CN116981528A - 结合固体的制造方法 - Google Patents

结合固体的制造方法 Download PDF

Info

Publication number
CN116981528A
CN116981528A CN202180095798.0A CN202180095798A CN116981528A CN 116981528 A CN116981528 A CN 116981528A CN 202180095798 A CN202180095798 A CN 202180095798A CN 116981528 A CN116981528 A CN 116981528A
Authority
CN
China
Prior art keywords
metal
producing
metal powder
solid according
point material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202180095798.0A
Other languages
English (en)
Chinese (zh)
Inventor
西冈和彦
景山宏治
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sun Meitarong Co ltd
Original Assignee
Sun Meitarong Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sun Meitarong Co ltd filed Critical Sun Meitarong Co ltd
Publication of CN116981528A publication Critical patent/CN116981528A/zh
Pending legal-status Critical Current

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/10—Sintering only
    • B22F3/105—Sintering only by using electric current other than for infrared radiant energy, laser radiation or plasma ; by ultrasonic bonding
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/20—Direct sintering or melting
    • B22F10/22—Direct deposition of molten metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/12—Metallic powder containing non-metallic particles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/10—Formation of a green body
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/10—Formation of a green body
    • B22F10/14—Formation of a green body by jetting of binder onto a bed of metal powder
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/20—Direct sintering or melting
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/20—Direct sintering or melting
    • B22F10/25—Direct deposition of metal particles, e.g. direct metal deposition [DMD] or laser engineered net shaping [LENS]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/20—Direct sintering or melting
    • B22F10/28—Powder bed fusion, e.g. selective laser melting [SLM] or electron beam melting [EBM]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/40—Structures for supporting workpieces or articles during manufacture and removed afterwards
    • B22F10/43—Structures for supporting workpieces or articles during manufacture and removed afterwards characterised by material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/50—Treatment of workpieces or articles during build-up, e.g. treatments applied to fused layers during build-up
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F10/00—Additive manufacturing of workpieces or articles from metallic powder
    • B22F10/60—Treatment of workpieces or articles after build-up
    • B22F10/66—Treatment of workpieces or articles after build-up by mechanical means
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/40—Radiation means
    • B22F12/41—Radiation means characterised by the type, e.g. laser or electron beam
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/50—Means for feeding of material, e.g. heads
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/50—Means for feeding of material, e.g. heads
    • B22F12/55—Two or more means for feeding material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/60—Planarisation devices; Compression devices
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/70—Gas flow means
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/004—Filling molds with powder
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/12—Both compacting and sintering
    • B22F3/14—Both compacting and sintering simultaneously
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/12—Both compacting and sintering
    • B22F3/16—Both compacting and sintering in successive or repeated steps
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/24—After-treatment of workpieces or articles
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F5/00—Manufacture of workpieces or articles from metallic powder characterised by the special shape of the product
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/008—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression characterised by the composition
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/02—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/02—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers
    • B22F7/04—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers with one or more layers not made from powder, e.g. made from solid metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/06—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools
    • B22F7/062—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools involving the connection or repairing of preformed parts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/06—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools
    • B22F7/08—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite workpieces or articles from parts, e.g. to form tipped tools with one or more parts not made from powder
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F9/00—Making metallic powder or suspensions thereof
    • B22F9/16—Making metallic powder or suspensions thereof using chemical processes
    • B22F9/18—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds
    • B22F9/20—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds starting from solid metal compounds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/005—Soldering by means of radiant energy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y10/00—Processes of additive manufacturing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y30/00—Apparatus for additive manufacturing; Details thereof or accessories therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B33—ADDITIVE MANUFACTURING TECHNOLOGY
    • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
    • B33Y70/00—Materials specially adapted for additive manufacturing
    • B33Y70/10—Composites of different types of material, e.g. mixtures of ceramics and polymers or mixtures of metals and biomaterials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/10—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on aluminium oxide
    • C04B35/111—Fine ceramics
    • C04B35/117—Composites
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B37/00—Joining burned ceramic articles with other burned ceramic articles or other articles by heating
    • C04B37/02—Joining burned ceramic articles with other burned ceramic articles or other articles by heating with metallic articles
