg；
氧化锆空心球 8Kg。
将以上组份均匀混合，加入10Kg酚醛树脂结合剂，按照前文所述的方法制造成浸入式水口。
实施例3
铝碳锆材质的各组份为：
鳞片石墨 22Kg；
碳化硅 5Kg；
赛隆 10Kg；
电熔锆莫来石 10Kg；
白刚玉 48Kg；
漂珠 5Kg。
将以上组份均匀混合，加入10Kg酚醛树脂结合剂，按照前文所述的方法制造成浸入式水口。
上述产品的性能如表1所示。
表1本发明浸入式水口的性能
| 实施例1产品 | 实施例2产品 | 实施例3产品 | |
| 显气孔率％ | 14.5 | 14.8 | 15.1 |
| 耐压强度MPa | 33.5 | 32.8 | 31.5 |
| 抗折强度MPa | 8.5 | 8.2 | 8.0 |
| 使用寿命min | 280 | 300 | 290 |
| 侵蚀渣线厚度mm | 10 | 11 | 11 |
| 开浇时有无炸裂现象 | 无 | 无 | 无 |
从以上数据可以看出本发明的非预热浸入式水口的性能十分优良。
综上所述，本发明的新型非预热铝碳锆质浸入式水口具有良好的热震稳定性、抗冲击性，不需预热即可安全使用，提高了使用寿命，大大提高了连续铸钢的作业效率，并且降低了成本。
Claims (6)
1.一种非预热铝碳锆质浸入式水口，其特征是作为浸入式水口的铝碳锆材质由以下按重量百分数计的组份组成：鳞片石墨10-35％，碳化硅1-10％，赛隆5-15％，电熔锆莫来石5-15％，白刚玉35-50％，其余为低导热系数的耐火材料。
2.按照权利要求1的非预热铝碳锆质浸入式水口，其特征是所述的低导热系数的耐火材料为氧化铝空心球或氧化锆空心球或漂珠。
3.按照权利要求2的非预热铝碳锆质浸入式水口，其特征是所述鳞片石墨25％，碳化硅5％，赛隆5％，电熔锆莫来石10％，白刚玉48％，氧化铝空心球7％。
4.按照权利要求2的非预热铝碳锆质浸入式水口，其特征是所述鳞片石墨23％，碳化硅5％，赛隆7％，电熔锆莫来石10％，白刚玉47％，氧化锆空心球8％。
5.按照权利要求2的非预热铝碳锆质浸入式水口，其特征是所述鳞片石墨22％，碳化硅5％，赛隆10％，电熔锆莫来石10％，白刚玉48％，漂珠5％。
6.一种非预热铝碳锆质浸入式水口的制造方法，其特征是作为浸入式水口的铝碳锆材质由以下按重量百分数计的组份组成：鳞片石墨10-35％，碳化硅1-10％，赛隆5-15％，电熔锆莫来石5-15％，白刚玉35-50％，其余为低导热系数的耐火材料；制造方法是将上述无机非金属材料均匀混合，往其中加入上述组份重量之合10％的酚醛树脂结合剂，使用高速造粒机将原料造粒，造粒料经流动烘干床烘干，使挥发份满足成型要求，使用冷等静压机在120-150MPa下成型，成型产品在梭式窑炉中于1200-1300℃及还原气氛下烧制，烧成产品经过立式仿型车床加工，产品表面再涂敷防氧化涂层，烘干后即制成非预热浸入式水口。