CN116600983A - 涂布工具用液体收纳构件 - Google Patents
涂布工具用液体收纳构件 Download PDFInfo
- Publication number
- CN116600983A CN116600983A CN202180085062.5A CN202180085062A CN116600983A CN 116600983 A CN116600983 A CN 116600983A CN 202180085062 A CN202180085062 A CN 202180085062A CN 116600983 A CN116600983 A CN 116600983A
- Authority
- CN
- China
- Prior art keywords
- layer
- paper
- paper base
- liquid storage
- coating tool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
提供:通过将以往用聚丙烯等塑料成型而成的墨等的液体收纳管置换为包含纸基材的材料从而减少塑料的用量、减少对环境的影响的涂布工具用液体收纳构件。一种涂布工具用液体收纳构件,其特征在于,具有包含纸基材层叠体和外层的至少三层,所述纸基材层叠体具备:纸基材的内层、和形成于前述内层的外表面侧、且为金属层或二氧化硅蒸镀层的中间层,所述外层形成于前述内层的外表面侧、且包含纸基材,所述涂布工具用液体收纳构件具有如下结构:将前述纸基材层叠体以螺旋状缠绕的结构、和将前述包含纸基材的外层以螺旋状缠绕于前述中间层的外表面侧的结构,且在前述内层与中间层之间和前述中间层与外层之间的至少一者中具有包含聚烯烃树脂的粘接剂的层。
Description
技术领域
本发明涉及:使用纸基材代替塑料的、减少了对环境的影响的涂布工具用液体收纳构件。
背景技术
例如,圆珠笔等的笔用具用墨收纳管通过将其一端部(前端部)压入嵌合至作为笔构件的圆珠笔笔芯或支撑圆珠笔笔芯的中继构件而收纳于笔具的轴筒中。
而且,为了确保成型的容易性和墨量的视觉识别性,一直以来,使用例如聚丙烯等透明或半透明的塑料作为墨收纳管。
然而,近年来,微塑料向海洋流出的问题备受关注,解决地球环境问题的势头越来越高,例如避免使用一次性的塑料等。
也提出了着眼于对于构成笔具的各部件进行脱塑的提案,专利文献1中公开了一种笔具,其具备使用复合材料并将该复合材料螺旋成型而成的轴筒,所述复合材料是将纸作为基材、在其上层叠具有阻隔性的合成树脂、铝等金属而成的。
为了改善耐水性、阻气性,该笔具所使用的轴筒具有如下结构:从轴筒的外表面侧重叠了背面由牛皮纸形成的铝箔标签纸和衬纸这2层,然后在内表面层叠了聚乙烯层、接着层叠外侧具有铝蒸镀膜的聚酯膜。
根据该轴筒,通过使用包含纸基材的复合材料,从而可以提供能边维持耐内容物性和耐久性边实现低公害化的笔具。
另一方面,专利文献2中提出了一种多层结构的使用了墨收纳管的水性墨收纳构件,其是在由生物降解性树脂成型而成的收纳管基体的内侧形成一层或二层以上的其他树脂层而成的。
由此,由生物降解性树脂成型而成的收纳管基体不会因水性墨中发生溶胀而引起尺寸变化,另外,随着时间的推移而被生物降解,因此,可以有利于废弃处理量的少量化。
现有技术文献
专利文献
专利文献1:日本特开昭62-70097号公报
专利文献2:日本特开2001-146091号公报
发明内容
发明要解决的问题
如前述,使用了生物降解性树脂、纸基材的制品适于低公害化,尤其如果使用包含纸浆或纸的原材料作为基材,则认为可以提供能替代塑料的考虑了环境问题的制品。
本发明是鉴于前述观点而作出的,其通过将使用聚丙烯等塑料成型而成的墨等的液体收纳管替换为包含纸基材的材料,可以实现脱塑。
用于解决问题的方案
本发明的涂布工具用液体收纳构件的特征在于,具有包含纸基材层叠体和外层的至少三层,所述纸基材层叠体具备:纸基材的内层、和形成于前述内层的外表面侧、且为金属层或二氧化硅蒸镀层的中间层,所述外层形成于前述内层的外表面侧、且包含纸基材,所述涂布工具用液体收纳构件具有如下结构:将前述纸基材层叠体以螺旋状缠绕的结构、和将前述包含纸基材的外层以螺旋状缠绕于前述中间层的外表面侧的结构,且在前述内层与中间层之间和前述中间层与外层之间的至少一者中具有包含聚烯烃树脂的粘接剂的层。
