CN117203256A - 硅烷改性脂族聚脲 - Google Patents
硅烷改性脂族聚脲 Download PDFInfo
- Publication number
- CN117203256A CN117203256A CN202280029430.9A CN202280029430A CN117203256A CN 117203256 A CN117203256 A CN 117203256A CN 202280029430 A CN202280029430 A CN 202280029430A CN 117203256 A CN117203256 A CN 117203256A
- Authority
- CN
- China
- Prior art keywords
- group
- silane
- coating composition
- composition
- carbon atoms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种新型固化剂组合物和涂料组合物。所述涂料组合物通过提供一种硅烷改性脂族聚脲涂料来解决常规涂料的问题,所述涂层改进了工艺性能,包括更长的开放时间和适用期以及快速干燥、更快的硬度发展、改进的对环氧树脂和其它聚脲涂层的附着力和改进的耐化学性。所述涂料组合物由至少一种多异氰酸酯树脂和一种组合物组成,所述组合物包含含有至少一种仲二胺的异氰酸酯反应性试剂、至少一种硅烷组分和任选地,至少一种粘度改进剂。
Description
背景技术
聚脲涂料在行业内以快速固化、在宽温度/湿度范围内固化的能力和优异的工艺性能(performance)性质著称。聚脲涂料是非常通用的并作为商业和工业保护涂料具有广泛的应用,一些脂族聚脲用作墙壁、地板和其它表面上的装饰涂料。
某些现有技术的聚脲涂料已知有些缺陷阻碍其为基底提供足够保护或改进基底性质的有效性。例如,已知的聚脲涂料组合物可能由于异氰酸酯组分和胺组分之间的高度反应性而具有有限的适用期或工作时间。此外,某些聚脲涂料组合物可能对先前施加的涂层或对基底本身具有差的粘附性质,和/或在长时间暴露于紫外线辐射和/或湿度条件时表现出差的耐久性。
已经付出相当大的努力来开发在保护性质、美观性质和操作性质方面具有改进工艺性能的涂料组合物。用于克服一些所述缺陷的方法的一个实例是在聚脲制剂中使用溶剂或挥发性有机化合物(VOC)。但是,大多数VOC对环境和施加涂料的涂施人员都有害。此外,溶剂或VOC的使用限制了可施加到基底上的涂层的厚度。
因此,希望提供在不使用溶剂的情况下具有改进的适用期或工作时间并且可以增强对先前施加的涂层或对基底的附着力的聚脲涂料组合物。还希望在不牺牲聚脲涂料的快速固化速度、高美观性和保护性质的情况下实现这些工艺性能。
发明内容
发明概述
本发明可以通过提供一种硅烷改性脂族聚脲涂料来解决常规涂料的问题,所述聚脲涂料提供改进的工艺性能,包括更长的开放时间和适用期以及快速干燥、更快的硬度发展、改进的对环氧树脂和其它聚脲涂层的附着力和改进的耐化学性。
本发明的一个方面涉及一种组合物,其包含:
A.异氰酸酯反应性试剂,其包含至少一种仲二胺,其中所述仲二胺包含由至少一种二胺与2-丁烯二酸烷基酯形成的反应产物;
B.至少一种硅烷组分;和
C.任选地,至少一种粘度改进剂。
