CN117045827A - 一种用于神经电生理检测的导电膏 - Google Patents
一种用于神经电生理检测的导电膏 Download PDFInfo
- Publication number
- CN117045827A CN117045827A CN202210481221.XA CN202210481221A CN117045827A CN 117045827 A CN117045827 A CN 117045827A CN 202210481221 A CN202210481221 A CN 202210481221A CN 117045827 A CN117045827 A CN 117045827A
- Authority
- CN
- China
- Prior art keywords
- hyaluronate
- conductive paste
- conductive
- neurophysiologic
- detection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于神经电生理检测的导电膏，涉及医疗诊断领域，按质量百分比，该导电膏包括0.1％～2％透明质酸盐，70％～90％水，5％～20％保湿剂，0.8％～5％导电剂，1％～5％凝胶剂，0.1％～0.5％防腐剂。本发明能够避免破坏头部皮肤，避免创伤感染，且能够有效降低阻抗。
Description
技术领域
本发明涉及医疗诊断领域，具体涉及一种用于神经电生理检测的导电膏。
背景技术
脑电检测是常用的医学诊断方法，通过将带有电极的导电帽套接在头部合适部位，通过导电膏形成稳定的微电检测通道，捕获微弱的生物电信号，再通过放大器将生物电信号放大，通过脑电仪显示和记录脑电波，以此判断患者是否存在脑部疾病。
医用导电膏填充在电极与皮肤之间，能够降低皮肤与电极之间的阻抗，是电极与皮肤导通的桥联，保证电极与皮肤表面的接触良好，使得测量信号清晰，误差小、噪音低，从而增强测试效果。
在实际进行脑电检测时，由于头皮汗腺发达，患者的头部存在大量的油脂以及角质层，会大大增加皮肤的阻抗，即使使用导电膏也难以达到较好的效果，为了降低皮肤油脂、角质层对电信号的影响，医生会提前去除电极接触之处的头发，并用磨砂膏对对应头皮进行磨砂处理，去除油脂和角质层，但是磨砂操作不仅增加了医生的操作难度，效率较低，而且也可能磨破头皮，增加创伤感染的风险。
同时，为了增加导电效果，目前通常在导电膏中加入导电盐或者导电金属颗粒、金属合金颗粒或纳米颗粒，但是，这些成分会刺激患者头部皮肤甚至进入患者体内，造成金属沉积等危害，同时，金属颗粒难以在导电膏中均匀分布，导电性能稳定性较差。
专利文献CN201310507415.3公开了一种电极磨砂导电胶及其制备方法，其通过在常规的导电胶中添加磨砂粒子，实现磨砂导电一体化，此方法节约了效率，但是使用时仍然需要对头皮进行磨砂处理，因此，依然会有磨破头皮增加创伤的风险。
发明内容
为改善现有技术的不足，本发明的目的在于提供一种用于神经电生理检测的导电膏，能够避免破坏头部皮肤，避免创伤感染，且能够有效降低阻抗。
为达到以上目的，本发明采取的技术方案是：
一种用于神经电生理检测的导电膏，按质量百分比，包括：
进一步地，按质量百分比，所述透明质酸盐包括分子量为450kDa-700kDa的透明质酸盐20％-35％，分子量为1000kDa-1500kDa的透明质酸盐40％-65％。
进一步地，所述导电剂为透明质酸-多巴胺聚合物和/或透明质酸-聚吡咯聚合物。
进一步地，所述透明质酸盐衍生物中透明质酸盐的分子量为450kDa-700kDa，透明质酸盐衍生物的分子量为3500kDa-5500kDa。
进一步地，所述保湿剂包括神经酰胺和/或甘油。
进一步地，所述凝胶剂包括纤维素衍生物、卡波姆、海藻酸盐中的至少一种。
进一步地，所述防腐剂包括山梨酸钠、羟基苯甲酸丁酯、乳酸钠中的至少一种。
