CN117004890B - 一种高锡量气雾阀门用镀锡铁及其制造方法 - Google Patents

一种高锡量气雾阀门用镀锡铁及其制造方法 Download PDF

Info

Publication number
CN117004890B
CN117004890B CN202310788394.0A CN202310788394A CN117004890B CN 117004890 B CN117004890 B CN 117004890B CN 202310788394 A CN202310788394 A CN 202310788394A CN 117004890 B CN117004890 B CN 117004890B
Authority
CN
China
Prior art keywords
tin
equal
class
less
cold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202310788394.0A
Other languages
English (en)
Other versions
CN117004890A (zh
Inventor
韩刚
司永强
赵冬冬
张鋆慧
侯晓叶
谷潇静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Handan Jintai Packaging Material Co ltd
Original Assignee
Handan Jintai Packaging Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Handan Jintai Packaging Material Co ltd filed Critical Handan Jintai Packaging Material Co ltd
Priority to CN202310788394.0A priority Critical patent/CN117004890B/zh
Publication of CN117004890A publication Critical patent/CN117004890A/zh
Application granted granted Critical
Publication of CN117004890B publication Critical patent/CN117004890B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本申请涉及钢压延及表面处理技术领域，公开了一种高锡量气雾阀门用镀锡铁，化学成分质量百分比为：C：0.04％～0.07％，Mn：0.45％～0.55％，Si：≤0.03％，P％≤0.015％，S％≤0.02％，余量为铁和不可避免的杂质；所述镀锡铁的夹杂物水平：B类+D类+Ds类夹杂物等级之和≤1级，所述镀锡铁的拉深成型指标：0°、45°及90°方向上塑性应变比r值均大于1.0，其各项异性Δr＜0.5。通过全流程工艺设计，冷轧退火工艺参数控制、平整及镀锡工艺参数控制，所得一种高锡量阀门用镀锡板，具备较低的夹杂物水平，较好的性能均匀性以及优良的锡层附着力，所得镀锡板的夹杂物B类+D类+Ds类夹杂物等级之和≤1级。

Description

一种高锡量气雾阀门用镀锡铁及其制造方法
技术领域
本发明涉及钢压延及表面处理技术领域，具体为一种高锡量气雾阀门用镀锡铁及其制造方法。
背景技术
气雾罐由罐身、顶盖、底盖及阀门组成，阀门铁所用原材厚度一般为0.25—0.3mm，由钢板制成阀门需要经过8道反复冲压的成型方式，在此过程中，原始钢带厚度发生变化，最薄处减薄40％-50％，其反复弯折的成型方式导致其对铁基材的稳定性要求高，包括对冲压成型制耳的要求，对铁材纯净度、拉深性能、厚度及性能均匀性的要求。
阀门用铁根据其内容物的性质不同，镀锡量要求一般为5.6或8.4g/m2，高锡量的表面在反复冲压的过程中极易发生锡层划伤及脱落问题。因此，阀门用铁对表面锡层的附着力等参数均提出了严格的要求。目前国内多数研究都集中在镀锡板涂膜后的附着力，从而导致锡层本身的附着力较低，会导致对于部分冲压品种质量降低的问题。
发明内容
针对现有技术的不足，本发明提供了一种高锡量气雾阀门用镀锡铁及其制造方法，解决了导致锡层本身的附着力较低，会导致对于部分冲压品种质量降低的问题。
为实现以上目的，本发明通过以下技术方案予以实现：一种高锡量气雾阀门用镀锡铁及其制造方法，化学成分质量百分比为：C：0.04％～0.07％，Mn：0.45％～0.55％，Si：≤0.03％，P％≤0.015％，S％≤0.02％，余量为铁和不可避免的杂质；
所述镀锡铁的夹杂物水平：B类+D类+Ds类夹杂物等级之和≤1级；
所述镀锡铁的拉深成型指标：0°、45°及90°方向上塑性应变比r值均大于1.0，其各项异性Δr＜0.5，屈服强度250-300MPa，延伸率≥35％；
所述镀锡铁的表面形貌：Ra达到0.3-0.6μm，Rpc可实现超过180，Rz≤3.0μm，Rq≤0.5μm；
所述高锡量气雾阀门用镀锡铁制造方法，包括以下步骤；
S1、将钢水经炼钢连铸后得到连铸坯；所述钢水的成分与所述气雾阀门用镀锡板的成分相同；浇铸中包液面波动控制±1mm，拉速控制1.0—1.3m/min；
S2、将S1中得到的连铸坯进行热轧，所述热轧的加热温度为1150℃～1250℃，粗轧出口温度为1050℃～1110℃，终轧温度为860℃～890℃，卷取温度为580℃～620℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，所述冷轧的压下率为80％～90％，厚度波动±0.003mm；
S4、将S3中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，所述罩式退火的保温温度为600℃～660℃，保温时间为13h，升温速率20-40℃/h；
S5、将S4中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，所述平整处理的压下率为2％～4％，采用工作辊表面粗糙度1.0～1.5μm；
S6、将S5中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；所述镀锡工序的镀锡量为5.6～8.4g/m2，锡铁合金层≥1.2g/m2；
所述锡铁合金层≥1.2g/m2，氧化锡≤1.5g/cm2，钝化膜4～8g/m2。
本发明提供了一种高锡量气雾阀门用镀锡铁及其制造方法。具备以下有益效果：
本发明通过全流程工艺设计，包括炼钢成份、浇铸、热轧工艺参数控制，冷轧退火工艺参数控制、平整及镀锡工艺参数控制，所得一种高锡量阀门用镀锡板，具备较低的夹杂物水平，较好的性能均匀性以及优良的锡层附着力，满足气雾阀门成型及使用的要求，所得镀锡板的夹杂物B类+D类+Ds类夹杂物等级之和≤1级，所得镀锡板整卷测量头、中、尾部边中边共计9个位置，均可以实现0°、45°及90°方向上塑性应变比r值大于1.0，各项异性Δr＜0.5，屈服强度250-300MPa，延伸率≥35％。采用弯曲及划圈法试验观察镀锡板表面无剥落或分离现象。
附图说明
图1气雾阀门用镀锡板夹杂物检测图；
图2气雾阀门用镀锡板光扫描表面形貌图；
图3气雾阀门用镀锡板划圈法检测附着力结果图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
请参阅附图1－附图3，本发明实施例提供一种高锡量气雾阀门用镀锡铁，包括化学成分质量百分比为：C：0.04％，Mn：0.5％，Als：0.035％，Si：0.015％，P：0.012％，S：0.009％，N：0.0038％，余量为铁和不可避免的杂质。
镀锡板厚度范围0.28mm。
镀锡板夹杂物水平：B类+D类+Ds类夹杂物等级之和0.5级。
本实施例中高锡量气雾阀门用镀锡板，其制造过程包括：
S1、将钢水经炼钢连铸后得到连铸坯；钢水的成分与气雾阀门用镀锡板的成分相同。浇铸中间包液面波动曲线最大0.8mm，结晶器拉速控制1.2m/min。
S2、将S1中得到的铸坯进行热轧，热轧地加热温度为1180℃，粗轧出口温度为1080℃，终轧温度为890℃，卷取温度为600℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，冷轧的压下率为88.8％，厚度波动±0.003mm；
S4、将S4中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，罩式退火的保温温度为620℃，保温时间为13h，升温速率25℃/h；
S5、将S5中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，平整处理的压下率为2％，采用工作辊表面粗糙度1.25μm，电火花毛化采用正极+负极+正极三遍毛化的方式，去除尖峰，同时增加峰值密度；
S6、将S6中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；镀锡工序的镀锡量为5.62g/m2，软熔线距淬水水面距离控制70cm，软熔温度控制280℃。
实施例2：
请参阅附图1－附图3，本发明实施例提供一种高锡量气雾阀门用镀锡铁，化学成分质量百分比为：C：0.05％，Mn：0.46％，Al s：0.045％，Si：0.015％，P：0.012％，S：0.01％，N：0.0042％，余量为铁和不可避免的杂质。
镀锡板厚度范围0.29mm。
镀锡板夹杂物水平：B类+D类+Ds类夹杂物等级之和1级。
本实施例中高锡量气雾阀门用镀锡板，其制造过程包括：
S1、将钢水经炼钢连铸后得到连铸坯；钢水的成分与气雾阀门用镀锡板的成分相同。浇铸中间包液面波动曲线最大1mm，结晶器拉速控制1.2m/min。
S2、将S1中得到的铸坯进行热轧，热轧地加热温度为1180℃，粗轧出口温度为1080℃，终轧温度为890℃，卷取温度为620℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，冷轧的压下率为88.1％，厚度波动±0.003mm；
S4、将S3中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，罩式退火的保温温度为600℃，保温时间为13h，升温速率25℃/h；
