CN116410631A - 凹版抗粘连金属油墨、及其制品、制备和应用 - Google Patents
凹版抗粘连金属油墨、及其制品、制备和应用 Download PDFInfo
- Publication number
- CN116410631A CN116410631A CN202310312581.1A CN202310312581A CN116410631A CN 116410631 A CN116410631 A CN 116410631A CN 202310312581 A CN202310312581 A CN 202310312581A CN 116410631 A CN116410631 A CN 116410631A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- vinyl chloride
- gold powder
- polyethylene wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种凹版抗粘连金属油墨、及其制品和应用。所述凹版抗粘连金属油墨，包括：8‑12份重量计的丙烯酸树脂；10‑15份重量计的氯醋树脂；10‑20份重量计的聚氨酯树脂；20‑30份重量计的金粉；0.5‑3份重量计的聚乙烯蜡；15‑20份重量计的乙酸正丙酯；10‑20份重量计的乙酸乙酯，以及3‑8份重量计的异丙醇。
Description
技术领域
本发明涉及一种凹版抗粘连金属油墨、及其制品、制备和应用。
背景技术
目前，凹版金属油墨主要组成部分是色料及连结料。其中，色料起显示颜色的作用，色料又分为有机色料及无机色料。目前常见的凹版金属油墨以铜金粉作为颜色料，在大表面张力的薄膜上表现良好，但在低表面张力的薄膜上附着力不佳（尤其是对于BOPP膜），印刷后容易脱落被材料另外一面粘住。
发明内容
本发明提供了一种凹版抗粘连金属油墨、及其制品、制备和应用，可以有效解决上述问题。
本发明是这样实现的：
本发明进一步提供一种凹版抗粘连金属油墨，包括：8-12份重量计的丙烯酸树脂；10-15份重量计的氯醋树脂；10-20份重量计的聚氨酯树脂；20-30份重量计的金粉；0.5-3份重量计的聚乙烯蜡；15-20份重量计的乙酸正丙酯；10-20份重量计的乙酸乙酯，以及3-8份重量计的异丙醇。
本发明进一步提供一种薄膜制品，包括：
低表面张力材料薄膜；以及
凹版抗粘连金属油墨，其中，其包括：8-12份重量计的丙烯酸树脂；10-15份重量计的氯醋树脂；10-20份重量计的聚氨酯树脂；20-30份重量计的金粉；0.5-3份重量计的聚乙烯蜡；15-20份重量计的乙酸正丙酯；10-20份重量计的乙酸乙酯，以及3-8份重量计的异丙醇。
本发明进一步提供一种上述凹版抗粘连金属油墨的应用。
本发明提供一种上述凹版抗粘连金属油墨的制备方法，包括：
将乙酸正丙酯、乙酸乙酯，以及异丙醇均匀混合；
然后依次加入丙烯酸树脂、氯醋树脂、聚氨酯树脂、聚乙烯蜡以及金粉，充分均质搅拌，然后过滤包装。
本发明的有益效果是：本发明提供的凹版抗粘连金属油墨，具有良好的金属效果，且在OPP处理面的附着牢度可以大于60%（显著高于现有的属油墨的20%）。另外，本发明的凹版抗粘连金属油墨还具有长时间存放稳定性的效果，大大提高了凹版抗粘连金属油墨的性能。最好，本发明的制备方法，还具有简单易行，易于工业化生产等特点。
附图说明
为了更清楚地说明本发明实施方式的技术方案，下面将对实施方式中所需要使用的附图作简单地介绍，应当理解，以下附图仅示出了本发明的某些实施例，因此不应被看作是对范围的限定，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他相关的附图。
图1是本发明实施例提供的凹版抗粘连金属油墨制备方法流程图。
具体实施方式
为使本发明实施方式的目的、技术方案和优点更加清楚，下面将结合本发明实施方式中的附图，对本发明实施方式中的技术方案进行清楚、完整地描述，显然，所描述的实施方式是本发明一部分实施方式，而不是全部的实施方式。基于本发明中的实施方式，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施方式，都属于本发明保护的范围。因此，以下对在附图中提供的本发明的实施方式的详细描述并非旨在限制要求保护的本发明的范围，而是仅仅表示本发明的选定实施方式。基于本发明中的实施方式，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施方式，都属于本发明保护的范围。
参照图1所示，本发明实施例提供一种凹版抗粘连金属油墨，包括：8-12份重量计的丙烯酸树脂；10-15份重量计的氯醋树脂；10-20份重量计的聚氨酯树脂；20-30份重量计的金粉；0.5-3份重量计的聚乙烯蜡；15-20份重量计的乙酸正丙酯；10-20份重量计的乙酸乙酯，以及3-8份重量计的异丙醇。
所述金粉一般为过800-1200目筛网的金粉。
