CN1168351A - 无铁液体硫酸铝的生产工艺 - Google Patents

无铁液体硫酸铝的生产工艺 Download PDF

Info

Publication number
CN1168351A
CN1168351A CN 97105241 CN97105241A CN1168351A CN 1168351 A CN1168351 A CN 1168351A CN 97105241 CN97105241 CN 97105241 CN 97105241 A CN97105241 A CN 97105241A CN 1168351 A CN1168351 A CN 1168351A
Authority
CN
China
Prior art keywords
aluminium
aluminium sulfate
weight percent
sulfuric acid
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 97105241
Other languages
English (en)
Other versions
CN1048472C (zh
Inventor
张德明
舒莉萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN 96111165 external-priority patent/CN1146974A/zh
Application filed by Individual filed Critical Individual
Priority to CN97105241A priority Critical patent/CN1048472C/zh
Publication of CN1168351A publication Critical patent/CN1168351A/zh
Application granted granted Critical
Publication of CN1048472C publication Critical patent/CN1048472C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种无铁液体硫酸铝的生产制备方法。它的分子式为：Al2(SO4)3·XH2O，分子量为342.15(按1979年国际原子量无水硫酸铝计)，是无机混凝剂中具有代表性一种。本发明采用氢氧化铝或硫酸铝与硫酸进行一步反应而得，与无铁固体硫酸铝的生产工艺相比具有工艺流程简单、成本低、使用方便等优点，是当今造纸业生产高档白版纸可采用的最佳施胶剂。

Description

无铁液体硫酸铝的生产工艺
本发明涉及一种无铁液体硫酸铝的生产制备方法。
本发明的无铁液体硫酸铝是一种高档的白版纸最新型、最理想的施胶剂，目前国内虽有固体无铁硫酸铝生产，而无铁液体硫酸铝尚属空白。现在目前使用的固体硫酸铝需除铁过程、蒸发、结晶，故工艺复杂、成本高，而且使用时需用水稀释均匀，使用不方便而且控制杂质困难等缺点。
本发明的目的在于提供一种工艺简单、使用方便的无铁液体硫酸铝的制备方法。
本发明的无铁液体硫酸铝的制备方法的技术方案是这样实现的。它把含重量百分比为60％-80％三氧化二铝的氢氧化铝和水进行搅拌，然后与重量百分比98％-105％的硫酸反应，而且氢氧化铝∶硫酸∶水重量配比为1-1.2∶1.5-2∶0.9-1.5，反应后的物料经固液分离，将杂质除去，其滤液即为铁离子含量在100ppm以下的无铁液体硫酸铝。
上述的无铁液体硫铝的制备工艺，它最佳是把含重量百分比64％三氧化二铝的氢氧化铝和水进行搅拌，然后与重量百分比98％的硫酸反应而且氢氧化铝∶硫酸∶水重量配比为1∶1.5∶1.3，反应后的物料经固液分离，将杂质除去，其滤液即为铁离子含量在100ppm以下的无铁液体硫酸铝。上述的制备方法中反应是在搅拌反应釜中进行，搅拌速度为50转/分-70转/分，反应釜内蒸汽压力为2.0千克/厘米2-3千克/厘米2，反应时间为3小时-4小时。
上述的重量百分比60-80％三氧化铝的氢氧化铝可为重量百分比40-60％的碳酸铝代替。
下面对本发明的实施例作进一步描述。
实施例1。
本发明无铁液体硫酸铝采用山东铝厂的氢氧化铝和硫酸为原料。
      氢氧化铝产品理化性能数据
  Al2O3％   SiO2％     Fe2O3％   Na2O％ 灼减％(＜0.1)
60~64 ≤0.03  0.006~0.01   ≤0.45     ≤35
将含重量百分比64％三氧化二铝的氢氧化铝与水搅拌成浆，再加重量百分比98％的硫酸，其中铁含量为80ppm-120ppm，在加温加压条件下进行反应，而上述氢氧化铝∶硫酸∶水的重量配比为1∶1.5∶1.3。反应是在KR5000立升的耐酸搪瓷反应釜中进行，将氢氧化铝和水在打浆池搅拌打成浆，用泥浆泵送入反应釜内，其搅拌速度控制在60±10转/分，再加入硫酸进行搅拌均匀，然后随其自身进行放热反应，釜内的压力逐渐上升，直至2.5±5千克/厘米2，开始保温，3-4小时后反应结束，釜的夹套内通水冷却至釜内压力降至常压打开底阀放料，得到无铁液体硫酸铝为无色澄清液体，无杂质，其分子式为Al2(SO4)3·XH2O，分子量为342.15(按1979年国际原子量无水硫酸铝计)，比重1.25，Be30°，三氧化二铝含量7％，铁含量≤0.0037％，酸值(2％)≥3.2，水不溶物≤0.06％。产品极易溶解水，存期一年内不变质，不影响使用效果，产品经宁波市化工产品质量监督检验站检测，符合无铁液体硫酸铝企业标准的技术要求。
实施例2。
将含重量百分比60％三氧化二铝的氢氧化铝、重量百分比98％的硫酸、水按1.2∶2∶0.9重量配比反应，其余如实施例1。
实施例3。
将含重量百分比80％三氧化二铝的氢氧化铝、重量百分比105％的硫酸、水按1∶1.5∶1.5重量配比反应，其余如实施例1。
实施例4。
将重量百分比50％碳酸铝、重量百分比98％的硫酸、水按1∶1.5∶1.3重量配比反应，其余如实施例1。
实施例5。
将重量百分比40％碳酸铝、重量百分比98％的硫酸、水按1.2∶2∶0.9重量配比反应，其余如实施例1。
实施例6。
将重量百分比60％碳酸铝、重量百分比105％的硫酸、水按1∶1.5∶1.5重量配比反应，其余如实施例1。
本发明的无铁液体硫酸铝制备工艺，具有工艺流程简单、成本低、而且使用方便。经宁波中华纸业股份有限公司一年半使用表明，无铁液体硫酸铝的水不溶物极少，产品清晰，透明无杂质，比固体无铁硫酸铝稀释均匀，产品质量完全符合高档白版纸施胶的要求，同时改善劳动环境、使操作简便、省力省时、降低制浆成本、是一种值得推广应用的施胶剂。