本发明的另一个方面涉及一种涂料组合物,其包含至少一种多异氰酸酯树脂和一种组合物,所述组合物包含
A.异氰酸酯反应性试剂,其包含至少一种仲二胺,其中所述仲二胺包含由至少一种二胺与2-丁烯二酸烷基酯形成的反应产物;
B.至少一种硅烷组分;和
C.任选地,至少一种粘度改进剂。
优选地,所述涂料组合物是非水性的。“非水性”是指涂料组合物包含小于大约1重量%的水,通常大约0重量%的水。
本发明的另一个方面涉及一种组合物,其包含至少一种硅烷组分,至少一种粘度改进剂,以及双(4-氨基环己基)甲烷与2-丁烯二酸乙酯的反应产物。
本发明的进一步方面涉及一种组合物,其包含至少一种硅烷组分,至少一种粘度改进剂,以及双(4-氨基-3-甲基环己基)甲烷与2-丁烯二酸乙酯的反应产物。
本发明的各个方面可以单独使用或彼此组合使用。
发明详述
本发明涉及可有利地用于为各种基底提供保护,如对磨损、冲击、化学、沾污和UV的耐受性和/或可用于装饰目的以增强特定表面的外观的固化剂组合物、涂料组合物和涂层。
术语“涂料组合物”是指未固化的流体组合物,其可喷涂或可刷涂/辊涂到基底上,或可将基底浸渍到其中。术语涂层是指衍生自涂料组合物并且基本不含水和/或溶剂并且已经以有效形成热固性膜的量经过固化的层。短语“基本不含水”是指涂料组合物包含小于大约1重量%的水,通常大约0重量%或非水性。保护涂层被定义为直接或间接设置在基底上的涂层并且可以包含一个或多个层,其中一个层衍生自该涂料组合物。术语“间接设置”是指通过其它层与基底分隔的涂层,而术语“直接设置”是指与基底紧密物理接触的层。尽管可以涂布任何合适的基底,但这样的基底的实例包括混凝土、木材、金属、塑料、复合材料等合适基底中的至少一种。
本发明的一个方面涉及一种组合物,其包含:
A.异氰酸酯反应性试剂,其包含至少一种仲二胺,其中所述仲二胺包含由至少一种二胺与2-丁烯二酸烷基酯形成的反应产物;
B.至少一种硅烷组分;和
C.任选地,至少一种粘度改进剂。
优选地,该组合物包含至少一种异氰酸酯反应性试剂,其包含至少一种通过二胺与2-丁烯二酸烷基酯的反应形成的仲二胺。该仲二胺产物具有通式(I):
R1O2CCH2CH(CO2R2)NH-X-NHCH(CO2R3)CH2CO2R4(I)
其中R1、R2、R3和R4相同或不同并且各自是具有大约1至大约12个碳原子的烷基。
优选地,在一个实施方案中,仲二胺产物的烷基具有1至大约4个碳原子;且X-代表通过从以下物质中的至少一种中除去氨基而获得的二价烃基:1,4-二氨基丁烷、1,6-二氨基己烷、2,2,4-和/或2,4,4-三甲基-1,6-二氨基己烷、1-氨基-3,3,5-三甲基-5-氨基甲基-环己烷、双(4-氨基环己基)甲烷、双(4-氨基-3-甲基环己基)甲烷、乙二胺、1,2-二氨基丙烷、1,4-二氨基丁烷、2,5-二氨基-2,5-二甲基己烷、1,11-二氨基十一烷、1,12-二氨基十二烷、2,4’和/或2,6-六氢甲苯二胺、2,4-和/或2,6-二氨基甲苯和2,4-和/或4,4’二氨基二苯甲烷和聚醚二胺。一种示例性的烷基是乙基。异氰酸酯反应性试剂的量通常为涂料组合物的大约20至大约70重量%;包括大约25至大约65重量%;和大约30至大约60重量%。胺当量可为大约100至大约500,包括大约150至大约450;和大约200至大约400。