    • C04B37/021—Joining burned ceramic articles with other burned ceramic articles or other articles by heating with metallic articles in a direct manner, e.g. direct copper bonding [DCB]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F12/00—Apparatus or devices specially adapted for additive manufacturing; Auxiliary means for additive manufacturing; Combinations of additive manufacturing apparatus or devices with other processing apparatus or devices
    • B22F12/90—Means for process control, e.g. cameras or sensors
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/10—Sintering only
    • B22F3/105—Sintering only by using electric current other than for infrared radiant energy, laser radiation or plasma ; by ultrasonic bonding
    • B22F2003/1054—Sintering only by using electric current other than for infrared radiant energy, laser radiation or plasma ; by ultrasonic bonding by microwave
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/02—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers
    • B22F7/04—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers with one or more layers not made from powder, e.g. made from solid metal
    • B22F2007/042—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers with one or more layers not made from powder, e.g. made from solid metal characterised by the layer forming method
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F7/00—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression
    • B22F7/02—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers
    • B22F7/04—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers with one or more layers not made from powder, e.g. made from solid metal
    • B22F2007/042—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers with one or more layers not made from powder, e.g. made from solid metal characterised by the layer forming method
    • B22F2007/045—Manufacture of composite layers, workpieces, or articles, comprising metallic powder, by sintering the powder, with or without compacting wherein at least one part is obtained by sintering or compression of composite layers with one or more layers not made from powder, e.g. made from solid metal characterised by the layer forming method accompanied by fusion or impregnation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2201/00—Treatment under specific atmosphere
    • B22F2201/01—Reducing atmosphere
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2201/00—Treatment under specific atmosphere
    • B22F2201/10—Inert gases
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2201/00—Treatment under specific atmosphere
    • B22F2201/50—Treatment under specific atmosphere air
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2202/00—Treatment under specific physical conditions
    • B22F2202/11—Use of irradiation
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/05—Light metals
    • B22F2301/052—Aluminium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/35—Iron
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy
    • B22F2998/10—Processes characterised by the sequence of their steps
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2999/00—Aspects linked to processes or compositions used in powder metallurgy
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
    • C04B2235/422—Carbon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/94—Products characterised by their shape
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/94—Products characterised by their shape
    • C04B2235/945—Products containing grooves, cuts, recesses or protusions
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/95—Products characterised by their size, e.g. microceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/341—Silica or silicates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/343—Alumina or aluminates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/345—Refractory metal oxides
    • C04B2237/346—Titania or titanates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/345—Refractory metal oxides
    • C04B2237/348—Zirconia, hafnia, zirconates or hafnates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/36—Non-oxidic
    • C04B2237/363—Carbon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/36—Non-oxidic
    • C04B2237/365—Silicon carbide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/40—Metallic
    • C04B2237/402—Aluminium
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/40—Metallic
    • C04B2237/405—Iron metal group, e.g. Co or Ni
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/40—Metallic
    • C04B2237/405—Iron metal group, e.g. Co or Ni
    • C04B2237/406—Iron, e.g. steel
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/40—Metallic
    • C04B2237/407—Copper
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/40—Metallic
    • C04B2237/408—Noble metals, e.g. palladium, platina or silver
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/68—Forming laminates or joining articles wherein at least one substrate contains at least two different parts of macro-size, e.g. one ceramic substrate layer containing an embedded conductor or electrode
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/70—Forming laminates or joined articles comprising layers of a specific, unusual thickness
    • C04B2237/704—Forming laminates or joined articles comprising layers of a specific, unusual thickness of one or more of the ceramic layers or articles
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/70—Forming laminates or joined articles comprising layers of a specific, unusual thickness
    • C04B2237/706—Forming laminates or joined articles comprising layers of a specific, unusual thickness of one or more of the metallic layers or articles
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/76—Forming laminates or joined articles comprising at least one member in the form other than a sheet or disc, e.g. two tubes or a tube and a sheet or disc
    • C04B2237/765—Forming laminates or joined articles comprising at least one member in the form other than a sheet or disc, e.g. two tubes or a tube and a sheet or disc at least one member being a tube
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/84—Joining of a first substrate with a second substrate at least partially inside the first substrate, where the bonding area is at the inside of the first substrate, e.g. one tube inside another tube