一种上述用于神经电生理检测的导电膏的制备方法，包括以下步骤：
将水、保湿剂、防腐剂混合，搅拌加热至60-70℃；先加入凝胶剂进行混合，再加入导电剂混合，最后加入透明质酸盐混合。
进一步地，所述凝胶、导电剂、透明质酸盐的混合在均质条件下进行。
与现有技术相比，本发明的优点在于：
(1)本发明中的用于神经电生理检测的导电膏，保湿剂神经酰胺能够在角质层中形成网状结构，并缔合水分子，增加角质层中的水分含量，有效降低皮肤的阻抗，同时，小分子的透明质酸盐、保湿剂和导电剂能够进入真皮层中，与位于真皮层外部的导电剂形成良好的导电通道，在不进行磨砂的情况下，也能够获得较好的脑电数据，可以避免磨砂破坏头部皮肤，避免创伤感染。
(1)本发明中的用于神经电生理检测的导电膏，导电剂为具有导电性的透明质酸盐衍生物，且选用的是小分子的透明质酸盐与多巴胺和/或吡咯的聚合物，聚合物的分子量为3500kDa-5500kDa，聚合物分子中存在大量的-OH，具有良好的亲水性，导电剂能够与透明质酸盐和水均匀混合，形成稳定的监测通道，得到导电率高于35mS/cm的导电膏；与此同时，中分子的透明质酸盐能够保持导电膏中的水分，维持导电膏的有效性，延长监测时间，进一步地，本发明的导电膏不需要另外加入导电盐或者导电金属颗粒，避免导电盐或金属颗粒刺激患者头部皮肤，同时，也能避免金属颗粒难以在导电膏中均匀分布，导电性能不稳定的缺陷。
具体实施方式
以下结合的实施例对本发明作进一步详细说明。
本发明实施例提供一种用于神经电生理检测的导电膏，按质量百分比，包括：
其中，按质量百分比，透明质酸盐包括分子量为450kDa-700kDa的透明质酸盐20％-35％(以下简称小分子透明质酸盐)，分子量为1000kDa-1500kDa的透明质酸盐40％-65％(以下简称中分子透明质酸盐)。
导电剂为具有导电性的透明质酸盐衍生物，例如为透明质酸-多巴胺聚合物和/或透明质酸-聚吡咯聚合物。
透明质酸盐衍生物中透明质酸盐的分子量为450kDa-700kDa，透明质酸盐衍生物的分子量为3500kDa-5500kDa。
保湿剂包括神经酰胺和/或甘油。
凝胶剂包括纤维素衍生物、卡波姆、海藻酸盐中的至少一种。
防腐剂包括山梨酸钠、羟基苯甲酸丁酯、乳酸钠中的至少一种。
本发明中保湿剂能够在角质层中形成网状结构，并缔合水分子，增加角质层中的水分含量，有效降低皮肤的阻抗，同时，小分子的透明质酸盐、保湿剂和导电剂能够进入真皮层中，与位于真皮层外部的导电剂形成良好的导电通道，在不进行磨砂的情况下，也能够获得较好的脑电数据，可以避免磨砂破坏头部皮肤，避免创伤感染。
同时，本发明的导电膏中的导电剂为具有导电性的透明质酸盐衍生物，且选用的是小分子的透明质酸盐与多巴胺和/或吡咯的聚合物，聚合物的分子量为3500kDa-5500kDa，聚合物分子中存在大量的-OH，具有良好的亲水性，导电剂能够与透明质酸盐和水均匀混合，形成稳定的监测通道，与此同时，中分子的透明质酸盐能够保持导电膏中的水分，维持导电膏的有效性，延长监测时间，进一步地，本发明的导电膏不需要另外加入导电盐或者导电金属颗粒，避免导电盐或金属颗粒刺激患者头部皮肤，同时，也能避免金属颗粒难以在导电膏中均匀分布，导电性能不稳定的缺陷。
实施例1
一种用于神经电生理检测的导电膏，按质量百分比，包括：
其中，透明质酸-多巴胺聚合物的分子量为3500kDa-4000kDa。
将水，神经酰胺、山梨酸钠混合后，在搅拌速度为5rpm下从常温加热至温度为70℃，加入卡波姆，进行高剪切均质15min(速度为6000rmp)，加入透明质酸-多巴胺聚合物高剪切均质15min(速度为7000rmp)，再加入透明质酸钠高剪切均质5min(速度为3000rmp)，得到导电膏。
实施例2
一种用于神经电生理检测的导电膏，按质量百分比，包括：
其中，透明质酸-多巴胺聚合物的分子量为4000kDa-5000kDa。