优选地,在一个实施方案中,该组合物包含至少一种硅烷组分,其包含烷氧基官能硅烷,其中烷氧基官能硅烷包含由以下通式表示的化合物:
其中各R,可以相同或不同,选自具有最多6个碳原子的烷基、具有最多6个碳原子的芳基和具有最多6个碳原子的烷氧基;或其中各R,可以相同或不同,选自氢、具有最多6个碳原子的烷基和具有最多6个碳原子的芳基。
优选地,烷氧基官能硅烷包含选自以下物质组的至少一个成员:三甲基-甲氧基硅烷、三甲基乙氧基硅烷、三乙基-甲氧基硅烷、三甲基异丙氧基硅烷、三甲基-丁氧基硅烷、三苯基甲氧基硅烷、二甲基-叔丁基甲氧基硅烷、三苯基乙氧基硅烷、二甲基-苯基甲氧基硅烷;二甲基-二甲氧基硅烷、二甲基二乙氧基硅烷、二乙基-二甲氧基硅烷、二苯基二甲氧基硅烷、二苯基-二乙氧基硅烷、甲基苯基二甲氧基硅烷、甲基-苯基二乙氧基硅烷;甲基-三甲氧基硅烷、甲基三乙氧基硅烷、乙基三甲氧基硅烷、苯基三甲氧基硅烷、苯基三乙氧基硅烷;四甲氧基硅烷、四乙氧基硅烷和四异丙氧基硅烷。
优选地,在一个实施方案中,仲二胺包含双(4-氨基环己基)甲烷与2-丁烯二酸乙酯的反应产物。
优选地,在一个实施方案中,仲二胺包含双(4-氨基-3-甲基环己基)甲烷与2-丁烯二酸乙酯的反应产物。
优选地,在任一前述实施方案中,该组合物是固化组合物。
本发明的另一个方面涉及一种涂料组合物,其包含至少一种多异氰酸酯树脂和一种组合物,所述组合物包含
A.异氰酸酯反应性试剂,其包含至少一种仲二胺,其中所述仲二胺包含由至少一种二胺与2-丁烯二酸烷基酯形成的反应产物;
B.至少一种硅烷组分;和
C.任选地,至少一种粘度改进剂。
优选地,该涂料组合物是非水性的。“非水性”是指涂料组合物包含小于大约1重量%的水,通常大约0重量%的水。
优选地,该涂料组合物包含至少一种异氰酸酯反应性试剂,其包含至少一种通过二胺与2-丁烯二酸烷基酯的反应形成的仲二胺。该仲二胺产物具有通式(I):
R1O2CCH2CH(CO2R2)NH-X-NHCH(CO2R3)CH2CO2R4(I)
其中R1、R2、R3和R4相同或不同并且各自是具有大约1至大约12个碳原子的烷基。
优选地,在一个实施方案中,仲二胺产物的烷基具有1至大约4个碳原子;且X-代表通过从以下物质中的至少一种中除去氨基而获得的二价烃基:1,4-二氨基丁烷、1,6-二氨基己烷、2,2,4-和/或2,4,4-三甲基-1,6-二氨基己烷、1-氨基-3,3,5-三甲基-5-氨基甲基-环己烷、双(4-氨基环己基)甲烷、双(4-氨基-3-甲基环己基)甲烷、乙二胺、1,2-二氨基丙烷、1,4-二氨基丁烷、2,5-二氨基-2,5-二甲基己烷、1,11-二氨基十一烷、1,12-二氨基十二烷、2,4’和/或2,6-六氢甲苯二胺、2,4-和/或2,6-二氨基甲苯和2,4-和/或4,4’二氨基二苯甲烷和聚醚二胺。一种示例性的烷基是乙基。异氰酸酯反应性试剂的量通常为涂料组合物的大约20至大约70重量%;包括大约25至大约65重量%;和大约30至大约60重量%。胺当量可为大约100至大约500,包括大约150至大约450;和大约200至大约400。
优选地,该涂料组合物包含至少一种多异氰酸酯树脂,其中所述至少一种多异氰酸酯树脂包含具有以下通式的异氰酸酯官能化合物:
R(NCO)i,(II)
其中R是化合价为i的有机基团,其中i大于或等于大约2。优选地,R可以是取代或未取代的烃基(例如亚甲基或亚芳基)。