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Composite Materials (AREA)
  • Ceramic Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • Optics & Photonics (AREA)
  • Structural Engineering (AREA)
  • General Health & Medical Sciences (AREA)
  • Toxicology (AREA)
  • Health & Medical Sciences (AREA)
  • Organic Chemistry (AREA)
  • Civil Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Powder Metallurgy (AREA)
  • Welding Or Cutting Using Electron Beams (AREA)
  • Pressure Welding/Diffusion-Bonding (AREA)
CN202180095798.0A 2021-03-15 2021-12-13 结合固体的制造方法 Pending CN116981528A (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2021-041553 2021-03-15
JP2021041553 2021-03-15
PCT/JP2021/045831 WO2022195989A1 (ja) 2021-03-15 2021-12-13 結合固体の製造方法

Publications (1)

Publication Number Publication Date
CN116981528A true CN116981528A (zh) 2023-10-31

Family

ID=83320030

Family Applications (2)

Application Number Title Priority Date Filing Date
CN202180095798.0A Pending CN116981528A (zh) 2021-03-15 2021-12-13 结合固体的制造方法
CN202280021675.7A Pending CN117062683A (zh) 2021-03-15 2022-03-15 金属固体的制造方法

Family Applications After (1)

Application Number Title Priority Date Filing Date
CN202280021675.7A Pending CN117062683A (zh) 2021-03-15 2022-03-15 金属固体的制造方法

Country Status (7)

Country Link
US (7) US20240189902A1 (https=)
EP (4) EP4309837A4 (https=)
JP (4) JP7450312B2 (https=)
KR (2) KR20230156938A (https=)
CN (2) CN116981528A (https=)
IL (2) IL305935A (https=)
WO (2) WO2022195989A1 (https=)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN118989323A (zh) * 2024-08-19 2024-11-22 四川大学 电热力多物理场快速烧结超细铁铜镍预合金粉的方法

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP4486560A4 (en) * 2022-03-01 2026-01-21 Magnus Metal Ltd SYSTEM AND METHOD OF DEPOSIT BY ADDITIVE POURING
WO2024202964A1 (ja) * 2023-03-31 2024-10-03 株式会社Sun Metalon 固体製造装置及び固体の製造方法
JPWO2025121382A1 (https=) * 2023-12-08 2025-06-12
JP7709708B1 (ja) 2024-03-08 2025-07-17 トヨタ自動車株式会社 加熱装置
WO2025187682A1 (ja) * 2024-03-08 2025-09-12 株式会社Sun Metalon 加熱促進剤、金属の加熱方法、及び金属固体の製造方法
JP2025167154A (ja) 2024-04-25 2025-11-07 株式会社Sun Metalon 金属酸化物の還元体の製造方法
US12411481B1 (en) 2024-12-19 2025-09-09 K.K. Sun Metalon Control system, control method, and method of producing solid

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107107222A (zh) * 2014-10-01 2017-08-29 贝卡尔特公司 采用激光熔覆金属合金的锯元件
CN107262714A (zh) * 2017-05-23 2017-10-20 北京科技大学 一种适用于多种材料的微波烧结3d打印装置及其打印工艺
JP2020517824A (ja) * 2017-04-20 2020-06-18 エックスジェット・リミテッドＸｊｅｔ Ｌｔｄ． 印刷物を作成するシステムおよび方法