优选前述纸基材层叠体的宽度方向的长度为4~20mm。
优选前述内层的纸基材的密度为0.8g/cm3以上。
优选前述内层的纸基材为玻璃纸、羊皮纸或硬化纸板(vulcanized fiber)。
前述涂布工具用液体收纳构件优选具有如下结构:沿涂布工具用液体收纳构件的长度方向,使前述纸基材层叠体以不使其相邻面彼此重叠的方式接触并缠绕成螺旋状的结构和使前述包含纸基材的外层以使其相邻面彼此接触的方式缠绕成螺旋状的结构。
前述涂布工具用液体收纳构件优选具有两组以上的前述纸基材层叠体
优选前述纸基材层叠体彼此的接触部位与前述包含纸基材的外层彼此的接触部位沿涂布工具用液体收纳构件的长度方向、错开1mm以上且错开前述纸基材层叠体或前述包含纸基材的外层的宽度的二分之一以下。
前述涂布工具用液体收纳构件优选为笔用具用纸制笔芯。
发明的效果
根据本发明,纸基材层叠体中,使内层与中间层之间、和中间层与外层之间的至少任一者由聚烯烃树脂粘接剂、或包含聚烯烃树脂和其他树脂的粘接剂贴合,从而涂布工具用液体收纳构件的层间密合,可以抑制墨向液体收纳构件的外部漏出的情况。为了抑制墨的漏出,使用宽幅的纸基材层叠体,扩大纸基材层叠体彼此的接缝4彼此的间隔、和外层的接缝4’彼此的间隔是更有效的。
由此,根据本发明,可以提供减少了塑料的用量的、减少了对环境的影响的涂布工具用液体收纳构件。
附图说明
图1为示出包含本发明的涂布工具用液体收纳构件的笔芯的构成的一例的图。图1的(a)为笔芯的外观的主视图,图1的(b)为笔芯的A-A箭头剖视图。
图2为示出:本构成发明的涂布工具用液体收纳构件的内层、中间层和外层的三层结构中、在内层和中间层之间具有粘接剂层的形态(2a)的图、在中间层和外层之间具有粘接剂层的形态(2b)的图、以及在内层、中间层和外层之间具有粘接剂层的形态(2c)的图。
图3为示出构成本发明的涂布工具用液体收纳构件的纸基材层叠体的多层结构[纸基材层叠体(内层1+粘接剂层5+中间层2)、粘接剂层5、内层1、粘接剂层5、内层1、粘接剂层5、纸基材层叠体(中间层2+粘接剂层5+内层1)、粘接剂层5、外层3、粘接剂层5、外层3]的形态(3a)、以及多层结构[纸基材层叠体(内层1+粘接剂层5+中间层2)、粘接剂层5、纸基材层叠体(内层1+粘接剂层5+中间层2)、粘接剂层5、外层3、粘接剂层5和外层3]的形态(3b)的图。
具体实施方式
对本发明的涂布工具用液体收纳构件,边参照附图边以下详细进行说明。
图1为示出包含本发明的涂布工具用液体收纳构件10的笔芯的构成的一例的图,图1的(a)示出笔芯的外观的主视图,图1的(b)示出笔芯的A-A箭头剖视图。
图1中,例如,收纳于圆珠笔的轴筒的笔芯具备:将纸作为基材、且为收纳未做图示的墨的细长的圆筒形状的墨收纳管的涂布工具用液体收纳构件10(以下也简称为“液体收纳构件10”。);安装于该液体收纳构件10的前端的接头11;和,作为笔构件安装于接头11的前端的圆珠笔尖端12。
具体地,接头11上形成有与液体收纳构件10接合的圆筒形状的后端部分、和外径大于该后端部分的圆筒形状的前端部分,在该前端部分安装有圆珠笔尖端12。另外,在接头11的后端部分,对与液体收纳构件10的接合部分预先涂布粘接剂以使其具有一定的接合强度,在该状态下,通过将接头11的后端部分压入到液体收纳构件10的前端内部,从而将接头11与液体收纳构件10接合。由此,液体收纳构件10与圆珠笔尖端12借助接头11以能使墨流通的方式连接。
前述液体收纳构件10具有包含纸基材层叠体和外层3的至少三层,所述纸基材层叠体具备:纸基材的内层1、和形成于前述内层1的外表面侧、且为金属层或二氧化硅蒸镀层的中间层2,所述外层3形成于前述中间层2的外表面侧、且包含纸基材,所述液体收纳构件10具有如下结构:将前述纸基材层叠体以内层1成为内侧的方式缠绕成螺旋状的结构、和将前述包含纸基材的外层以螺旋状缠绕于前述中间层2的外表面侧的结构,且在前述内层1与中间层2之间、和前述中间层2与外层3之间的至少一者中具有包含聚烯烃树脂的粘接剂的层。