异氰酸酯可以是芳族或脂族的。可用的芳族二异氰酸酯可包含例如2,4-甲苯二异氰酸酯和2,6-甲苯二异氰酸酯(各自通常被称为TDI);两种TDI异构体的混合物;4,4'-二苯甲烷二异氰酸酯(MDI);对苯二异氰酸酯(PPDI);二苯基-4,4'-二异氰酸酯;二苄基-4,4'-二异氰酸酯;--4,4'-二异氰酸酯;二苯甲酮-4,4'-二异氰酸酯;1,3-和1,4-二甲苯二异氰酸酯;等等,或包含至少一种前述芳族异氰酸酯的组合。用于制备聚氨酯预聚物的示例性芳族二异氰酸酯包括TDI、MDI和PPDI。
可用的脂族二异氰酸酯可包含例如1,6-六亚甲基二异氰酸酯(HDI);1,3-环己基二异氰酸酯;1,4-环己基二异氰酸酯(CHDI);被称为H(12)MDI的饱和二苯甲烷二异氰酸酯;(商业上也称为双{4-异氰酸根合环己基}甲烷、4,4'-亚甲基二环己基二异氰酸酯、4,4-亚甲基双(二环己基)二异氰酸酯、亚甲基二环己基二异氰酸酯、亚甲基双(4-亚环己基异氰酸酯)、饱和亚甲基二苯基二异氰酸酯和饱和甲基二苯基二异氰酸酯)、异佛尔酮二异氰酸酯(IPDI);等等,或包含至少一种前述异氰酸酯的组合。一种示例性的脂族二异氰酸酯是H(12)MDI。
其它示例性的多异氰酸酯包括六亚甲基二异氰酸酯(HDI)、2,2,4-和/或2,4,4-三甲基-1,6-六亚甲基二异氰酸酯、十二亚甲基二异氰酸酯、1,4-环己烷二异氰酸酯、1-异氰酸根合-3,3,5-三甲基-5-异氰酸根合甲基环己烷(IPDI)、2,4'-和/或4,4'-二异氰酸根合-二环己基甲烷、2,4-和/或4,4'-二苯甲烷二异氰酸酯以及这些异构体与它们的更高级同系物的混合物(其通过苯胺/甲醛缩合物的光气化获得)、2,4-和/或2,6-甲苯二异氰酸酯和这些化合物的任何混合物。已发现更高官能的六亚甲基二异氰酸酯(HDI)多异氰酸酯,如缩二脲、三聚体和二聚体,特别可用于本发明的目的。多异氰酸酯的量通常为涂料组合物的大约10至大约60重量%,包括大约25至大约55重量%;和大约20至大约50重量%。
在本发明的一个方面,式(II)中的R也可以代表化合价为i的聚氨酯基团,在这种情况下R(NCO)i是被称为异氰酸酯封端的聚氨酯预聚物或半预聚物的组合物。当过量的有机二异氰酸酯单体与含活性氢的组分反应时,形成预聚物或半预聚物。
本发明的组合物还包含至少一种硅烷组分。本发明的涂料组合物包含烷氧基官能硅烷。本文所用的术语“烷氧基官能硅烷和/或硅烷醇官能有机硅”是指包含烷氧基官能团的有机硅,其中R是烷基或芳基。本文所用的术语“有机硅”是指基于包含交替的硅和氧原子的结构的硅氧烷聚合物。
优选地,在一个实施方案中,该涂料组合物包含至少一种硅烷组分,其包含烷氧基官能硅烷,其中烷氧基官能硅烷包含由以下通式表示的化合物:
其中各R,可以相同或不同,选自具有最多6个碳原子的烷基、具有最多6个碳原子的芳基和具有最多6个碳原子的烷氧基;或其中各R,可以相同或不同,选自氢、具有最多6个碳原子的烷基、和具有最多6个碳原子的芳基。在某些实施方案中,各R可包含具有少于6个碳原子的烷基、芳基或烷氧基以促进快速水解,该反应由水解的醇类似物产物的挥发性驱动。