将水，甘油、羟基苯甲酸丁酯混合后，在搅拌速度为5rpm下从常温加热至温度为65℃，加入海藻酸钠，进行高剪切均质15min(速度为5000rmp)，加入透明质酸-吡咯聚合物高剪切均质13min(速度为6000rmp)，再加入透明质酸钠高剪切均质6min(速度为4000rmp)，得到导电膏。
实施例3
一种用于神经电生理检测的导电膏，按质量百分比，包括：
其中，透明质酸-多巴胺聚合物的分子量为3500kDa-4000kDa，透明质酸-吡咯聚合物的分子量为4000kDa-5500kDa。
将水，神经酰胺、羟基苯甲酸丁酯混合后，在搅拌速度为8rpm下从常温加热至温度为65℃，加入海藻酸钠，进行高剪切均质10min(速度为5500rmp)，加入透明质酸-吡咯聚合物高剪切均质12min(速度为6000rmp)，再加入透明质酸钠高剪切均质6min(速度为4000rmp)，得到导电膏。
对比例1
本对比例中，除了透明质酸钠的分子量均为450kDa-500kDa外，其他成分与实施例1相同。
对比例2
本对比例中，除了导电剂选用质量百分比为3.6％的金属铁外，其他成分与实施例1相同。
对比例3
本对比例中，除了透明质酸钠的分子量均为1000kDa-1200kDa外，其他成分与实施例1相同。
测试例
将实施例1-3和对比例1-3的导电膏分别涂布在不同的电极上，电极连接在头部，再连接阻抗测定仪，每10min读取一次导电膏的阻抗读数，连续测量6h，得到实施例1-3的导电膏阻抗在20min后稳定且阻抗均小于1.5kΩ，而对比例1的阻抗稳定后大于4kΩ，对比例2的阻抗稳定后大于3kΩ，对比例3的阻抗稳定后大于2kΩ。
将实施例1-3和对比例1-3的导电膏分别涂布在不同相对设置的平行电极板上，在电极板的两端施加电压，测定流过电极板的电流，得到实施例1的电导率为43mS/cm(连续测量6h，导电率的误差为±0.3mS/cm)，实施例2的电导率为38mS/cm(连续测量6h，导电率的误差为±0.4mS/cm)，实施例3的电导率为50mS/cm(连续测量6h，导电率的误差为±0.4mS/cm)，对比例1的电导率为35mS/cm(连续测量6h，在3h后，导电率低于31mS/cm)，对比例2的电导率为28mS/cm，对比例3的电导率为37mS/cm(连续测量6h，在2h后，导电率低于20mS/cm)。
本发明不仅局限于上述最佳实施方式，任何人在本发明的启示下都可得出其他各种形式的产品，但不论在其形状或结构上作任何变化，凡是具有与本发明相同或相近似的技术方案，均在其保护范围之内。
Claims (9)
1.一种用于神经电生理检测的导电膏，其特征在于：按质量百分比，包括：
2.根据权利要求1所述的用于神经电生理检测的导电膏，其特征在于：按质量百分比，所述透明质酸盐包括分子量为450kDa-700kDa的透明质酸盐20％-35％，分子量为1000kDa-1500kDa的透明质酸盐40％-65％。
3.根据权利要求1所述的用于神经电生理检测的导电膏，其特征在于：所述导电剂为透明质酸-多巴胺聚合物和/或透明质酸-聚吡咯聚合物。
4.根据权利要求3所述的用于神经电生理检测的导电膏，其特征在于：所述透明质酸盐衍生物中透明质酸盐的分子量为450kDa-700kDa，透明质酸盐衍生物的分子量为3500kDa-5500kDa。
5.根据权利要求1-4任一项所述的用于神经电生理检测的导电膏，其特征在于：所述保湿剂包括神经酰胺和/或甘油。
6.根据权利要求1-4任一项所述的用于神经电生理检测的导电膏，其特征在于：所述凝胶剂包括纤维素衍生物、卡波姆、海藻酸盐中的至少一种。
7.根据权利要求1-4任一项所述的用于神经电生理检测的导电膏，其特征在于：所述防腐剂包括山梨酸钠、羟基苯甲酸丁酯、乳酸钠中的至少一种。
8.一种权利要求1-7任一项所述用于神经电生理检测的导电膏的制备方法，其特征在于：包括以下步骤：
将水、保湿剂、防腐剂混合，搅拌加热至60-70℃；先加入凝胶剂进行混合，再加入导电剂混合，最后加入透明质酸盐混合。
9.根据权利要求8所述的制备方法，其特征在于：所述凝胶、导电剂、透明质酸盐的混合在均质条件下进行。