前述液体收纳构件10具有与液体接触的内层1、中间层2和外层3的至少三层,且在前述内层1与中间层2之间、和中间层2与外层3之间的至少一者中具有包含聚烯烃树脂的粘接剂的层5(以下简称为“粘接剂层5”)。图2c示出在前述内层1与中间层2之间、和中间层2与外层3之间这两者中具有粘接剂层5的形态。这种三层结构中内层1和中间层2是作为在纸基材的表面层叠有金属层或二氧化硅蒸镀层的复合材料的纸基材层叠体。如前述,粘接剂层5可以夹设于纸基材层叠体。
作为构成内层1的纸基材,可以使用优质纸、中等纸、单面光泽纸、牛皮纸、单面光泽牛皮纸、漂白牛皮纸、板纸、白板纸、内衬、微涂工纸、涂布纸、铜版纸、浇铸涂布纸、玻璃纸、羊皮纸、和硬化纸板等各种公知的物质。
这些纸基材的密度优选0.8g/cm3以上。通过使用密度0.8g/cm3以上的纸基材,从而可以赋予充分的耐水性、耐油性。
构成内层1的纸基材更优选为玻璃纸、羊皮纸或硬化纸板、且密度为0.8g/cm3以上。
玻璃纸是高密度且透明性高的纸,是通过将原纸浆高度地打浆,增大比表面积,并进行抄纸,对抄纸后的纸用超级压光机进行处理,进行致密化的同时增强纤维素纤维彼此的结合而成者。本发明中,使用单位面积质量为20~50g/m2的玻璃纸。通过使用玻璃纸作为构成内层1的纸基材,从而容易赋予耐水性、耐油性。另外,也可以使用:将单位面积质量为20~50g/m2的玻璃纸作为基纸在其单面或两面涂覆聚乙烯醇水溶液等涂覆液而成者。玻璃纸的厚度通常为20~50μm、优选20~30μm。
羊皮纸和硬化纸板是通过制造过程中的基于浓硫酸、氯化锌溶液的处理而增强纤维素纤维彼此的直接结合而成者,即,增加纤维素纤维之间的纤维素的氢键的密度而成者。由此,如果使用羊皮纸和硬化纸板作为构成内层1的纸基材,则可以有效地抑制纸屑的发生。
羊皮纸例如使用单位面积质量为20~100g/m2者,优选使用的是,以依据纸和板纸的吸水度试验方法(Cobb法)使用矿物油代替水时的吸油度成为13g/m2以下的方式提高了耐油性而成者。羊皮纸的厚度通常为20~100μm、优选20~60μm。
硬化纸板由于制造过程中的反应性的差异而容易制成比羊皮纸还厚。因此,适于作为纸基材需要厚纸的情况。如果考虑形成液体收纳构件10后的纸管部分的压缩强度、制造时的操作容易性,则硬化纸板的厚度通常为0.08~1mm、优选0.1~0.5mm。另外,硬化纸板的密度高于一般的纸管原纸,通常为0.8~1.4g/cm3,本发明中,如果考虑纸管部分的强度、获得容易性,则优选0.8~1.3g/cm3。
另外,可以对羊皮纸和硬化纸板实施树脂浸渗处理或玻璃涂覆处理。通过实施前述处理,从而纤维素纤维彼此的结合进一步得到增强,使用这些纸作为构成内层1的纸基材的情况下,也可以抑制纸屑的发生。
中间层2为金属层或二氧化硅蒸镀层。金属层可以如下设置:将铝箔等金属箔由包含聚烯烃树脂的粘接剂粘接在纸基材的单面、或者将铝、或铝和锌的合金等在真空下进行电子束蒸镀,从而设置。
此处,对本发明中使用的包含聚烯烃树脂的粘接剂进行说明。包含聚烯烃树脂的粘接剂可以为由一种或两种以上的聚烯烃树脂形成的粘接剂,也可以为混合有该聚烯烃树脂与其他树脂的粘接剂。
聚烯烃树脂具体而言,除聚乙烯系离聚物、聚丙烯离聚物、聚丙烯弹性体、聚乙烯弹性体、高密度聚乙烯和低密度聚乙烯等之外,还包含马来酸酐改性聚丙烯等改性聚烯烃树脂。它们之中,优选聚丙烯离聚物和马来酸酐改性聚丙烯等。
其他树脂中,具体而言,可以举出丙烯酸共聚物、乙烯·乙烯醇共聚物(EVOH)、乙烯·丙烯酸共聚物(EAA)、乙烯·甲基丙烯酸共聚物(EMAA)、环氧树脂、碳二亚胺交联剂、乙烯·乙酸乙烯酯共聚物或聚乙烯醇等。
将聚烯烃树脂与其他树脂混合的情况下,粘接剂总量中、聚烯烃树脂的比率为60~97重量%左右、优选90~97重量%。另外,聚烯烃树脂与其他树脂的总计中、聚烯烃树脂的比率为68~98重量%左右、优选93~98重量%。
本发明的包含聚烯烃树脂的粘接剂以将聚烯烃树脂、或聚烯烃树脂和其他树脂的混合物作为基础聚合物的、分散液型或乳液型的树脂液的形态使用。前述树脂液中,可以根据需要添加硅烷偶联剂等添加剂。它们之中,出于粘接性和操作性优异的方面,优选聚丙烯离聚物和马来酸酐改性聚丙烯等分散液型粘接剂。
包含聚烯烃树脂的粘接剂涂布于内层1与中间层2之间、和中间层2与外层3之间的至少一者。即,如图2所示,可以在内层1与中间层2之间设置粘接剂层5(图2a),也可以在中间层2与外层3之间设置粘接剂层5(图2b),还可以在内层1、中间层2和外层3之间设置粘接剂层5(图2c)。通过对纸材涂布具有优异的粘接力和墨耐性的包含聚烯烃树脂的粘接剂,从而液体收纳构件的层间密合在内层1、中间层2和外层3之间,可以有效地防止墨向液体收纳构件10的外部漏出的情况。此处,墨耐性是指能抑制粘接剂树脂成分向墨溶出的程度。墨耐性如果不充分,则引起笔芯的强度降低、挥发减量的增加。另外,产生漏墨所导致的笔芯的外观不良。使用包含聚烯烃树脂的粘接剂的情况下,与墨的相溶性低,因此,聚烯烃树脂不会溶出到墨中,可以期待对它们的墨耐性的效果。
需要说明的是,本发明中,只要使内层1、中间层2和外层3之间的任意者由包含聚烯烃树脂的粘接剂贴合即可,也可以并用其他粘接剂、例如乙酸乙烯酯树脂系、丙烯酸类树脂系和聚乙烯醇等通用粘接剂。
包含聚烯烃树脂的粘接剂以在内层1或中间层2的中央附近隆起的方式进行涂布。接着,边挤压内层1与中间层2边将粘接剂扩展至粘接面整面,以不使气泡残留在粘接部、无粘接缺陷部的方式将两层粘接。使内层1和中间层2贴合后,进行加压固定直至粘接剂固化。
对内层1或中间层2,以5~50g/m2左右、优选以5~25g/m2的量涂布包含聚烯烃树脂的粘接剂。
液体收纳构件10的内层1和中间层2可以全部由同等厚度的纸基材和由使用了金属层或二氧化硅蒸镀层的纸基材层叠体形成,或者也可以适宜组合不同厚度的纸基材和使用了金属层或二氧化硅蒸镀层的纸基材层叠体而形成。
纸基材层叠体中,纸基材的厚度与金属层或二氧化硅蒸镀层的厚度的比率为2/1~1200/1左右。
使中间层2密合在内层1上后,用原纸分切机等裁切成宽4~20mm,从而得到为带状的片的纸基材层叠体。接着,将前述纸基材层叠体以螺旋状缠绕于液体收纳构件10加工用的芯棒(纸管制造机)使得内层1成为内侧。需要说明的是,对于芯棒,为了在形成内层1、中间层2和外层3后使芯棒的拉拔容易,优选预先用适当的润滑剂对表面进行处理,或在内层1(纸基材)的缠绕于芯棒一侧的面上涂布适量的润滑剂。之后,为了粘接外层3,在外侧的中间层2上涂布包含聚烯烃树脂的粘接剂等粘接剂。
纸基材层叠体更优选为裁切成宽4~20mm、优选宽5~15mm的带状片。如果使用这种宽幅的纸基材层叠体并形成螺旋卷,则即使不大量卷绕,也可以达到所需的液体收纳构件10的长度,作为结果,纸基材彼此的接触面、即接缝4的数量少,可以抑制收纳于液体收纳构件10内的液体的漏出。
在中间层2的外侧进一步将纸基材缠绕成螺旋状而形成外层3。外层3也优选使用宽4~20mm、具体地宽6~15mm的纸基材而形成。与纸基材层叠体同样地,这是由于,如果减少接缝4’的数量,则可以抑制液体收纳构件10内的液体漏出。
构成外层3的纸基材中可以使用构成上述内层1的纸基材。另外,也可以使用前述包含聚烯烃树脂的粘接剂,使外层3粘附在中间层2上。此时的包含聚烯烃树脂的粘接剂的涂布方法和涂布量也与对内层1或中间层2的涂布方法和涂布量为同等程度。
内层1、中间层2和外层3的各自的厚度(μm)的比率通常为20~60:0.025~12:50~200、优选20~30:0.025~12:50~200。
根据纸基材的种类、厚度,也可以如图3所示在中间层2和外层3之间进一步夹设内层1。该情况下,中间层2和内层1、或内层1和外层3可以使用包含聚烯烃树脂的粘接剂而粘接。
另外,纸基材层叠体可以具有两组以上,例如,如图3所示,前述液体收纳构件10可以具有纸基材层叠体(内层1+粘接剂层5+中间层2)、粘接剂层5、内层1、粘接剂层5、内层1、粘接剂层5、纸基材层叠体(中间层2+粘接剂层5+内层1)、粘接剂层5、外层3、粘接剂层5、外层3所形成的结构(3a);或,纸基材层叠体(内层1+粘接剂层5+中间层2)、粘接剂层5、纸基材层叠体(内层1+粘接剂层5+中间层2)、粘接剂层5、外层3、粘接剂层5和外层3所形成的结构(3b)。前述多层结构中,内层1、中间层2和外层3的各自的厚度(μm)的比率可以与具有各一层内层1、中间层2和外层3的三层结构的情况同样,存在的多个内层1、中间层2和外层3的各自的厚度也可以不同。这种多层结构的实施方式的液体收纳构件10在防止液体的漏出、挥发的方面是更优选的方式。