优选地,烷氧基官能硅烷包含选自以下物质组的至少一个成员:三甲基-甲氧基硅烷、三甲基乙氧基硅烷、三乙基-甲氧基硅烷、三甲基异丙氧基硅烷、三甲基-丁氧基硅烷、三苯基甲氧基硅烷、二甲基-叔丁基甲氧基硅烷、三苯基乙氧基硅烷、二甲基-苯基甲氧基硅烷;二甲基-二甲氧基硅烷、二甲基二乙氧基硅烷、二乙基-二甲氧基硅烷、二苯基二甲氧基硅烷、二苯基-二乙氧基硅烷、甲基苯基二甲氧基硅烷、甲基-苯基二乙氧基硅烷;甲基-三甲氧基硅烷、甲基三乙氧基硅烷、乙基三甲氧基硅烷、苯基三甲氧基硅烷、苯基三乙氧基硅烷;四甲氧基硅烷、四乙氧基硅烷和四异丙氧基硅烷。
本发明的烷氧基硅烷的实例包括单烷氧基硅烷,如三甲基-甲氧基硅烷、三甲基乙氧基硅烷、三乙基-甲氧基硅烷、三甲基异丙氧基硅烷、三甲基-丁氧基硅烷、三苯基甲氧基硅烷、二甲基-叔丁基甲氧基硅烷、三苯基乙氧基硅烷和二甲基-苯基甲氧基硅烷;二烷氧基硅烷,如二甲基-二甲氧基硅烷、二甲基二乙氧基硅烷、二乙基-二甲氧基硅烷、二苯基二甲氧基硅烷、二苯基-二乙氧基硅烷、甲基苯基二甲氧基硅烷和甲基-苯基二乙氧基硅烷;三烷氧基硅烷,如甲基-三甲氧基硅烷、甲基三乙氧基硅烷、乙基三甲氧基硅烷、苯基三甲氧基硅烷和苯基三乙氧基硅烷;以及四烷氧基硅烷,如四甲氧基硅烷、四乙氧基硅烷和四异丙氧基硅烷。硅烷的量通常为涂料组合物的大约1至大约30重量%,包括大约5至大约25重量%;和大约10至大约20重量%。
其它任选的硅烷组分包括如专利US2013/0244043(Evonik)中所述的异氰酸根合烷基三烷氧基硅烷和脂族的烷基支化二醇或多元醇的加合物。优选地,在一个实施方案中,该涂料组合物包含至少一种硅烷组分,其中所述至少一种硅烷组分选自以下物质的加合物:异氰酸根合烷基三烷氧基硅烷;脂族的烷基支化二醇;和脂族的烷基支化多元醇。
商业产品包括Vestanat EP-M 60、EP-M 95、EP-MF 203、EP-MF 204、EP-MF 205、EP-EF 201和EP-EF 202等。
该涂料组合物还可包含至少一种粘度改进剂。粘度改进剂可包含至少一种极性或非极性溶剂或非反应性稀释剂。优选地,该涂料组合物还可包含至少一种粘度改进剂,其中所述至少一种粘度改进剂包含至少一种溶剂,其选自己烷、庚烷、二甲苯、甲苯、环己烷;酯型溶剂,如乙酸甲酯、乙酸乙酯、乙酸叔丁酯、乙酸乙二醇单甲醚、1,2,3-三乙酰氧基丙烷、乙酸二乙二醇单甲醚、二元酯;醚型溶剂,如异丙醚、乙二醇单甲醚、二乙二醇单丁醚;酮类型,如甲基异丁基酮、甲乙酮、异佛尔酮、苯乙酮;碳酸酯类型,如碳酸亚丙酯、碳酸二甲酯;吡咯烷酮类型,如N-甲基吡咯烷酮、N-乙基吡咯烷酮;卤化溶剂类型,如对氯三氟甲苯、1,1,2,2-四氯乙烷、1,1-二氯乙烷和任何其它对胺或多异氰酸酯呈惰性的质子或非质子溶剂。优选地,该涂料组合物还可包含至少一种粘度改进剂,其中所述至少一种粘度改进剂包含至少一种非反应性稀释剂,其选自邻苯二甲酸酯类型,如邻苯二甲酸双(2-乙基己基)酯、邻苯二甲酸二异壬酯、邻苯二甲酸丁基苄基酯;酯类型,如己二酸二辛酯、癸二酸二丁酯、1,2-环己烷二甲酸二异壬酯、2,2,4-三甲基-1,3-戊二醇二异丁酸酯、烷基磺酸苯酯;柠檬酸酯类型,如乙酰基柠檬酸三乙酯、柠檬酸三乙酯;偏苯三酸酯类型,如偏苯三酸三甲酯、偏苯三酸三-(2-乙基己基)酯和其它种类的非反应性稀释剂,如苯甲酸酯、磺酰胺、环氧化植物油、有机磷酸酯、二醇、聚醚、聚丁烯及其组合。粘度改进剂的量通常为涂料组合物的大约2至大约30重量%,包括大约5至大约25重量%;和大约10至大约20重量%。
优选地,该涂料组合物还可包含选自流平剂、消泡剂、除气剂、抗氧化剂、紫外线稳定剂、流变改性剂、颜料、分散剂、增塑剂、稀释剂、填料及其组合的至少一种其它添加剂。这些添加剂的量通常为涂料组合物的大约0至大约10%,包括大约1至大约5重量%;和大约2至大约5重量%。
优选地,在任一前述实施方案中,该涂料组合物是非水性的。
具体实施方式
实施例
本发明的涂料组合物的组分可以使用任何合适的常规设备和方法合并。前述设备和方法的实例包括掺混机、用叶轮叶片搅拌、用搅拌棒手动混合、高速混合器等常规设备。
涂料组合物的组分通常以下列顺序合并:1)异氰酸酯反应性试剂、2)粘度改进剂、3)硅烷、4)添加剂(混合直至溶液均匀);和5)多异氰酸酯。
本发明的各个方面可以单独使用或组合使用。通过以下实施例例示本发明的某些方面。这些实施例不意于限制所附权利要求书的范围。
制剂中使用的以下成分显示在表1中:
表1
实施例1
第一实施例显示包含如表1中所示的仲二胺产物的涂料组合物,所述仲二胺产物为原样使用和与来自Evonik Corporation的商业硅烷共混,即不含和含有来自EvonikCorporation的商业硅烷。然后将多异氰酸酯,即六亚甲基二异氰酸酯三聚体以1.05NCO/胺的化学计量比添加到异氰酸酯反应性混合物中,并在施加之前使用高速混合器混合在一起以形成均匀混合物。使用各种试验程序测试该混合物和干膜的固化性质。含有二胺与硅烷的共混物的样品表现出低混合粘度以及如通过Persoz摆杆测试测得的高最终硬度。
表2
表3
实施例2
第二实施例显示包含与硅烷和粘度改进剂共混的仲二胺的涂料组合物。然后将多异氰酸酯,即六亚甲基二异氰酸酯三聚体以1.05NCO/胺的化学计量比添加到异氰酸酯反应性混合物中,并在施加之前使用高速混合器混合在一起以形成均匀混合物。将该混合物和干膜的固化性质与不含硅烷组分的商业二胺的固化性质进行比较。数据显示长的固化曲线时间(cure profile time)、低混合物粘度以及在3天内的高硬度发展。
在两种不同的有机涂层基底上测试样品的涂层间附着力。将样品涂料作为顶涂层施加在基底、脂族聚脲涂层和环氧涂层上。脂族聚脲涂层是Amicure IC-221,而环氧涂层是用液体环氧树脂固化的Ancamine2850。这两种材料都由Evonik Corporation供应。在施加Amicure IC-221和Ancamine 2850的初始涂层后以不同的时间间隔施加顶涂层。样品2F和2G甚至在3个月后仍表现出对脂族聚脲和环氧涂层的优异附着力。
表4
表5
1.使用具有Thermosel附件(Accessory)(独立的(Stand Alone))的布氏(Brookfield)粘度计测量粘度固化曲线和初始混合粘度(ASTM D2196)
2.使用ASTM D5895测量6密耳厚度的固化膜的干燥时间。
3.使用ASTM D4366测量大约6-8密耳厚度的薄膜的Persoz硬度。
表6.在各种时间间隔下脂族聚脲涂层在有机涂层基底(脂族聚脲和环氧树脂)上的涂层间附着力测试
4.使用ASTM方法D3359方法A的划格法胶带附着力。给出从0A至5A的评级,其中5A是最好的。
本发明在范围上不意于受实施例中公开的具体方面或实施方案的限制,实施例旨在例示本发明的几个方面,并且功能上等同的任何实施方案都在本发明的范围内。除本文显示和描述的那些外,本发明的各种变型将是本领域技术人员显而易见的并且意图落在所附权利要求书的范围内。
Claims (19)
1.一种组合物,其包含:
异氰酸酯反应性试剂,其包含至少一种仲二胺,其中所述仲二胺包含至少一种二胺与2-丁烯二酸烷基酯的反应产物;
至少一种硅烷组分;和
任选地,至少一种粘度改进剂。
2.权利要求1的组合物,其中所述异氰酸酯反应性试剂具有通式(I):
R1O2CCH2CH(CO2R2)NH-X-NHCH(CO2R3)CH2CO2R4(I)其中R1、R2、R3和R4相同或不同并且各自是具有大约1至大约12个碳原子的烷基。
3.权利要求2的组合物,其中所述烷基具有1至大约4个碳原子;且X-代表通过从以下物质中的至少一种中除去氨基而获得的二价烃基:1,4-二氨基丁烷、1,6-二氨基己烷、2,2,4-和/或2,4,4-三甲基-1,6-二氨基己烷、1-氨基-3,3,5-三甲基-5-氨基甲基-环己烷、双(4-氨基环己基)甲烷、双(4-氨基-3-甲基环己基)甲烷、乙二胺、1,2-二氨基丙烷、1,4-二氨基丁烷、2,5-二氨基-2,5-二甲基己烷、1,11-二氨基十一烷、1,12-二氨基十二烷、2,4’和/或2,6-六氢甲苯二胺、2,4-和/或2,6-二氨基甲苯和2,4-和/或4,4’二氨基二苯甲烷和聚醚二胺。
4.权利要求1的组合物,其中所述至少一种硅烷组分包含烷氧基官能硅烷,其中所述烷氧基官能硅烷包含由以下通式表示的化合物:
其中各R,可以相同或不同,选自具有最多6个碳原子的烷基、具有最多6个碳原子的芳基和具有最多6个碳原子的烷氧基;或其中各R,可以相同或不同,选自氢、具有最多6个碳原子的烷基和具有最多6个碳原子的芳基。
5.权利要求4的组合物,其中所述烷氧基官能硅烷包含选自以下物质组的至少一个成员:三甲基-甲氧基硅烷、三甲基乙氧基硅烷、三乙基-甲氧基硅烷、三甲基异丙氧基硅烷、三甲基-丁氧基硅烷、三苯基甲氧基硅烷、二甲基-叔丁基甲氧基硅烷、三苯基乙氧基硅烷、二甲基-苯基甲氧基硅烷;二甲基-二甲氧基硅烷、二甲基二乙氧基硅烷、二乙基-二甲氧基硅烷、二苯基二甲氧基硅烷、二苯基-二乙氧基硅烷、甲基苯基二甲氧基硅烷、甲基-苯基二乙氧基硅烷;甲基-三甲氧基硅烷、甲基三乙氧基硅烷、乙基三甲氧基硅烷、苯基三甲氧基硅烷、苯基三乙氧基硅烷;四甲氧基硅烷、四乙氧基硅烷和四异丙氧基硅烷。
6.权利要求1的组合物,其中所述仲二胺包含双(4-氨基环己基)甲烷与2-丁烯二酸乙酯的反应产物。
7.权利要求1的组合物,其中所述仲二胺包含双(4-氨基-3-甲基环己基)甲烷与2-丁烯二酸乙酯的反应产物。
8.权利要求1-7中任一项的组合物,其中所述组合物是固化组合物。
9.一种涂料组合物,其包含至少一种多异氰酸酯树脂和根据权利要求1的组合物,所述组合物包含
异氰酸酯反应性试剂,其包含至少一种仲二胺,其中所述仲二胺包含至少一种二胺与2-丁烯二酸烷基酯的反应产物;
至少一种硅烷组分;和
任选地,至少一种粘度改进剂。
10.权利要求9的涂料组合物,其中所述异氰酸酯反应性试剂具有通式(I):
R1O2CCH2CH(CO2R2)NH-X-NHCH(CO2R3)CH2CO2R4(I)其中R1、R2、R3和R4相同或不同并且各自是具有大约1至大约12个碳原子的烷基。