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4880578A (en) * 1988-08-08 1989-11-14 The United States Of America As Represented By The United States Department Of Energy Method for heat treating and sintering metal oxides with microwave radiation
CA2124093C (en) * 1994-03-31 2001-04-17 Prasad S. Apte Microwave sintering process
JP3274960B2 (ja) * 1996-02-23 2002-04-15 相田化学工業株式会社 金属焼結品の製造方法
JP2001228031A (ja) 2000-02-17 2001-08-24 Aida Kagaku Kogyo Kk 温度検知材、温度検知方法、及び貴金属製品の製造方法
JP4659951B2 (ja) 2000-08-18 2011-03-30 相田化学工業株式会社 温度検知方法、貴金属焼結品の製造方法、及び七宝製品の製造方法
US6544315B2 (en) 2001-03-12 2003-04-08 Gadi Har-Shai Sintered jewelry and decorative articles
WO2007038950A1 (en) * 2005-09-28 2007-04-12 Stichting Dutch Polymer Institute Method for generation of metal surface structures and apparatus therefor
JP5162181B2 (ja) 2007-08-01 2013-03-13 国立大学法人東京工業大学 マイクロ波製鉄炉
CN101323529B (zh) * 2008-07-11 2013-03-13 中国科学院上海硅酸盐研究所 微波烧结中的梯度透波结构及其用于制备陶瓷材料的方法
US9186742B2 (en) * 2009-01-30 2015-11-17 General Electric Company Microwave brazing process and assemblies and materials therefor
JP2012158790A (ja) 2011-01-31 2012-08-23 Nippon Steel Corp マイクロ波を利用した製鉄原料の還元方法
JP5811017B2 (ja) 2012-04-09 2015-11-11 新日鐵住金株式会社 還元鉄の製造方法
EP2900404B1 (en) 2012-09-27 2021-08-04 Allomet Corporation Methods of forming a metallic or ceramic article having a novel composition of functionally graded material
US20150054204A1 (en) * 2013-08-26 2015-02-26 Escape Dynamics Inc. Additive Manufacturing Microwave Systems And Methods
CN105492138B (zh) * 2013-08-30 2018-09-25 旭有机材工业株式会社 层叠铸模的造型方法
CN103882423B (zh) * 2013-12-25 2016-08-17 华侨大学 一种在Cu基体表面微波熔覆CuW合金的方法
US20180265417A1 (en) * 2015-01-23 2018-09-20 Hewlett-Packard Development Company, L.P. Susceptor materials for 3d printing using microwave processing
US10682699B2 (en) 2015-07-15 2020-06-16 Hrl Laboratories, Llc Semi-passive control of solidification in powdered materials
EP3325191B1 (en) * 2015-07-24 2020-09-30 Hewlett-Packard Development Company, L.P. Stabilizing liquid functional material for three-dimensional (3d) printing
JP6797642B2 (ja) 2015-12-10 2020-12-09 キヤノン株式会社 原料粉体の処理方法、および三次元造形物の製造方法
JP6756115B2 (ja) 2016-02-15 2020-09-16 日本製鉄株式会社 非晶質炭素材の黒鉛化処理方法および黒鉛を回収する際に生成する生成物並びに黒鉛
WO2018017130A1 (en) * 2016-07-22 2018-01-25 Hewlett-Packard Development Company, L.P. Additive manufacturing
CA3040921C (en) 2016-12-06 2024-02-20 Markforged, Inc. Additive manufacturing with heat-flexed material feeding
US10189204B2 (en) 2016-12-14 2019-01-29 Desktop Metal, Inc. Composite feedstock for additive manufacturing
US10960497B2 (en) 2017-02-01 2021-03-30 Hrl Laboratories, Llc Nanoparticle composite welding filler materials, and methods for producing the same
JP6810355B2 (ja) 2017-03-08 2021-01-06 Jsr株式会社 はんだ付け方法およびはんだ付け装置
US12121964B2 (en) 2018-11-07 2024-10-22 James J. Myrick Processes, compositions and systems for 2D and 3D printing
JP2020151993A (ja) 2019-03-20 2020-09-24 株式会社リコー 立体造形物の製造装置及び立体造形物の製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107107222A (zh) * 2014-10-01 2017-08-29 贝卡尔特公司 采用激光熔覆金属合金的锯元件
JP2020517824A (ja) * 2017-04-20 2020-06-18 エックスジェット・リミテッドＸｊｅｔ Ｌｔｄ． 印刷物を作成するシステムおよび方法
CN107262714A (zh) * 2017-05-23 2017-10-20 北京科技大学 一种适用于多种材料的微波烧结3d打印装置及其打印工艺