作为进一步改进的，优选的，所述氯醋树脂选自羟基氯醋树脂，其不仅仅对有机颜料及无机颜料（金粉）有优良的分散性，还可以提高凹版抗粘连金属油墨的吸附性能。
优选的，所述凹版抗粘连金属油墨包括：包括：9-11份重量计的丙烯酸树脂；11-13份重量计的氯醋树脂；13-16份重量计的聚氨酯树脂；24-26份重量计的金粉；1.5-2.5份重量计的聚乙烯蜡；15-18份重量计的乙酸正丙酯；14-16份重量计的乙酸乙酯，以及4-6份重量计的异丙醇。在其中一个实施例中，所述凹版抗粘连金属油墨包括：10份重量计的丙烯酸树脂；12份重量计的氯醋树脂；15份重量计的聚氨酯树脂；25份重量计的金粉；2份重量计的聚乙烯蜡；16份重量计的乙酸正丙酯；15份重量计的乙酸乙酯，以及5份重量计的异丙醇。
本发明实施例提供的所述凹版抗粘连金属油墨，可以用于表面未处理的BOPP膜。
本发明实施例进一步提供一种薄膜制品，所述薄膜制品包括：
低表面张力材料薄膜；以及印刷于所述低表面张力材料薄膜的凹版抗粘连金属油墨。
本发明实施例还进一步提供一种上述凹版抗粘连金属油墨在低表面张力材料的应用。
请参见图1，本发明实施例还进一步提供一种上述凹版抗粘连金属油墨的制备方法，包括：
将乙酸正丙酯、乙酸乙酯，以及异丙醇均匀混合；
然后依次加入丙烯酸树脂、氯醋树脂、聚氨酯树脂、聚乙烯蜡以及金粉，充分均质搅拌，然后过滤包装。
实施例1：
将16份重量计的乙酸正丙酯；15份重量计的乙酸乙酯，以及5份重量计的异丙醇均匀混合，然后依次加入10份重量计的丙烯酸树脂、12份重量计的氯醋树脂、15份重量计的聚氨酯树脂、2份重量计的聚乙烯蜡以及25份重量计的金粉充分均质搅拌，然后过滤包装。
对比例1：市售某品牌凹版抗粘连金属油墨。
对比例2：
将16份重量计的乙酸正丙酯；15份重量计的乙酸乙酯，以及5份重量计的异丙醇均匀混合，然后依次加入10份重量计的丙烯酸树脂、5份重量计的氯醋树脂、15份重量计的聚氨酯树脂、2份重量计的聚乙烯蜡以及25份重量计的金粉充分均质搅拌，然后过滤包装。
对比例3：
将16份重量计的乙酸正丙酯；15份重量计的乙酸乙酯，以及5份重量计的异丙醇均匀混合，然后依次加入10份重量计的丙烯酸树脂、0份重量计的氯醋树脂、15份重量计的聚氨酯树脂、2份重量计的聚乙烯蜡以及25份重量计的金粉充分均质搅拌，然后过滤包装。
对比例4：
将16份重量计的乙酸正丙酯；15份重量计的乙酸乙酯，以及5份重量计的异丙醇均匀混合，然后依次加入10份重量计的丙烯酸树脂、20份重量计的氯醋树脂、15份重量计的聚氨酯树脂、2份重量计的聚乙烯蜡以及25份重量计的金粉充分均质搅拌，然后过滤包装。
测试例，分别用实施例1和对比例1-3的凹版抗粘连金属油墨用14微米的涂布器涂布于低表面张力材料薄膜上，用60℃烘箱干燥1分钟，对涂层性能进行检验和评定。对上述凹版抗粘连金属油墨进行测试如下：
从上述表格可以看出，随着氯醋树脂的重量增加到20份，其粘度显著增加，进而不利于凹版抗粘连金属油墨的稳定存储。进一步的，当氯醋树脂的重量减少到10份以下时，其粘附度显著降低，且易于粉化（即金属颜料停留于表面，造成容易从承印物中脱落）。
以上所述仅为本发明的优选实施方式而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种凹版抗粘连金属油墨，其特征在于，包括：8-12份重量计的丙烯酸树脂；10-15份重量计的氯醋树脂；10-20份重量计的聚氨酯树脂；20-30份重量计的金粉；0.5-3份重量计的聚乙烯蜡；15-20份重量计的乙酸正丙酯；10-20份重量计的乙酸乙酯，以及3-8份重量计的异丙醇。
2.如权利要求1所述的凹版抗粘连金属油墨，其特征在于，包括：9-11份重量计的丙烯酸树脂；11-13份重量计的氯醋树脂；13-16份重量计的聚氨酯树脂；24-26份重量计的金粉；1.5-2.5份重量计的聚乙烯蜡；15-18份重量计的乙酸正丙酯；14-16份重量计的乙酸乙酯，以及4-6份重量计的异丙醇。
3.如权利要求1所述的凹版抗粘连金属油墨，其特征在于，包括：10份重量计的丙烯酸树脂；12份重量计的氯醋树脂；15份重量计的聚氨酯树脂；25份重量计的金粉；2份重量计的聚乙烯蜡；16份重量计的乙酸正丙酯；15份重量计的乙酸乙酯，以及5份重量计的异丙醇。
4.一种薄膜制品，其特征在于，包括：
低表面张力材料薄膜；以及
凹版抗粘连金属油墨，其中，其包括：8-12份重量计的丙烯酸树脂；10-15份重量计的氯醋树脂；10-20份重量计的聚氨酯树脂；20-30份重量计的金粉；0.5-3份重量计的聚乙烯蜡；15-20份重量计的乙酸正丙酯；10-20份重量计的乙酸乙酯，以及3-8份重量计的异丙醇。
5.如权利要求4所述的薄膜制品，其特征在于，所述低表面张力材料薄膜为BOPP膜。
6.一种如权利要求1所述的凹版抗粘连金属油墨的应用。
7.一种如权利要求1所述凹版抗粘连金属油墨的制备方法，其特征在于，包括：
将乙酸正丙酯、乙酸乙酯，以及异丙醇均匀混合；
然后依次加入丙烯酸树脂、氯醋树脂、聚氨酯树脂、聚乙烯蜡以及金粉，充分均质搅拌，然后过滤包装。