Claims (4)

1.一种无铁液体硫酸铝的生产工艺，它把含重量百分比60％-80％三氧化二铝的氢氧化铝和水进行搅拌，然后与重量百分比98％105％的硫酸反应，而且氢氧化铝∶硫酸∶水重量配比为1-1.2∶1.5-2∶0.9-1.5，反应后的物料经固液分离，将杂质除去，其滤液即为铁离子含量在100ppm以下的无铁液体硫酸铝。
2.如权利要求1所述的无铁液体硫酸铝生产工艺，其特征在于它最佳是把含重量百分比64％三氧化二铝的氢氧化铝和水进行搅拌，然后与98％重量百分比的硫酸反应而且氢氧化铝∶硫酸∶水重量配比为1∶1.5∶1.3，反应后的物料经固液分离，将杂质除去，其滤液即为铁离子含量在100ppm以下的无铁液体硫酸铝。
3.如权利要求1所述的无铁液体硫酸铝生产工艺，其特征在于上述反应是在搅拌反应釜中进行，搅拌速度为50转/分-70转/分，反应物釜内蒸汽压力为2千克/厘米2-3千克/厘米2，反应时间为3小时～4小时。
4.如权利要求1所述的无铁液体硫酸铝的生产工艺，其特征在于所述的重量百分比60-80％三氧化铝的氢氧化铝可为重量百分比40-60％的碳酸铝代替。
CN97105241A 1996-08-15 1997-07-03 无铁液体硫酸铝的生产工艺 Expired - Fee Related CN1048472C (zh)