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
AMIT BANSAL, ET AL: "Characterization of bulk stainless steel joints developed through microwave hybrid heating", 《MATERIALS CHARACTERIZATION》, vol. 91, 15 February 2014 (2014-02-15), pages 34 - 41 *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN118989323A (zh) * 2024-08-19 2024-11-22 四川大学 电热力多物理场快速烧结超细铁铜镍预合金粉的方法

Also Published As

Publication number Publication date
KR20230156938A (ko) 2023-11-15
US20240165700A1 (en) 2024-05-23
EP4374992A2 (en) 2024-05-29
EP4309837A1 (en) 2024-01-24
JP7450312B2 (ja) 2024-03-15
US12246378B2 (en) 2025-03-11
EP4310064A1 (en) 2024-01-24
US20240165707A1 (en) 2024-05-23
CN117062683A (zh) 2023-11-14
WO2022195989A1 (ja) 2022-09-22
US20240165706A1 (en) 2024-05-23
US20250187074A1 (en) 2025-06-12
IL305937A (en) 2023-11-01
JP2024059860A (ja) 2024-05-01
KR20230156939A (ko) 2023-11-15
US20250018473A1 (en) 2025-01-16
EP4434654A1 (en) 2024-09-25
JPWO2022196681A1 (https=) 2022-09-22
US12263525B2 (en) 2025-04-01
IL305935A (en) 2023-11-01
JP7844042B2 (ja) 2026-04-13
EP4310064A4 (en) 2024-09-25
WO2022196681A1 (ja) 2022-09-22
US20240189902A1 (en) 2024-06-13
JP7450313B2 (ja) 2024-03-15
EP4309837A4 (en) 2024-09-25
US12115579B2 (en) 2024-10-15
EP4374992A3 (en) 2024-08-28
JPWO2022195989A1 (https=) 2022-09-22
JP2024059859A (ja) 2024-05-01
US20250281977A1 (en) 2025-09-11

Similar Documents

Publication Publication Date Title
CN116981528A (zh) 结合固体的制造方法
US6828026B2 (en) Hollow balls and a method for producing hollow balls and for producing light-weight structural components by means of hollow balls
JPWO2022196681A5 (https=)
DK2236229T3 (en) A process for preparing a powder-based article
US10625337B2 (en) Adhesion to build plate in 3D printer
JP2024059859A5 (https=)
JP2024059860A5 (https=)
US20220203454A1 (en) Manufacturing method with additive component production and post-processing
WO2019025801A1 (en) METHODS AND COMPONENTS OF ADDITIVE MANUFACTURE
US20190240734A1 (en) Geometry For Debinding 3D Printed Parts
JPWO2022195989A5 (https=)
WO2019079423A1 (en) METHOD AND APPARATUS FOR ADDITIVE MANUFACTURING
CA3147884A1 (en) Casting mould
CN101612665B (zh) 压制部件的选择性烧结
WO2016030654A1 (en) A mould for use in a hot isostatic press
JP2025163316A (ja) 金属固体の製造方法
US20260102967A1 (en) Method for Processing Reactive and Non-Reactive Materials in the Presence of Binder Agents
KR102601962B1 (ko) 3차원 프린팅용 재료 및 이를 이용하는 3차원 프린터
CN120715232A (zh) 层叠造型用粉末以及层叠造型体
EP1210192A1 (en) A method of producing a body for electric heating, as well as a body produced by the method

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination