CN116988628A - 一种真石漆施工工艺 - Google Patents
一种真石漆施工工艺 Download PDFInfo
- Publication number
- CN116988628A CN116988628A CN202310983424.3A CN202310983424A CN116988628A CN 116988628 A CN116988628 A CN 116988628A CN 202310983424 A CN202310983424 A CN 202310983424A CN 116988628 A CN116988628 A CN 116988628A
- Authority
- CN
- China
- Prior art keywords
- parts
- stone paint
- real stone
- water
- construction process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种真石漆施工工艺,包括以下步骤;S1、基面检查;S2、清理基层;S3、基面处理;S4、批刮外墙柔性防水腻子(两遍)上阳角;S5、辊涂透明渗透底漆(抗碱同色底漆);S6、化黑线分格;S7、喷涂真石漆(两遍);S8、辊涂或喷涂哑光罩面(一遍);S9、清理现场;通过水、纤维素HEC3万、ap‑95、分散剂、407、乙二醇、JT‑16份、950钛白(外墙)、1250高岭土、800硅灰石、800重钙、1512、C‑12、9203乳液、TK1、ASE‑60、水、L‑344、水、余水的原料制备的真石漆中,能够有效提高真石漆的附着性能,使得涂布后的家具具有良好附着力、有效提高了真石漆层的稳定性、抗裂性等性能。
Description
技术领域
本发明涉及建筑涂料施工的技术领域,具体是一种真石漆施工工艺。
背景技术
真石漆是一种装饰效果酷似大理石、花岗岩的涂料。主要采用各种颜色的天然石粉配制而成,应用于建筑外墙的仿石材效果,因此又称液态石。真石漆具有仿天然石材、大理石、花岗岩的厚浆型涂料。自然色泽,具有天然石材的质感,各种线格设计,能提供各种立体形状的花纹结构,能从视觉上彰显整个建筑的高雅与庄重之美,是外墙干挂石材最佳替代品。
真石漆与天然真石的效果高度一致,且具有硬度高,耐候性号,防火、耐酸碱、耐污染、无毒、无味等特点,因此广泛应用于各种外墙装饰施工。真石漆由于其施工方便,具有天然石材的质感和装饰效果,从而常用在高层建筑外墙外装饰工程中,深受广大业主和建设者的青睐。真石漆装修后的建筑物,具有天然真实的自然色泽,给人以高雅、和谐、庄重之美感,适合于各类建筑物的室内外装修。特别是在曲面建筑物上装饰,生动逼真,有一种回归自然的效果。
真石漆上漆工艺提供工艺简单,操作安全,外表美观、成本低廉、对环境无污染、对人体无害等特点,促进了生产的可持续发展,有利于减少人为健康的损害。但是,附着力、稳定性、抗裂性等性能还有待提高。
因此,本领域技术人员提供了一种真石漆施工工艺,以解决上述背景技术中提出的问题。
发明内容
本发明的目的在于提供一种真石漆施工工艺,以解决上述背景技术中提出的问题。
为实现上述目的,本发明提供如下技术方案:
一种真石漆施工工艺,包括以下步骤;
S1、基面检查;
S2、清理基层;
S3、基面处理;
S4、批刮外墙两遍柔性防水腻子上阳角;
S5、辊涂透明渗透底漆;
S6、化黑线分格;
S7、喷涂两遍真石漆;
S8、辊涂或喷涂一遍哑光罩面;
S9、清理现场;
其中,按重量份计,所述真石漆的制备原料包括有以下组分:水;1035-1050份、纤维素HEC3万;12.5-15份、ap-95;10-15份、分散剂;30-40份、407;7.5-10份、乙二醇;75-95份、JT-16;5-10份、950钛白;625-650份、1250高岭土;375-400份、800硅灰石;375-390份、800重钙;875-900份、1512;5-10份、C-12;75-100份、9203乳液;1250-1300份、TK1;10-20份、ASE-60;20-30份、水;50-80份、L-344;15-30份、水;50-70份、余水;100-150份。
作为本发明进一步的方案:按重量份计,所述真石漆的制备原料包括有以下组分:水;1035份、纤维素HEC3万;12.5份、ap-95;10份、分散剂;30份、407;7.5份、乙二醇;75份、JT-16;5份、950钛白;625份、1250高岭土;3750份、800硅灰石;375份、800重钙;875份、1512;5份、C-12;75份、9203乳液;1250份、TK1;10份、ASE-60;20份、水;50份、L-344;15份、水;50份、余水;100份。