11.权利要求10的涂料组合物,其中所述烷基具有1至大约4个碳原子;且X-代表通过从选自以下物质中的至少一种中除去氨基而获得的二价烃基:1,4-二氨基丁烷、1,6-二氨基己烷、2,2,4-和/或2,4,4-三甲基-1,6-二氨基己烷、1-氨基-3,3,5-三甲基-5-氨基甲基-环己烷、双(4-氨基环己基)甲烷、双(4-氨基-3-甲基环己基)甲烷、乙二胺、1,2-二氨基丙烷、1,4-二氨基丁烷、2,5-二氨基-2,5-二甲基己烷、1,11-二氨基十一烷、1,12-二氨基十二烷、2,4’和/或2,6-六氢甲苯二胺、2,4-和/或2,6-二氨基甲苯和2,4-和/或4,4’-二氨基二苯甲烷和聚醚二胺。
12.权利要求9的涂料组合物,其中所述至少一种多异氰酸酯树脂包含具有以下通式的异氰酸酯官能化合物:
R(NCO)i,(II)
其中R是化合价为i的有机基团,其中i大于或等于大约2。
13.权利要求9的涂料组合物,其中所述至少一种硅烷组分包含烷氧基官能硅烷,其中所述烷氧基官能硅烷包含由以下通式表示的化合物:
其中各R,可以相同或不同,选自具有最多6个碳原子的烷基、具有最多6个碳原子的芳基和具有最多6个碳原子的烷氧基;或其中各R,可以相同或不同,选自氢、具有最多6个碳原子的烷基和具有最多6个碳原子的芳基。
14.权利要求13的涂料组合物,其中所述烷氧基官能硅烷包含选自以下物质组的至少一个成员:三甲基-甲氧基硅烷、三甲基乙氧基硅烷、三乙基-甲氧基硅烷、三甲基异丙氧基硅烷、三甲基-丁氧基硅烷、三苯基甲氧基硅烷、二甲基-叔丁基甲氧基硅烷、三苯基乙氧基硅烷、二甲基-苯基甲氧基硅烷;二甲基-二甲氧基硅烷、二甲基二乙氧基硅烷、二乙基-二甲氧基硅烷、二苯基二甲氧基硅烷、二苯基-二乙氧基硅烷、甲基苯基二甲氧基硅烷、甲基-苯基二乙氧基硅烷;甲基-三甲氧基硅烷、甲基三乙氧基硅烷、乙基三甲氧基硅烷、苯基三甲氧基硅烷、苯基三乙氧基硅烷;四甲氧基硅烷、四乙氧基硅烷和四异丙氧基硅烷。
15.权利要求9的涂料组合物,其中所述至少一种硅烷组分选自以下物质的加合物:异氰酸根合烷基三烷氧基硅烷;脂族的烷基支化二醇;和脂族的烷基支化多元醇。
16.权利要求9的涂料组合物,其中所述涂料组合物进一步包含至少一种粘度改进剂,其中所述至少一种粘度改进剂包含至少一种溶剂,其选自己烷、庚烷、二甲苯、甲苯、环己烷;乙酸甲酯、乙酸乙酯、乙酸叔丁酯、乙酸乙二醇单甲醚、1,2,3-三乙酰氧基丙烷、乙酸二乙二醇单甲醚、二元酯;异丙醚、乙二醇单甲醚、二乙二醇单丁醚;甲基异丁基酮、甲乙酮、异佛尔酮、苯乙酮;碳酸亚丙酯、碳酸二甲酯;N-甲基吡咯烷酮、N-乙基吡咯烷酮;对氯三氟甲苯、1,1,2,2-四氯乙烷和1,1-二氯乙烷。
17.权利要求9的涂料组合物,其中所述涂料组合物进一步包含至少一种粘度改进剂,其中所述至少一种粘度改进剂包含至少一种非反应性稀释剂,其选自邻苯二甲酸双(2-乙基己基)酯、邻苯二甲酸二异壬酯、邻苯二甲酸丁基苄基酯;己二酸二辛酯、癸二酸二丁酯、1,2-环己烷二甲酸二异壬酯、2,2,4-三甲基-1,3-戊二醇二异丁酸酯、烷基磺酸苯酯;乙酰基柠檬酸三乙酯、柠檬酸三乙酯;偏苯三酸三甲酯、偏苯三酸三-(2-乙基己基)酯、苯甲酸酯、磺酰胺、环氧化植物油、有机磷酸酯、二醇、聚醚和聚丁烯。
18.权利要求9的涂料组合物,其中所述涂料组合物进一步包含至少一种其它添加剂,其选自流平剂、消泡剂、除气剂、抗氧化剂、紫外线稳定剂、流变改性剂、颜料、分散剂、增塑剂、稀释剂、填料及其组合。
19.权利要求9-18中任一项的涂料组合物,其中所述涂料组合物是非水性的。