如前述,液体收纳构件10具有沿该液体收纳构件10的长度方向、使纸基材层叠体以使其相邻面彼此不重叠的方式接触并缠绕成螺旋状的结构。该相邻面的重叠假定在前述纸基材层叠体彼此的接触部位、即在接缝4相邻面彼此重叠,重叠幅度最大也设为1mm。通过以不使接缝4重叠的方式接触、或使重叠幅度最大为1mm,从而可以抑制液体自接缝4的漏出。在接缝4中重叠幅度如果超过1mm,则在该重叠部分产生高度差,有时导致液体漏出。
前述外层3也与纸基材层叠体同样地,优选使该相邻面彼此接触并缠绕。优选外层3彼此的接缝4’与纸基材层叠体彼此的接缝4沿涂布工具用液体收纳构件的长度方向、错开1mm以上且错开前述纸基材层叠体或前述外层3的宽度的二分之一以下的间隔,更优选错开3mm以上且错开前述纸基材层叠体或前述外层3的宽度的二分之一以下的间隔。需要说明的是,外层3彼此的接缝4’即使稍微重叠,也没有液体漏出的问题。
如前述制作的液体收纳构件10如下完成:形成内层1、中间层2和外层3后,拔出芯棒,将筒状的成型体切成涂布工具用的液体收纳构件10所需的规定长度,在适度的温度和湿度下,干燥几小时,从而完成。
得到的液体收纳构件10与通常的纸管等相比为细径,其外径通常为20mm以下、优选15mm以下、进一步优选10mm以下,前述外径的下限通常为1mm以上、优选2mm以上。这种细径的液体收纳构件要求严格的尺寸精度。由此,液体收纳构件10的外径越小,将纸基材层叠体和包含纸基材的外层越以螺旋状缠绕时,优选使纸基材层叠体以不使其相邻面彼此重叠方式接触,且使包含纸基材的外层与该相邻面彼此接触。
液体收纳构件10的管厚通常为0.07~0.6mm、具体地为0.2~0.4mm。通过使液体收纳构件10的管厚为前述范围,从而可以收纳充足量的液体,且阻隔性改善,容易抑制液体的泄漏、劣化。
液体收纳构件10被收纳于涂布工具内,因此,对其大小有一定的限制,但以横截面最大长度计为1~20mm、具体为3~10mm。
本发明的涂布工具只要具备前述液体收纳构件10就无限制,可以为内棉式和直液式的笔用具,也可以为眼线、睫毛膏和遮瑕膏等化妆道具。
笔用具的情况下,笔尖可以为纤羽、软笔和硬笔等均可。更具体可以举出钢笔、圆珠笔、记号笔、毡头笔、修正器和毛笔等。此时,收纳于液体收纳构件10的墨的种类可以为水性(凝胶)墨和油性墨,均可,如果考虑笔的用途,则可以举出圆珠笔用、加压圆珠笔用、或记号笔用等的墨。
本发明中,涂布工具为笔用具、前述液体收纳构件10为笔用具用纸制笔芯时,显著发挥本发明的效果,故优选。
实施例
[实施例1]
[涂布工具用液体收纳构件的制造]
将用包含聚烯烃树脂的粘接剂Chemipearl S500三井化学株式会社制贴合有厚度25μm的玻璃纸(单位面积质量25g/m2、密度1.0g/cm3)与厚度6.5μm的铝箔的粘接层厚度6.5μm且总计厚度为38μm的贴合纸用原纸分切机裁切成宽13mm。
用辊型涂抹器,在作为条形的贴合纸的外侧层的铝箔侧涂布前述包含聚烯烃树脂的粘接剂12g/m2,以玻璃纸成为内侧的方式单层螺旋卷绕在纸管制造机(Langston)的芯棒的外周面。
接着,将用原纸分切机裁切成宽13mm的、厚度66μm的涂布纸(单位面积质量85g/m2)单层螺旋卷绕在作为贴合纸外侧层的铝箔上。
此时,贴合纸和涂布纸分别以不使相邻面彼此重叠而对接(butting)的方式缠绕。另外,以贴合纸彼此的接触部位与涂布纸彼此的接触部位沿长度方向错开3mm的方式缠绕。
将得到的螺旋管裁切成长度89.3mm,得到内径3.8mm的涂布工具用液体收纳构件。将前述液体收纳构件作为纸管1。
[涂布工具用液体收纳构件的评价]
(1)挥发减量的测定
在得到的纸管1中填充以下述配方制备的涂布液1 0.7g,进一步填充聚丁烯至约10mm的长度,密封涂布液的后端。
<涂布液1>(总量100质量%)
SPIRON violet C-RH[保土谷化学工业株式会社制]8%
SPIRON yellowC-GNH[保土谷化学工业株式会社制]5%