作为本发明再进一步的方案:检查主体墙面平整度及线条是否顺直清晰,要求基层表面平整、水泥砂浆面保养15天,无浮灰、沥青等污渍,且PH<10,含水率<10%。
作为本发明再进一步的方案:腻子层施工;批刮柔性防水腻子2遍,养护,其用量2kg/㎡。
作为本发明再进一步的方案:底涂层施工;底漆施工:待墙面干燥后,处理浮灰,即进行渗透底漆底漆施工,底漆用量0.1kg/㎡,底漆干燥后,进行弹线、描黑线、分格用量为0.03kg/㎡。
作为本发明再进一步的方案:主涂层真石漆施工:待底涂层完全干燥后,即可进行施工,根据不同的装饰要求,先进行试验对比,大约用量3.5kg/㎡,主涂层:喷涂两遍。
作为本发明再进一步的方案:辅助处理:揭去分割胶带,根据装饰需要进行勾缝处理。
作为本发明再进一步的方案:罩面层施工:在主涂层完全干燥后,一般24-48进行施滚涂或者喷涂,罩光漆用量0.1kg/㎡。
作为本发明再进一步的方案:同一墙面的涂料应用同一批次的涂料施工,当同一批次的涂料不够时,应预先混匀,搅拌均匀,以保证同一墙面不产生色差。
作为本发明再进一步的方案:加强成品保护,严禁乱写乱画和污染。作业时如有小面积污染,应立即清洗干净,恢复原状。使用不同颜色涂料时,应用美纹纸进行分格,防止交叉污染,做好门窗部位、阳台栏杆、扶手等部位的成品保护。
作为本发明再进一步的方案:真石漆施工应以墙体的分格线、阴阳角、落水管、窗套等为边界分段施工。
作为本发明再进一步的方案:若开桶后的真石漆使用时占用了较长时间(比如超过1小时),在施工过程中以及再次施工时应再次搅拌,使桶内材料整体均匀一致,这样能够达到更好的施工效果。
作为本发明再进一步的方案:真石漆漆膜的干燥受到温度和湿度的影响较大,所以真石漆在喷涂时要连续施工,中间不要停顿,直到墙面全做完为止。
与现有技术相比,本发明的有益效果是:
涂刷完毕后的家具具有良好附着力、有效提高了真石漆层的稳定性、抗裂性等性能。
附图说明
图1为一种真石漆施工工艺的流程图。
具体实施方式
实施例1
一种真石漆施工工艺,包括以下步骤:
基面检查:用腻子找平家具板材表面,保证平整度;
漆施工:在外墙表面上用真石漆料和砂子(天然彩石砂)的混合物(砂子与真石漆料的质量比为2:1),批刮涂出纹理;
批刮外墙:室外高温加热烤漆,待纹理干燥后,用真石漆料纹理表面批平、表面打磨;
用罩面漆喷涂纹理表面,亚光处理,完成施工工序。
其中,腻子的用量为2kg/m2,底漆的厚度为0.5mm;批评工序升温用料为3kg/m2;罩面漆的厚度为0.5mm。
其中,所述真石漆料,包括以下组分:
按照重量份数计,所述真石漆料,包括以下组分:水;1035份、纤维素HEC3万;12.5份、ap-95;10份、分散剂;30份、407;7.5份、乙二醇;75份、JT-16;5份、950钛白(外墙);625份、1250高岭土;3750份、800硅灰石;375份、800重钙;875份、1512;5份、C-12;75份、9203乳液;1250份、TK1;10份、ASE-60;20份、水;50份、L-344;15份、水;50份、余水;100份;
实施例2
一种真石漆施工工艺,包括以下步骤:
基面检查:用腻子找平家具板材表面,保证平整度;
漆施工:在外墙表面上用真石漆料和砂子(天然彩石砂)的混合物(砂子与真石漆料的质量比为3:2),批刮涂出纹理;
批刮外墙:室外高温加热烤漆,待纹理干燥后,用真石漆料纹理表面批平、表面打磨;
用罩面漆喷涂纹理表面,亚光处理,完成施工工序。
其中,腻子的用量为3kg/m2,底漆的厚度为1mm;批评工序升温用料为5kg/m2;罩面漆的厚度为1mm。
其中,所述真石漆料,包括以下组分:
按照重量份数计,所述真石漆料,包括以下组分:水;1835份、纤维素HEC3万;14份、ap-95;15份、分散剂;40份、407;9份、乙二醇;90份、JT-16;7份、950钛白(外墙);725份、1250高岭土;4250份、800硅灰石;390份、800重钙;890份、1512;7份、C-12;95份、9203乳液;1450份、TK1;15份、ASE-60;30份、水;60份、L-344;20份、水;60份、余水;150份;
实施例3
一种真石漆施工工艺,包括以下步骤:
基面检查:用腻子找平家具板材表面,保证平整度;