S5、将S4中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，平整处理的压下率为2.5％，采用工作辊表面粗糙度1.3μm，电火花毛化采用正极+负极+正极三遍毛化的方式，去除尖峰，同时增加峰值密度；
S6、将S5中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；镀锡工序的镀锡量为5.54g/m2，软熔线距淬水水面距离控制76cm，软熔温度控制280℃。
实施例3：
请参阅附图1－附图3，本发明实施例提供一种高锡量气雾阀门用镀锡铁，化学成分质量百分比为：C：0.055％，Mn：0.52％，Als：0.048％，Si：0.08％，P：0.013％，S：0.009％，N：0.0035％，余量为铁和不可避免的杂质。
镀锡板厚度范围0.25mm。
镀锡板夹杂物水平：B类+D类+Ds类夹杂物等级之和0.5级。
本实施例中高锡量气雾阀门用镀锡板，其制造过程包括：
S1、将钢水经炼钢连铸后得到连铸坯；钢水的成分与气雾阀门用镀锡板的成分相同。浇铸中间包液面波动曲线最大1mm，结晶器拉速控制1.2m/min。
S2、将S1中得到的铸坯进行热轧，热轧地加热温度为1180℃，粗轧出口温度为1095℃，终轧温度为880℃，卷取温度为600℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，冷轧的压下率为90％，厚度波动±0.003mm；
S4、将S3中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，罩式退火的保温温度为580℃，保温时间为13h，升温速率30℃/h；
S5、将S4中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，平整处理的压下率为3％，采用工作辊表面粗糙度1.15μm，电火花毛化采用正极+负极+正极三遍毛化的方式，去除尖峰，同时增加峰值密度；
S6、将S5中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；镀锡工序的镀锡量为8.4g/m2，软熔线距淬水水面距离控制65cm，软熔温度控制280℃。
实施例4：
请参阅附图1－附图3，本发明实施例提供一种高锡量气雾阀门用镀锡铁，。
化学成分质量百分比为：C：0.058％，Mn：0.52％，Al s：0.05％，Si：0.012％，P：0.01％，S：0.007％，N：0.0035％，余量为铁和不可避免的杂质。
镀锡板厚度范围0.3mm。
镀锡板夹杂物水平：B类+D类+Ds类夹杂物等级之和0.5级。
本实施例中高锡量气雾阀门用镀锡板，其制造过程包括：
S1、将钢水经炼钢连铸后得到连铸坯；钢水的成分与气雾阀门用镀锡板的成分相同。浇铸中间包液面波动曲线最大1mm，结晶器拉速控制1.2m/min。
S2、将S1中得到的铸坯进行热轧，热轧地加热温度为1180℃，粗轧出口温度为1080℃，终轧温度为890℃，卷取温度为620℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，冷轧的压下率为88％，厚度波动±0.003mm；
S4、将S4中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，罩式退火的保温温度为580℃，保温时间为13h，升温速率35℃/h；
S5、将S5中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，平整处理的压下率为4％，采用工作辊表面粗糙度1.5μm，电火花毛化采用正极+负极+正极三遍毛化的方式，去除尖峰，同时增加峰值密度；
S6、将S6中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；镀锡工序的镀锡量为8.4g/m2，软熔线距淬水水面距离控制60cm，软熔温度控制260℃。
对比例1；
本实施例中高锡量气雾阀门用镀锡板，化学成分质量百分比为：C：0.04％，Mn：0.5％，Als：0.035％，Si：0.015％，P：0.012％，S：0.009％，N：0.0038％，余量为铁和不可避免的杂质。
镀锡板厚度范围0.25mm。
镀锡板夹杂物水平：B类+D类+Ds类夹杂物等级之和0.5级。
本实施例中高锡量气雾阀门用镀锡板，其制造过程包括：
S1、将钢水经炼钢连铸后得到连铸坯；钢水的成分与气雾阀门用镀锡板的成分相同。浇铸中间包液面波动曲线最大0.8mm，结晶器拉速控制1.25m/min。
S2、将S1中得到的铸坯进行热轧，热轧地加热温度为1180℃，粗轧出口温度为1080℃，终轧温度为890℃，卷取温度为600℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，冷轧的压下率为91.6％，厚度波动±0.003mm；
S4、将S4中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，罩式退火的保温温度为620℃，保温时间为13h，升温速率25℃/h；
S5、将S5中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，平整处理的压下率为2％，采用工作辊表面粗糙度1.25μm，电火花毛化采用正极+负极+正极三遍毛化的方式，去除尖峰，同时增加峰值密度；
S6、将S6中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；镀锡工序的镀锡量为5.62g/m2，软熔线距淬水水面距离控制70cm，软熔温度控制280℃。
对比例2；
本实施例中高锡量气雾阀门用镀锡板，化学成分质量百分比为：C：0.05％，Mn：0.46％，Als：0.045％，Si：0.015％，P：0.012％，S：0.01％，N：0.0042％，余量为铁和不可避免的杂质。
镀锡板厚度范围0.29mm。
镀锡板夹杂物水平：B类+D类+Ds类夹杂物等级之和0.5级。
本实施例中高锡量气雾阀门用镀锡板，其制造过程包括：
S1、将钢水经炼钢连铸后得到连铸坯；钢水的成分与气雾阀门用镀锡板的成分相同。浇铸中间包液面波动曲线最大1mm，结晶器拉速控制1.2m/min。
S2、将S1中得到的铸坯进行热轧，热轧地加热温度为1180℃，粗轧出口温度为1080℃，终轧温度为890℃，卷取温度为600℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，冷轧的压下率为88％，厚度波动±0.003mm；
S4、将S3中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，罩式退火的保温温度为620℃，保温时间为13h，升温速率25℃/h；
S5、将S4中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，平整处理的压下率为2％，采用工作辊表面粗糙度1.25μm，电火花毛化采用正极+负极+正极三遍毛化的方式，去除尖峰，同时增加峰值密度；
S6、将S5中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；镀锡工序的镀锡量为5.76g/m2，软熔线距淬水水面距离控制85cm，软熔温度控制340℃。
图1为镀锡板的夹杂物低倍检测图，可以看出，视图中仅有尺寸较小的B类氧化铝夹杂，且等级小于1级。因此种成份的铝脱氧钢硫含量及S i含量均很低，不存在A类硫化物和C类硅酸盐类夹杂物。图2为镀锡板光扫描表面形貌图，可以看出，整个表面较为均匀，其波峰和波谷分布均衡，可最大限度降低因表面高点而导致的锡层脱落。
图3为镀锡板划格法附着力试验图，经3M胶带粘附10s撕下后，表面无明显的剥落痕迹，附着力较好。
表1实施例与对比例性能及表面参数对比
表2实施例与对比例过程工艺参数对比
表1为上述制造方法的四种实施例和两种对比例的镀锡板的性能、表面形貌对比。表2为上述制造方法的四种实施例和两种对比例的制造过程工艺参数的对比。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (1)

1.一种高锡量气雾阀门用镀锡铁，其特征在于，化学成分质量百分比为：C：0.04％～0.07％，Mn：0.45％～0.55％，Si：≤0.03％，P％≤0.015％，S％≤0.02％，余量为铁和不可避免的杂质；
所述镀锡铁的夹杂物水平：B类+D类+Ds类夹杂物等级之和≤1级；
所述镀锡铁的拉深成型指标：0°、45°及90°方向上塑性应变比r值均大于1.0，其各项异性Δr＜0.5，屈服强度250-300MPa，延伸率≥35％；
所述镀锡铁的表面形貌：Ra达到0.3-0.6μm，Rpc可实现超过180，Rz≤3.0μm，Rq≤0.5μm；
所述高锡量气雾阀门用镀锡铁制造方法，包括以下步骤；
S1、将钢水经炼钢连铸后得到连铸坯；所述钢水的成分与所述气雾阀门用镀锡板的成分相同；浇铸中包液面波动控制±1mm，拉速控制1.0—1.3m/min；
S2、将S1中得到的连铸坯进行热轧，所述热轧的加热温度为1150℃～1250℃，粗轧出口温度为1050℃～1110℃，终轧温度为860℃～890℃，卷取温度为580℃～620℃，得到热轧卷；
S3、热轧卷酸洗后进行冷轧，得到冷轧薄板，所述冷轧的压下率为80％～90％，厚度波动±0.003mm；
S4、将S3中得到的冷轧薄板进行表面脱脂和罩式退火，得到罩退后的冷轧薄板，所述罩式退火的保温温度为600℃～660℃，保温时间为13h，升温速率20-40℃/h；
S5、将S4中得到的退火后的冷轧薄板进行平整处理，得到平整后的薄板，所述平整处理的压下率为2％～4％，采用工作辊表面粗糙度1.0～1.5μm；
S6、将S5中得到的平整后的薄板进行镀锡工序，得到气雾罐阀门用镀锡板；所述镀锡工序的镀锡量为5.6～8.4g/m2，锡铁合金层≥1.2g/m2；
氧化锡≤1.5g/cm2，钝化膜4～8g/m2。
CN202310788394.0A 2023-06-29 2023-06-29 一种高锡量气雾阀门用镀锡铁及其制造方法 Active CN117004890B (zh)