Printex#35[Degussa Japan Co.,Ltd.制]8%
聚乙烯醇缩丁醛BL-1[积水化学株式会社制]4%
聚乙烯醇缩丁醛BH-3[积水化学株式会社制]0.7%
Hilac 110H[Hitachi Chemical Co.,Ltd.制]10%
SOLSPERSE 28000[Lubrizol Japan Ltd.制]1%
(酸值:29、重均分子量:约3400)
苯并三唑0.5%
3-甲氧基-3-甲基-1-丁醇62.8%
接着,在与前述密封部相反侧的液体收纳构件端部压入不锈钢制的盖子。使塞住了两端的纸管1横放,静置在50℃10%RH的环境下10天,由涂布液的减少量求出挥发减量(%)。
纸管1的挥发减量为0.51%。
(2)弯曲试验
将支点间距设为75mm,将纸管1的中央利用弯曲楔形治具以30mm/分钟的速度挤压,将弯曲时的测定值作为弯曲强度。
纸管1的弯曲强度为1.6N。
(3)漏墨评价
使填充有涂布液1的纸管1朝下,以50℃保管4周。
按照下述评价基准、以目视评价漏墨。
A:确认不到漏墨
B:稍确认到漏墨
C:确认到显著的漏墨
使用纸管1的情况下,确认不到漏墨,评价为A。
[比较例1]
[涂布工具用液体收纳构件的制造]
实施例1中,使用丙烯酸共聚物(987B Japan Coating Resin Corporation制)代替Chemipearl S500作为粘接剂,除此之外,与实施例1同样地,制作液体收纳构件。将前述液体收纳构件作为纸管9。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管9的弯曲强度为1.5N、漏墨评价的结果为B。另一方面,挥发减量的测定中,涂布液1渗出,因此,不具有含义,记作无法测定。将结果示于表1。
[比较例2]
[涂布工具用液体收纳构件的制造]
实施例1中,使用乙烯·乙酸乙烯酯共聚物(EVA AD-92、昭和电工株式会社制)代替Chemipearl S500作为粘接剂,除此之外,与实施例1同样地,制作液体收纳构件。将前述液体收纳构件作为纸管10。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管10的弯曲强度为1.2N、漏墨评价的结果为C。另外,挥发减量中,涂布液1渗出,因此,记作无法测定。将结果示于表1。
[比较例3]
[涂布工具用液体收纳构件的制造]
实施例1中,使用乙酸乙烯酯树脂(AX-428、昭和电工株式会社制)代替ChemipearlS500作为粘接剂,除此之外,与实施例1同样地,制作液体收纳构件。将前述液体收纳构件作为纸管11。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管11的弯曲强度为1N、漏墨评价的结果为C。另外,挥发减量中,涂布液1渗出,因此,记作无法测定。将结果示于表1。
[实施例2]
[涂布工具用液体收纳构件的制造]
实施例1中,使条形的贴合纸以双层而不是以单层螺旋卷绕在纸管制造机(Langston)的芯棒的外周面,除此之外,与实施例1同样地得到液体收纳构件。将前述液体收纳构件作为纸管2。
[涂布工具用液体收纳构件的评价]
在得到的纸管2中填充涂布液1,用聚丁烯密封后端,与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管2的挥发减量为0.26%、弯曲强度为2.5N、漏墨评价的结果为A。将结果示于表1。
[比较例4]
[涂布工具用液体收纳构件的制造]
实施例2中,使用丙烯酸共聚物(987B Japan Coating Resin Corporation制)代替Chemipearl S500作为粘接剂,除此之外,与实施例2同样地,制作液体收纳构件。将前述液体收纳构件作为纸管12。
[涂布工具用液体收纳构件的评价]
在得到的纸管12中填充涂布液1,用聚丁烯密封后端,与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。将结果示于表1。
纸管12的弯曲强度为2N、漏墨评价的结果为A,但挥发减量多至2.89%。
[比较例5]
[涂布工具用液体收纳构件的制造]
实施例2中,使用乙烯·乙酸乙烯酯共聚物(EVA AD-92、昭和电工株式会社制)代替Chemipearl S500作为粘接剂,除此之外,与实施例2同样地,制作液体收纳构件。将前述液体收纳构件作为纸管13。
[涂布工具用液体收纳构件的评价]
在得到的纸管13中填充涂布液1,用聚丁烯密封后端,与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管13的弯曲强度为1.9N。漏墨评价的结果为B,但涂布液1渗出,因此,记作无法测定。将结果示于表1。
[比较例6]
[涂布工具用液体收纳构件的制造]
实施例2中,使用乙酸乙烯酯树脂(AX-428、昭和电工株式会社制)代替ChemipearlS500作为粘接剂,除此之外,与实施例2同样地,制作液体收纳构件。将前述液体收纳构件作为纸管14。
[涂布工具用液体收纳构件的评价]
在得到的纸管14中填充涂布液1,用聚丁烯密封后端,与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管14的弯曲强度为1.8N、漏墨评价的结果为B。另一方面,挥发减量的测定中,涂布液1渗出,因此,记作无法测定。将结果示于表1。
[表1]
实施例1 | 比较例1 | 比较例2 | 比较例3 | 实施例2 | 比较例4 | 比较例5 | 比较例6 | |
纸管 | 1 | 9 | 10 | 11 | 2 | 12 | 13 | 14 |
涂布液 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 |
挥发减量(%) | 0.51 | - | - | - | 0.26 | 2.89 | - | - |
弯曲强度(N) | 1.6 | 1.5 | 1.2 | 1 | 2.5 | 2 | 1.9 | 1.8 |
漏墨 | A | B | C | C | A | A | B | B |
[实施例3]
[涂布工具用液体收纳构件的制造]
实施例1中,使条形的贴合纸以双层而不是以单层螺旋卷绕在纸管制造机(Langston)的芯棒的外周面,除此之外,与实施例1同样地得到液体收纳构件。将前述液体收纳构件作为纸管3。
[涂布工具用液体收纳构件的评价]
实施例1中,代替涂布液1,在纸管3中填充涂布液2,除此之外,与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。涂布液2以下述处方制备。
<涂布液2>(总量100质量%)
FUJI RED 2510[富士色素株式会社制]8%
JONCRYL 61J[BASF Japan Ltd.制]6%
黄原胶KELSAN S[Sansho Co.,Ltd.制]0.32%
磷酸异丙酯0.5%
Bioden 421[日本曹达株式会社制]0.2%
苯并三唑0.3%
三乙醇胺1.4%
丙二醇15%
离子交换水68.28%
纸管3的挥发减量为5.59%、弯曲强度为2.5N、漏墨评价的结果为A。将结果示于表2。
[实施例4]
[涂布工具用液体收纳构件的制造]
实施例1中,使条形的贴合纸以双层而不是以单层螺旋卷绕在纸管制造机(Langston)的芯棒的外周面,除此之外,与实施例1同样地得到液体收纳构件。将前述液体收纳构件作为纸管4。
[涂布工具用液体收纳构件的评价]
实施例1中,代替涂布液1,在纸管4中填充涂布液3,除此之外,与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。涂布液3以下述处方制备。
<涂布液3>(总量100质量%)
Vinyblan GV5651[日信化学工业株式会社制]80%
(聚乙酸乙烯酯乳液;固体成分40%)
酸性染料 红227号 0.22%
黄4号0.34%
蓝1号0.08%
纯化水19.36%
纸管4的挥发减量为4.16%、弯曲强度为2.5N、漏墨评价的结果为A。将结果示于表2。
[实施例5]
[涂布工具用液体收纳构件的制造]
实施例2中,作为贴合纸,使用用包含聚烯烃树脂的粘接剂贴合厚度25μm的羊皮纸(单位面积质量25g/m2、密度1.0g/cm3)与厚度6.5μm的铝箔而成者代替玻璃纸,除此之外,与实施例2同样地得到液体收纳构件。将前述液体收纳构件作为纸管5。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管5的挥发减量为0.42%、弯曲强度为2.2N、漏墨评价为A。将结果示于表2。
[实施例6]
[涂布工具用液体收纳构件的制造]
实施例2中,作为贴合纸,使用在厚度25μm的玻璃纸(单位面积质量25g/m2、密度1.0g/cm3)上形成厚度0.4μm的二氧化硅蒸镀层而不是铝箔者,除此之外,与实施例2同样地得到液体收纳构件。将前述液体收纳构件作为纸管6。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管6的挥发减量为0.79%、弯曲强度为2.2N、漏墨评价为A。将结果示于表2。
[实施例7]
[涂布工具用液体收纳构件的制造]
实施例2中,不将涂布纸的相邻面彼此对接,而是进行重叠1mm并缠绕,除此之外,与实施例2同样地得到液体收纳构件。将前述液体收纳构件作为纸管7。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管7的挥发减量为0.28%、弯曲强度为2.5N、漏墨评价为A。将结果示于表2。
[实施例8]
[涂布工具用液体收纳构件的制造]
实施例2中,使贴合纸彼此的接触部位与涂布纸彼此的接触部位的间隔分开5mm而不是3mm,除此之外,与实施例2同样地得到液体收纳构件。将前述液体收纳构件作为纸管8。
[涂布工具用液体收纳构件的评价]
与实施例1同样地,进行挥发减量的测定、弯曲试验和漏墨评价。
纸管8的挥发减量为0.31%、弯曲强度为2.1N、漏墨评价为A。将结果示于表2。
[表2]
实施例3 | 实施例4 | 实施例5 | 实施例6 | 实施例7 | 实施例8 | |
纸管 | 3 | 4 | 5 | 6 | 7 | 8 |
涂布液 | 2 | 3 | 1 | 1 | 1 | 1 |
挥发减量(%) | 5.59 | 4.16 | 0.42 | 0.79 | 0.28 | 0.31 |
弯曲强度(N) | 2.5 | 2.5 | 2.2 | 2.2 | 2.5 | 2.1 |
漏墨 | A | A | A | A | A | A |
附图标记说明
10 涂布工具用液体收纳构件
11 接头
12 圆珠笔尖端
1 内层
2 中间层
3 外层
4、4’ 接缝
5 粘接剂层。
Claims (8)
1.一种涂布工具用液体收纳构件,其特征在于,具有包含纸基材层叠体和外层的至少三层,
所述纸基材层叠体具备:纸基材的内层、和形成于所述内层的外表面侧、且为金属层或二氧化硅蒸镀层的中间层。
所述外层形成于所述中间层的外表面侧、且包含纸基材,
所述涂布工具用液体收纳构件具有如下结构:将所述纸基材层叠体以螺旋状缠绕的结构、和将所述包含纸基材的外层以螺旋状缠绕于所述中间层的外表面侧的结构,且
在所述内层与中间层之间和所述中间层与外层之间的至少一者中具有包含聚烯烃树脂的粘接剂的层。
2.根据权利要求1所述的涂布工具用液体收纳构件,其中,所述纸基材层叠体的宽度方向的长度为4~20mm。
3.根据权利要求1或2所述的涂布工具用液体收纳构件,其中,所述内层的纸基材的密度为0.8g/cm3以上。
4.根据权利要求1~3中任一项所述的涂布工具用液体收纳构件,其特征在于,所述内层的纸基材为玻璃纸、羊皮纸或硬化纸板。
5.根据权利要求1~4中任一项所述的涂布工具用液体收纳构件,其具有如下结构;
沿涂布工具用液体收纳构件的长度方向,
使所述纸基材层叠体以不使其相邻面彼此重叠方式接触并缠绕成螺旋状的结构、和
使所述包含纸基材的外层以使其相邻面彼此接触的方式缠绕成螺旋状的结构。
6.根据权利要求1~5中任一项所述的涂布工具用液体收纳构件,其中,具有两组以上的所述纸基材层叠体。
7.根据权利要求1~6中任一项所述的涂布工具用液体收纳构件,其中,
所述纸基材层叠体彼此的接触部位、与
所述包含纸基材的外层彼此的接触部位沿涂布工具用液体收纳构件的长度方向、错开1mm以上且错开所述纸基材层叠体或所述包含纸基材的外层的宽度的二分之一以下。
8.根据权利要求1~7中任一项所述的涂布工具用液体收纳构件,其为笔用具用纸制笔芯。