漆施工:在外墙表面上用真石漆料和砂子(天然彩石砂)的混合物(砂子与真石漆料的质量比为5:3),批刮涂出纹理;
批刮外墙:室外高温加热烤漆,待纹理干燥后,用真石漆料纹理表面批平、表面打磨;
用罩面漆喷涂纹理表面,亚光处理,完成施工工序。
其中,腻子的用量为4kg/m2,底漆的厚度为1.5mm;批评工序升温用料为7kg/m2;罩面漆的厚度为1.5mm。
其中,所述真石漆料,包括以下组分:
按照重量份数计,所述真石漆料,包括以下组分:水;2385份、纤维素HEC3万;18份、ap-95;20份、分散剂;60份、407;12份、乙二醇;110份、JT-16;9份、950钛白(外墙);825份、1250高岭土;4825份、800硅灰石;120份、800重钙;910份、1512;9份、C-12;115份、9203乳液;1650份、TK1;17份、ASE-60;40份、水;70份、L-344;30份、水;70份、余水;180份;
性能测试
观察上述施工工艺涂布好的真石漆的外观,并通过耐洗刷性试验测试上述真石漆的附着性能,
结果显示:采用上述施工工艺涂布好的真石漆均呈现外观平整、无硬块、手感好、光泽度好的特点。
而耐洗刷性试验中,采用上述施工工艺涂布好的真石漆通过2000次试验,真石漆膜无破损。
上述测试结果说明通过水、纤维素HEC3万、ap-95、分散剂、407、乙二醇、JT-16份、950钛白(外墙)、1250高岭土、800硅灰石、800重钙、1512、C-12、9203乳液、TK1、ASE-60、水、L-344、水、余水的原料制备的真石漆中,能够有效提高真石漆的附着性能,使得涂布后的家具具有良好附着力、有效提高了真石漆层的稳定性、抗裂性等性能。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (8)
1.一种真石漆施工工艺,包括以下步骤;
S1、基面检查;
S2、清理基层;
S3、基面处理;
S4、批刮外墙两遍柔性防水腻子上阳角;
S5、辊涂透明渗透底漆;
S6、化黑线分格;
S7、喷涂两遍真石漆;
S8、辊涂或喷涂一遍哑光罩面;
S9、清理现场;
其中,按重量份计,所述真石漆的制备原料包括有以下组分:水;
1035-1050份、纤维素HEC3万;12.5-15份、ap-95;10-15份、分散剂;
30-40份、407;7.5-10份、乙二醇;75-95份、JT-16;5-10份、950钛白;625-650份、1250高岭土;375-400份、800硅灰石;375-390份、800重钙;875-900份、1512;5-10份、C-12;75-100份、9203乳液;1250-1300份、TK1;10-20份、ASE-60;20-30份、水;50-80份、L-344;15-30份、水;50-70份、余水;100-150份。
2.根据权利要求1所述的一种真石漆施工工艺,其特征在于,按重量份计,所述真石漆的制备原料包括有以下组分:水;1035份、纤维素HEC3万;12.5份、ap-95;10份、分散剂;30份、407;7.5份、乙二醇;75份、JT-16;5份、950钛白;625份、1250高岭土;3750份、800硅灰石;375份、800重钙;875份、1512;5份、C-12;75份、9203乳液;1250份、TK1;10份、ASE-60;20份、水;50份、L-344;15份、水;50份、余水;100份。
3.根据权利要求1所述的一种真石漆施工工艺,其特征在于,检查主体墙面平整度及线条是否顺直清晰,要求基层表面平整、水泥砂浆面保养15天,无浮灰、沥青等污渍,且PH<10,含水率<10%。
4.根据权利要求1所述的一种真石漆施工工艺,其特征在于,腻子层施工;批刮柔性防水腻子2遍,养护,其用量2kg/㎡。
5.根据权利要求1所述的一种真石漆施工工艺,其特征在于,底涂层施工;底漆施工:待墙面干燥后,处理浮灰,即进行渗透底漆底漆施工,底漆用量0.1kg/㎡,底漆干燥后,进行弹线、描黑线、分格用量为0.03kg/㎡。
6.根据权利要求1所述的一种真石漆施工工艺,其特征在于,主涂层真石漆施工:待底涂层完全干燥后,即可进行施工,根据不同的装饰要求,先进行试验对比,大约用量3.5kg/㎡,主涂层:喷涂两遍。
7.根据权利要求1所述的一种真石漆施工工艺,其特征在于,辅助处理:揭去分割胶带,根据装饰需要进行勾缝处理。
8.根据权利要求1所述的一种真石漆施工工艺,其特征在于,罩面层施工:在主涂层完全干燥后,一般24-48小时进行滚涂或者喷涂,罩光漆用量0.1kg/㎡。